Polypropylene (PP) composites with wood flour/wax/coupling agent were manufactured by melt compounding and injection molding. The influence of wood flour(WF), wax, and coupling agent on the mechanical and thermal properties of the composites was investigated. The addition of wood flour to neat PP has the higher tensile modulus and strength compared with neat PP. The presence of wax also improved the tensile modulus. At the same loading of PP and WF, the addition of coupling agent highly decreased the tensile modulus, and increased the tensile strength. From thermogravimetric analysis (TGA), the addition of wax improved the thermal stability of the composites in the later stages of degradation. The presence of MAPP and wood flour in turn decreased thermal stabilities of composites. From differential scanning calorimetry analysis (DSC), neither the loading of wax. nor the presence of MAPP has shown significant effect on the thermal transition of composites.

고준위방사성폐기물 처분장의 완충재 후보물질 선정을 위해 경주 벤토나이트를 대상으로 수리특성, 팽윤특성, 열적특성, 역학특성 및 핵종유출 저지특성을 조사하였다. 실험결과, 압축 벤토나이트의 수리전도도는 m/s 이하로 매우 낮았으며 건조밀도가 증가할수록 감소하였다. 팽윤압은 0.66 ㎫∼14.4 ㎫ 사이의 값을 보였으며 건조밀도에 따라 증가하였다. 건조밀도가 1.4 Ms/㎥ ∼ 1.8 Mg/㎥1.4 일때, 열전도도, 열축압축강도 (unconfined compressive strength), 탄성계수 (Young's modulus of elasticity), Poisson 비는 각각 0.80 ㎉/m ∼1.52 ㎉/m , 0.55 ㎫ ∼ 8.83 ㎫, 59 ㎫ ∼ 1275 ㎫, 0.05 ∼ 0.20의 값을 나타내었다. 압축벤토나이트에 대한 핵증 확산계수는 산화 환경에서 측정되었으며, 주어진 실험조건에서 삼중수소 (H-3)는 1.7 /s ∼ 3.4 /s. 양이온 핵종 (Cs, Sr , Ni)은 8.6 /s ∼ 1.3 /s, 음이온 핵종 (I, Tc)은 1.2 /s ∼ 9.5 /s, 악티나이드 핵종은 3.0 /s ∼ 1.8 /s 사이의 값을 나타내었다. 이때 확산계수는 모든 핵종에 대해 압축벤토나이트의 건조밀도가 증가할수록 감소하는 경향을 보였다.

급냉응고방식으로 제조한 비정질 Z r62-xN i10C u20A l8 Tix (x=3, 6, 9at%) 합금을 사용하여 열적, 기계적 성질을 조사하였다. 시효온도에 따른 결정화 거동은 Ti 3at%에서는 비정질→비정질+Z r2A l3+Zr+(Ni,Ti)→Z r2Cu+Al+(Ni,Ti)의 결정화 거동을 나타내었으며, Ti 6at%에서는 비정질→비정질+Al→A l2Ti+NiZr+CuTi, Ti 9at%에서는 비정질→비정질+Zr+Al→Zr+A l2Zr+Al Ti3+CuTi의 결정화 거동을 보였다. 시효온도가 증가할수록 비정질 모상에 석출상의 체적율( Vf )이 증가하고 그에 따라 비커스 경도 ( Hv )간이 증가하였다. 파괴인장강도(σf )는 Vf 의 증가에 따라 증가하다가 Z r59A l10N i20C u8 Ti3은 Vf =38%에서 1219MPa의 최대값을 보이고, Z r56A l10N i20C u8 Ti6은 Vf =2%에서 1203MPa의 최대값을 보이고, Z r53A l10N i20C u8 Ti9 Vf =5%에서 1350MPa의 최대값을 나타낸 후 그 이상의 Vf 에서는 급격히 감소하였다. σf 가 급격히 감소하는 Vf 와 연성 파면에서 취성파면으로 천이되는 Vf 가 일치하였다.f/가 일치하였다.

We have evaluated the role of Ag additions on the strength, fracture toughness, elastic modulus and resistance to thermal shock of (YBCO) superconductor. Addition of 10 vol.% Ag improved strength and fracture toughness, whereas, decreased elastic modulus of YBCO. In addition, YBCO-Ag composites improved resistance to thermal shock probably due to enhanced strength, fracture toughness and thermal conductivity as a result of Ag addition. It is to be noted that YBCO-Ag made by mixing with solution showed slightly higher strength, fracture toughness and resistance to thermal shock, compared to that made by mixing with metallic Ag powder. These improvements are believed to be due to the microstructure of more finely and uniformly distributed Ag particles.

반응성 첨가제로 사용된 HQ-PGE가 DGEBA/MDA계의 기계적 성질에 미치는 영향을 살펴보기 위해서 충격강도와 인장강도를 측정하였다. HQ-PGE의 함량이 25phr일 때 충격 강도는 첨가되지 않았을 때보다 40% 증가하고, 인장강도도 약간 증가하였다. 이것은 HQ-PGE가 합성될 때 생성된 수산기가 자촉매 반응을 하면서 에폭시 수지의 미반응된 에폭시기와 반응한 결과로 사료된다. Young's modulus와 신장율은 HQ-PGE의 함량이 증가함에 따라 크게 변화하지 않았다.

소량의 misch metal과 Zr을 함유한 CuZnAI형상기억 합금의 변태온도에 미치는 열사이클 및 기계적 성질 변화에 대하여 고찰하였다. 합금원소 첨가에 따라 결정립에 매우 미세화 되었으며 용체화 처리후 100~350˚C구간에서 경도값 변화를 조사하기 위하여 post quench aging과 step quench aging처리한 결과 200˚C와 250˚C에서 최고의 경도값을 나타냈다. Mf온도이하에서 인당시험한 결과 파단강도와 연실율은 결저립이 미세할수록 증가하는 경향을 보였다. 또한 파단강도는 as quenching처리한 경우보다 post quench aging처리한 경우에 보다더 증가하였다. β-상에서의 시효는 Ms온도를 강하시켰으며 마르텐사이트상에서의 시효는 As 온도를 증가시켰다. post quench aging 에 따른 As의 변화는 β에서의 회복율에 기여하였으며 변태온도 (As-Ms)히스테리시스는 열사이클에 의하여 증가하는 경향을 보였다.

Multi-Walled Carbon Nanotubes (MWCNTs) were modified with epoxy and aminosilane diethanolamine (DEA), and nanocomposites of poly(butylene adipate-co-terephthalate) (PBAT) and the modified MWCNTs were prepared with the aim of improving the physical properties of biodegradable PBAT. The physical and the thermal properties of the PBAT/MWCNT nanocomposites were investigated using various techniques. Fourier transform infrared spectroscopy measurements revealed that the MWCNTs were efficiently modified with DEA. Scanning electron micrographs of the nanocomposites indicated that the modified MWCNTs were dispersed homogeneously in PBAT. The thermal stability of the nanocomposite decreased with increase in the content of epoxy-MWCNT-DEA due to the poor thermal stabilities of epoxy and amino silane DEA. However, the surface hydrophobicity of the nanocomposite increased. The highest stress (170% of PBAT) was observed when the content of epoxy-MWCNT-DEA in the nanocomposite was 2 wt%.

This paper investigated the thermal and mechanical properties of high-volume fly ash concrete for potential application in mass concrete.