Titanium, which has excellent strength and toughness characteristics, is increasingly used in the aerospace field. Among the titanium alloys used for body parts, more than 80 % are Ti-6Al-4V alloys with a tensile strength of 931 MPa. The spark plasma sintering (SPS) method is used for solidification molding of powder manufactured by the mechanical milling (MM) method, by sintering at low temperature for a short time. This sintering method avoids coarsening of the fine crystal grains or dispersed particles of the MM powder. To improve the mechanical properties of pure titanium without adding alloying elements, stearic acid was added to pure titanium powder as a process control agent (PCA), and MM treatment was performed. The properties of the MM powder and SPS material produced by solidifying the powder were investigated by hardness measurement, X-ray diffraction, density measurement and structure observation. The processing deformation of the pure titanium powder depends on the amount of stearic acid added and the MM treatment time. TiN was also generated in powder treated by MM 8 h with 0.50 g of added stearic acid, and the hardness of the powder was higher than that of Ti-6Al-4V alloy when treated with MM for 8 h. When the MM-treated powder was solidified in the SPS equipment, TiC was formed by the solid phase reaction. The SPS material prepared as a powder treated with MM 8 h by adding 0.50 g of stearic acid also formed TiN and exhibited the highest hardness of Hv1253.

We report the structural, morphological and magnetic properties of the Ni70Mn30 alloy prepared by Planetary Ball Mill method. Keeping the milling time constant for 30 h, the effect of different ball milling speeds on the synthesis and magnetic properties of the samples was thoroughly investigated. A remarkable variation in the morphology and average particle size was observed with the increase in milling speed. For the samples ball milled at 200 and 300 rpm, the average particle size and hence magnetization were decreased due to the increased lattice strain, distortion and surface effects which became prominent due to the increase in the thickness of the outer magnetically dead layer. For the samples ball milled at 400, 500 and 600 rpm however, the average particle size and hence magnetization were increased. This increased magnetization was attributed to the reduced surface area to volume ratio that ultimately led to the enhanced ferromagnetic interactions. The maximum saturation magnetization (75 emu/g at 1 T applied field) observed for the sample ball milled at 600 rpm and the low value of coercivity makes this material useful as soft magnetic material.

Two sorghum(Sorghum bicolor L. Moench cv. Hwanggeumchal-susu and Miryang 3) samples were milled using different milling methods, and their physicochemical properties were tested. Particle size was classified into five groups such as pin mill and low temperature-microparticulation(LTM; 10, 000, 20, 000, 30, 000, and 40, 000 rpm). The water absorption index (WAI), water solubility index(WSI), and a rapid Visco analyzer(RVA) were used to examine particle size distribution and color differences. Particle size of sorghum flour prepared using LTM was lower than that prepared using a pin mill. Particle size was further reduced by successive dry milling of the LTM flour. Lightness of colored pigments increased when particle size decreased. The WAI of Miryang 3 pin milling(M1) flour was the lowest after LTM, and WSI was higher in the order of M2, M3, M4, and M5. LTM sorghum flour had significantly higher pasting viscosity, as determined using a rapid Visco analyzer. LTM Miryang 3 sorghum flour(M2～M5) flour showed lower breakdown viscosity and higher final viscosity compared to those of M1 flour, resulting in an increased setback value.

Al2O3 sol with long-term stability was prepared by mechanical milling. Thin films were evaluated and created for use as coating materials. The particle size of the manufactured sol was 98 nm when 2 wt% of nitric acid was added. This indicates that the viscosity of the sol is 12 cps and that it has long-term stability. The thickness of the thin films, which varied from 100 nm to 500 nm, could be managed by adjusting the draw rate and the amount of an organic additive. A thin film heated to 500˚C indicated a hydrophilic property against water and excellent permeability against a visible ray.

Recently, the fabrication process of the W-Cu nanocomposite powders has been studied to improve the sinterability through the mechanical alloying and reduction of W and Cu oxide mixtures. In this study. the W-Cu composites were produced by mechanochemical process (MCP) using mixtures with two different milling types of low and high energy, respectively. These ball-milled mixtures were reduced in atmosphere. The ball-milled and reduced powders were analyzed through XRD, SEM and TEM. The fine W-Cu powder could be obtained by the high energy ball-milling (HM) compared with the large Cu-cored structure powder by the low energy ball-milling (LM). After the HM for 20h, the W grain size of the reduced W-Cu powder was about 20-30 nm.