Carbon supports for dispersed platinum (Pt) electrocatalysts in direct methanol fuel cells (DMFCs) are being continuously developed to improve electrochemical performance and catalyst stability. However, carbon supports still require solutions to reduce costs and improve catalyst efficiency. In this study, we prepare well-dispersed Pt electrocatalysts by introducing titanium dioxide (TiO2) into biomass based nitrogen-doped carbon supports. In order to obtain optimized electrochemical performance, different amounts of TiO2 component are controlled by three types (Pt/TNC-2 wt%, Pt/TNC-4 wt%, and Pt/TNC-6 wt%). Especially, the anodic current density of Pt/TNC-4 wt% is 707.0 mA g−1 pt, which is about 1.65 times higher than that of commercial Pt/C (429.1 mA g−1 pt); Pt/TNC-4wt% also exhibits excellent catalytic stability, with a retention rate of 91 %. This novel support provides electrochemical performance improvement including several advantages of improved anodic current density and catalyst stability due to the well-dispersed Pt nanoparticles on the support by the introduction of TiO2 component and nitrogen doping in carbon. Therefore, Pt/TNC-4 wt% may be electrocatalyst a promising catalyst as an anode for high-performance DMFCs.

군락 광합성 모델의 도출을 위하여 생육 챔버가 필요하며, 이를 위한 광합성의 효율적인 측정 방법이 필요하다. 본 연구의 목적은 내부 환경 제어가 가능한 생육 챔버를 이용하여 광도 및 이산화탄소 농도 변수를 갖는 로메인 상추(Lactuca sativa L.)의 군락 광합성 곡선을 도출하는 방법을 확립하는 것이다. 실험에 사용한 상추는 식물공장 모듈에서 재배되었으며, 군락 광합성을 측정하기 위하여 아크릴로 제작된 생육 챔버(1.0x0.8x0.5m)를 이용하였다. 첫 번째로, 다음의 두 방법을 적용하여 측정된 군락 광합성 속도를 통해 각 방법의 시정수를 계산하여 비교하였다. 즉, 1) CO2 농도를 고정(1,000μmol·mol-1) 하고 광도를 변화(340, 270, 200, and 130μmol·m-2·s-1) 시키거나, 2) 광도를 고정(200μmol·m-2·s-1)하고 CO2 농도를 변화(600, 1,000, 1,400, and 1,800μmol·mol-1) 시켰다. 두 번째로, 1)과 2)의 방식을 적용하여 군락 광합성을 측정했을 때, 특정 광도(200μmol·m-2·s-1)와 특정 CO2 농도(1,000μmol·mol-1)에서 측정된 군락 광합성 속도 값을 비교하였다. 실험 결과 CO2 농도를 변화시키는 방식의 시정수는 광도를 변화시키는 방식에 비해 3.2배 큰 값을 나타내었다. 광도를 변화시키며 측정할 때 군락 광합성 속도는 1분 이내에 안정되었고, CO2 농도를 변화시킬 경우에는 6분 이상의 시간이 소요되었다. 따라서 광도를 변화시키는 측정 방식이 생육 챔버를 이용하여 작물의 군락 광합성 속도를 측정할 때 적합한 방식임을 확인하였다.

본 논문에서는 이산화탄소 친화적인 PBEM-POEM (PBE) 공중합체를 기반으로 고분자 블렌드 분리막을 제조하 는 방법을 제시한다. PBE 공중합체는 자유 라디칼 중합 반응을 통해 손쉽게 합성이 가능하며, 이를 상용 고분자인 PEG와 다 양한 비율로 혼합하여 이산화탄소/질소 분리막을 제조하였다. 이산화탄소/질소 분리 성능을 테스트한 결과, PEG의 함량이 높을수록 이산화탄소 투과도는 감소하는 반면 이산화탄소/질소 선택도는 크게 증가하는 상충(trade-off) 관계가 나타났다. 그러 나 PBE/PEG (9 : 1)과 PBE/PEG (7 : 3)을 비교하면 이산화탄소 투과도는 단지 8.3% 감소한 반면에 질소 투과도는 69.1%나 감소하였다. 따라서 이산화탄소/질소 선택도가 33.8에서 100.3으로 크게 증가하였다. 이것은 PBE 공중합체의 80%를 차지하 는 POEM 사슬이 PEG와 상호작용하여 더욱 조밀한 구조가 되었기 때문이며, 이를 FT-IR, XRD, SEM 분석으로 확인하였다. PBE/PEG (7 : 3) 블렌드 막이 가장 최적의 기체 분리 성능을 가졌고, 이산화탄소투과도는 170.5 GPU, 이산화탄소/질소 선택 도는 100.3이었다.

본 연구에서는 비불소계 트리이소프로필 아민 아세테이트 (TAA) 화합믈을 사용하여 반도체 웨이퍼의 포토레지스트 패턴 건조 성능을 조사하였으며, 초임계이산화탄소 용 계면활성제로 잘 알려진 불소계 저분자량 화합물, PFPE-COOH 및 PFPE-COO-NH4 +과 비교하였다. 초임계 공정 후 얻어진 포토레지스트 패턴의 모양은 이산화탄소 압력, 온도, 시간 등 공정 처리 조건에 따라 달라졌으며, 최적의 조건에서 포토레지스트 패턴 붕괴가 거의 없는 결과를 얻을 수 있었다. TAA를 사용하는 초임계 세정은 PFPE-COOH에 비해 다소 떨어지지만 일반 습식 세정 방법보다는 우수한 패턴 형성 성능을 나타내었으며, 이것은 경제적이고 환경친화적인 새로운 계면활성제로서의 가능성을 보였다.

This paper presents a literature review on the active technologies to regulate the levels of carbon dioxide and oxygen in Kimchi packaging. In this study, laser-etched pouches and O2 scavengers were used for Kimchi packaging, and the efficiency of each packaging technique to regulate the CO2 and O2 levels inside Kimchi packages was investigated. When Kimchi was packaged with a laser-etched pouch, the CO2 concentration in the sample with a high gas transmission rate was less than that in other pouches (p<0.05), and a low CO2 level had little effect on the expansion of the package volume. Kimchi treated with an O2 absorber exhibited a significantly lower (p<0.05) O2 concentration inside the packages relative to the control. A low O2 concentration inside the Kimchi package effectively inhibited the growth of total aerobic bacteria and lactic acid bacteria, as well as yeasts and molds on Kimchi. These results suggest that O2 absorbers have a positive effect on the microbial quality of Kimchi. Therefore, packaging in a laser-etched pouch and the use of an O2 scavenger could provide a novel packaging material for regulating the CO2 and O2 levels during Kimchi packaging.

본 연구에서는 초임계 이산화탄소를 사용해 도라지(balloonflower, Platycodon grandiflorum A. DC) 종자로부터 추출한 유지의 기능성과 에멀전 특성에 대해 조사하였다. 종자에 비해 도라지 종자유는 총 polyphenol(8 mg/100 g)의 함량이 낮았으나 α-tocopherol(14.15 mg/ 100 g), β -sitosterol(116 mg/100 g) 및 stigmasterol(8 mg/100 g)의 함량은 높았다. DPPH 라디칼 소거능으로 분석한 종자유(IC50=1235.5 μg/mL)의 항산화능은 종자(IC50=1138.2 μg/mL)와 유사하였다. 1%(w/w) lecithin 농도에서 도라지 종자유를 사용해 제조한 에멀젼은 탁도, 지방구 입자 크기 및 형상, 유화안정 성에서 콩기름을 사용한 에멀젼과 유사하였으나 들기름 사용 에멀젼보다는 탁도 및 유화안정성이 낮았고 지방구 입자는 크게 나타났다. 도라지 종자유 에멀젼의 표면장력은 들기름 에멀젼과 유사하였다.

Poly(ether block amide) (PEBA)는 이산화탄소 분리에 매우 적합한 상용 블록 공중합체 중 하나이다. 기체분리막의 경우 높은 투과도 뿐 아니라 강한 기계적 강도 또한 필요로 한다. PEBA공중합체의 결정성 폴리아마이드(polyamide) 블록은 기계적 강도를 제공하며 동시에 rubbery한 폴리에테르(polyether) 부분은 이산화탄소와의 친화도를 부여하여 이산화탄소 촉진 수송에 기여한다. PEBA공중합체에서 결정성 상과 rubber한 상의 조성은 기체분리막에 적합하게 조절될 수 있다. PEBA 공중합체를 기반으로 한 분리막은 좋은 투과도를 갖지만 추가적으로 분자체 효과를 이용하여 큰 기체 투과도 손실 없이 분리막의 선택도를 향상시킬 수 있다. 혼합 매질 분리막은 혼합막의 한 종류로서 고분자 매트릭스와 유기 첨가제로 이루어져 있다. 하지만 고분자 매트릭스와 유기 첨가제간의 양립성(compatibility)에 따른 문제점 또한 존재한다. 따라서 본 총설에서는 PEBA 공중합체를 기반으로 한 혼합막의 장점과 한계에 대해 다루고자 한다.

The transfer characteristics of zinc tin oxide(ZTO) on silicon dioxide(SiO2) thin film transistor generally depend on the electrical properties of gate insulators. SiO2 thin films are prepared with argon gas flow rates of 25 sccm and 30 sccm. The rate of ionization of SiO2(25 sccm) decreases more than that of SiO2(30 sccm), and then the generation of electrons decreases and the conductivity of SiO2(25 sccm) is low. Relatively, the conductivity of SiO2(30 sccm) increases because of the high rate of ionization of argon gases. Therefore, the insulating performance of SiO2(25 sccm) is superior to that of SiO2(30 sccm) because of the high potential barrier of SiO2(25 sccm). The ZTO/SiO2 transistors are prepared to research the CO2 gas sensitivity. The stability of the transistor of ZTO/SiO2(25 sccm) as a high insulator is superior owing to the high potential barrier. It is confirmed that the electrical properties of the insulator in transistor devices is an important factor to detect gases.

온실가스의 주범인 이산화탄소를 효과적으로 분리하기 위하여 이산화탄소와 친화성이 좋은 에틸렌글리콜 사슬이 도입된 폴리설폰 기반의 고분자와 아민이 기능화된 ZIF8 무기입자 (ZIF8-A) 를 복합화한 유무기 복합 기체분리막 (MMM)을 제조하였다. 제조된 분리막은 XRD, TGA, FT-IR, SEM 및 NMR 분석을 통해 분리막의 구조와 물성특성을 확인하였다. CO2/N2, CO2/CH4에 대한 가스 투과 특성을 조사하였고, 그 결과 ZIF8-A 구조 내 아민 함량 증가에 따라 이산화탄소에 대한 투과도 및 선택도가 증가하는 경향을 나타냈다. 이는 ZIF8-A 구조 아민기능기와 에칠렌글라이콜 사슬과의 입자와의 계면저항성이 낮은 것에 기인한 것으로 판단하였다.