The ultra-fine and less agglomerated titanium carbonitride particles were successfully synthesized by magnesiothermic reduction with low feeding rate of solution. The sub-stoichiometric titanium carbide () particles were produced by reduction of chlorine component by liquid magnesium at of gaseous and the heat treatments in vacuum were performed for 5 hours to remove the residual magnesium and magnesium chloride mixed with produced . The final particle with near 100 nm in mean size and high specific surface area of was obtained by nitrification under nitrogen gas at for 2 hrs.

본 연구에서는 CCl4 존재하에서 Cl2(g) and ultra violet(200~300nm) 파장으로 maleic anhydride 와 Cl2(g)을 반응시켜 α,β-dichlorosuccinic acid 를 합성하였다. 그리고 두 번째 반응은 N-(α,β-dichloro)succinic acid 함유 glucosamine 유도체(I)를 합성하는 것으로 methanol 함유 2% acetic acid 용매 하에서 glucosamine과 과량의 α,β-dichlorosuccinic anhydride을 넣은 후 온도를 70℃로 올리면서 반응시켰다. 우리는 합성한 유기산 유도체들이 해태 김 재배와 피부미용에 주로 유용하게 활용할 것으로 본다.

Green phosphors K2BaW2O8:Tb3+(1.0mol%) were synthesized by solid state reaction method. Differential thermalanalysis was applied to trace the reaction processes. Three endothermic values of 95, 706, and 1055oC correspond to the lossof absorbed water, the release of carbon dioxide, and the beginning of the melting point, respectively. The phase purity of thepowders was examined using powder X-ray diffraction(XRD). Two strong excitation bands in the wavelength region of 200-310nm were found to be due to the WO42− exciton transition and the 4f-5d transition of Tb3+ in K2BaW2O8. The excitationspectrum presents several lines in the range of 310-380nm; these are assigned to the 4f-4f transitions of the Tb3+ ion. The strongemission line at around 550nm, due to the 5D4→7F5 transition, is observed together with weak lines of the 5D4→7FJ(J=3,4, and 6) transitions. A broad emission band peaking at 530nm is observed at 10K, while it disappears at room temperature.The decay times of Tb3+ 5D4→7F5 emission are estimated to be 4.8 and 1.4ms, respectively, at 10 and 295 K; those of theWO42− exciton emissions are 22 and 0.92µs at 10 and 200K, respectively.

La1-xSrxMnO3(LSM,0≤x≤0.5) powders as the air electrode for solid oxide fuel cell were synthesized by a glycine-nitrate combustion process. The powders were then examined by X-ray diffraction(XRD) and scanning electron microscopy (SEM). The as-formed powders were composed of very fine ash particles linked together in chains. X-ray maps of the LSM powders milled for 1.5 h showed that the metallic elements are homogeneously distributed inside each grain and in the different grains. The powder XRD patterns of the LSM with x< 0.3 showed a rhombohedral phase; the phase changes to the cubic phase at higher compositions(x≥0.3) calcined in air at 1200˚C for 4 h. Also, the SEM micrographs showed that the average grain size decreases as Sr content increases. Composite air electrodes made of 50/50 vol% of the resulting LSM powders and yttria stabilized zirconia(YSZ) powders were prepared by colloidal deposition technique. The electrodes were studied by ac impedance spectroscopy in order to improve the performance of a solid oxide fuel cell(SOFC). Reproducible impedance spectra were confirmed using the improved cell, which consisted of LSM-YSZ/YSZ. The composite electrode of LSM and YSZ was found to yield a lower cathodic resistivity than that of the non-composite one. Also, the addition of YSZ to the La1-xSrxMnO3 (0.1≤x≤0.2) electrode led to a pronounced, large decrease in the cathodic resistivity of the LSM-YSZ composite electrodes.

본 연구에서는 H1-길항체로 알려진 항히스타민제의 일종인 염산 아젤라스틴을 합성하기 위하여 phthalic anhydride, 4-chlorophenylacetic acid, hydrazine 2HCl를 이용하여 4단계 반응을 거쳐 합성하였다. 첫 번째 반응은 카르복실기와 히드록실기가 제거되는 반응이고, 두 번째 반응은 3-(4-chlorobenzylidene)phthalide의 비누화 반응이다. 세 번째 반응은 일차아민의 친핵성 첨가반응이 일어나는 반응이며, 네 번째 반응은 N-methyl-1-aza-bicyclo[3,2,0]heptane에 세 번째 반응의 생성물을 첨가하여 반응시키면 4-(4-chlorobenzyl)-1-(2H)phthalazinone가 합성되는 반응이다. 합성한 생성물을 FT-IR, 1H-NMR을 이용하여 분석하였고, 80%의 수율로 합성물을 얻었다.

무기안료는 인체에 대한 안정성과 다른 소재와의 상용성이 우수하며, 미적 특성을 감미하기 위한 화장품, 인쇄잉크, 페인트, 건설자재 등 다양한 분야에서 관심 받고 있다. 본 논문에서는 망간과 철이 도핑된 이산화티탄 안료를 합성하기 위하여 수열합성법을 이용하였다. 공정 변수로는 망간 전구체의 양, 철 전구체의 양 및 하소온도 등을 변화시켰다. 제조된 안료의 최적 조건은 망간 전구체의 양이 1.0wt%, 철 전구체의 양이 1.5wt% 그리고 하소온도 550℃일 때였다. 제조된 안료는 XRD, EDS, FE-SEM, Spectrophotometer, UV-Vis Spectrometer 등으로 분석 하였다.

본 연구에서는 변위기반 성능설계 개념에 의해 기존 철근콘크리트 기둥과 콘크리트에 강재를 매입한 SRC 합성기둥에 대하여 최대 설계지진 가속도에 대한 내진성능개선의 성능설계을 비교하였다. SRC 합성기둥은 구조물의 강도를 증가시킬 뿐 아니라 연성도를 증가시키는 효과가 있다. SRC 합성기둥의 단면은 H형 강재와 원형의 중공 강관을 매입한 형태로 구성되어 있다. SRC 합성기둥에 대한 P-M상관도와 단면 공칭휨모멘트를 분석하고 이를 바탕으로 SRC 합성기둥에 대한 설계 변위 추정을 위해 변위기반 내진 설계 알고리즘을 제시하였다. 성능기반설계에 의한 성능개선설계를 위하여 목표성능변위 및 설계지진가속도 조건에 대해 직접변위 기반 설계방법 및 변위계수법에 의한 내진성능개선 설계 방법을 제시하였다. SRC 합성기둥은 기존 RC 기둥과 비교하여 성능개선 설계 결과 변위 연성비 및 변위성능에서 크게 개선된 성능설계 결과를 나타내었다.

Concrete filled steel tube (CFT) columns have been widely used in moment resisting frame structures both in seismic zones. This paper discusses the design of such members based on the advanced methods introduced in the 2005 AISC Specification and the 2005 Seismic Provisions. This study focuses particularly on design following both linear and nonlinear methods utilizing equivalent static and dynamic loads for low-rise moment frames. The paper begins with an examination of the significance of pseudo-elastic design interaction equations and the plastic ductility demand ratios due to combined axial compressive force and bending moment in CFT members. Based on advanced computational simulations for a series of five-story composite moment frames, this paper then investigates both building performance and new techniques to evaluate building damage during a strong earthquake. It is shown that 2D equivalent static analyses can provide good design approximations to the force distributions in moment frames subjected to large inelastic lateral loads. Dynamic analyses utilizing strong ground motions generally produce higher strength ratios than those from equivalent static analyses, but on more localized basis. In addition, ductility ratios obtained from the nonlinear dynamic analysis are sufficient to detect which CFT columns undergo significant deformations.

Nanocrystalline powder could be synthesized by solid-state reaction using the mixture which was prepared by a high energy milling process in a bead mill for and nanocrystalline powders mixture. Effect of the milling time on the powder characteristic of the synthesized powder was investigated. Nanocrystalline with a particle size of 50 nm was obtained at . High tetragonal powder with a tetragonality(=c/a) of 1.009 and a specific surface area of was acquired after heat-treatment at for 2 h. High energy ball milling was effective in decreasing the reaction temperature and increasing the tetragonality.

nanotubes were successfully synthesized using an electrospinning technique followed by calcination in air. The nanotubes were the single phase nature of and consisted of approximately 14 nm nanocrystals. SEM and TEM characterizations demonstrated that uniform hollow fibers with an average outer diameter of around 124 nm and wall thickness of around 25 nm were successfully obtained. As anode materials for lithium ion batteries, the nanotubes exhibited excellent cyclability and reversible capacity of up to 25 cycles at as compared to nanoparticles with a capacity of . Such excellent performance of the nanotube was related to the one-dimensional hollow structure which acted as a buffer zone during the volume contraction and expansion of Sn.

Glasses were prepared with compositions of (13-x)BaO-80B2O3-7Li2O·xSm2O3, BBLSx(x=0.5, 0.4, 0.3) by melting the starting materials of boron oxide(99.9%), lithium oxide(99.9%), barium carbon oxide(99.9%), and samarium oxide(99.9%) and then quenching the melt at 1350˚C. This led to good-quality BBLSx(x=0.4, 0.3) and poor-quality BBLSx(x=0.5) glasses. The physical and structural properties of the BBLSx glasses were studied by means x-ray diffraction, scanning electron microscopy(SEM), differential scanning calorimetry(DSC), and dielectric spectroscopy. From the x-ray diffraction and SEM results, the quality of the BBLSx glasses significantly depends on the Sm2O3 concentration. The x-ray diffraction pattern showed that the crystallites in the BBLSx glasses after heat treatment at 700˚C may be LiBaB9O15. From the DSC results, the glass transition temperatures(Tg), crystallization temperatures(Tc), and the maximum temperatures of the crystallized(Tp) BBLSx glasses all changed with the Sm2O3 concentration. According to the dielectric spectroscopy results, the values of the real dielectric constant and Tan δ of the BBLSx glasses depended on the Sm2O3 concentration. The values of the real dielectric constant and Tan δ were also shown to depend on the measuring temperature, possibly due to the ion migration in the bulk of the BBLSx glasses.

Li1+xAlxTi2-x(PO4)3(LATP) is a promising solid electrolyte for all-solid-state Li ion batteries. In this study, LATP isprepared through a sol-gel method using relatively the inexpensive reagents TiCl4. The thermal behavior, structuralcharacteristics, fractured surface morphology, ion conductivity, and activation energy of the LATP sintered bodies areinvestigated by TG-DTA, X-ray diffraction, FE-SEM, and by an impedance method. A gelation powder was calcined at 500oC.A single crystalline phase of the LiTi2(PO4)3(LTP) system was obtained at a calcination temperature above 650oC. The obtainedpowder was pelletized and sintered at 900oC and 1000oC. The LTP sintered at 900~1000oC for 6 h had a relatively low apparentdensity of 75~80%. The LATP(x=0.3) pellet sintered at 900oC for 6 h was denser than those sintered under other conditionsand showed the highest ion conductivity of 4.50×10−5S/cm at room temperature. However, the ion conductivity of LATP(x=0.3) sintered at 1000oC decreased to 1.81×10−5S/cm, leading to Li volatilization and abnormal grain growth. For LATPsintered at 900oC for 6 h, x=0.3 shows the lowest activation energy of 0.42eV in the temperature range of room temperatureto 300oC.

본 연구에서는 밀크 카제인과 WPU를 이용한 하이브리드 수지를 합성하였다. 합성한 하이브리드 수지를 피혁(Full-Grain) 표면에 코팅을 하여 카제인이 하이브리드수지에 어떤 영향을 주는지에 대해 분석 하였다. 내용제성 테스트 데이터에 의하면 WPU 와 하이브리드 수지 양쪽 모두 높은 물성치를 나타내었다. 인장 강도 측정치에서는 WPU 단독 결과(2.130 kgf/mm2)가 가장 낮은 수치를 나타내었으며, WPC-3(WPU 91: casein resin 9)의 경우가 가장 높은 인장력(2.191 kgf/mm2)을 나타내었다. 또한 내마모도 측정에서는 WPC-3(50.090 mg.loss)가 좋은 물성값을 나타내었다. 연실률의 경우 WPU(637 %) 단독 코팅물의 분석값이 가장 높은 637%로 알 수 있었다.

용해성이 우수하며, 강한 electron-withdrawing 특성을 나타내는 cyano group 을 가지는, 새로운 전자acceptor 재료인 malononitrile 유도체 (2-(2,6-bis((E)-4-tert-butylstyryl)-4H-pyran-4-ylid-ene)malononitrile (t-BuPM)을 합성하였다. 합성된 acceptor 재료 t-BuPM을 donor와 acceptor 재료로 널리 사용되고 있는 poly[2-Methoxy-5-(2-EthylHexyloxy)-P-Phenylene-Vinylene](MEH-PPV)와 (6)-1-(3-(methoxycarbonyl)propyl)-{5}-1-1-phenyl-[5,6]-fullerene (PCBM)과 함께ternary blend system으로 유기 태양전지 소자를 제작하였다. 소자는 ITO/PEDOT:PSS/MEH-PPV:t-BuPM:PCBM/Al 구조와 같이 제작하여 광전변환 특성을 측정하였다. 합성된 재료의 HOMO와LUMO energy level은 -5.97,-3.49eV로 측정되었으며, t-BuPM을 사용하여 ternary blend system 으로 제작된소자의 에너지변환 효율은 AM 1.5G, 1 sun 조건(100mA/cm2)에서 1.85%로 측정되었다. Short circuit current density (Jsc)는 5.54mA/cm2, fillfactor(FF)는 41%, open circuit voltage(Voc)는 0.80 V로 측정되었다.

본 연구에서는 말단기에 diene 기와 dithiol 기를 갖는 두 가지 새로운 액정 단량체의 합성을 보고하며, 이를 배향 후 광경화하여 광학 위상지연 필름을 제조하는 방법에 대해 논의하였다. 특히 합성된 두 가지액정단량체의 구조를 확인하였으며, 이들의 액정특성을 연구하였다. 또한 이들을 광개시제와 혼합하여광경화형 액정조성물을 제조하고 이를 러빙 배향막이 코팅된 표면 위에서배향시킨 후 광조사하여 thiol-ene 중합에 의해 경화함으로써 광학 위상지연 필름을 제조하였다.

4'-formylbenzo-15-crown-5와 RHD, RED의 반응에 의해 새로운 두 종류의 크라운 에테르 RHDC 와REDC를 합성하였다. RHD, RED는 로다민 6G와 hydrazine, ethylenediamine을 이용하여 합성하였다.합성된 화합물들에 여러 가지 금속 양이온을 첨가하여 선택적인 형광 인식 특성을 알아보고, 형광 센서로서의 가능성에 대해 검토하였다. 합성된 화합물의 금속 인식 특성을 형광스펙트럼으로 측정한 결과 형광이 증가하였으며 Fe3+ 대한 인식이 가장 좋았다.

Mass production-capable powder was synthesized for use as cathode material in state-of-the-art lithium-ion batteries. These batteries are main powder sources for high tech-end digital electronic equipments and electric vehicles in the near future and they must possess high specific capacity and durable charge-discharge characteristics. Amorphous silicone was quite superior to crystalline one as starting material to fabricate silicone oxide with high reactivity between precursors of sol-gel type reaction intermediates. The amorphous silicone starting material also has beneficial effect of efficiently controlling secondary phases, most notably . Lastly, carbon was coated on powders by using sucrose to afford some improved electrical conductivity. The carbon-coated cathode material was further characterized using SEM, XRD, and galvanostatic charge/discharge test method for morphological and electrochemical examinations. Coin cell was subject to 1.5-4.8 V at C/20, where 74 mAh/g was observed during primary discharge cycle.