Most Recently, with rapid development in marine industries such as marine structures and ship, there occurs much interest in the study of corrosion characteristics which play an important role in design of cooling water system like heat-exchanger. Especially, as operating environment of fresh cooling water system in vessels is acidified, this system is seriously corroded. In this study, to study on the corrosion characteristics of Al-alloy shell for cooler, the electrochemical polarization test of materials for the marine fresh water cooler such as Al-alloy, Cu and naval brass was carried out in fresh water. And thus the polarization resistance and anodic polarization behavior of Al-alloy, Cu and naval brass are investigated. Also, galvanic corrosion characteristics of Al-alloy coupled with Cu and naval brass is considered. The main results obtained are as follows ; (1) The current density of corrosion is high in order of Al-alloy > naval brass > Cu (2) As anodic potential increases, the corrosion resistance of naval brass is better than that of Cu. (3) The galvanic corrosion of Al-alloy coupled with Cu and naval brass is activated than corrosion of Al-alloy.

Acidic degreasing agent(AADA) was prepared by blending sorbitol, Newpol PE-68, Na-dioctyl sulfosuccinate, Tetronix T-70l, MJU-100A, n-octanoic acid, and phosphoric acid, The physical properties of AADA tested with aluminum specimen showed the following results ; when 3wt% AADA-5 was performed at 70℃, the degreasing rate was 95% which is comparitively good, and the percentage of etching was 0.277% which was found to be less than that of commercialized product. when 20wt% of AADA-5 was added at 65℃, the percentage of derusting was 91% and the good defoaming effect proved by following low foaming power tests respectively : Ross and Miles, and Ross and Clark methods.

A study to analyze and solve problems of multi wire installation duct experiment has presented in this paper. We have taken Taguchi's parameter design approach, specifically orthogonal array, and determined the optimal levels of the selected variables through analysis of the experimental results using S/N ratio.

A nitrogen gas atomized aluminum powder was consolidated by powder-in sheath rolling method. A pure aluminum tube with outer diameter of 12 mm and wall thickness of 1mm was used as a sheath. The aluminum tube filled with the aluminum powder, first, was cold-rolled to the thickness of 6mm for performing, and then consolidated by the cold rolling and/or subsequent hot rolling at 360, 460 and . The aluminum powder compact fabricated by the sheath rolling showed high relative density more than 0.96 at any rolling conditions. The 0.2% proof stress increased with increasing hot rolling reduction and hot rolling temperature. Tensile strength was hardly affected by change in the hot rolling reduction, whereas it decreased with increasing hot rolling temperature. The powder compact showed the large elongation when cold rolling or hot rolling reduction was large. It was found that the sheath rolling was an effective method for consolidation of aluminum powder.

본 논문에서 알루미늄 하니콤 샌드위치판 구조(AHSP)의 특성에 대해 해석한 결과는 다음과 같다. 1) AHSP의 H/T비가 낮아질수록 응력이 감소하며, 셀 크기(H)보다는 코어의 두께(T)가 두꺼워질수록 강도와 강성이 증가함을 알 수 있다. 2) AHSP 구조가 동일한 질량에서부터 증가하면서 EASP 구조에 비해 2.5～6.0배 정도의 높은 강도를 보이는 것을 알 수 있다. 3) AHSP의 면재의 두께변화는 AHSP 전체의 강성에 별로 영향을 미치지 못했으나, 심재의 두께가 증가할수록 단면 2차 모멘트의 값이 커지기 때문에 AHSP의 강성이 매우 커짐을 알 수 있다. 4) EASP보다 강성이 큰 AHSP의 고유진동수가 크며, 진동 모드 사이의 차도 커짐을 알 수 있다. 5) 비교연구 결과 AHSP 구조가 EASP 구조보다 적은 질량으로 훨씬 더 높은 강성을 갖는, AHSP 구조의 우수성이 입증된다. 따라서 중량경감이 가장 중요한 문제 중의 하나인 초고속선 및 대형선의 경우 AHSP 구조가 높은 굽힘강성을 갖고 다른 재료에 비해 상대적으로 적은 중량이 필요하므로 구조 재료로서의 적합성을 알 수 있다.

A study to analyze and solve problems of multi wire installation duct experiment has presented in this paper We have taken Taguchi's parameter design approach, specifically orthogonal array, and determined the optimal levels of the selected variables through analysis of the experimental results using S/N ratio.

붕산용액에서 양극산화법으로 장벽형 산화피막을 형성시킨 후 미세조직을 관찰하였다. 양극산화시 인가되는 전압에 따른 피막의 성장속도는 1.54nm/v의 직선적인 관계를 나타냈으며 300v의 인가전압에서 생성된 산화피막의 조직은 500˚C에서 열처리하였을 경우 피막의 상 전이가 일어나지 않았으나 높은 인가전압에서 생성된 산화피막의 경우는 피막의 조직이 비정질에서 γ-alumina로 변태되는 것이 관찰되었다. 또한 피막이 전자빔 조사에 의해서도 γ-alumina로 전이가 일어났다.

고순도알루미늄 유전체의 내부표면적을 증가시키기 위하여 1M의 염산 에칭용액에 첨가제를 사용했을 때 나타나는 에칭특성의 변화를 조사하였다. 염산용액에 에틸렌글리콜이 첨가된 혼합용액에서 에칭을 실시했을 경우 알루미늄 기지 표면에 미세하고 균일한 에치피트가 형성되어 표면적 증가 효과가 크게 나타났으며, 또한 양극 산화 후 측정된 정전용량의 결과에서도 에틸렌 글리콜이 첨가된 에칭액에서 제조된 유전체는 표면적 증가에 의한 높은 정전용량 값을 나타냈다.

전해콘텐서용 알루미늄박을 ammonium adipate 용액을 이용하여 65˚C에서 10분간 100V 및 140V로 각각 양극 산화시켜 산화 알루미늄 유전체를 만들었다. 유전층의 두께, 화학양론적 관계, 결정구조 등을 RBS 및 TEM을 이용하여 분석하였고, 알루미늄박의 에칭시 황산 첨가로 인한 표면적의 변화는 임피던스 분석법으로 조사 하였다. 생성된 유전피막은 100V 및 140V의 전압을 사용했을 경우 각각 약 130nm 및 190nm 두께의 비정질로 나타났으며 피막의 알루미늄과 산소원소의 화학양자론적 비는 약 2:3의 비율로 존재했다. 또한 유전피막은 전자빔은 조사에 의해 쉽게 γ-Al2</TEX>O3 형태의 결정질로 변태 되었다. 염산 에칭욕에 황산 첨가시 나타나는 알루미늄박의 표면변화는 임피던스 분석결과와 정전 용략의 변화가 일치하는 경향을 나타냈다.