The concrete wall panels are composed of various members such as studs, brackets, bolts and nuts, etc. Embedded studs in the concrete wall resist transferred lateral and horizontal load in the structure. The thickness of the concrete wall influences shear behavior of embedded studs. The finite element analysis was carried out with respect to the thickness of the concrete wall to investigate shear behavior of embedded studs. The numerical analysis results were compared with the experimental results and confirmed that The deformation of the stud anchor is reduced with an increase of the thickness of the concrete wall.

This study investigates the flexural shear strength of ultra high performance concrete I-girder. The effect of aspect ratio on the flexural - shear strength of UHPC was analyzed using finite element analysis. The UHPC I-type girder was modeled using 3D shell elements and analyzed using geometric and material nonlinear analysis. The boundary condition is simple support condition and a displacement load is applied to the center of the upper flange. The results shows that shear strength decreased as the aspect ratio increased and the bending-shear failure of UHPC I-girder does not occur even at larger moment than ordinary concrete due to the cross-linking action of steel fiber.

Prestress is a reinforcement method to control crack due to moment on concrete girders with low tensile strength. In the existing literature, it is mentioned that prestress for ordinary concrete affects not only crack control but also shear strength enhancement. As the construction material improves, UHPC(Ultra-HIgh Performance Concrete) with excellent strength and ductility has been developed by combining ultra-high strength concrete and steel fiber. However, study on the effect of prestress on the shear strength of UHPC with different material properties from ordinary concrete is lacking. Therefore, in this paper, the effect of prestress on the shear behavior of UHPC I-girder is studied by finite element analysis. As a result of the analysis, it has been confirmed that the prestress increases crack strength and shear strength of UHPC.

Sewerage age more rapidly than other facilities, leading to the destruction of the pipeline. Therefore, the replacement of old sewer pipes through long-term construction is costly. In order to solve this problem, this study investigated the ferronickel based sewer pipe with improved chemichal resistance and durability from concrete rigidity pipe. ABAQUS was used as the finite element analysis program and the load was calculated by the method given in the sewage facility standard. Therefore, the results of this study can be referenced in the design and construction of sewer pipes.

콘크리트 혼화제의 무수축 그라우트에서 산란체와 흡수체의 영향은 빛산란에 의해 파장에 대 한 산란세기로 설명된다. New Austria Tunnel Method의 수지에 대한 산란의 분자특성들은 연구하기 위해 Monte Carlo Simulation하였다. 이는 산란매질에서 광학적 파라미터들(μs, μa, μt)에 의해 조사 되어 그들의 영향을 알 수 있었다. 산란매질에서 광자에 대한 빛 분포에 의한 결과는 광원에서 검출기 까지 거리가 가까우면 무수축혼화제의 산란이 증가하여 산란세기가 크게 나타나는데 혼화제가 첨가함에 따라 무수축 성질이 크게 나타났다. 이는 강구조물의 내구성을 위한 코팅과 부식에서 좋은 모델을 디자 인하는데 도움이 될 것이다.

In fire design for floors, the three criteria of stability, integrity and insulation are required for the specified fire resistance duration. Among these, stability is not easy to confirm. For solid prestressed concrete slabs of uniform thickness, Eurocode 2 provides tabulated data and specifies an axis distance to the centroid of strands to achieve particular fire resistance ratings, but it is not clear if this data can be used for a wide range of different prestressed slab profiles. In order to verify the current code-fire ratings for precast prestressed slabs, both simple and advanced calculation methods are investigated. This paper examines the use of calculation methods, accounting for the real behaviour of unprotected simply supported prestressed concrete slabs exposed to the standard ISO 834 fire. The calculated fire resistance of each prestressed concrete slab is compared with tabulated data in Eurocode part 1.2, with detailed discussion.

When reinforcing an existing reinforced concrete beam-column building with a precast concrete panel, special connection between the PC member and the RC member is required to solve the time dependent deformation of the RC member and to receive the large shear forces. The aim of this study is to obtain the shear strength of upper connection between the existing RC beam-column and infilled PC wall panels in experimentally and theoretically. Thus, the static shear loading tests were conducted on the 6 specimens with the plate connection. Shear failure was resulted from the weakest portion of interior PC panel, exterior RC, and the connection, when the PC portion which located at the center of specimen was pulled upward from the bottom. T he experimental result was compared with analytical result from ACI 318M-14 Chapter 17 for the shear strength of post-installed anchor and PCI Handbook 7th edition 6.8 Structural Steel Corbel (PCI Design Handbook 7th edition, 2010) for the strength of cast-in H-beam. The analytical and experimental results show final failure at the same location. The failure loading of experiment showed larger than average 6% to that of the analysis.

PURPOSES :Infiltration of moisture, polluted material, and deicer into concrete, accompanied by freeze and thaw can cause significant deterioration of concrete pavement. In order to protect concrete from deterioration, it is necessary to prevent the infiltration of these concrete external materials. The moisture-repellent agent, which is a surface treatment and maintenance material added to concrete structures to render them water resistant, has advantages such as prevention of water infiltration and security against air permeation. Nano-coat, which is referred to as silicon hydride, is typically used as a moisture-repellent agent. Therefore, in this study, an attempt is made to use penetration-type Nano-coat as an alternative in order to evaluate its applicability through environmental resistance tests.METHODS:This study aimed to evaluate the applicability of penetration-type Nano-coat, which can provide water repellency to concrete, in concrete pavements, through various environmental resistance tests such as freezing and thawing resistance, chloride ion penetration resistance, and surface scaling resistance tests. The applicability of penetration-type Nano-coat was demonstrated based on the specification of KS F 2711, KS F 2456, and ASTM C 672.RESULTS :In the case of penetration-type Nano-coat applied on sound concrete, an increase in concrete durability was demonstrated by the negligible chloride ion penetrability and the absence of scaling, as revealed by visual observation of the surface, after 50 cycles of scaling resistance test. In addition, test result of the application of penetration-type Nano-coat on deteriorated concrete established that concrete surface pretreated by grinding provided improved durability than non-treated concrete.CONCLUSIONS:This study indicates that penetration-type Nano-coat is applicable as an effective alternative, to increase the durability of concrete structures. In addition, it was known that pretreatment of deteriorated concrete surface, such as grinding, is required to improve the long-term performance of concrete pavement.

국내에서 개발중인 콘크리트 저장용기는 방사성 물질의 격납 건전성을 유지하기 위하여 내부에 캐니스터를 포함하고 있다. 본 논문에서는 콘크리트 저장용기 내부 캐니스터의 뚜껑 용접시, 용접시간 저감과 이에 따른 캐니스터 용접부의 구조적 건 전성을 확보하기 위한 방안으로, 정상, 비정상 및 사고조건에서 캐니스터 용접부 균열을 진전시키는 하중에 의해 발생되는 균열 깊이를 분석하여, 용접부의 최대 허용결함깊이를 평가하였다. 정상, 비정상 및 사고조건에서의 구조해석은 범용 유한 요소해석 프로그램인 ABAQUS를 사용하였으며, 허용결함깊이는 ASME B&PV Code Section XI에 따라 막응력과 조합하중 에 대해 평가하였다. 평가결과 콘크리트 저장용기의 캐니스터 용접부의 허용결함깊이는 18.75 mm로 평가되었으며, 이는 NUREG-1536에서 권고하고 있는 임계결함깊이를 만족하고 있는 것으로 나타났다.

지난 수십 년간 공공시설 및 사유지 적용을 위한 롤러전압콘크리트포장의 사용실적은 꾸준히 증가 하고 있는 추세이다. 롤러전압콘크리트포장은 아스팔트포장의 시공특성과 전통적 콘크리트포장의 재 료적 특성을 동시에 나타낸다. 또한 작업성(workability)과 다짐성(compactibility)은 롤러전압콘크 리트포장의 우수한 배합설계를 결정하기 위한 주요요소로써, 강도가 충분히 확보된 콘크리트라 할지 라도 적정 반죽질기 또는 작업성이 확보되지 않으면 시공이 용이하지 않을 수 있다. 일반적으로 포장 적용을 위한 롤러전압콘크리트의 배합설계 시 흙다짐 방법 및 반죽질기 방법을 사 용하고 있으나, 흙다짐 방법의 경우 작업성을 고려하지 못하며 반죽질기 방법은 작업성만을 고려하고 있다. 이에 본 연구에서는 포장 적용을 위한 롤러전압콘크리트에 대하여 실내실험 변수와 현장 공용성을 모두 만족시키는 배합설계방법의 개선방안을 제안하였다. 이를 위하여 실내실험 변수를 현장 공용성 으로 연계하여 적정 공용성을 확보할 수 있는 최적 롤러전압콘크리트 배합을 도출하였으며, 롤러전압 콘크리트의 주요 물성인 반죽질기, 강도 및 내구성과 배합비 간의 상관관계를 규명하기 위하여 다양 한 실내실험을 진행하였다. 또한 실제 현장 조건에서 이와 같은 물성들을 연계시키기 위하여 속초인 근 고속도로 부체도로에 총 5개 구간의 롤러전압콘크리트포장을 시공하여 품질관리 변수인 반죽질기 에 근거하는 하중지지력과 표면 물성에 대하여 조사하였다. 이와 같은 물성들의 새로운 이해는 포장 적용을 위한 롤러전압콘크리트의 배합설계절차 개선으로 이어진다.