OBJECTIVES: This study is to develop the optimum mixing proportions for cement concrete pavement with using recycled aggregates. METHODS: The mixture varied recycled coarse aggregates content from 50 % to 100 % to replace the natural coarse aggregates by weight. Tests for fundamental properties as a cement concrete pavement were conducted before and after hardening of the concrete. RESULTS: It was found that the variation in the amount of the recycled aggregate affected the compressive and flexural strength development, as well as the chloride ion penetration resistance. As the amount of the recycled aggregate content increased the compressive and flexural strength and the resistance to chloride ion penetration decreased. However, the resistance to freeze-thaw reaction was affected significantly. In addition, the gradation of the aggregate became worse and hence so did the coarseness factor as the recycled aggregate amount increased. CONCLUSIONS : The fundamental properties of the concrete with recycled aggregate does not seem to be appropriate when the recycled aggregate quality is not guaranteed up to a some level and its replacement ratio is over 50%. The optimized gradation of the aggregates should also be sought when the recycled aggregate is used for the cement concrete pavement materials.

일반적으로 교량 슬래브는 구조용 콘크리트로 구체를 시공하고 난 후 교면포장용 콘크리트로 포장공사를 실시하여 완성한다. 교면포장은 교통하중과 환경하중에 저항할 수 있도록 적절한 강도와 내구성을 가지는 재료로 시공되어야 한다. 현재 국내에서 적용되고 있는 교면포장용 콘크리트에는 합성고무 라텍스 수지를 첨가한 콘크리트 (Latex Modified Concrete)와 실리카흄을 첨가한 콘크리트가 있으며, 이들 콘크리트는 일반콘크리트에 비해 내구성을 향상시킨 고내구성 교면포장용 콘크리트로 분류되나, 고가의 재료로 경제성을 저하시키는 요인이 있다. 기존의 고내구성 콘크리트보다 경제적 효율을 강화하고, 콘크리트의 내구성을 향상을 통해, 궁극적으로 콘크리트 교면 포장의 공용성능을 향상시키고자 고분말도 플라이애시와 슬래그를 첨가한 교면포장용 삼성분계 시멘트 콘크리트의 최적배합을 도출하고, 이에 대한 실내 내구성을 평가하고자 한다. 콘크리트 교면포장에서 발생되는 파손 중 가장 많은 부분을 차지하는 것이 균열이며, 그 주요한 원인이 콘크리트 수축에 의한 것이다. 이에 교면포장의 내구성능 조건을 만족시키기 위해 고분말도 혼화재를, 수축균열 억제를 위해 팽창제와 수축저감제를 검토하였다. 실내 내구성 평가를 위해 재령별 압축강도시험과 수축에 대한 검토를 위해 자기수축시험을 진행하였다. 또한 내구성 평가를 위해 동결융해저항성시험, 표면박리 시험을 진행 하였다. 표. 1은 고분말도 플라이애시와 슬래그로 치환한 삼성분계 시멘트 콘크리트에 팽창제와 수축저감제를 비율에 따라 첨가한 배합비이며, 비교배합으로 포틀랜드시멘트만 사용한 배합을 통해 결과를 비교하였다. 압축강도 시험결과 삼성분계 시멘트 콘크리트는 재령 90일에 60MPa이상을 나타내었으며, 팽창제 치환율에 따라 감소하였으나, 충분한 강도를 확보하였다. 자기수축 시험결과 팽창제 치환율의 증가에 따라 자기수축 거동이 환화되며, 치환율이 8%에서 12%로 증가 시 오히려 팽창거동이 전환되는 특성을 보였으며, 수축저감제를 사용 시 수축보상측면에서 유리하였다. 동결융해저항성 시험결과 C5S1배합을 제외한 모든 배합에서 상대동탄성계수가 90%이상 나타났으며, 표면박리저항성 시험결과 모든 배합에서 Boras Method 기준 “Acceptable”등급이상, ASTM기준 2등급이상을 나타내어 적정한 저항성을 확보한 것으로 평가되었다.

PURPOSES : As a research to develop a cement treated base course for an airport pavement which can enhance its drainage, this paper investigated the strength, infiltration performance and durability of the pervious concrete with respect to maximum coarse aggregate sizes and compaction methods. METHODS : This study measured compressive strength, infiltration rate, continuous porosity and freeze-thaw resistance of pervious concrete specimens, which were fabricated with five different compaction methods and different maximum aggregate sizes. In addition, in order to reduce the usage of Portland cement content and to enhance environment-friendliness, a portion of the cement was replaced with Ground Granulated Blast Furnace Slag (GGBS). RESULTS: Compressive strength requirement, 5 MPa at 7 days, was met for all applied compaction methods and aggregate sizes, except for the case of self-compaction. Infiltration rate became increased as the size of aggregate increased. The measured continuous porosities varied with the different compaction methods but the variation was not significant. When GGBS was incorporated, the strength requirement was successfully satisfied and the resistance to freezing-thawing was also superior to the required limit. CONCLUSIONS: The infiltration rate increased as the maximum size of aggregate increased but considering construct ability and supply of course aggregate, its size is recommended to be 25mm. With the suggested mix proportions, the developed pervious concrete is expected to successfully meet requirements for strength, drainage and durability for cement treated base or subbase course of an airport pavement.

PURPOSES : This study is to investigate the fundamental properties of limestone added cement concrete for application of pavement. METHODS : As the production of Portland cement causes environmental problems, engineers have sought more environment-friendly concrete construction materials. Limestone powder can be used for concrete as a partial replacement of Portland cement. One of the great applications of limestone powder added cement concrete might be a cement concrete pavement since the concrete pavement consumes massive quantity of Portland cement. Experimental variables were different replacement level of limestone powder by 0% to 25% with 5% increment. Before hardening of fresh concrete, setting time and plastic shrinkage characteristics were investigated in addition to other basic properties. Properties of hardened concrete included compressive, tensile and flexural strength as well as drying shrinkage. RESULTS : The addition of limestone powder did not significantly affect the properties of fresh concrete. Strength deceased as the replacement ratio increased and when the replacement ratio was greater than 10% decrease rate increased. CONCLUSIONS : It was found that the partial replacement of the limestone powder to cement in pavement materials can be positively considered as its mechanical properties show comparable performance to those normal concrete.

본 연구에서는 고로슬래그 미분말 및 플라이애시와 같은 광물질 혼화재를 사용한 친환경 고성능 3성분계 시멘트 콘크리트 교면 포장의 성능을 평가하기 위하여 실험을 하였다. 광물질 혼화재의 혼입률 변화에 따른 3성분계 시멘트 콘크리트의 최적배합을 찾기 위하여 압축강도 및 휨강도 시험을 하였으며 최적배합을 사용하여 내구성 시험인 염소이온 침투저항성, 동결융해, 박리 저항성, 균열 저항성 및 알칼리골재반응 시험으로 친환경 고성능 3성분계 시멘트 콘크리트 교면 표장의 내구성 평가 및 신 구 콘크리트의 부착력을 평가하기 위하여 부착강도 시험을 하였다. 시험결과, 시멘트 70%, 고로슬래그 미분말15% 및 플라이애시 15%의 배합 바인더에서 압축강도 및 휨강도가 우수하게 나타났으며 이를 최적배합으로 도출하였다. 실내 및 시험시공에서 최적 배합을 사용한 실험결과는 염소이온 침투 저항성, 동결융해 저항성, 표면박리 저항성, 알칼리골재 반응 억제 및 내마모성이 우수하게 나타났다. 또한, 특수 제작된 Polymer Cement Mortar(Brooming)를 사용한 신 구 콘크리트의 부착력에서도 우수한 성능을 나타냈다.

국내 고속도로의 60% 이상이 시멘트 콘크리트 포장으로 건설되었으며, 그 중 공용년수가 20년이 넘어선 구간이 절반 이상에 달하고 있다. 노후화된 시멘트 콘크리트 포장의 보수 보강은 국내의 교통여건상 우회도로가 준비되기 어렵기 때문에 조기 교통개방이 요구되며 현재까지는 주로 아스팔트 덧씌우기가 사용되고 있다. 반면에 아스팔트 덧씌우기 포장은 조기 파손으로 인해 많은 유지보수비용이 지출됨과 동시에 도로사용자의 불편을 초래하고 있다. 최근 들어 노후화 된 시멘트 콘크리트 포장의 효율적인 보강공법으로 접착식 콘크리트 덧씌우기 공법에 대해서 적용을 시도하고 있다. 따라서 아스팔트 덧씌우기 포장과 접착식 콘크리트 덧씌우기 포장의 합리적인 선택에 대한 비교 분석을 위해 포장의 연도별 파손상태에 대한 다양한 data가 필요하다. 하지만, 국내에서는 아스팔트 덧씌우기 포장과 접착식 콘크리트 덧씌우기 포장의 공용 중 파손상태에 대한 자료가 체계적으로 구축되어있지 않다. 본 연구에서는 아스팔트 덧씌우기와 접착식 콘크리트 덧씌우기 공법이 적용된 구간의 파손에 대해 충분한 자료를 구축하고 있는 미국의 LTPP Data를 이용하여, 공용성에 대해서 평가하였다. 단, 아스팔트 덧씌우기와 접착식 콘크리트 덧씌우기 공법은 파손형태가 서로 상이함으로써, 상대적인 비교를 위해 각각의 구간에 대해 포장상태지수(PCI, Pavement Condition Index)를 Database화 하였으며, 아스팔트 덧씌우기 구간과 접착식 콘크리트 덧씌우기 구간의 수명에 대해서 비교 분석을 수행하였다.

국내 고속도로의 60% 이상이 시멘트 콘크리트 포장으로 건설되었으며, 그 중 공용년수가 20년이 넘어선 구간이 절반 이상에 달하고 있다. 노후화된 시멘트 콘크리트 포장의 보수 보강은 국내의 도로 교통여건상 우회도로가 준비되기 어렵기 때문에 조기 교통개방이 요구되며 현재까지는 주로 아스팔트 덧씌우기가 사용되고 있다. 반면에 아스팔트 포장은 조기파손과 잦은 보수 때문에 보수 보강에 대한 비용이 크다. 현 시점에서 아스팔트 덧씌우기가 국내에서 가장 많이 사용되고 있는 현실을 감안할 때, 아스팔트 덧씌우기의 수명에 미치는 영향인자가 무엇인지 검토할 필요가 있다. 따라서 아스팔트 덧씌우기 공법의 성능에 영향을 미치는 인자에 대해 조사할 필요가 있으나, 국내의 경우 아스팔트 덧씌우기의 공용 중 파손상태에 대한 자료가 체계적으로 구축되어있지 않다. 본 연구에서는 아스팔트 덧씌우기 수명과 영향인자간의 상관성을 비교하기 위해 다양한 파손자료를 구축하고 있는 미국의 LTPP data를 이용하여 노후화 된 시멘트 콘크리트 포장의 아스팔트 덧씌우기에 대해 조기파손을 방지하고, 효율적인 보수 보강을 위해서 아스팔트 덧씌우기 구간의 수명에 미치는 영향인자에 대해서 통계분석을 수행하였다.

본 연구는 고로슬래그미분말 및 실리카흄과 같은 광물질혼화재를 사용한 시멘트콘크리트 포장의 성능에 대한 역학적, 물리적 평가를 수행하였다. 광물질혼화재 사용 시멘트콘크리트 포장의 휨강도, 압축강도, 통과전하량, 염소이온 확산계수 및 초기표면흡수율을 소정의 재령에서 측정하였으며, 그 결과를 기준 콘크리트 포장의 성능과 비교하였다. 실험결과, 광물질혼화재의 종류에 따라 시멘트 콘크리트 포장의 강도거동은 다르게 나타났으며, 대체적으로 실리카흄을 사용한 콘크리트의 압축강도 발현이 다소 우수하게 나타났다. 뿐만 아니라, 콘크리트의 염소이온 확산계수는 기준 콘크리트에 비하여 매우 작은 경향을 나타냄으로써, 이는 광물질혼화재를 사용한 시멘트콘크리트 포장의 우수한 내염성을 다시 한번 확인 할 수 있었다. 도출된 실험결과를 바탕으로 하여, 향후 고성능 시멘트콘크리트 포장 설계를 위한 재료적 기초 데이터를 제시하고자 한다.