An environmentally friendly and low-cost chitosan-containing polysaccharide (CP) composite ZIF-8/CP was designed and prepared based on the difficulty of separating the traditional adsorbent from the water phase. ZIF-8/CP was synthesized through in-situ growth approach. The physical, chemical and structure properties of ZIF-8/CP were determined through a series of characterization methods, including SEM, FT-IR and PXRD. The effects of touch time, pH, temperature, and coexisting ions on adsorption were assessed. In addition, kinetics, isotherms of adsorption and thermodynamics were examined. The data of isotherms for adsorption indicated that the adsorption of ZIF-8/CP on MG was similar to the Langmuir model, with a maximum adsorption capacity of 1428.57 mg/g. Moreover, the kinetic parameters were consistent with the pseudo- 2nd-order equation. Thermodynamic studies (ΔG < 0, ΔH > 0) demonstrated a heat-absorbing and spontaneous adsorption process. Our study reveals that ZIF-8/CP has good adsorption properties and environmental properties.

For practical applications of graphene sheets in a variety of fields, mass production of high-quality graphene sheets is necessary. Herein, we reported a cost-effective, green, and simple approach to synthesizing mass production exfoliated graphene (EG) flakes employing electrochemical exfoliation of pencil graphite in neutral aqueous electrolytes. Pencil graphite cores of different grades were applied as anode and cathode electrodes and exposed to the electrolyte solution at a different voltage. Several parameters were examined and optimized, including pencil grade (2,4,6,8 B), applied voltage (10, 15, 20, 30 V), different inorganic electrolytes ((NH4)2SO4, Na2SO4, NaNO3, NaCl, and CH3COONa), and the concentration of electrolytes. The optimal condition was chosen by considering the mass of produced graphene and the conductivity of the graphene solution. The optimal conditions were as follow: pencil grade: 6B; applied voltage: 10 V; electrolyte type: Na2SO4; electrolyte concentration: 0.1 M. Under these conditions, the production yield was > 95% within 3 h and 9 min. The EG was characterized by utilizing FT-IR, XRD, Raman spectroscopy, FE-SEM, Cyclic Voltammetry, and Electrochemical Impedance Spectroscopy (EIS). Characterization indicates that the synthesized EG had an XRD peak at 2θ = 26.6° and an ID/ IG ratio of 0.36. Furthermore, the EG showed good conductivity when tested by cyclic voltammetry and EIS whereas the R2 values were 985.8 and 76.3 Ω for bare GCE and EG/GCE, respectively. In addition, EG effectively removed cadmium (Cd(II)) with an adsorption level of 8.72 mg/g. The results from this study suggest that EG can be scaled up and commercialized in an environmentally friendly and low-cost manner, especially in low-income countries, and using it to rectify metal ions.

In this study, a method to remove residual powder on a multi-layered graphene and a new approach to transfer multi-layered graphene at once are studied. A graphene one-step transfer (GOST) method is conducted to minimize the residual powder comparison with a layer-by-layer transfer. Furthermore, a residual powder removing process is investigated to remove residual powder at the top of a multi-layered graphene. After residual powder is removed, the sheet resistance of graphene is decreased from 393 to 340 Ohm/sq in a four-layered graphene. In addition, transmittance slightly increases after residual powder is removed from the top of the multi-layered graphene. Optical and atomic-force microscopy images are used to analyze the graphene surface, and the Ra value is reduced from 5.2 to 3.7 nm following residual powder removal. Therefore, GOST and residual powder removal resolve the limited application of graphene electrodes due to residual powder.

본 실험에서는 고분자의 농도, 첨가제의 종류 및 함량에 따라 도프 용액을 이용하여 분리막제조하였다. 분리막의 모폴로지는 전자주사현미경(SEM)을 통해 관찰 하였으며, 막의 모폴로지와 순수투과도의 관계를 확인 할 수 있었다. 필터화 모듈을 제조하여 수투과도 및 바이러스, 박테리아 등과 같은 미생물 제거성능을 측정하였다. 제조된 중공사막의 단면은 sponge 형태로 표명으로 갈수록 치밀한 형태를 띄는 것을 확인하였으며, 수투과도는 50-70 ml/min 으로 높은 값을 나타내었으며, 필터화모듈의 경우 수투과도는 1.6 LPM의 높은 투수량을 나타내며, 박테리아와 바이러스의 제거성능은 log 6 의 값의 높은 수치를 보였다.

Heavy metals are typical contaminant in water and need to be removed because they are non-biodegradable and can accumulate in human body. To remove metal and other contaminants from water, chemical absorbents are widely used due to their low cost. Herein, hybrid materials comprised of amylose and single wall carbon-nanotube (swCNT) was developed as the absorbent for water purification. A high adsorption properties of carbon-nanotubes have been utilized in designing effective absorbent but its poor dispersity in water is a limiting factor for practical use. Single wall carbon-nanotube was hybridized with amylose chain produced by enzyme reaction of amylosucrase and their tendency to self-assemble in aqueous environment. The amylose-swCNT microparticles were characterized by FE-SEM and turned out to be spherical structure with CNTs embedded throughout the amylose matrix. The ability of amylose-CNT microparticles to remove copper was examined. Concentration of copper was decreased after reaction with amylose-swCNT microparticles. Although amount of decreasing copper was less than swCNT on same total mass, Adsorption efficiency of amylose-swCNT microparticles was good because their swCNT content was only 10% of total mass.

Deseeded jujubes are commonly consumed as snacks. This study was conducted to develop a seed-removing machine for jujubes that relieves hard work in manual seed removal. The seed-removing machine consists of a jujube supplying unit, a punching unit, and a discharging unit. To test the performance of the machine, shape characteristics, seed removing rate, sarcocarp cracking rate, and flesh hardness were analyzed throughout the jujube storage period. The machine showed good seed removing and sarcocarp cracking rates at room temperature and cold temperature storage on days 2, 15, and 50. Seed removing rates were 80% at day 15 and 96% at day 50. The sarcocarp cracking rates were 33% for day 15 and 30% for day 50. Hardness started to decrease from day 8 to day 70 at both room temperature and cold temperature storage. The working capacity of the machine was 900 fruits/h. The results showed that the jujube seed removing machine is useful for reducing the labor requirements of postharvest jujube processing.