In this work, narrow-band green-emitting CsPbBr3 particles are embedded in commercialized glass composites by a facile dry process. By optimizing the method through sintering in glass frit (GF) composites including CsBr and PbBr2, used as precursors, the encapsulation of CsPbBr3 particles made them waterproof with green fluorescence. To improve the fluorescent properties by reducing aggregation of CsPbBr3, fumed silica (FS) is additionally used to help particles avoid bulking up in the glass matrix. The CsPbBr3 perovskite/glass composites are characterized using scanning electron microscopy (SEM) images and energy-dispersive X-ray spectroscopy (EDS) maps, which support the existence of CsPbBr3 particles in the glass matrix. The photoluminescence (PL) properties demonstrate that the emission spectrum peak, full width at half maximum (FWHM), and photoluminescence quantum yield (PLQY) values are 519 nm, 17 nm, and 17.7 %. We also confirm the water-resistant properties. To enhance water/moisture stability, the composite sample is put directly into water, with its PLQY monitored periodically under UV light.

친수성 및 소수성 나노실리카를 tetraethyl orthosilicate(TEOS)를 커플링제로 사용하여 유리 표면에 거친 스파이크 구조 형성과 반응성 hydroxyl기를 동시에 도입한 후 불소를 함유한 실란으로 2차 코팅처리하여 궁극적으로 발수성 유리 표면 형성의 최적 조건을 확립하는 연구를 수행하였다. 소수 성 나노실리카인 실리카 에어로졸을 이용한 초소수 도막의 형성은 나노실리카 표면에 반응성인 -OH기가 존재하지 않아 내구성이 있는 소수성 도막을 형성할 수 없었다. 이에 반하여 친수성기를 가진 나노 실리카와 가수분해된 TEOS를 포함하는 코팅액 이용하여 유리 표면을 1차 코팅한 후 2차로 trichloro-(1H,1H,2H,2H)perfluorooctylsilane(TPFOS) 용액으로 코팅하여 150o 이상의 수접촉각을 가지는 초소수 표면을 제조하였으며, 1o 이하의 물 슬라이딩각을 보여 초발수성도 동시에 가지고 있었다. 이에 덧붙여 친수성 나노실리카의 함량이 증가할수록 광투과도가 감소하였으며, TPFOS 용액에 의해서도 광투과도가 감소하였다. 코팅된 유리시편의 내구성 50회 문지름까지는 초소수성을 유지하였으나, 200회 문지름에서는 단지 소수성만을 유지하였다. 결론적으로 최적의 코팅액의 조건은 친수성 나노실리카의 함량이 0.3 g인 HP3 코팅액을 2회 코팅한 후 2차로 TPFOS 용액으로 코팅하는 것이었다. 이렇게 제조된 코팅액은 광투과도가 중요한 솔라셀의 표면 처리제로 사용이 가능할 것으로 판단된다.

Glass wool is widely used as a typical soundproofing material because it has superior characteristics as a soundproofing material as well as excellent marketability. However, moisture penetration through condensation and cleaning up causes deterioration of insulation and soundproofing performance. In this study, we evaluate the wettability and sound absorption performance when the metal is deposited on the surface of glass wool. The performance is examined based on parameters such as the angle test, drying speed, the absorbency, the moisture content, the wettability. The wettability data shows that Cu coated glass wool is the best performance compaed to Ti coated one. The sound insulation characteristics are also compared by using the impedance tube. At the low frequency range, there is no difference among the test specimens, however, at the frequency above the 250 Hz range, Cu coating shows 10 % better in th sound asorption. Ti coating has almost same to the existing glasss wool performance. It turns out that metal coating on the glass wool seems to be very promising: the metal deposition reveals strong water repellency and sound absorption performance is equivalent to the existing glass wool.

Glass wool is a fiber made by melting sand and waste glass at high temperature. It has been used as an inorganic fiber for sound absorption, insulation, and non-combustible materials for automobiles, ships, and household appliances. However, the disadvantage comes from the moisture penetration through condensation and cleaning up so that it deteriorates insulation and soundproofing performance. In order to overcome the disadvantages of glass wool, we investigate the water repellency by plating metal on the surface of glass wool with Cu and Ti while coating stability is considered. The thickness of the deposited metal is about 300 nm. The deposition chemicals and the image of the specimen are analyzed by using SEM equipment. The electron microscopic result shows that quite amount of Cu and Ti metals are deposited on the glass wool surface.

Synthesis of nano-silica using water glass in a Sol-Gel process is one of several methods to manufacture nano-silica. In nano-silica synthesized from water glass, there are various metal impurities. However, synthesis of nano-silica using water glass in a Sol-Gel process is an interesting method because it is relatively simple and cheap. In this study, nano-silica was synthesized from water glass; we investigated the effect of pH on the synthesis of nano-silica. The morphology of the nanosilica with pH 2 was flat, but the surface of the nano-silica with pH 10 had holes similar to small craters. As a result of ICPOES analysis, the amount of Na in the nano-silica with pH 2 was found to be 170 mg/kg. On the other hand, the amount of Na in the nano-silica with pH 10 was found to be 56,930 mg/kg. After calcination, the crystal structure of the nano-silica with pH 2 was amorphous. The crystal structure of the nano-silica with pH 10 transformed from amorphous to tridymite. This is because elemental Na in the nano-silica had the effect of decreasing the phase transformation temperature

Silica nano-powder (SNP) is an inorganic material able to provide high-performance in various fields because of its multiple functions. Methods used to synthesize high purity SNP, include crushing silica minerals, vapor reaction of silica chloride, and a sol-gel process using TEOS and sodium silicate solution. The sol-gel process is the cheapest method for synthesis of SNP, and was used in this study. First, we investigated the shape and the size of the silica-powder particles in relation to the variation of HCl and sodium silicate concentrations. After drying, the shape of nano-silica powder differed in relation to variations in the HCl concentration. As the pH of the solution increased, so did the density of crosslinking. Initially, there was NaCl in the SNP. To increase its purity, we adopted a washing process that included centrifugation and filtration. After washing, the last of the NaCl was removed using DI water, leaving only amorphous silica powder. The purity of nano-silica powder synthesized using sodium silicate was over 99.6%.

Geopolymer is a term covering a class of synthetic aluminosilicate materials with potential use in a number of areas, but mainly as a replacement for Portland cement. In this study, geopolymers with fly ash and meta kaolin were prepared using KOH as an alkali activator and water glass. The effect of water glass on the microstructures and the compressive strength of the geopolymer was investigated. As the amount of water glass increased, the dissolved inorganic binder particles in the geopolymers increased due to polymerization, resulting in a dense microstructure. The meta kaolin-based geopolymer showed a better extent of polymerization and densification than that of the fly ash-based geopolymer. XRD data also suggested that polymerization in meta kaolin-based geopolymers should be active resulting in the formation of an amorphous phase with an increasing amount of water glass. The compressive strength of the geopolymer was also dependent on the amount of water glass. The compressive strength of the geopolymers from both fly ash and meta kaolin increased with an increasing amount of water glass because water glass improved the extent of polymerization of the inorganic binder and resulted in a dense microstructure. However, the addition of water glass to the geopolymer did not seem to be effective for the improvement of compressive strength because the meta kaolin-based geopolymer mainly consisted of a clay component. For this reason, the fly ash-based geopolymer showed a higher value of compressive strength than the meta-kaolin geopolymer.

The present research was undertaken to evaluate the possibility of water purification filter with activated carbon fibers (ACFs) using a very low cost precursor consisting of phenolic resin coated on glass fibers. The simplified procedure involving coating, curing and activation and a very low cost glass fiber as a raw material were adopted in order to reduce manufacturing cost. The breakthrough curves of the manufactured ACFs and the commercial activated carbon (AC, Calgon F-200) were investigated in the initial concentration range from 19 to 49 ppm for benzene, toluene and ethylbenzene. From breakthrough profiles, the manufactured ACFs had significantly faster adsorption kinetics than the AC. Especially the benzene breakthrough curves, the manufactured ACF (13 g of ACF with 32% of carbon on the glass) was over the limited level (5 ppb) after flowing of 32 l at initial concentration of 15 ppm, while the commercial AC was shown about 3 ppm in initial adsorption.

GFRP복합재료의 피로거동은 하중형식, 재질 및 섬유의 강화구조, 환경적인 인자들의 영향을 크게 받는것으로 알려져 있다. 본 연구에서는GFRP의 피로거동에 미치는 증류수 흡습의 영향을 알아보기 위해 chopped strand glass mat강화 불포화 polyester수지 복합재료의피로특성을 조사하였다. 피로균열은 건조재와 흡습재 모두 피로 cycle초기에 발생하며 그 후 균열성장이 점차 둔화되는 영역과 가속되는 영역으로 나뉘어졌다. 또한 증류수의 흡습은 섬유와 기지재 사이의 결합력을 저하시키며 그로 인해 균영성장방향에 수직인곳에서의 fiber pull-out 발생과 균열성장방향에 있는 섬유들에서의 debonding이 증가하여 피로강도가 저하하였다.

기후 변화가 가속화되어 국내에서는 국지성 호우가 증가하는 추세이며, 이에 대해 도심지역 토지의 불투수층이 증가하여 도로 유출수, Combined Sewer Overflows(이하 CSOs라고 한다.) 등 도심에서의 비점오염원에 의하여 하천 수중생물의 폐사, 부영양화, 대장균 및 병원성 미생물의 증가, 중금속 오염 등의 방류 수계에 타격을 줄 수 있기 때문에 이에 따른 환경오염 문제가 대두되고 있다. 그 중에서도 CSOs는 합류식 하수도 시스템에서 강우 시에 처리시설을 거치지 않고 하천이나 해안 등의 수계로 직접 방류되는 경우를 의미하며, 해당 오염 부하량은 강우의 지속시간 및 강우량에 큰 영향을 받는다. 이 때 합류식 하수관로에서는 관로 내부의 퇴적물이 강우 초기에 유출되는 초기세척효과(first flush effect)에 의해 강우 초기에 오염부하량이 높은 값으로 유출된다. 이런 CSOs에 대하여 현재 국내에는 3Q로 차집한 용량에 대하여 2Q의 월류수를 스크리닝 및 완충저류로 이루어진 간이처리만을 통하여 수계로 배출되고 있는 실정이다. 이러한 CSOs의 주된 오염물질은 입자성 물질이 가장 큰 비율을 차지한다. 환경부에서 제시한 임의의 도시지역 하수 평균 SS는 60 mg/L의 값을 나타내는데 강우 초기의 CSOs의 SS는 1,936 mg/L의 값으로 고농도의 값을 나타낸다. 이러한 입자성 물질을 제거해 줌으로써 입자성 물질에 영향을 받는 다른 항목에 대해서도 그 농도를 낮출 수 있다. 이에 본 연구에서는 CSOs의 입자성 물질을 제거하기 위한 공정으로 여과(filtration)방법을 선정하였으며, 여과용 담체로는 폐유리를 발포시켜 제조한 여재를 사용하였다. 여과속도 및 여과층 구성에 따른 SS제거효율 및 폐색된 여재의 효율을 복구시키기 위한 역세척 조건에 따른 역세척 효율에 대해 알아보고자 하였다.