A study on the corrosion inhibition of metals is important in many industrial applications (carbon steel, copper, aluminum, SUS 304, nickel). In this study, we investigated the C-V diagrams related to the surface corrosion of metals. It was observed through the SEM that the surface corrosion state of the various metals had the corrosion potential by the scan rate and the organic inhibitor containing an amine group. We determined to measure cyclic voltammetry using the three-electrode system. The measurement of oxidation and reduction ranged from -1350mV to 1650mV. The scan rate was 50, 100, 150, and 200mV/s. It turned out that the C-V characterization of SUS 304 was irreversible process caused by the oxidation current from the cyclic voltammogram. After adding organic inhibitors, the adsorption film was constituted, and the passive phenomena happened. As a result, it was revealed that the inhibition effect of metal corrosion depends on the molecular interaction, and the interaction has influence on the adsorption complex.

In this research, the welding experiment was carried out with both the steel materials (SS400+SS400, SUS304+SUS304) and the different steel materials (SS400+ SUS304), where SS400 is a general structural rolled steel material and SUS304 is a cold strip stainless steel sheet. The average of yield point of a SS400 experimental piece was the most highest point with 2015.54 N/m2. Although welding defects were not found with the naked eye, it was sure that there were some wilding defects because there were no stress against load through experiments. The rate of yield point of experimental piece A, experimental piece B and experimental piece C was respectively 1.7mm, 1.3mm and 2.6mm. The rate of breakdown was respectively 39.77mm, 17.97mm and 2.6mm. So considering price and efficiency with use condition is very important. SS400 and SUS304 will be profited from considering price and mechanical property with use condition.

본 연구는 사문암 토양의 화학적 성질과 토양미생물량 및 토양효소 등 토양의 생물학적 활성을 대조구의 비사문암 토양과 비교하고, 사문암과 비사문암에서 공통으로 서식하는 새(Arundinella hirta)와 억새(Miscanthus sinensis var. purpurascens)의 낙엽이 입지가 다른 사문암지역과 비사문암 지역에서 분해될 때 분해율의 차이가 어떻게 유발되는지 9개월 동안 야외에서 교차 실험하였다. 사문암 토양은 비사문암 토양에 비하여 높은 pH, 낮은 dehydrogenase 와 urease활성을 나타내었으며 alkaliphosphatase의 활성은 높았다. 두 토양에서 microbial biomass-C와 N의 차이는 유의하지 않았으나 사문암 토양에서 microbial biomass-N함량이 더 높게 나타나 비사문암 토양에서 보다 낮은 토양의 C/N을 나타내는 원인이 되었다. 사문암지역에서의 낙엽분해실험에서는 사문암지역에서 획득한 새와 억새 낙엽이 각각 39.8%, 38.5%의 중량감소를 보였으며, 비사문암 토양에서 획득한 낙엽은 각각 41.1%, 41.7%의 중량감소를 나타내었다. 비사문암지역에서의 낙엽분해실험에서는 사문암낙엽이 46.8%, 42.2% 그리고 비사문암낙엽은 44.8%, 37.4%의 중량감소를 각각 보였다. 이러한 결과는 중금속을 포함하는 토양의 영향보다는 낙엽의 질적 차이가 분해율에 더 큰 영향을 미쳤음을 나타내준다. 일반적으로 낮은 C/N을 갖는 낙엽이 더 빨리 분해된다는 결과와는 달리 낮은 C/N을 갖는 사문암낙엽의 분해가 느린 것은 낙엽에 포함된 중금속의 저해가 낙엽의 C/N이나 lignin/N과 같은 낙엽의 질적 차이에서 유발되는 낙엽분해의 저해보다 큰 영양을 미친다는 결과를 보여주었다. 또한 낙엽분해가 진행되는 동안 낙엽내의 Cr, Ni과 Mg, Fe의 농도는 점차 증가하였으며 이러한 경향은 사문암지역에서 현저하였다.

For this paper, we investigated the area specific resistance (ASR) of commercially available ferritic stainless steels with different chemical compositions for use as solid oxide fuel cells (SOFC) interconnect. After 430h of oxidation, the STS446M alloy demonstrated excellent oxidation resistance and low ASR, of approximately 40 mΩcm2, of the thermally grown oxide scale, compared to those of other stainless steels. The reason for the low ASR is that the contact resistance between the Pt paste and the oxide scale is reduced due to the plate-like shape of the Cr2O3(s). However, the acceptable ASR level is considered to be below 100 mΩcm2 after 40,000 h of use. To further improve the electrical conductivity of the thermally grown oxide on stainless steels, the Co layer was deposited on the stainless steel by means of an electroless deposition method; it was then thermally oxidized to obtain the Co3O4 layer, which is a highly conductive layer. With the increase of the Co coating thickness, the ASR value decreased. For Co deposited STS444 with 2 μmhickness, the measured ASR at 800˚ after 300 h oxidation is around 10 mΩcm2, which is lower than that of the STS446M, which alloy has a lower ASR value than that of the non-coated STS. The reason for this improved high temperature conductivity seems to be that the Mn is efficiently diffused into the coating layer, which diffusion formed the highly conductive (Mn,Co)3O4 spinel phases and the thickness of the Cr2O3(S), which is the rate controlling layer of the electrical conductivity in the SOFC environment and is very thin

본 연구는 중금속이 낙엽의 분해에 미치는 영향을 알아보기 위하여 충남 청양의 폐금광의 광미에 분포하는 쑥(Artemisia princeps var. orientalis)과 쇠뜨기(Equisetum arvense)를 이용하여 실험하였다. 광미는 높은 중금속 함량과 낮은 유기물 함량을 가지고 있었다. 광미의 중금속 함량은 대조구 토양에 비해 비소(As)는 약 13배, 카드뮴(Cd)은 약 28배 높은 것으로 나타났다. 또한 크롬(Cr), 니켈(Ni) 및 아연(Zn)은 약 3배에서 6배 높게 측정되었다. 광미와 대조구 토양에서 채집한 식물체내의 중금속 함량은 광미에서 채집한 식물에서 현저히 높게 나타났으며, 쑥 잎의 경우 As는 약 23배, Cd은 25배 높게 나타났으며, 쇠뜨기 지상부의 경우 As는 58배, Cd은 11배 높은 것으로 나타났다. 대조구에서 분해 결과 중금속 농도가 높은 쑥의 잎과 대조구에서 채취한 잎이 각각 50.4%, 65.7%가 분해되었다. 또한 광미에서 진행된 분해 결과 쑥의 잎은 폐광지역에서 채취한 잎과 대조구에서 채취한 잎이 각각 31.6%, 57.5%가 분해되었다. 쑥의 줄기의 분해결과도 잎의 분해율과 비슷한 양상을 나타내었다. 쇠뜨기의 지상부의 분해는 대조구에서 분해된 결과 광미에서 채집된 쇠뜨기와 대조구에서 채집한 쇠뜨기가 각각 77.8%와 89.3%가 분해되었으며, 광미지역에서 분해 결과 각각 67.6%와 82.1%가 분해된 것으로 나타났다. 따라서 광미에서 생육하는 식물체의 중금속의 함량이 높을수록 분해가 느린 것으로 나타났으며, 이는 중금속이 낙엽의 분해에 영향을 미친 것이라고 판단된다.

본 연구에서는 2006년부터 2008년까지 3년간 봄철에 PM10과 PM2.5를 채취하여 질량농도와 금속원소의 화학적 특성, 기상인자와의 관계 분석, 황사 및 비황사시의 미세먼지 특성 그리고 이동경로에 따른 농도의 특성을 고찰하였다. 연구기간동안의 PM10, PM2.5, PM10-2.5평균농도는 각각 126.2±89.8, 85.5±41.6, 40.7±54.9μg/m3이었으며 PM2.5/PM10 및 PM10-2.5/PM2.5 비는 각각 0.70, 0.48이었다. 우리나라의 북서쪽인 북경을 포함한 지역과 서쪽인 상해를 포함한 지역에서 공기덩어리가 이류 할 때 가장 높은 미세먼지농도를 나타내었다.

The investigation was initiated with data from 27 abandoned mines along with 12 locations in Kyongbuk abandoned mines. The analyses for soil pollution by heavy metal pollutants were conducted by using correlation analysis, cluster analysis, and principal component analysis. The correlation analysis indicated that Ni and pH were highly correlated compared to those of other heavy metal ions. The principal component analyses showed that the heavy metal ions might be classified into two catagories, such as antropogenic and lithogenic components. The cluster analysis was also clearly divided by two groups. The respective two groups might be Pb-Zn-Cd-Cu and As-Hg-Ni.

EAF dust which is contained around 30% of zinc, 15% of iron and 3% of lead individually, is chemically treated by ammonium chloride, ammonia water, ammonia gas and carbon dioxide, and also tested and identified the ratios of the recovery of In by applied the variations of particle size, pH and heating temperature as well, in order to getting optimized recovery of the In metal after performing all of those processes. Experimental results showed that the rate of Zn recovery is 97% when the mixture of 1.3 of NH4Cl/EAF is heated to the temperature of 400℃ and leached by water, and 95% recovery of In when ammonia gas and carbon dioxide is added simultaneously and adjust the 9.5 of pH to the same mixture above. For the purpose of remove the impurities in the mixed sample, which is prepared by the two samples, indicated above showing as the ratio of 95% and 97% recovery, in case of applied the cementation process to it, and also by electrolytic process, produced the In plate of 95~97%, and acquired 99-99.5% of In metal ingot finally by applied the heating process at 470~500℃.

본 연구는 양성전해질막의 금속이온 특성을 조사하기 위하여 Taurine (TAU)막을 제조하였다. 제조방법으로는 방사선조사법에 의한 Glycidyl methacrylate (GMA)의 중공사막 표면위에 고정시키고, 이후 Taurine의 염기성 부분인 -NH2기(amine fuction)와 GMA의 glycididyl의 개환 반응을 통하여 안정된 막을 형성하도록 하였다. 한편 TAU막과 비교를 위해 GMA가 고정된 중공사 막에 Sodium sulfite로 화학적 결합을 형성 SS막을 제조하였다. 이렇게 제조된 TAU막의 타우린 밀도가 높아져도 투과유속은 0.9 m/h로 변화 없으나, SS막은 술폰산기의 밀도가 높아짐에 따라 투과유속이 급격히 감소하는 것을 나타내었다. 타우린 밀도가 0.8 mmol/g인 막을 사용한 결과 금속이온의 량은 Cu > Cd > Mg > Sb > Pb의 순으로 나타내었다. 전반적으로 타우린막은 전화율과 밀도의 증가에 따라 많은 양의 금속이온 흡착과 높은 투과유속을 나타내었다.