The purpose of this experimental study is to chloride ion penetration resistance performance of concrete using Nano-TiO2 Carrier. As a result, concrete using Nano-TiO2 Carrier was confirmed to be superior than ordinary concrete and commercial TiO2 concrete chloride ion penetration resistance performance.

Recently, a great social damage has been caused by the sargassum homeri, which has flowed from China in the Jeju and Namhae coasts. In this study, biopolymer was prepared by using sargassum homeri and applied to bridge pavement concrete. The performance of chloride ion penetration resistance of the bridge pavement concrete made of biopolymer was evaluated. As a result, excellent penetration resistance performance was shown.

In this study, chloride penetration resistance and electrical resistivity properties of concrete using industrial waste were evaluated. From the results, the chloride diffusion coefficient increases and electrical resistivity decreases when electric furnace slag is mixed. It is needed that the comparison of results with long-term because the electric furnace slag has a ferrous component.

In this study, the effect of calcium leaching on chloride ion penetration resistance of mortar specimens was evaluated. According to test results, the penetration depth of chloride ion was increased after the calcium leaching attack.

본 연구에서는 표면 침투 및 코팅형 흡수방지재인 Polydimethylsiloxane(PDMS)을 고인성 섬유복합체(ECC)에 적용하여 적용성, 강도 평가 및 염화물이온 침투 저항성능에 대한 연구를 수행하였다. PDMS 적용 방법에 따른 침투깊이를 분석한 결과 모든 방법에서 KS F4930 의 기준을 만족하는 것을 확인하였다. 적용 방법 중, 침지 방법이 가장 우수한 침투깊이를 보였으나 현장적용성을 고려할 경우 스프레이 방법이 적용 가능한 것으로 확인되었다. ECC 배합에 따른 PDMS 침투깊이 실험 결과 배합강도가 감소할수록 침투깊이는 최대 70% 이상 증가하는 경향을 나타났다. 압축강도 시험 결과에서는 PDMS 침투 깊이가 큰 M4-A, M4-B 시험체의 압축강도는 PDMS를 적용하지 않은 M4 시험체와 비교하여 9.6%, 8.0% 압축강도가 감소하였다. 또한, 침투깊이가 작은 M1-A와 M1-B 시험체의 압축강도는 M1 시험체와 비교하여 4%, 2.2% 감소하여 PDMS 침투깊이가 클수록 강도감소율이 증가하였다. 염소이온침투 저항성능 평가 시험결과, PDMS의 침투깊이가 클수록 염소이온 침투 저항성능이 향상되는 것을 확인하였다.

This study is to perform experiment of concrete according to addition of blast furnace slag powder and sulfur activator dosages. Blast furnace slag powder used at 30, 50, 80% replacement by weight of cement, and liquid sulfur additives was chosen as the alkaline activator. As a result, it should be noted that the sulfur alkali-activators can not only solve the disadvantage of blast furnace slag concrete but also offer the chloride resistance of alkali-activated blast furnace slag concrete to blast furnace slag concrete.

This study was evaluated the chloride penetration resistance performance of Surface Protection Material(SPM). SPM was applied 0.25 and 0.51 kg/㎡ to the surface of the mortar and immersed aging of the chloride solution 7, 14, and 28 days. As a results, In the case of SPM was applied, chloride did not penetrate until the 28th day.

In this study, the resistance of chloride penetration and sulfate attack of mortar substituted heavyweight waste glass were evaluated. As a result, chloride penetration depth and diffusion coefficient decreased with the substitution of waste glass, chloride penetration resistance is increased. For sulfate attack resistance, the effect of heavyweight waste glass was little.

In this study, the absorption protection agent was applied to the surface of fiber reinforced concrete to evaluate the chloride ion penetration resistance. The evaluation was based on the method presented in KS F 2711. It was confirmed that the resistance performance against chloride ion was improved by 56∼71% when the coating material was applied.

In this study, poly-silicon sludge was used in replacement with Portland cement as SCMs. Poly-silicon sludge has an ability to improve the durability to the concrete system. Thus, the chloride penetration test of PS specimens was conducted for the confirmation of the durability. From the results, The penetration depth of the plain specimens is deepest, and gradually decreases as PS substitution rate increases.

From the test results, it was found that the compressive strength and the resistance of chloride ion penetration were evaluated the slag content of the concrete for bridge pavement. Compressive strength test results showed that initial strength was decreased as slag replacement ratio increased. The chlorine ion penetration performance increased with increasing strength.

From the test results, it was found that the compressive strength and the resistance of chloride ion penetration were evaluated the slag content of the concrete for bridge pavement. Compressive strength test results showed that initial strength was decreased as slag replacement ratio increased. The chlorine ion penetration performance increased with increasing strength.

The Chloride ion penetration resistance of Engineered cementitious composite using surface coating material was evaluated in this study. The test results showed that the amount of chloride ion of surface coated specimens were decreased approximately 22 % lower than that of plain specimens

This study is the study of the chlorine ion penetration resistance of the study of the natural durability enhancement materials that can reduce cracking of the concrete. The durability enhancement materials of natural were substituted 10%, 20%, 30% of cement, the results were confirmed excellent chlorine ion penetration resistance as the more increasing the natural durability enhancement.

This paper is to investigate experimentally the effect of waste cooking oil on compressive strength and chloride penetration resistance of high volume fly ash and blast furnace slag concrete. According to results, the incorporation of waste cooking oil resulted in an improvement of penetration resistance of chloride.

콘크리트 구조물은 일반적으로 동결융해 작용을 받는 조건에 노출되고, 이러한 동결융해작용은 콘크리트의 공극구조를 변화시키고, 콘크리트의 내구성을 저하시킬 우려가 있다. 따라서 본 연구에서는 동결융해작용에 의한 콘크리트 내부공극구조 변화와 동결융해작용을 받은 콘크리트의 내구특성을 평가하고자 하였다. 실험결과, 기존의 동결융해 평가기법에 따르면 모든 배합에서 우수한 내구성능을 나타내었으나, 동결융해 작용에 노출됨에 따라 50~100nm 크기의 공극이 크게 증가하며, 콘크리트 염화물침투저항성이 저하하였다. 수중양생 콘크리트의 공극구조와 염화물 침투저항성은 선형관계를 보이지만, 동결융해작용을 받으면 내부공극구조의 변화로 선형관계가 저하하였다. 동결융해작용과 염화물침투를 동시에 받는 구조물의 내구성 평가기준에 대한 재검토가 필요할 것으로 판단된다.

본 연구에서는 초기 균열을 도입한 철근콘크리트 부재에 대한 침지 염화물 침투 실험을 수행하였다. 염화물 확산 특성과 임계 균열폭을 비교하였으며, 콘크리트 자기복원 특성을 검토하였다. 실험결과에 따르면, 표면 균열폭이 증가할수록 염화물 침투저항성이 크게 감소하였으며, 광물질 혼화재를 사용할 경우, 비균열 부재의 염화물 침투저항성은 크게 개선되었지만, 고로슬래그 및 플라이애쉬 혼화재를 사용할 경우에 균열이 발생하게 되면 도리어 염화물 침투저항성은 보통 콘크리트에 비해 크게 저하하였다. 임계 균열폭은 침지 염화물 침투 실험 결과 평균 29㎛으로 측정되었다. 자기복원 현상에 의해 4∼15㎛범위의 균열이 복원되었다. 그러나 콘크리트 자기복원 현상에 의해 시각적으로 복원된 부분의 염화물 침투 저항성은 완전히 회복되지 않았다.