Many Korean domestic masonry structures constructed since 1970 have been found to be vulnerable to earthquakes because they lack efficient lateral force resistance. Many studies have shown that the brick and mortar suddenly experience brittle fracture and out-of-plane collapse when they reach the inelastic range. This study evaluated the seismic retrofitting of non-reinforced masonry with Hybrid Super Coating (HSC) and Cast, manufactured using glass fiber. Four types of specimen original specimen (BR-OR), one layered HSC (BR-HS-O), two-layered HSC (BR-HS-B), one layered HSC, and Cast (BR-CT-HS-O) were constructed and analyzed using compression, flexural tensile, diagonal compression, and triplet tests. The specimen responses were presented and discussed in load-displacement curves, maximum strength, and crack propagation. The compressive strength of the retrofit specimens slightly increased, while the flexural tensile strength of the retrofit specimens increased significantly. In addition, the HSC and Cast also produced a considerable increase in the ductile response of specimens before failure. Diagonal compression test results showed that HSC delayed brittle cracks between the mortar and bricks and resulted in larger displacement before failure than the original brick. The triplet test results confirmed that the bonding strength of the retrofit specimens also increased. The application of HSC and Cast was found to restrain the occurrence of brittle failure effectively and delayed the collapse of masonry wall structures.

The purpose of this experimental research is to evaluate the workability and strength properties of hybrid fiber reinforced concrete containing amorphous steel fiber and organic fiber. For this purpose, the hybrid fiber reinforced concrete containing amorphous steel fiber(ASF) with polyamide(PA) and polyvinyl alcohol(PVA) fiber, respectively were made according to their total volume fraction of 0.5% for water-binder ratio of 33%, and then the characteristics such as the workability, compressive strength, and flexural strength of those were investigated. It was observed from the test results that the workability and compressive strength at 7 and 28 days were decreased and the flexural strength at 7 and 28 days was increased with increasing ASF and decreasing organic fiber.

본 연구에서는 단일강섬유와 하이브리드강섬유로 보강된 UHPC의 휨강도 및 연성을 평가하기 위해 세 개의 휨파괴형 보에 대한 4점 가력 실험을 수행하였다. 실험 결과 단일섬유로 보강된 UHPC보다 하이브리드 섬유로 보강된 UHPC가 강도 및 연성 모든 측면에서 더 우수한 구조성능을 보유한 것으로 나타났다. 설계시의 안전성에 대해 평가하기 위하여, K-UHPC 구조설계지침에서 제공하는 방법에 따라 실험 체의 강도와 연성을 평가해본 결과 현재의 재료모델은 강도에 대해서는 보수적으로 평가할 수 있으나 연성에 대해서는 과대평가하는 것으로 나타났다.

The purpose of this study was to evaluate the tensile fracture energy absorption capacity of hybrid fiber reinforced cement composite by strain rate. Experiment result, it was confirmed that PVA suppressed the microcrack around the HSF at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the HSF.

The purpose of this study was to evaluate the direct tensile fracture behavior of steel fiber hybrid reinforced cement composite by strain rate. Experiment result, it was confirmed that SSF suppressed the microcrack around the HSF at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the HSF.

콘크리트의 낮은 인장강도 및 균열제어 능력 등의 약한 재료성질을 개선하기 위하여 수년간 하이브리드 섬유보강 콘크리트에 관한 많은 연구가 진행되어 왔다. 그러나 비정질 강섬유와 유기섬유를 이용한 하이브리드 섬유보강 콘크리트에 관한 연구는 이루어지지 않은 실정이다. 따라서, 본 연구의 목적은 비정질 강섬유와 유기섬유로서 폴리아미드 섬유를 이용한 하이브리드 섬유보강 콘크리트의 압축강도, 장기 건조수축 및 내동해성을 평가하는 것이다. 이를 위하여 목표 압축강도 40 및 60 MPa 각각에 대해서 하이브리드 섬유 혼입률을 전체 체적비로 1.0%로 설정하여 비정질 강섬유와 폴리아미드 섬유를 이용한 하이브리드 섬유보강 콘크리트를 제작하였다. 제작된 하이브리드 섬유보강 콘크리트의 장기 건조수축 및 내동해성을 평가한 결과, 재령 365일 및 730일에서의 장기 길이변화율은 플레인 콘크리트보다 각각 30%, 25% 이상 감소된 것으로 나타났으며, 동결융해 300 사이클 후의 내구성 지수는 90% 이상으로, 내동해성이 있는 것으로 나타났다.

The purpose of this study was to evaluate the direct tensile fracture behavior of fiber hybrid reinforced cement composite by strain rate. Experiment result, it was confirmed that PVA suppressed the microcrack around the steel fiber at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the steel fiber.

In this study, the fiber blending ratio and strain rate effect on the tensile behavior of hybrid fiber reinforced cement composite was evaluated. Hooked steel fiber and polyvinyl alcohol fiber were used for reinforcing fiber. The fiber blending ratio of HSF+PVA were 1.5+0.5, 1.0+1.0 and 0.5+1.5vol.%. As a results, the tensile strength, strain capacity and fracture toughness of the hooked steel fiber reinforced cement composites were improved by the increase of the bond strength of the fiber and the matrix according to increase of strain rate. However, the tensile stress sharply decreased after the peak stress because of the decrease in the number of straightened pull-out fibers by micro cracks in the matrix around hooked steel fiber. On the other hand, PVA fiber showed cut-off fracture at strain rate 10-6/s with multiple cracks. However, at the strain rate 101/s, the multiple cracks and strain capacity were decreased because of the pull-out fracture of PVA fiber. The HSF1.5PVA0.5 shown the highest tensile strength because the PVA fiber suppressed the micro cracks in the matrix around the hooked steel fiber and improved the pull-out resistance of hooked steel fiber. Thus, DIF of strain capacity and fracture toughness of HSF1.5PVA were greatly improved. In addition, the synergistic response of fracture toughness was positive because the tensile stress was slowly decreased after the peak stress by improvement of the pull-out resistance of hooked steel fiber at strain rate 101/s

The purpose of this study was to evaluate the tensile fracture behavior of fiber hybrid reinforced cement composite according to the strain rate. Experiment result, it was confirmed that the number of cracks and the strain capacity tended to decrease with increasing PVA fiber volume fraction at the strain rate of 101/s.

This research investigated the effects of matrix strength on the direct tensile behavior of high performance hybrid fiber reinforced cementitious composites (HPHFRCCs) at high strain rates. 3 different type matrixes were used (56 MPa, 81 MPa and 180 MPa). And macro fiber was long hooked fiber (H, =0.3 mm,=30 mm) and micro fiber was short smooth fiber (S, =0.2 mm,  =13 mm). The volume content of macro fibers was 1.0% and the volume content of micro fibers was 1.0%. The high matrix strength clearly increased the tensile strength and peak toughness of HPHFRCCs even at high strain rates (74 ~ 161 /sec).

In this study, four reinforced concrete beam-column joints, replacing recycled materials with hybrid fiber were constructed and tested under monotonic loading. Experimental programs were carried out to improve and evaluate the seismic performance of such test specimens, such as the load-displacement, the failure mode, and the maximum load carrying capacity. All the specimens were modeled in 1/2 scale-down size.

본 연구에서는 표준실험체 (BSS), 순환굵은골재와 고로슬래그 미분말의 치환과 하이브리드섬유를 보강한 실험체 (BSPRR1, BSPRR2시리즈), 순환굵은골재와 고로슬래그 미분말의 치환과 PVA섬유를 보강한 실험체 (BSPG시리즈)로 총 13개의 실험체를 실물크기의 1/2로 축소 제작하여 실험을 수행하였다. 실험을 통하여 얻어진 결과를 비교⋅분석하여 하중-변위, 파괴형태, 최대내력 등을 규명함으로써 구조성능의 개선정도를 평가하였다. 실험결과 순환굵은골재와 고로슬래그 미분말을 치환한 콘크리트에 하이브리드섬유를 보강한 실험체 (BSPRR1, BSPRR2시리즈)의 경우 표준실험체 (BSS)에 비하여 압축강도는 최대 13%, 최대내력은 4~21%, 연성능력은 각각 4~28% 증가하는 결과를 나타내었다. 그리고 또한, 충분한 연성적인 거동과 안정적인 휨인장 파괴를 나타내었다.

In this study, it was developed hybrid fiber reinforced concrete using ground granulated blast furnace slag, the industrial wastes, and recycled aggregate. As a result of experiments on improvement of performances of eco-friendly buildings utilizing recycled resources (recycled coarse aggregates and ground granulated blast furnace slag), the following conclusions are drawn. As hybrid fiber(PVA Fiber+ Steel Fiber) was mixed with the concrete in which the replacement was conducted with recycled coarse aggregates and ground granulated blast furnace slag, the structural performance were increased.

For hybrid fiber reinforced UHPC with two kinds of steel fibers, variation of the flexural behavior with different fiber distribution characteristics was estimated by experiments, and a prediction of the flexural behavior using smeared crack model. it was found that adopting a crack bandwidth considering the fiber distribution characteristics enable to predict the fractural behavior of UHPC beam.

Mechanical performance of UHPC is known to be strongly influenced by placing method. In this study, in order to estimate variation in tensile behavior of hybrid fiber reinforced UHPC, two different placing methods were adopted in fabricating test specimens. Test results presents that placing method causes a noticeable variation in the tensile behavior

본 연구는 콘크리트의 열전도 역문제의 해를 통해 온도의존적 열전도도를 추정하는 방법을 제안하였다. 온도의존적 열전도도의 추정은 실물모형 화재실험에서 측정된 하이브리드 섬유보강 쉴드터널 라이닝의 시간 및 깊이별 온도분포 데이터를 이용하였다. 추정된 온도의존적 열전도도는 실험시간이 짧은 시점에서는 상온 영역에서 열전도도의 급격한 감소가 나타나는 것으로 추정되었다. 반면 깊이 25mm 위치에서 최대온도가 측정된 실험시간대에서는 온도에 따른 콘크리트의 특성변화 및 강섬유 혼입 효과를 반영하고 있다. 따라서 온도의존적 열전도도 추정 시 가열면 부근에서 최대온도가 측정된 시점을 기준으로 실험시간을 결정해야 한다. 추정된 열전도도는 유사배합을 사용한 기존연구와 유사한 결과를 나타내고 있다.

이 연구에서는 콘크리트 구조물의 섬유보강재인 하이브리드 섬유시트(HFC)와 하이브리드 섬유바(HFB)의 성능을 평가하였다. 실험결과에 의하면, 하이브리드 섬유보강재(시트, 바)로 보강된 보는 무보강보에 비해 약 60%~2배 이상의 높은 보강효과를 보였고 보강된 보는 항복점 이후 연성적인 거동을 보이며 파괴되는 이상적인 파괴모습을 보여주었다. 특히, 하이브리드 섬유바 보강의 경우 하이브리드 섬유바를 에폭시 주입과 접착제로 부착한 보강보는 비슷한 파괴거동을 보여줌으로써 부착방식에 따른 차이가 거의 없는 것으로 나타났다.