PURPOSES: The purpose of this study is to compare the lane curing time of natural drying and a lane drying device when painting lines on a highway. METHODS: The painting process was carried out in July 2015 and September 2015, respectively, for the Gimcheon IC - Gimcheon JC. After the painting, measurements were obtained three times at six measurement points located at 20 m intervals on the shoulder line and the dividing line. The curing time was measured for natural drying and drying using a lane drying device, and compared for different pavement types (asphalt, concrete) and paint types (waterborne paint, methyl methacrylate paint). RESULTS : The results of the lane curing time comparison on the highway are as follows. The combination of asphalt and methyl methacrylate paint cured more rapidly during both the natural drying and drying using the lane drying device. Finally, it was cured at least 32.2% and 40.7% faster when using a drying device than in natural drying. CONCLUSIONS: The comparison of lane curing time of the highway showed that the combination of asphalt and methyl methacrylate paint cured more rapidly when using both natural drying and a lane drying device.

PURPOSES:The objective of this study is to ascertain the curing period of cementless cold central plant recycled asphalt base-layer, using mechanical analyses and specimen quality tests on the field.METHODS :Cold central plant recycled asphalt base-layer mixture was produced in the plant from reclaimed asphalt, natural aggregate, filler for the cold mix, and the modified emulsion AP using asphalt mix design and plant mix design. In order to examine the applicability of the curing period during the field test, the international standards for the possibility of core extraction and the degree of compaction and LFWD deflection were analyzed. Moreover, Marshall stability test, porosity test, and indirect tensile strength test were performed on the specimens of asphalt mix and plant mix design.RESULTS :The plant production process and compaction method of cementless cold central plant recycled asphalt base-layer were established, and the applicability of the optical moisture content for producing the mixture was verified through the field test. In addition, it was determined that the core extraction method of the conventional international curing standard was insufficient to ensure performance, and the LFWD test demonstrated that the deflection converges after a two-day curing. However, the back-calculation analysis reveals that a three-day curing is satisfactory, resulting in a general level of performance of dense asphalt base-layer. Moreover, from the result of the specimen quality test of the asphalt mix design and plant mix design according to the curing period, it was determined that the qualities satisfied both domestic and international standards, after a two-day curing. However, it was determined that the strength and stiffness after three-day curing are higher than those after a two-day curing by approximately 3.5 % and 20 %, respectively.CONCLUSIONS:A three-day curing period is proposed for the cementless cold central plant recycled asphalt base-layer; this curing period can be demonstrated to retain the modulus of asphalt-base layer in the field and ensure stable quality characteristics.

FRP Hybrid Bar, composite structures composed of synthetic resins, deformed bar and glass fiber, was invented in order to solve corrosion of rebar in reinforced concrete structures. In order to bond deformed bar and glass fiber to FRP Hybrid Bar, synthetic resins is used. Curing time of the synthetic resins greatly affect productivity. If curing time of synthetic resins is short, cost of facilities is reduced and productivity is increased. Also, If this curing time is shorter or omitted, FRP Hybrid Bar can be commercialized. So, it can cause mass-production and substantial economic effect. Therefore, in this paper, optimum mix proportion is observed in order to increase economic efficiency of FRP Hybrid Bar and reduce curing time of synthetic resins. Total 9 variables are set, adjusting ratio of hardener ratio, and 3 resin moulds on each variables are fabricated. Optimum mix proportion is suggested based on data measured by temperature sensor.

This study used transmission electron microscopy (TEM) to investigate the micro-morphological features of two formaldehyde to urea (F/U) mole ratio liquid urea-formaldehyde (UF) resins with three hardener levels as a function of the curing time. The micro-morphological features of the liquid UF resins were characterized after different curing times. As a result, the TEM examination revealed the presence of globular/nodular structures in both liquid UF resins, while spherical particles were only visible in the low F/U mole ratio resins. The high F/U mole ratio liquid UF resins also showed extensive particle coalescence after adding the hardener, along with the appearance of complex filamentous networks. When the resins were cured with a higher amount of hardener and longer curing time, the spherical particles disappeared. For the low mole UF resins, the particles tended to coalesce with a higher amount of hardener and longer curing time, although discrete spherical particles were still observed in some regions. This is the first report on the distinct features of the crystal structures in low F/U mole ratio UF resins cured with 5% hardener and after 0.5 h of curing time. In conclusion, the present results indicate that the crystal structures of low F/U mole ratio UF resins are formed during the curing process.

본 연구에서는 아스팔트 혼합물의 특성을 평가하는 대표적인 방법인 마샬안정도와 간접인장강도 시험시 양생온도와 양생시간 및 시험온도에서의 처리시간이 결과에 미치는 영향을 비교분석 하였다. 마샬안정도 시험은 공시체를 60°C로 유지되는 수조에 30분 수침 후 수행하지만, 공시체의 양생시간에 관한 기준은 없다. 간접인장강도 시험의 경우는 시험온도는 25°C라고 정해져 있지만 마샬안정도 시험과 마찬가지로 양생시간에 관한 기준은 없다. 또한 간접인장강도 시험을 하기 전 공시체의 온도를 25°C로 맞추기 위하여 항온항습기 등과 같은 장치에 일정시간 보관해야 하는데 이것 역시 정해진 규정이 없다. 연구결과, 공시체의 양생온도에 따라 안정도와 간접인장강도 값은 많은 차이를 나타냈다. 따라서, 실험실 온도가 25°C보다 높거나 낮으면, 혼합물의 양생이 제대로 되지 않아 시험결과의 신뢰성이 떨어질 것이다. 양생온도 변화에 따른 시험값 변화를 최소화하기 위하여. 마샬안정도 시험시 공시체를 60°C 수조에 수침해야 하는 시간과 간접인장강도 시험 전 공시체를 25°C에 보관해야 하는 시간을 제안하였다.

본 연구에서는 아스팔트 혼합물의 특성을 평가하는 대표적인 방법인 마샬안정도와 간접인장강도 시험시 양생온도와 양생시간 및 시험온도에서의 처리시간이 결과에 미치는 영향을 비교분석 하였다. 마샬안정도 시험은 공시체를 60℃로 유지되는 수조에 30분 수침 후 수행하지만, 공시체의 양생시간에 관한 기준은 없다. 간접인장강도 시험의 경우는 시험온도는 25℃라고 정해져 있지만 마샬안정도 시험과 마찬가지로 양생시간에 관한 기준은 없다. 또한 간접인장강도 시험을 하기 전 공시체의 온도를 25℃로 맞추기 위하여 항온항습기 등과 같은 장치에 일정시간 보관해야 하는데 이것 역시 정해진 규정이 없다. 연구결과, 공시체의 양생온도에 따라 안정도와 간접인장강도 값은 많은 차이를 나타냈다. 따라서, 실험실 온도가 25℃보다 높거나 낮으면, 혼합물의 양생이 제대로 되지 않아 시험결과의 신뢰성이 떨어질 것이다. 양생온도 변화에 따른 시험값 변화를 최소화하기 위하여. 마샬안정도 시험시 공시체를 60℃ 수조에 수침해야 하는 시간과 간접인장강도 시험 전 공시체를 25℃에 보관해야 하는 시간을 제안하였다.

본 연구에서는 플라이애시가 90 %만큼 다량치환된 모르타르에 알칼리 활성화를 통한 강도증진을 동일한 양생온도 조건 에서 양생방법 및 유지시간 변화에 따라 비교 분석하고자 하였다. 연구 결과로 플래이애시를 90 % 치환한 경우, 소생재 도 포 후 40℃로 24시간 기중양생시 가장 높은 압축강도를 발휘하였지만, OPC의 압축강도까지 발휘하는 것은 어려울 것으로 분석되었다.

Recently, high-performance and high-fluidity concrete have been studied and developed because high-rised build is constructed. An early-age properties of these concretes have been studied and developed bacause of comparing existed concrete. This study proposed non-destructive method as electrical resistivity measurement, which evaluates setting time of cement-based materials. An assessment of the effect on the setting time was studied on the addition of a superplasticizer to delay the setting time and the curing temperature to promote the setting time. 6th of samples prepared mortar according to adding superplasticizer(PNS) or curing temperature and measured the electrical resistivity during 24 h. As the results, mortars which curing higher temperature were promoted rising time which is setting time in the electrical resistivity, also mortars which adding superplasticizer were retard rising time.

Concrete structure for nuclear power plant is mass concrete structure with large wall depth and easily permits cracking in early age due to hydration heat and drying shrinkage. It always needs cooling water so that usually located near to sea shore. The crack on concrete surface permits rapid chloride intrusion and also causes more rapid corrosion in the steel. In the study, the effect of age and crack width on chloride diffusion is evaluated for the concrete for nuclear power plant with 6000 psi strength. For the work, various crack widths with 0.0~1.4 mm are induced and accelerated diffusion test is performed for concrete with 56 days, 180days, and 365 days. With increasing crack width over 1.0mm, diffusion coefficient is enlarged to 2.7~3.1 times and significant reduction of diffusion is evaluated due to age effect. Furthermore, apparent diffusion coefficient and surface chloride content are evaluated for the concrete with various crack width exposed to atmospheric zone with salt spraying at the age of 180 days. The results are also analyzed with those from accelerated diffusion test.

현재 전 세계적으로 자연적, 인위적 요인으로 인하여 이상기후가 나타나고 있다. 이상기후의 대표적인 것으로 슈퍼태풍, 극한폭설, 폭염과 같은 극한 기후현상이 초래된다. 1970년대 산업화 시대 이후 급격하게 지구의 온도가 상승하는 것을 알 수 있으며, 이로 인하여 발생하는 가장 큰 문제점은 지구 온난화이다. 지구 온난화에 영향을 미치는 온실가스의 종류로는 이산화탄소, 과불화탄소, 아산화질소, 메탄과 같은 다양한 종류의 화학성분이 존재하며 특히 이산화탄소가 약 90%의 비중을 차지하는 것을 알 수 있다. 콘크리트의 경우 건설재료로써 탁월한 내구성능을 지니고 있으며, 사회기반시설물 건설 재료로 70%이상 사용되고 있다. 그러나 콘크리트는 타설직후 물리·화학적으로 다양한 환경조건으로부터 성능저하 현상이 발생하기도 한다. 특히 대기중의 이산화탄소는 콘크리트 알칼리도 저하에 따른 철근을 부식시키고 내구성 저하를 초래하게 된다. 따라서 본 연구에서는 풍속, 일조시간에 관하여 양생 한 후 콘크리트의 탄산화 실험을 접목시켜 탄산화 깊이와 탄산화 속도 계수를 측정하고 이를 바탕으로 만족도 확률 곡선을 통하여 성능중심평가(Performance Based Evaluation(PBE))를 수행 할 것이다.

공시품종으로 Burley 21과 KB101을 수확한 후 건조상내에서 온도 처리와 습도 3처리를 조합하여 엽분별로 건조하였고, 수확시기에 엽중수분함량이 다른 잎을 우기에 비닐건조실 내에서 건조하여 부패엽발생정도를 조사하였던 바 그 결과는 다음과 같다. 1. 부패엽발생은 30℃ 에서 최대였고, 25℃ 에서 약간 감소하였으며, 35℃ 에서는 현저히 감소하여 40℃ 에서는 100% RH 조건에서도 전혀 발생되지 않았다. 2. 습도 82%구에서는 부패엽이 10%정도로 아주 적었으나 이보다 고습조건일 수록 급속하게 증가되었다. 3. KB 101 육성계통이 Burley 21보다 부패엽 발생이 약간 적은 경향이었다. 4. 부패엽발생 부위는 주로 잎 엮은 부위에서 가장 많았고, 다음은 수확시 절단부위에서 않았다. 5. 엽분별로는 중엽에서 본엽에서 보다 부피엽발생율이 더 높았다. 6. 우기에 엽중수분함양이 높은 잎을 수확시는 부패엽발생이 않았고, 강우 4일 후의 수분상태 잎을 수확시는 거의 부패엽이 발생되지 않았다.