알칼리 수전해용 격막으로 사용하기 위해 음이온교환막을 제작하였다. 음이온교환막은 PVC (polyvinyl chloride)를 출발물질로 하여 클로로메틸화 및 아민화에 의해 제작하였다. 제작한 막은 막 특성(막 저항, 이온교환용량)을 평가하였다.제작한 음이온교환막의 1M NaOH수용액에서의 최저 막 저항은 2.9 Ω·cm2를 나타냈다. 이 막은 2.17 meq./g-dry-membrane의 이온교환용량과 43.4%의 함수율을 보였다. 제작한 음이온교환막의 막 특성을 시판의 막 특성과 비교 평가하였다. 1M NaOH수용액에서의 막 저항은 AHT>IOMAC>Homemade membrane>AHA>APS=AFN의 순으로 저항 값이 높았다. 이온교환용량은 Homemade membrane>AFN>APS>AHT>AHA>IOMAC의 순으로 높은 값을 가졌다.

This research presents a preparation method of dental components by metal injection molding process (MIM process) using titanium scrap. About 20 μm sized spherical titanium powders for MIM process were successfully prepared by a novel dehydrogenation and spheroidization method using in-situ radio frequency thermal plasma treatment. The effects of MIM process parameters on the mechanical and biological properties of dental components were investigated and the optimum condition was obtained. After sintering at 1250oC for 1 hour in vacuum, the hardness and the tensile strength of MIMed titanium components were 289 Hv and 584 MPa, respectively. Prepared titanium dental components were not cytotoxic and they showed a good cell proliferation property.

Lanthanum/gadolinium zirconate coatings are deposited via suspension plasma spray with suspensions fabricated by a planetary mill and compared with hot-pressed samples via solid-state reaction. With increase in processing time of the planetary mill, the mean size and BET surface area change rapidly in the case of lanthanum oxide powder. By using suspensions of planetary-milled mixture between lanthanum or gadolinium oxide and nano zirconia, dense thick coatings with fully-developed pyrochlore phases are obtained. The possibilities of these SPS-prepared coatings for TBC application are also discussed.

본 연구에서는 metal organic frameworks (MOFs)의 한 종류인 MIL-100(Fe)을 이용하여 혼합기질막(mixed matrix membranes, MMMs)을 제조하였다. MIL-100(Fe)의 함량을 고분자 대비 0∼30 wt%까지 변화시키면서 첨가된 MOF의 함량에 따른 기체의 투과 특성을 살펴보았다. H2, CO2, O2, N2, CH4의 기체 투과도는 MIL-100(Fe) 첨가량이 증가함에 따라 투과도가 증가하는 경향을 보여주었으며, 상대적으로 큰 입자크기를 가진 SF6의 투과도는 MIL-100(Fe)의 첨가량이 증가함에 따라 투과도가 감소하였다. 이상 선택도는 N2/SF6의 경우 폴리이미드막 대비 약 40% 증가하였으며, 이를 통해 N2/SF6 분리에 적합한 분리막임을 확인할 수 있었다.

본 연구의 목적은 활성탄의 CO2 흡착능을 향상시키기 위하여 화학적 전처리 방법을 개발하는 것이다. 다양한 방법과 이론이 존재하지만 이번 연구에서는 아미노화와 분해를 비교하여 흡착능을 비교하기로 하였다. 본 연구에서는 4가지 유형의 활성탄 입자를 원료 물질과 크기에 따라 준비하였고, 수산화칼륨으로 전처리하여 열처리 및 아민화과정을 거 친 후, CO2 흡착능을 비교 평가하였다. 실험결과, 단순 열처리과정만 적용할 때는 600℃ 가 가장 우수하였고, 800℃에서 아민화시킨 시료가 1.4 mmol/g의 가장 좋은 흡착능을 보 였다. 400～600℃에서 아민화를 시킨 시료는 처리온도와 비례하는 선택도를 보여주었다. 분해시간 또한 흡착능과 정비례하는 관계가 나타났다.

Needle coke is an important material for graphite electrodes. Delayed coking is used to produce needle coke. Producing good quality needle coke is not simple because it is a multi-parameter controlled process. Apart from that, it is important to understand the mechanism responsible for the delayed coking process, which involves mesophase formation and uniaxial rearrangement. Temperature and pressure need to be optimized for the different substances in every feedstock. Saturate hydrocarbon, aromatic, resin and asphaltene compounds are the main components in the delayed coking process for a low Coefficient Thermal Expansion value. In addition, heteroatoms, such as sulphur, oxygen, nitrogen and metal impurities, must be considered for a better graphitization process that prevents the puffing effect and produces better mesophase formation.

본 연구는 농산물 중 식중독세균 검출을 위한 시료 전처리 법을 확립하기 위하여 전처리용액, 전처리 시간, 전처리용액과 시료의 비율에 따른 회수율을 비교하였다. 이를 위하여 양상추, 들깻잎, 오이, 고추, 방울토마토에 E. coli O157:H7, S. Typhimurium, L. monocytogenes, S. aureus, B. cereus를 6.0 log CFU/ cm2로 접종하고 0.1% 펩톤수와 D/E broth로 처리하였다. 또한 처리시간은 30, 60, 90, 120초, 시료와 전처리용액의 비율은 1 : 2, 1 : 4, 1 : 9, 1 : 19로 각각 처리하였다. 그 결과, D/E broth로 처리하였을 때 0.1% 펩톤수로 처리하였을 때에 비하여 전반적으로 식중독균의 회수율이 높았다(P < 0.05). 특히 방울토마토의 경우, D/E broth로 처리한 구의 S. Typhimurium의 수는 0.1% 펩톤수로 처리한 구 보다 1.05 log CFU/cm2 높았다(P < 0.05). 또한 들깻잎, 양상추, 오이, 고추, 토마토와 전처리용액의 최적 비율은 1 : 9, 1 : 4, 1 : 2, 1 : 2, 1 : 2였다. 한편, 처리시간에 따른 회수율의 유의적인 차이는 없었다. 따라서 본 연구 결과를 통 해 볼 때 농산물 중 식중독균 검출을 위한 전처리용액은 D/E broth가 적절한 것으로 판단되며 표면적에 따라 시료와 전처리 용액의 비율을 결정하는 것이 분석의 정확성을 높일 수 있을 것으로 사료된다.

이 연구에서는 전문무용수의 고용형태에 따른 오디션 불안이 무용은퇴준비에 미치는 영향을 규명하고자 하였다. 이를 위하여 서울, 경기, 대전, 대구, 광주 5개 지역에 소재한 국공립단체, 민간단체, 프로젝트단체에서 활동하고 있는 전문무용수를 유의표집방법을 사용하여 최종 422명 을 대상으로 분석하였다. 연구결과는 다음과 같다. 첫째, 전문무용수의 성에 따라 오디션 신체불안과 건강은퇴준비 및 여가은퇴준비에 유의한 차 이가 있고, 연령대에 따라 경제은퇴준비에 유의한 차이가 있으며, 전공에 따라 무용은퇴준비 하 위변인 모두에서 유의한 차이가 있는 것으로 나타났다. 또한 단체소속형태에 따라 오디션 불안과 무용은퇴준비의 하위변인 모두에서 유의한 차이가 있는 것으로 나타났다. 둘째, 고용형태에 따라 오디션 심리불안과 무용은퇴준비의 하위요인 모두에서 유의한 차이가 있는 것으로 나타났다. 셋 째, 정규직 전문무용수의 오디션 심리불안은 경제은퇴준비, 심리은퇴준비, 여가은퇴준비에 영향을 미치고, 오디션 신체불안은 심리은퇴준비와 여가은퇴준비에 영향을 미치는 것으로 나타났다. 또 한 비정규직 전문무용수의 오디션 신체불안은 경제은퇴준비에 영향을 미치고, 나머지 오디션 불 안은 건강은퇴준비, 심리은퇴준비, 여가은퇴준비에 영향을 미치지 않는 것으로 나타났다.

Poly vinylidene fluoride (PVDF) 중공사막을 polyethylenimine (PEI)와 p-xylylene dichloride (XDC)를 이용해 친 수화 시킨 후 poly(vinyl alcohol) (PVA)과 가교제인 poly(acrylic acid-co-maleic acid) (PAM) 혼합용액을 코팅하여 막을 제조 하였다. 중공사막 표면의 코팅여부는 scanning electron microscope (SEM)을 통해 관찰하였으며, 막의 특성평가를 위해 물/에 탄올 혼합액에 대한 투과증발 실험을 수행하였다. 공급액 조성은 90 wt% 에탄올 수용액을 사용하였으며, 가교제 농도, 공급 액과 반응온도 변화에 따른 투과도 및 선택도를 측정하였다. 투과도는 반응온도 100°C, PAM 농도 3 wt%, 공급액온도 70°C 에서 1,480 g/m 2 hr, 그리고 선택도는 반응온도 100°C, PAM 농도 15 wt%, 공급액온도 25°C에서 αW/E = 82의 결과를 얻을 수 있었다.

발효공정으로부터 생산된 유기산의 회수를 위하여 나노여과 분리막 공정을 이용하는 경우 유기산을 제외한 발효 액 내 존재하는 당, 단백질 등의 부산물을 배제하면서 유기산을 선택적으로 투과시킬 수 있는 나노여과막이 요구된다. 본 연 구에서는 발효액으로부터 분자량이 상대적으로 작고 카르복실산기를 갖는 유기산의 효과적인 회수를 위하여 분리막 표면에 양전하를 도입하여 전기적 인력에 의해 젖산의 투과도를 향상시킬 수 있는 신규 나노여과 분리막을 제조하였다. 분리막 표면에 고분자 전해질 PEI (Polyethyleneimine)를 그라프팅시켜 제조된 분리막의 제타전위 측정 결과 표면 층이 양전하를 나타내 는 것을 확인하였다. 실제 젖산 용액 배제율 확인 결과 고분자 전해질 그라프팅 층이 형성된 막에서 배제율이 크게 감소하는 것으로 보아 그라프팅 층에 의한 젖산 배제율 저감에 효과를 나타내었다.

촉매 1,8-diazabicyclo[5,4,0]undec-7-ene(DBU)를 이용하여, poly(vinylidenefluoride-co-chlorotrifluoroethylene) P(VDF-co-CTFE) 고분자와 methacrylic acid (MAA)를 반응시켜, P(VDF-co-CTFE)-MAA 공중합체를 제조하였다. 또한 P(VDF-co-CTFE)-MAA와 2-sulfoethyl methacrylate (SEMA) 단량체를 4’,4’-azobis(4-cyanovaleric acid) (ACVA) 개시제 하에서 자유 라디칼 중합하여 수소 이온 전도성 막을 제조하였다. SEMA 함량이 많아짐에 따라 술폰산 그룹이 증가하였다. SEMA 함량이 50%일 때 최대 이온교환 용량값이 0.82 meq/g에 도달하였으며 이는 함수량 결과와 일치하였다. 또한, SEMA 함량이 50%일 때 수소이온 전도도가 0.041 S/cm까지 도달하였다. 이러한 결과는 분리막에서 SEMA 함량이 증가할수록 수소 이온을 전달시킬 수 있는 이온그룹이 증가하기 때문이다.

ZIF 재료는 독특한 기체 분리 특성을 포함한 물리적, 화학적 특성 때문에 큰 관심을 받아왔다. 본 연구에서는 α-alumina 지지체 위에 결함 없고 연속적인 ZIF-7 막을 형성하는 새롭고 효율적인 방법이 연구되었다. 지지체 위에 시딩 (seeding)을 하지 않고 직접 ZIF-7 박막을 합성하는데 정전분무법이 처음으로 적용되었다. 이 방법은 전구체 용액을 직접 정 전분무함으로 α-alumina 지지체에 ZIF-7 박막을 형성할 수 있었다. ZIF-7 박막은 XRD, FE-SEM, 단일 기체 투과 장치 등을 이용해 분석하였다.

Isotropic pitch fibers were stabilized and carbonized for preparing carbon fibers. To optimize the duration and temperature during the stabilization process, a thermogravimetric analysis was conducted. Stabilized fibers were carbonized at 1000, 1500, and 2000℃ in a furnace under a nitrogen atmosphere. An elemental analysis confirmed that the carbon content increased with an increase in the carbonization temperature. Although short graphitic-like layers were observed with carbon fibers heat-treated at 1500 and 2000℃, Raman spectroscopy and X-ray diffraction revealed no significant effect of the carbonization temperature on the crystalline structure of the carbon fibers, indicating the limit of developing an ordered structure of isotropic pitch-based carbon fibers. The electrical conductivity of the carbonized fiber reached 3.9×10⁴S/m with the carbonization temperature increasing to 2000℃ using a four-point method.

본 연구에서는 생분해성 고분자인 PLA(polylactic acid)의 기계적 열적 물성 향상을 위해 목재에서 얻은 펄프분말을 블랜딩하여 펄프분말의 함량에 따른 PLA/펄프 복합필름의 기계적, 열적 물성을 확인하였으며, 또한 이 복합필름에 가교제로 TDI(toluene diisocyanate)를 첨가하여 복합필름의 물성 향상을 확인하였다. 그 결과 순수한 PLA 필름의 경우 인장강도가 565.25kgf/cm2인 것을 확인하였으며, 펄프분말의 함량이 0.25 wt% 일 때의 인장강도가 624.20kgf/cm2로 약 9.1 % 증가하는 것을 확인하였다. 반면 연신율의 경우 전 복합필름이 순수 PLA 필름에 비해 약 50% 감소하는 것을 확인하였다. 그리고 가교제로 TDI를 첨가한 PLA/펄프분말의 경우도 TDI의 함량에 관계없이 0.25 wt%의 펄프분말만을 첨가한 복합필름에 비해 연신율이 낮았으며, 인장강도의 경우 500% TDI를 첨가한 경우 640.43kgf/cm2로 증가하였다. 또한, PLA/펄프 복합필름에서 TDI를 가교시킨 PLA/펄프 복합필름은 가교시키지 않은 PLA/펄프 복합필름에 비해 300℃ 이하에서의 열적 안정성은 우레탄기의 형성에 의해 TDI의 함량이 높은 경우 약간 증가하였다.

피부 노화를 방지하고 지속적으로 보습을 유지하기 위해 다양한 베시클들이 연구되고 있다. 최근에 활성물질의 흡수, 투과 및 보습의 유지와 관련하여 리포좀, 액정 및 다중층 라멜라 에멀젼 같은 많은 제조 방법들이 소개되고 있다. 본 연구에서는 인지질과 유사한 cetearyl alcohol/ceteth-20 phosphate/dicetyl phosphate 계면활성제를 이용하여 전단세기 및 pH 변화에 따른 다중층 라멜라 베시클을 개발하였으며 편광현미경을 통해 확인하였다. 결과로서 낮은 전단세기 및 pH에서는 라멜라 베시클 입자의 형태가 불균일하게 형성됨을 확인하였다. 42℃에서 2개월 간의 라멜라 베시클 내의 레티놀 함량의 변화를 측정한 결과 낮은 pH에서 레티놀의 함량이 감소하였다. 또한, 이 라멜라 베시클은 일반 O/W 에멀젼에 비해 피부 수분손실량이 14% 감소됨을 확인하였으며, O/W 썬 크림과 내수성 in vitro SPF를 측정하여 비교한 결과 UVB와 UVA 영역 모두에서 자외선을 잘 차단하여 유사한 내수성을 보이고 있음을 확인하였다.

무지개 빛을 내는 무기진주광택안료는, 내광성, 내용제성 및 내열성 등이 물리적 화학적 안정성이 우수하여 다양한 분야에서 응용되고 있다. 본 연구는 수열합성방법을 사용하여 마이카 티타니아에 파란색 코팅 안료인 염화코발트를 기본으로 화장품 안료로 사용되는 진주광택안료를 합성하였다. 코발트에 의한 안료의 색상을 보완하고자 코발트와 금속 염의 비를 달리하여 안료를 코팅하고, 이를 통해 금속염의 종류에 따라 다양한 색차값을 구현하는 진주광택 안료를 합성하였다. 코발트와 첨가된 금속 염 전구체의 조성비와, 금속 염의 종류에 따라 코팅 특성과 색상을 조절할 수 있었고, 안료의 다양한 색상변화 특성을 색차계를 통해 확인 하였다. 합성된 안료는 SPM, SEM, XRD, EDS 기기를 통해 특성을 분석하였다.

Recently, many cosmetic researchers have been focused on the development of high functional cosmetics including anti-wrinkle and whitening. In these studies, they couldn't afford to pay a deep attention to stable encapsulations for unstable materials and efficient drug deliveries for them. Particularly, in order to show a degree of instant effects as cosmetics, they can't also ignore moisturizing effect enough to satisfy customers just after applying and its maintenance by improving the function of skin barrier as well as above two effects. Therefore, skin analogue systems have attracted considerable attention in the view of structural and compositional similarity to intercellular membrane in stratum corneum. And, some models for skin analogue composition were developed to improve the function of skin barrier, stably encapsulate unstable materials such as retinol, vitamin B, C, E, etc., and control their skin penetration in order to show good effects as cosmetics. In this study, we suggest the new skin analogue model having the compositional similarity as well as conventional structural ones. Our skin analogue membrane(SAM) is mainly composed of ceramide/ cholesterol/phosphatidylcholin/fatty acids and its structural defects are compensated by including cholesterol amphiphile and controlling the ratio of ceramide/cholesterol. It was possible to confirm the formation of skin analogue membrane having highly-densed multilamella structure and compare them according to the change of each ratio with a polarized microscope, X-ray diffraction. More detaily, we observed their structures with a electron microscope(TEM). Finally, we dispersed them in excess of continuous water phase, observed the formation of maltese-cross liquid crystalline and measured the efficiency of drug deliveries and moisturizing effects.

A novel route to prepare Nd-Fe-B magnetic particles by utilizing both spray drying and reduction/diffu- sion processes was investigated in this study. Precursors were prepared by spray drying method using the aqueous solu- tions containing Nd salt, Fe salt and boric acid with stoichiometric ratios. Precursor particles could be obtained with various sizes from 2 to 10 µm by controlling concentrations of the solutions and the average size of 2 µm of precursors were selected for further steps. After heat treatment of precursors in air, Nd and Fe oxides were formed through desalt- ing procedure, followed by reduction processes in Hydrogen (H2) atmosphere and with Calcium (Ca) granules in Argon (Ar) successively. Moreover, diffusion between Nd and Fe occurred during Ca reduction and Nd2Fe14B particles were formed. With Ca amount added to particles after H2 reduction, intrinsic coercivity was changed from 1 to 10 kOe. In order to remove and leach CaO and residual Ca, de-ionized water and dilute acid were used. Acidic solutions were more effective to eliminate impurities, but Fe and Nd were dissolved out from the particles. Finally, Nd2Fe14B magnetic particles were synthesized after washing in de-ionized water with a mean size of 2 µm and their maximum energy prod- uct showed 9.23 MGOe.

This article is to review the change of perception of Japanese Army on the public after Russo-Japanese War and its impact on military training system. I Keywords: Total War, military training, mobilization, Training for youths- Japanese War and World War I. Tanaka has been deeply interested in the relationship of between the public and the army earlier on. He regarded the army as a school to train ‘good citizens’ and is also interested in training of young people. After World War I, the thought of Total War System was more and more shaped up in Japan and the efforts to inspire it to the public through trainings were made. Especially the army implemented the military training sessions in all the schools as well as established “Training Institutes for youths” for non-school youth in order to get more suitable citizens for the army. These ideology educations enabled reformation of the public, and which effected positively to build Total War System lead mainly by the army later on.