In this study, the physical properties and fracture characteristics according to the tensile load are evaluated on the materials of the polymeric filler and carbon fiber-based composite sleeve technique. The polymeric filler and the composite sleeve technique are applied to areas where the pipe body thickness is reduced due to corrosion in large-diameter water pipes. First, the tensile strength of the polymeric filler was 161.48~240.43 kgf/cm2, and the tensile strength of the polyurea polymeric filler was relatively higher than that of the epoxy. However, the tensile strength of the polymeric filler is relatively very low compared to ductile cast iron pipes(4,300 kgf/cm2<) or steel pipes(4,100 kgf/cm2). Second, the tensile strength of glass fiber, which is mainly used in composite sleeves, is 3,887.0 kgf/cm2, and that of carbon fiber is up to 5,922.5 kgf/cm2. The tensile strengths of glass and carbon fiber are higher than ductile cast iron pipe or steel pipe. Third, when reinforcing the hemispherical simulated corrosion shape of the ductile cast iron pipe and the steel pipe with a polymeric filler, there was an effect of increasing the ultimate tensile load by 1.04 to 1.06 times, but the ultimate load was 37.7 to 53.7% compared to the ductile cast iron or steel specimen without corrosion damage. It was found that the effect on the reinforcement of the corrosion damaged part was insignificant. Fourth, the composite sleeve using carbon fiber showed an ultimate load of 1.10(0.61T, 1,821.0 kgf) and 1.02(0.60T, 2,290.7 kgf) times higher than the ductile cast iron pipe(1,657.83 kgf) and steel pipe(2,236.8 kgf), respectively. When using a composite sleeve such as fiber, the corrosion damage part of large-diameter water pipes can be reinforced with same level as the original pipe, and the supply stability can be secured through accident prevention.

In this study, as the proportion of aged pipelines increases rapidly, in the event of an accident caused by corrosion and structural deterioration of metal pipes, appropriate overlay welding is applied in the field to partially repair it. The size of the base steel plate and the selection of a stable welding method were evaluated, and possible problems caused by the overlay welding were identified, and improvement measures were proposed. For the test, a new steel pipe coated with epoxy lining on the inner surface and polyethylene on the outer surface was subjected to a tensile test by processing the repaired specimen through overlay welding with a steel plate after artificial cracking, and structural safety was evaluated after repair. Furthermore, the influences of the size of the throat and the size of the steel plate were analyzed. As a result of the tensile test by dividing the repaired steel plate overlay into a constraint and non-constraint conditions, the tensile load was concentrated in the welded part and damage occurred in the welded part. It was found that the maximum load leading to breakage increases as the size of the welding throat increases. In addition, it was found that the resistance to load increased slightly as the size of the overlaid steel plate increased, but the effect was not significant, confirming the need for repair in consideration of the site conditions. As a result of evaluating the damage to the coating material on the back side of the welding, it was confirmed that the coating material on the opposite side of the welding burned black(epoxy) or was greatly deformed by heat(polyethylene). Therefore, it is necessary to secure structural stability through repainting, etc. in order to prevent damage to the coating material on the opposite side during overlay welding.

The purpose of this study was to evaluate the corrosion damage of large diameter metallic pipes buried in reclaimed land due to the corrosion effect by soil, and to propose a method of installing metal pipes in the reclaimed land. The results are as follow. First, the soil of the reclaimed land was gray clay, the soil specific resistance indicating soil corrosiveness was at least 120 Ω-cm, the pH was weakly acidic(5.04 to 5.60), the redox potential was at least 62 mV, the moisture content was at most 48.8%, and chlorine ions and sulfate ions were up to 4,706.1 mg/kg and 420 mg/kg. Therefore, the overall soil corrosivity score was up to 19, and the external corrosion effect seems to be very large. Second, the condition of straight part of pipes was in good condition, but most of KP joints were affected by corrosion at a severe level. The reason for this seems to be that KP joints accelerated corrosion due to stress and crevice corrosion in addition to galvanic corrosion in the same environment. Third, as a result of evaluating correlations of each item that affects the corrosion on the external part, the lower the soil resistivity and redox potential, the greater the effect on the KP joints corrosion, and the moisture content, chloride ion, and sulfate ion, the higher the value, the greater the effect on the corrosion of KP joints. In addition, among soil corrosion items, the coefficient of determination of soil resistivity with corrosion of KP joints was the highest with 0.6439~0.7672. Fourth, when installing metal pipes or other accessories because the soil of the reclaimed land is highly corrosive, it is necessary to apply a corrosion preventive method to extend the life of pipes and prevent leakage accidents caused by corrosion damage to the joint.

In this study, air scouring cleaning was selected and applied among 5 small blocks (S1~S5) in domestic S cities to analyze the cleaning effect of particles causing discoloration. In order to identify the cleaning effect, 10 locations were selected as water quality investigation point, such as the stagnant or water mains ends. Removal of solids, variation of particle components, weight and concentration were analyzed. And the level of the cleanness of the surface inside water mains using endoscope was investigated. As a result of analysis, the solids discharged after cleaning were mainly sand and gravel, pieces related to pipe materials, and corrosion products. As a result of analyzing the concentrated particles of the filter before and after cleaning, it was found that the change in discoloration on the filter was large. In addition, as a result of comparing the weight and the concentration of the particles, it was found that the particles causing discoloration were significantly removed after cleaning. From the results of the endoscopy, it was confirmed that most of the precipitated and accumulated dark yellow discoloration matters inside water mains were removed through cleaning. Therefore, it seems that the particles causing discoloration in water decreased after cleaning. Therefore, it is expected that, if properly cleaning was applied, matters that cause discoloration can be removed from the water mains, and customer's complaints can also be reduced through water quality improvement.

This research proposes an optimal flushing operation technique in an effort to prevent secondary water pollutions and accidents in aged pipes, and to improve the cleaning effect of unidirectional flushing. Water flow directions were analyzed using EPANET 2.0, while flushing and air scouring experiments in forward and reverse directions were performed in the field. In 42 experiments, average residual chlorine concentration and turbidity were improved after cleaning compared to before cleaning. It was found that even when the same cleaning method was used, further improvement of cleaning effect was possible by applying air injection and reverse direction cleaning techniques. By means of one-way ANOVA(Analysis of variance), it was also possible to statistically verify the need of actively utilizing air injection and reverse direction cleaning. Based on correlation between turbidity and TSS, the total amount of suspended solids removal was estimated for 874 flushing operations and 194 air scouring operations. The result showed that air scouring used more discharge water than flushing by an average of 4.9 m3 yet with larger amounts of suspended solids removal by an average of 145.9 g. The result of analysis on turbidity values from 887 flushing operations showed low cleaning effect of unidirectional flushing for the pipes with diameters over 300 mm. In addition, the turbidity values measured during cleaning showed an increasing tendency as pipe age increased. The methodology and results of this research are expected to contribute to the efficient maintenance and improvement of water quality in water distribution networks. Follow-up research involving the measurement of water quality at regular time intervals during cleaning would allow a more accurate comparison of discharge water quality characteristics and cleaning effects between different cleaning methods. To this end, it is considered necessary to develop a standardized manual that can be used in the field and to provide relevant trainings.

본 연구는 난방온실의 온도분포 균일화를 위한 기초자료 제공을 목적으로 온수난방 방식의 토마토 재배 온실 에서 난방실험을 통하여 난방배관의 표면온도와 실내기온 사이의 상관관계를 분석하고, 난방배관의 열전달특성 분석과 난방배관 배치의 개선을 통하여 난방배관 표면온도의 편차를 줄이고 균일도를 향상시키기 위한 방안을 도출하였다. 서로 다른 두 온실의 온도분포를 분석하여 최대편차와 균일도를 검토한 결과, 온수의 유량이 많고 난방배관의 길이가 짧게 배치된 온실의 온도편차가 작고, 균일도는 높은 것으로 나타났다. 또한 순환팬을 가동한 경우에 온도편차는 작아지고 균일도가 개선되는 것을 확 인할 수 있었다. 난방배관의 표면온도와 실내기온 사이의 상관관계를 분석한 결과, 두 온실 모두에서 유의적인 (p<0.01) 정적 상관관계가 있는 것으로 나타났다. 온수난방 온실에서 실내기온의 분포는 난방배관 표면온도의 분포에 영향을 받는다는 것을 확인할 수 있었고, 온도편차 가 최소화 되도록 난방배관을 배치함으로써 실내기온 분포의 균일도를 개선할 수 있는 것으로 판단되었다. 난방 배관의 열전달 특성을 분석한 결과 배관의 길이가 길어 지면 온도편차는 커지고, 관내의 유속이 빨라지면 온도 편차는 작아지는 것으로 나타났다. 따라서 지선배관의 길이가 짧아지도록 난방배관을 배치하고, 관내의 유속을 제어함으로써 온실의 온도분포와 환경의 균일성을 개선 할 수 있을 것으로 판단되었다. 국내 온실에서 가장 많 이 사용하고 있는 튜브레일(40A) 방식의 온수난방시스 템에서 하나의 지선배관에서의 온도편차를 3oC 이내로 조절하기 위해서는 관내의 유속이 0.2, 0.4, 0.6, 0.8, 1.0m·s-1일 때 난방배관의 길이는 각각 40, 80, 120, 160, 200m 이내로 제한해야 하는 것으로 분석되었다.

PURPOSES: The purpose of this study is to identify the mechanism of road subsidence caused by damaged water and sewer pipes. METHODS: A series of soil chamber test using damaged water and sewer pipe models were conducted under various conditions. RESULTS : Characteristics of cavity expansion and collapse caused by damaged pipes were affected by the damaged location in the sewer pipe, the head on the water pipe, the distance between the damaged water pipe and outlet, and relative soil density. CONCLUSIONS: Sewer-pipe damage was considered a direct cause of road subsidence, and the cavity expanded discontinuously. When the outlet was located under the damaged water pipe, the cavity expanded in the water pipe’s direction, and collapse occurred above the pipe. However, when the outlet was located atop the damaged water pipe, the cavity expanded toward the outlet direction and resulted in a subsidence. Cavity expansion speed was affected by various conditions, such as the pipe’s water head, outlet position, distance between the damaged water pipe and outlet, and relative soil density. However, the cavity expansion shape did not affect factors, except for outlet position.

Corrosion inhibitors including calcium hydroxide have been used to prevent corrosion in the pipes for tap water supply. The corrosion index (i.e., Langelier Index) differs by area and water quality. The corrosion indices of the areas studied differed by more than 2.0. The ‘homogenized’ calcium hydroxide was added to the treated water at the K water treatment plant, in order to increase the value of the corrosion index and the concentration of calcium. As the result, the concentration of calcium was increased while the turbidity and pH changed little. The corrosion rate of the tap water with the 'homogenized' calcium hydroxide could be slowed down pretty much. The results suggested that the technology of 'homogenization' of calcium hydroxide can applied to tap water and desalinated water to prevent corrosion in water pipes even in corrosive pipes.

Pipe Deterioration Prediction (PDP) and Pipe Failure Risk Prediction (PFRP) models were developed in an attempt to predict the deterioration and failure risk in water mains using fuzzy technique and the markov process. These two models were used to determine the priority in repair and replacement, by predicting the deterioration degree, deterioration rate, failure possibility and remaining life in a study sample comprising 32 water mains. From an analysis approach based on conservative risk with a medium policy risk, the remaining life for 30 of the 32 water mains was less than 5 years for 2 mains (7%), 5-10 years for 8 (27%), 10-15 years for 7 (23%), 15-20 years for 5 (17%), 20-25 years for 5 (17%), and 25 years or more for 2 (7%).

Deposits discharged through the cleaning mainly were cement mortar, bitumen paintings and rust pieces, and fragments of perforation, stones and gravels. Deposits were more removed through swabbing pig cleaning rather than air scouring cleaning on the whole. However, air scouring cleaning were not influenced by the constraint conditions such as a change in the diameter or the presence of the valve in water mains compare to swabbing pig cleaning. So, it was thought that air scouring cleaning might be more favorable to water distribution network cleaning in the future. After the cleaning, water quality including residual chlorine and turbidity also was improved because of the removal of a significant amount of the deposits. Therefore, if the cleaning is continuously and regularly implemented in water mains, it is expected that it will help to recover the reliability and to preserve the health of water quality.

극심한 고온으로 인해 정상적인 작물의 재배가 어려운 여름철의 온실 내 기온을 억제시키기 위한 방법 중 가장 효율을 인정받고 있는 증발냉각법은 실내 습도의 증가로 인해 그 사용에 제한을 받게 된다. 본 연구에서는 온실에서 증발냉각법의 냉방효율을 높이기 위한 방법으로 냉수파이프를 설치하여, 그 열적 특성을 분석하고, 제습효과를 조사하였으며, 그 결과를 요약하면 다음과 같다. 동파이프와 아연도금스틸파이프의 총열전달량을 비교한 결과, 동파이프가 다소 크게 나타났으나, 유의성이 없었으며, 두 가지 파이프 모두 이론값 보다 실측값이 더 작게 나타났다. 냉수파이프 표면에 응축되어 제거된 수증기의 양은 동파이프와 아연도금스틸파이프 사이에서 큰 차이를 보이지 않았으나, 두 가지 파이프 모두에서 제습효과는 충분히 큰 것으로 나타났다. 냉수파이프를 설치함으로써 증발냉각시스템의 냉방효율을 평균 48%만큼 높일수 있으며, 평균 1.3℃만큼의 실내기온을 추가로 냉각시킬 수 있는 것으로 예측되었다. 또한, 냉수파이프를 이용해 증발냉각시스템의 가동으로 인한 실내의 과습문제를 해결하기 위해서는 파이프표면의 응축된 수분을 효과적으로 제거할 수 있는 장치나 방법에 대한 추가적인 연구가 필요할 것으로 판단된다.

본 논문에서는 상수관로의 효율적인 유지 관리를 위해 상수도 기술진단에서 점수평가법으로 도출된 관망성능평가결과를 이용한 상수도 관로의 내구연수 및 잔존수명 산정 방법을 제시하였다. 본 연구에서 잔존수명은 ‘모델에 의해 추정된 매설 후 최적교체시기까지 경과년수’를 의미하는 ‘내구연수’와 매설 후 경과년수의 차이로 정의하였으며, 내구연수는 관망성능평가기준으로 제시된 노후관로 판정기준 점수에 도달하는 시점으로 정의하였다. 연구대상지역의 관망성능평가에 사용된 평가항목들과 노후도 점수를 상수도 관로의 잔존수명 추정을 위한 다중회귀모델의 변수로 사용하였다. 잔존수명의 산정에 필요한 내구연수를 추정하기 위하여 구축된 회귀모델에 독립변수로 사용된 노후도 점수를 나타내는 변수의 값으로 노후관로 판정기준 점수에 해당하는 값을 대입하였다. 개발된 회귀모델을 이용하여 연구대상지역 상수도 관로의 내구연수 및 잔존수명을 산정하였으며 그 결과를 지방공기업법에서 제시하고 있는 내용연수와 비교하여 분석하였다.

Because aging sewer on the ground due to cavitation are a lot of social problems occur, the existing aging pipes are to be replaced. But is not easy to accurately detect the aging water and sewage pipes. In this research, we present a technique that can detect defective sewerage pipes used in GPR through Test-bed, which can be used as urban planning resources for water supply and drainage pipes replaced.

수도의 인구가 급증함에 따라 수원확보에 어려움을 겪고 있는 실정이다. 상수도시설은 준공 후 관의 매설로 인하여 관의 부식 및 노후화를 파악하기가 어렵다. 이러한 이유로 수도관로의 누수 파악과 누수로 인한 경제적 손실을 막기가 어렵다. 본 연구에서는 S대교의 누수량을 조사하고 시축관 설치 후의 누수량과 비교하여 누수감소량을 조사하였다. 그 결과 누수감소율이 약 98 %로 나타났으며, 이는 신축관을 설치하여 누수량을 감소하고 경제적 손실을 줄일 수 있는 것으로 판단된다.

본 논문에서는 상수관로의 개량(교체또는갱생) 우선순위를 결정하는데 있어서 평가되어야 할 인자 또는 요소를 관로의 파손이 전체관망에 미치는 영향 및 개별관로의 특성으로 구분하였고, 이들을 퍼지기법을 적용하여 정량적으로 산정할 수 있는 모형을 개발하였다. 퍼지기법으로 산정되는 관로의 파손이 전체관망에 미치는 영향을 관로의 퍼지 중요도로 정의하였으며, 개별관로의 특성은 관로의 퍼지 특성도로 정의하였다. 퍼지 특성도는 다시 퍼지 노후도 및 퍼지 난이도 등으로

본 논문에서는 상수관로의 파손자료를 이용하여 관로의 위험률을 산정하기 위해 사용되는 비례위험모형의 관로의 순차적 파손시간 예측정확도를 분석하고 이를 이용하여 관로의 경제적 교체 시간구간을 산정할 수 있는 방법론을 제시하였다. 비례위험모형에 기초한 생존함수를 이용하여 연구대상 관로들의 순차적 파손시간을 예측하고 이들을 기록된 파손시간과의 차이를 분석하였다. 이를 통하여 비례위험모형의 파손시간 예측 오차를 최소화하는 생존확률은 0.70인 것으로 결정되었으며

본 논문에서는 연구대상 지역의 150 mm 주철 상수관로의 첫 번째 파손으로부터 일곱 번째 파손사건에 대한 비례 위험모형을 구축하였다. 모형의 구축과정에서 공변수의 위험률에 대한 비례위험 가정을 검사하여 이를 위배할 경우 시간종속형 공변수로 모형화하였다. 그 결과 첫 번째 파손에 대해서는 관로의 제원 및 연결 방식과 급수인구가, 그리고 두 번째 파손 사건에 대해서는 급수인구의 영향이 시간에 따라 변하는 것으로 나타났다. 각 생존시간군의 기저위험률에 대한

본 논문에서는 대수-선형 파손율 모형(log-linear ROCOF)과 와이블 파솔율 모형(Weibull ROCOF)을 이용하여 상수도 주철 배수관로의 파손율을 모형화하고, '수정된 시간 척도'를 이용하여 최적교체시기를 산정할 수 있는 방법이 개발되었다. 두 ROCOF의 모형화를 위하여 개별 관로의 파손시간을 기록한 '파손 시간자료(failure-time data)'와 일정 시간간격 사이에서 발생하는 파손횟수를 기록한 '파손 횟수자료(failure-nu