최근 한국기계연구원에서 개발된 Mechanochemical process (MCP)는 Spray conversion 법에 의하여 나노크기의 W/Cu 복합 분말을 제조하는 방법으로서, 현재 (주)나노테크에서 산업화를 위한 시험/개발이 진행 중이다. 이 방법에 의하여 W /1 0 ~ 40wt. %Cu 조성의 초미렵 W/Cu 복합 분말의 양산화가 가능하게 됨으로써, 나노복합분말을 사용한 초미립 W/Cu 합금의 소결 제조 연구 역시 나 노태크에서 분말사업화와

The characteristics of two commercial 2xxx series Al alloy powders, AMB2712 and 201AB, were evaluated and their compacting and sintering characteristics were discussed in tems of compacting pressure. The particle shapes of both two powder mixtures were irregular and their particle size distributions were broad. The compactibility of AMB2712 was superior to that of 201AB because of better fluidity. The sintered density was higher than the green density at low compacting pressure, however, it was lower than the green density when the samples were compacted at higher pressure due to the selling during sintering. The sintered density was alomost the same as the green density at the "homogeneous deformation" stage. It was observed that pores were created at the triple points due to the rapid diffusion of Cu in Al. Cu in Al.

SPS(Spark Plasma Sintering ) is known to be an excellent sintering method for porous materials. In the present work an attempt has been made of fabricating porous 316L Stainless steel with good mechanical properties by using controlled SPS process Porosity was 21%~53% at sintering temperature of ~100 The limit of porosity with available mechanical strength was 30% at given experimental conditions. Porosity can be controlled by manipulating the intial height of the compact by means of the supporter and punch length. The applied pressure can be exerted entirely upon the supporter, giving no influence on the specimen. The specimen is then able to be sintered pressurelessly. In this case porosity could be controlled from 38 to 45% with good mechanical strength at sintering temperature of 90. As the holding time increased, neck between the particles grew progressively, but shrinkage of the specimen did not occur, implying that the porosity remained constant during the whole sintering process.

Effects of chemical compositions on the sintering behavior of the lead borosilicate glass developed for barrier ribs of plasma display panels were investigated in this study. Formation of pores during sintering of the glass was noted and their formation mechanism was investigated using XPS, TG/DTA, and XRD. The results indicated that pores are formed by the oxygen released from Pb-oxides during sintering.

To investigate the effect of process parameters on selective laser sintering of Cu/polyamide mixed powder, Cu/polyamide mixed powder was sintered by selective laser with changing laser power and scanning speed. The properties of sintered body were evaluated by measuring the density and tensile strength, and analysis of XRD, FT-Raman and microstructure. With an increase in the laser power, the density and ultimate tensile strength of sintered Cu/polyamide body increase and then decrease. The maximum values of the density and ultimate tensile strength were decreased with increasing laser scanning speed. These changes were concerned with the difference of irradiation energy of laser into the powder layer. It was considered that the change of the mechanical property of the sintered body with irradiation energy of laser is due to the changes of amount of copper particle and property of polyamide.

Ti-37.5at%Si elemental powder mixtures were mechanically alloyed by a high-energy ball mill, followed by CIP (cold isostatic pressing) and HIP (hot isostatic pressing) for different processing conditions. Only elemental phases (Ti and Si) were observed for the 5 min mechanically alloyed (MA 5 min) powder, but only phase was observed for the 30 min mechanically alloyed (MA 30 min) powder. phase was observed for the HIPed compact of MA 5 min and 30 min powders at 150 and 190 MPa for 3 hr at . For the HIPed compacts, the highest sintered density was obtained to be 99.5% of theoretical density by a HIP step at at 190MPa for 3hr. The hardness values of the HIPed compacts at at 150/190 MPa for 3hr were higher than HRC 76. The densification and mechanical property of HIPed compacts was found to depend on more HIP temperature than HIP pressure.