In this thesis, using the 400 series ferrite stainless steel such as 434LD2 which are furter excellent then the existing ferric products in mechanical characteristics, and experiment has been conducted on corrosion resistance of sensor ring. The results are following. 1. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition. 2. 434LD2 ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. thus the decreasing production process has been obtained. 3. As hardness value of HRB 80 and tensile test, 434LD2 ferrite stainless steel with show a good endurance when it is combined to constant velocity joint (c/v joint), and has a good hardness properties endurable to sand and pebble impact.

용융탄산염 연료전지(MCFC)의 상용화에 있어서 가장 큰 문제점으로 지적되고 있는 분리판 wet-seal부의 내식성 향상을 위해 AISI 316L 스테인레스강에 Ni은 전기도금법으로, Y과 Al은 e-beam PVD법으로 피복하여 Ni/Y/Al충을 형성시켰다. 800˚C 환원분위기에서 5시간의 열처리를 통해 NiAlY 합금층을 얻을 수 있었으며, 그 후 650˚C 용융탄산염내에서 as-received AISI 316L 스테인레스강과 200시간의 침지실험을 퉁해 내식성이 비교.평가되었다. SEM/EDS를 통한 단면 관찰 결과, Y의 첨가에 의해 치밀한 산화막을 형성하여 분리판 wet-seal부의 내식성을 향상시킬 수 있었다.

In this paper, sensor ring for antilock brake system was studied using the 400 series ferrite stainless steel powder. Because of more excellent corrosion resistance and mechanical characteristics than iron, sensor ring has been manufactured by P/M(Powder Metallurgy) method 400 series ferrite stainless steel. the results are following. 1, Compared with sensor ring made by iron, 400 series ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. thus the decreasing production process has been obtained. 2. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition.

초강인 AISI 4340강을 850˚C에서 2시간 동안 오스테나이징 처리 후 수냉하고, 250, 400, 600˚C에서 각각 2시간 동안 템퍼링 처리를 하였다. AISI 4340강의 인장 특성은 상온에서 측정되었다. AISI 4340강 위에 니켈 전해도금된 것과 도금되지 않은 시편의 분극 특성이 3.5wt%NaCI 수용액과 인공해수에서 측정되었다. AISI 4340강위에 니켈 전해도금된 시편은 500mV(vs. Ag/AgCI)이하의 전위에서 부식 저항이 크게 향상되었다. 그러나 1A/cm2의 전류밀도에서 30분 이상 니켈 전해도금된 시편은 도금층에 불순물과 기공이 형성되었기 때문에 AISI 4340강의 부식 저항은 감소되었다. AISI 4340강의 수소취화형 응력부식균열을 여러 작용 응력과 음극인가전력에서 U-bend 시편을 이용하여 IN 3.5 wt% NaCI 수용액에서 조사되었고, 수소취화형 응력부식균열 거동은 주사전자현미경으로 조사되었다.

To improve the corrosion resistance of stainless steel and Fe, the adherence between fIlm and substarte and the corrosion resistance to ceramic fIlm (TiO2 and ZrO2), coated by RF magnetron sputtering, were studied. The adherence index (X) was determined by the measure of micro - hardness test. Also, the corrosion resistance on oxide coatings was studied using electrochemical measurement. The main results obtained are as the following: 1) In the micro - hardness test, with 1J.UI1 thickness fIlm, it has only one the value of X. Above 2J.UI1 thickness fIlm, however, get another value ofX as the cracks in fIlm. 2) The adhensivity of titania (TiO2) coated fIlm is superior to that of zirconia (ZrO2) coated fIlm. 3) All oxide fIlm used adhere well on the mild materials such as pure steel than high intensity materials like stainless steel. 4) The corrosion resistance of zirconia coated materials was improved compared to titania coated materials.

To ceramic mm, SiO2 and Al2O3, coated on pure Fe and stainless steel(SUS41O) by RF magnetron sputtering, the adherence between mm and substarte was studied. The adherence index (χ) was determined by the measure of micro hardness test. Also, the corrosion resistance on oxide coatings was studied using electrochemical measurement. The main results obtained are as the following: 1) In the micro-hardness test, with 1μm thickness mm, it has only one the value of χ. Above 2μthickness fIlm, however, get another value of χas the cracks in fIlm. 2) The oxide fIlm adhere well on the mild materials such as pure steel than high intensity materials like stainless. 3) Alumina(Al2O3) coated materials have better corrosion resistance than silica(SiO2)coated materialsterials

MATERIAL AND PROCESS VARIABLES THAT STRONGLY AFFECT THE CORROSION RESISTANCE OF PA4 STAINLESS STEELS, INCLUDE : ALLOY COMPOSITION, POWDER CLEANLINESS, NITROGEN, OXYGEN AND GARBON CONTENTS, CHROMIUM DEPLETION DUE TO SURFACE EVAPORATION AND SINTERED DENSITY. THE OPTIMUM PROCESS PARAMETERS FOR DELUBRICATION AND SINTERING THAT RESULT IN LOWEST LEVELS OF NITROGEN, OXYGEN AND CARBON AND MINIMUM LEVELS OF CHROMIUM DEPLETION WILL BE PRESENTED, FOR A NUMBER OF AUSTENTIC AND FERRITIC STAINLESS STEELS. THE EFFECT OF SINTERED DENSITY ON THE CORROSION RESISTANCE OF BOTH AUSTENITIC AND FERRITIC GRADES OF STAINLESS STEEL WILL ALSO BE COVERED.

Concept of primary solidification mode control was adopted to obtain optimal solidification crack resistance, hot ductility, corrosion resistance and toughness for austenitic stainless steel. By controlling primary solidification phase as primary δ and containing no ferrite at room temperature, optimal solidification crack resistance, hot ductility, corrosion resistance and cryogenic toughness could be obtained. The optimum chemical composition of austenitic stainless steel ranges 1.46~1.55(Creq/Nieq ratio) calculated by Schaeffler's equation.

우리나라 남부해안기후의 특성과 수온과의 관계를 알아보기 위하여 해안지방인 부산, 여수, 목포를 준표준 내륙지방으로 광주와 대구, 인근 해양의 가덕도, 소리도, 홍도의 수온을 선정하여 20년 간(1960~1979)의 관측자료로서 기온, 습도, 강수량을 조사 분석한 결과는 다음과 같다. 1) 해안지방(부산, 여수, 목포)은 해양의 영향으로 내륙지방(대구, 광주)보다 기온의 연교차가 적고 기온이 수온보다 높을 때는 내륙지방이 해안지방의 기온보다 높고, 수온이 기온보다 높을 때는 내륙지방이 해안지방보다 낮다. 2) 수온과 기온의 차에 따라서 내륙지방과 해안지방의 기온차가 결정되며(상관계수 0.9이상) 그 양적 예측도 상관관계식을 활용함으로써 가능하다고 생각된다. 3) 해안지방과 내륙지방의 습도의 차이도 기온의 경우와 비슷하게 나타났으나 목포는 지형적인 영향으로 다른 해안지방과 다르게 나타났다. 4) 수온과 기온의 차이에 따라서 해안지방과 내륙지방의 습도의 차이가 결정된다(상관계수 0.9이상, 목포제외), 그러므로 그 양적 해석도 가능하다. 5) 남해안지방의 강수량은 내륙지방과 그 차이가 뚜렷하게 나타나지는 않았다.

산업화, 도시화로 인해 수자원의 오염이 악화 되면서 기존에 염소를 이용한 정수처리 방법으로는 깨끗한 물을 공급하는데 어려운 실정이다. 이에 오존을 이용한 고도정수 처리 시설의 도입이 증가하고 있다. 그러나 기존의 방수⋅방식 공법으로 사용되는 에폭시계 방수⋅방식제 및 스테인리스는 오존의 강력한 산화력으로 인해 열화되어 박리 등 문제 발생하였으며, 콘크리트까지 영향을 미쳐 내구성 저하의 원인이 된다. 이에 따라 본 연구에서는 내오존성 및 내화학성이 뛰어난 금속 패널을 기존의 시공법 보다 손쉬운 방법으로 시공하기 위한 방법으로 금속용사 공법을 이용하여 수처리 시설 콘크리트 구조물의 열화를 원천적으로 방지하기 위한 마감공법 개발 연구의 일원으로 용사금속 종류 에 따른 내오존성 평가를 실시하였으며, 실제 하수처리장 환경에서의 전기화학적 안정성능 평가를 실시하였다. 실험결과 용사금속 Ti이 용사 후에도 내오존성이 뛰어난 것으로 나타났으며, 하수처리장 환경에서의 전기화학적 안정성능 평가 결과 용사금속 Ti가 403.83k∙ Ω∙cm2의 가장 높은 분극저항을 나타남으로써 높은 수준의 내구성을 확보하는 것을 확인할 수 있었다.

PSC 구조에서 덕트 내부의 그라우트는 텐던 부식에 효과적인 부식방어 기재이다. 본 연구에서는 일반적으로 사용되고 있는 그라우트와 낮은 물-시멘트비와 실리카 퓸을 혼입한 그라우트를 대상으로 역학적, 내구적 시험을 수행하였다. 높이 1000mm의 덕트를 이용하여 텐던 시스템을 제작하였으며, 두 가지 그라우트에 대하여 강도, 흡수율, 플로우, 블리딩, 팽창률 등을 평가하였다. 또한 내부 12.7mm 텐던에 대하여 ICM(Impressed Current Method)를 이용하여 2일 및 4일 동안 부식을 촉진시켰으며 부식량을 조사하였다. 개선된 그라우트에서는 10MPa 이상의 높은 강도와 50% 이하의 낮은 흡수율을 나타내었다. 또한 2일∼4일 동안의 부식촉진실험에서 39.8%∼48.2%의 뛰어난 부식 감소율 나타내었다.

본 실험 논문은 초단유리섬유(milled glass fibers)가 혼입된 PSC용 그라우트 몰탈의 강재부식성능을 평가하였다. 초단유리섬유를 함유한 배합이 PSC 그라우트 몰탈로서 소요성능을 만족시키는지를 확인하기 위하여 유하시간, 블리딩 및 압축강도를 측정하였다. 초단유리 섬유를 함유한 몰탈의 부식저항 성능은 염소이온 확산시험, 몰탈 흡수시험과 표면전기저항 측정 결과에 근거하여 수행되었다. 시험결과, 초단 유리가 혼입된 모든 배합은 OPC만 사용된 배합에 비하여 그라우트의 부식저항성능을 개선시키는 것으로 확인되었다. 다만, 초단유리섬유를 사용함으로서 유하시간은 단축되지만 블리딩이 발생하여 소요성능을 만족하지 못하는 것으로 확인되었다. 그러므로 PSC 그라우트에 적합한 초단유리섬유배합이 되기 위해서는 물-바인더비의 조정이 필요한 것으로 판단된다.

The purpose of this study is to evaluate the impact on flexural strength and compressive strength of the concrete, the mixing rate of the amorphous fibers.