In this research, We investigate evaluation on properties of mortars incorporated with waste LCD glass. LCD glass was grinded at 2,500, 3,500, 4,500 cm2/g blaine to replace 20% wt of cement. The compressive strength and Alkali-silica reaction test was carried out to verify effect of finess of LCD glass.

This study is corroborated as a fundamental resource to develop structural lightweight foamed concrete. Mortar using foaming agent decrease over 0.3 g/㎤ of weight of unit volume and increase over 27 MPa of compressive strength available structural purpose. After that, it is compared with Young's modulus of experiment and analysis from FEM analysis using SEM image.

In this paper, the tensile capacity of the grout-filled head splice sleeve experienced repeated loads was evaluated. From the tensile test of the sleeves, it was found that all the sleeves had enough tensile strength showing the tensile failure of the steel bars.

Two main parameters were examined such as CSA content and polymer-binder ratio to find effects on the strength, water absorption, chloride ion penetration depth, carbonation depth, length change and chemical resistance of polymer-modified mortar with CSA and EVA polymer powder (EVAPP). As results, compressive, flexural, tensile, adhesive strengths, and length change of the polymer-modified mortar with CSA and EVAPP increases with increasing CSA content and polymer-binder ratio, although the water absorption, chloride ion penetration depth, and carbonation depth decrease with increasing polymer-binder ratio and CSA content, and also the chemical resistance decreases. Such strength and durability development is attributed to the high tensile strength of EVA polymer and the improved bond between cement hydrates and aggregates because of the addition of EVAPP and CSA.

This study examines the compressive strength of cementless mortar in order to evaluate its mechanical characteristics according to the admixing of fly ash and blast furnace slag. This result showed that cementless mortar for shotcrete repair materials is profitable for using ZrSF.

강섬유는 콘크리트 부재의 인장영역에 효과적으로 작용하여 균열저항성을 높여주고 역학적 성능을 개선하는 것으로 알려져 있다. 본 연구는 팽창재를 사용한 강섬유 모르타르에 화학적 프리스트레싱을 인가하여 균열저항성 및 역학적 성능을 평가하는 연구이다. 이를 위해 시멘트 바인더의 10%를 치환한 CSA 팽장채가 사용되었으며 체적비 1%의 강섬유를 고려한 시멘트 모르타르 배합이 준비되었다. 기본적인 역학적인 성능평가 외에 노치를 가진 보를 제조하여 초기균열하중 및 파괴에너지를 평가하였다. 실험결과 강섬유와 CSA 팽창재를 혼입한 모르타르에서는 보통 강섬유 모르타르에 비하여 평균 1.75배의 균열저항성 하중이 증가하였으며, 파괴에너지 역시 1.41~1.53배 증가하였다. 최적의 강섬유 체적비와 팽창재의 혼입이 고려된다면 강섬유의 내부 화학적 프리스트레싱을 가진 복합재는 다양한 부재에 사용될 수 있으며, 외부하중에 효과적인 균열저감 기법으로 사용할 수 있다.

In this study, experimental research was carried out to study the high strength RC exterior beam-column joints regions using reinforcing detailings and high ductile fiber-reinforced mortar. Test results showed that specimen BCJISP were increased th maximum load-carrying capacity and showed stable hysteresis behavior and satisfactory crack pattern in comparison with th standard specimen BCJC.

This paper was manufactured for Self-compacting mortar using perlite. This results showed a good estimation that It will be able to examine for fire resistance.

최근, 프리캐스트를 통한 모듈화에 대한 관심으로 인해 교량 및 빌딩 뿐만 아니라, 원전구조물, LNG 가스탱크, 중소형 강합성 구조물 등 특수구조물에도 프리캐스트 모듈화에 대한 연구가 활발하게 이뤄지고 있다. 본 연구에서는 프리캐스트 제작의 시공 및 작업성, 원활한 자재의 조달할 수 있는 방법으로 페로시멘트 (ferrocement)를 바탕으로 한 스틸메쉬로 보강된 모르타르 프리캐스트 패널을 제작하였다. 모르타르는 고강도 및 고유동성을 지니도록 실리카퓸과 고로슬래그의 배합율에 대한 변수연구를 통해 최적의 배합을 선정하였으며, 1,200×600×150mm의 패널을 제작하여 스틸메쉬로 보강한 모르타르 시편과 일반 철근콘크리트 시편을 보강비 2%와 4%로 각각 제작하였다. 제작된 스틸메쉬로 보강한 모르타르의 프리캐스트 모듈화의 적용 가능성을 판단하기 위하여 기본적인 재료물성실험과 자유건조수축실험을 수행하였으며, 선하중으로 하중을 재하하여 3점 휨 시험으로 스틸메쉬로 보강한 모르타르의 구조성능을 검토하였다. 실험결과를 통해, 스틸메쉬로 보강된 모르타르 프리캐스트 패널은 높은 휨성능 및 연성효과가 있으나, 4%로 보강된 스틸메쉬 모르타르 프리캐스트 패널은 전단보강에 대한 고려가 필요하다고 판단되며, 이에 대한 조치가 이루어진다면 프리캐스트 모듈화 부재로 적용이 가능하다고 판단된다.

In this study, experimental research was carried out to study the high strength RC exterior beam-column joints regions, without the shear reinforcement, using high ductile fiber-reinforced mortar. Test results showed that specimen BCJNSP1.0 were increased th maximum load-carrying capacity and showed stable hysteresis behavior and satisfactory crack pattern in comparison with th specimen BCJNS without shear reinforcement in the beam-column joint region.

Girder type and slab type modular bridges require using UHSC(Ultra High Strength Concrete) and high performance mortar to connect each girder and slab modules at joint parts. This study presents the results of mock-up tests on the properties of UHSC and high performance mortar for modular bridge

Several researches of durability are proceeded domestically and internationally based on this circumstances and apply various integrity evaluation techniques and reinforcement methods of reinforced concrete structures to maintain the durability. Application of building coating materials on building external is effective as a popular material method to maintain durability of reinforced concrete structures as design.

본 연구에서는 alkali-free 및 aluminate 급결제를 사용한 OPC 및 GGBFS 숏크리트 모르타르의 응결특성, 강도특성, 전기저항성 및 염소이온 침투저항성을 실험적으로 고찰하였다. 실험결과에 따르면, alkali-free 급결제를 첨가한 GGBFS 모르타르는 응결시간 및 압축강도가 GGBFS 대체율에 관계없이 OPC 모르타르와 유사하게 나타났으나, aluminate 급결제를 첨가한 모르타르의 경우, GGBFS 대체율이 증가할수록 응결시간 및 압축강도가 크게 나타나는 경향을 보였다. 한편, 숏크리트 모르타르의 전기저항성 및 염소이온 침투저항성은 GGBFS를 50% 이상 대체한 모르타르가 우수한 경향을 나타내므로써, 적절한 대체율의 GGBFS를 사용한 모르타르가 숏크리트용 재료로써 우수한 성능을 나타낼 것으로 판단된다.

콘크리트내의 공극률은 콘크리트 구조물의 내구적인 특성과 밀접한 관련성이 있다. 특히, 콘크리트 시공시 가수된 물은 콘크리트의 비빔과 작업성에 일시적으로 도움이 되지만, 이러한 가수는 콘크리트의 공극을 증가하게 하며, 이는 콘크리트 구조물의 내구적인 성능저하를 야기하게 된다. 본 연구에서는 물시멘트비 0.45의 시멘트 모르타르에 대하여, 단위수량을 증가시켜 물멘트비를 0.45에서 0.60으로 증가시키면서 내구성능을 평가하였다. 즉, 각 물시멘트별로 소정의 재령까지 양생한 시험체에 대하여 강도, 염화물 확산, 투기성, 포화도 및 수분 확산계수 등의 다양한 내구성 실험을 수행하였으며, 이러한 실험결과들은 변화하는 공극률과 함께 분석되었다. 또한 내구성능의 변화 비율 및 그 패턴은 공극분포, 공극률, 그리고 단위수량을 고려하여 정량적으로 평가되었다.

The purpose of this study is to investigate the carbonation resistance of building coating materials applied to the mortar or concrete substrate including their cracked zone. The testing parameters for this experiment were the three crack widths in the substrate including non-crack, and two types of the coating materials.

본 연구는 최적의 투수성과 보수성 및 압축강도를 갖는 보투수 포장체의 개발을 위한 것으로, 단입도의 골재 및 SAP를 사용함으로써 투수계수 및 보수성능의 개선은 물론 포장체의 온도저감효과가 있음을 확인하였다. 이를 위하여 단입도 골재의 입경및 SAP 첨가량에 따른 압축 및 휨강도에 대한 시험을 실시하였으며, 보투수 포장체의 투수성능 및 보수량에 대한 시험을 실시하였다. 시험결과 단입도 골재의 입경이 작아질수록, SAP 첨가량이 증가할수록 압축/휨 강도는 증가하였으며, 투수계수는 SAP 첨가량이 증가함에 따라 감소하였다. 한편, 보투수 포장체의 흡수율 및 보수량은 골재의 입경이 작아질수록, SAP 첨가량이 증가할수록 증가하였으며, 보투수 포장의 온도저감효과는 아스팔트포장에 비해 최대 20℃ 까지 저감됨을 알 수 있었다.

본 연구는 표준실험체인 전단보강근이 없는 철근콘크리트 보(SSS)와 전단보강근이 있는 철근콘크리트 보(BSS), 성능개선실험체로는 전단보강근이 없는 철근콘크리트 보에 고로슬래그미분말을 혼입한 고인성섬유 복합모르타르를 타설한 실험체(SHF시리즈, SHFSC시리즈)로 총 11개의 실험체를 축소 제작하여 실험을 수행하였다. 실험을 통하여 얻어진 결과를 비교․분석하여 하중-변위, 파괴형태, 최대내력, 전단응력 등을 규명함으로써 구조성능의 개선정도를 평가하였다. 고로슬래그미분말을 혼입한 고인성섬유 복합모르타르를 이용한 철근콘크리트 보 실험체(SHF시리즈, SHFSC시리즈)의 경우 전단보강근이 없는 표준실험체(SSS)보다 전단응력은 각각 26%, 28%, 연성능력은 각각 5.27, 5.75배 증가하는 결과를 나타내었다. 또한, 충분한 연성적인 거동과 안정적인 휨인장 파괴를 나타내었다.

본 연구에서는 RC구조물의 내구 및 내화성능을 동시에 향상시킬 수 있는 고인성 모르타르 (FR-ECC)를 개발하여, 이를 RC구조물의 보수재료로서 사용하기 위한 실험적 연구를 실시하였다. 즉, FR-ECC를 이용하여 제조한 콘크리트 시험체의 강도, 열적특성, 모의부재의 철근부식특성, 내화성능 등에 대하여 검토하였으며, FR-ECC의 현장적용 가능성에 대해서도 평가하였다. 그 결과, FR-ECC는 기존 보수 모르타르에 비해 우수한 강도 및 내구성능을 보유하고, 휨균열 발생 후에도 외부열화 인자의 침입을 억제하여 철근부식을 방지하는 것으로 나타났다. 또한 FR-ECC를 적용한 부재는 ISO 834 가열조건에서도 우수한 내화성능을 갖는 것으로 나타났으며, 뿜칠성능 등의 현장시공 성능에서도 우수한 특성을 나타냈다.

본 연구에서는 보다 자유로운 형상의 슬리브를 만들 수 있는 구상흑연 주철을 이용하여 보다 효과적으로 구조성능을 발휘하면서 SD500 고강도 철근에 적합하게 개발된 모르타르 충전식 슬리브 철근이음을 대상으로 실물크기의 19개 실험체를 제작하여 반복가력실험을 실시하였다. 그리고 강도, 강성, 슬립을 중심으로 한 구조성능에 대하여 본 실험의 주요한 변수에 따르는 영향을 분석하고, 국내기준을 비롯한 주요기준의 요구 성능과 비교하였다. 본 연구결과에서는 SD500 고강도 철근용으로 개발한 모르타르 충전식 슬리브 철근이음은 반복하중이 작용하는 경우에 대하여 국내기준을 비롯한 주요기준에서 요구하는 구조성능을 보유하고 있는 것이 확인되었고, SD500 고강도 철근용 모르타르 충전식 슬리브 철근이음에 대한 구조설계 기준 정립에 필요한 정량적인 기술 데이터를 제시하였다.