Generally the side plate materials of FRP ship are composed of glass fiber and unsaturated polyester resin composites(GFRP composites). In this study, the effect of applied load and sliding speed on friction and wear characteristics of these materials were investigated at ambient temperature by pin-on-disc friction test. The cumulative wear volume, friction coefficient and wear rate of these materials for SiC abrasive paper were determined experimentally. The cumulative wear volume showed a tendency to increase nonlinearly with increase of sliding distance and was dependent on applied load and sliding speed for these composites. The friction coefficient of GFRP composites was increased as applied load increased at same sliding speed in wear test. It was verified by SEM photograph of worn surface that major failure mechanisms were microfracture, deformation of resin, cutting and cracking.

섬유복합재료(Fiber Reinforced Polymer, FRP)는 경량성, 높은 설계기준강도, 비전기 비자성 및 내부식성의 특징 등으로 인하여 최근 건설분야에서 많은 연구가 진행되고 있다. 그 중 GFRP(Glass Fiber Reinforced Polymer)는 가격 경쟁성에서 우수하여 일반적으로 많이 사용되고 있다. 그러나 GFRP는 상대적으로 낮은 탄성계수를 가지고 있어 처짐이 과대하게 발생함으로 구조부재 단면으로서 활용되기 위해서는 단면이 커야하며, 설계시 사용하중에 의한 처짐 제한에 대한 검토를 실시해야 한다. 이에 본 연구에서는 언급된 기술적인 문제점을 해결하기 위하여 대형 단면의 적용이 가능하도록 모듈형식의 단면을 제안하였다. 그리고 FRP의 낮은 강성을 확보하군 위하여 콘크리트를 충진하는 새로운 FRP+콘크리트 합성 거더 형상을 개발하였다. 개발된 FRP)콘크리트 합성 거더의 전단지간비와 콘크리트 충진 여부에 따른 전단강도 및 처짐, 중립축 변화를 확인하고자 전단실험을 실시하였다.

A scrapped fiber-reinforced plastic(FRP) fishing vessel causes many environmental problems, because technology development for recycling FRP vessel has not been adequately addressed. FRP is a main material for constructing a small coastal fishing vessel that is an object of reduction policy. Therefore, the FRP wastes derived a scrapped fishing vessel are increasing. In this study, I investigated an effective disposal process for FRP through the analysis of the actual conditions of scrapped FRP fishing vessel. The treatment processes of scrapped FRP fishing vessel are carried out with oil-removing, dismantling, intermediated processing(crushing), and then reclaiming follows burning in the final processing in Korea. However, in Japan, several recycling methods have been developed, for example, the incineration including thermal recovery, the use of cement-reclamation, and the use of asphalt concrete aggregate, because the method of reclaiming after incinerating which is generally used in Korea produces a toxic by-product such as dioxin.

건설 분야에서는 신소재인 FRP(fiber reinforced polymer) 복합재료는 그 경량성과 고강도로 점차 그 사용영역이 넓어지고 있다. 본 연구에서는 이러한 FRP 소재의 성능을 평가하기 위하여 제2 진도대교를 원형(prototype)으로 하는 3차원 선형 모델링을 하였고 케이블 및 거더에 복합소재를 적용하여 해석하였다. 해석 결과는 Steel 케이블 및 보강형을 사용한 경우와 비교를 통하여 분석하였고 정적해석 및 모드해석을 수행하였다. 정적해석에서는 각 부재의 최대 응력 및 중앙 지점의 최대 처짐을 비교하였다. 사하중 감소 때문에 복합소재를 사용한 경우 상판의 처짐이 감소하는 것을 확인하였으며, 케이블의 단면을 감소시켜 해석함으로써 그 결과를 다시 보였다. 단면 감소, 모드해석에서는 진동수 비를 통해 Flutter의 발생 풍속을 비교하였다.

본 연구는 복합재료 교량시스템의 규준 정립을 위한 연구로서 실제 설계 시공되어진 복합재료 교량의 정밀해석수행과 이를 통한 복합재료 교량의 파괴거동 및 설계기준 등을 조사하는데 그 목적이 있다. 본 연구의 효율적인 연구를 위하여 실제 미국 NEW YORK주 내에 설계 시공되어있는 Noncomposite-FRP 복합재료 교량을 대상으로 해석적 연구를 수행하였으며 본 연구에서 사용된 해석적 모델을 토대로 실제 미국에서 기 수행되어진 교량 거동에 관한 해석 및 실험하중 평가와 그 결과를 비교하였다. 특히 국내 복합재료 교량의 해석적 설계기준 평가를 위하여 보다 실질적이고 정확한 파괴모드의 조사 및 분석이 요구되어지므로 본 연구에서는 이를 위하여 기존의 해석적 연구에서 가벼운 중량으로 인하여 무시되었던 자중의 영향과 각 적층 layer에 설계된 ply orientation을 고려하여 해석하였다. 그 결과 자중을 고려한 복합재료 패널들의 경우, 제작 결함에 따른 이음부 파괴가 없을 경우 교량 상부 구조 중 횡축 보에서의 국부 좌굴 파괴가 교량의 파괴를 지배할 것으로 본 연구결과에서 예측되었다. 이는 복합재료 교량 제작 시 복합재료 상판 패널과 보의 이음부가 Noncomposite로 제작되는 경우 실제 제작되어진 복합재료 상판의 고 강성에 의하여 재하 하중에 의한 하부 강재 거더 좌굴이 선행되는 것으로 판단된다.

본 연구에서는, 기존 철근 콘크리트 구조물에 적용된 직접 변위-기반 설계법을 적용 FRP 피복 보강된 성능개선 콘크리트 부재에 대한 정밀 비선형 휨 해석 및 내진성능설계의 구체적 알고리즘을 제시하였다. 비선형 휨 해석의 정밀 예측을 위하여 콘크리트 및 FRP 복합재료의 다축 구성관계를 고려하였으며, Chopra 등 (1999)이 제안한 직접 변위-기반 설계법(DDM)을 개선하여 철근콘크리트 기둥에 대한 성능개선을 위한 FRP 피복 보강을 위한 성능설계 알고리즘을 제시하였다. 제시된 직접 변위-기반 설계법은, 변위계수법과 비교하여, 비선형 거동이 큰 경우에도 목표 변위 성능 값에 대한 정확한 추정을 해준다. 이는 변위계수법이 항복 이전의 유효탄성계수를 사용하는 반면, 직접 변위-기반 설계법은 유효탄할선탄성계수를 고려하고 있어, 목표 변위에 따른 성능설계 평가에 있어서 보다 높은 연성비의 거동을 반영하고 있기 때문인 것으로 평가된다.

본 논문에서는 내구성과 수명을 획기적으로 향상시키기 위해 제3세대 건설재료인 섬유강화 플라스틱(FRP) 소재로 제작된 사각형 중공 교량 바닥판의 파괴모드를 실험과 해석을 통해 분석하였다. 재하시험 결과 바닥판의 강축방향의 거동은 파괴 직전까지도 거의 선형탄성적으로 거동한 반면, 약축방향의 거동은 재하초기부터 작은 하중하에서도 큰 비선형성을 보였다. 이 약축방향 비선형성의 원인은 웨브와 플랜지 연결부의 불완전한 일체거동으로 인한 소성거동 때문인 것으로 판단된다. 웨브와 플랜지의 연결부에 소성힌지를 도입한 간단한 구조모델을 이용하여 이를 확인하였다. 접착부의 박리 파괴 가능성도 검토하였으나 이는 대상 중공바닥판의 약축방향 파괴에 직접적으로 관여하는 것은 아닌 것으로 판단된다 약축방향의 구조거동을 개선시키기 위한 방안으로 내부를 폼으로 충전하는 방법을 제시하였으며 그 가능성을 구조해석을 통해 확인하였다.

본 연구에서는 사각형 모듈의 인발성형된 복합재료 바닥판의 휨 거동에 대한 해석 모델을 개발하였다. FRP 바닥판의 해석 모델은 FSDT 평판 이론을 기반으로 임의 적층각을 지닌 FRP 바닥판의 처짐을 예측할 수 있었다. 수치적 예제에서는 네 변이 단순 지지된 등분포 하중을 받는 사각형 모듈의 FRP 바닥판을 2차원 평판 유한 요소해석을 적용하여 수행하였고, 해석 결과에 대해서는 바닥판 길이-높이의 비와 화이버 각도의 변화에 따른 효과에 대해 역점을 두고 다루었다. 연구 결과, 본 연구에서 제안한 해석 모델이 FRP 바닥판의 휨 거동을 해석하고 예측하는데 효과적이고 정확하다는 것이 입증되었다. 또한, FRP 바닥판의 높이가 높아질수록 plate 해석 이론에 있어서 일차전단변형이론(First order Shear Deformable laminated plate Theory : FSDT)이 아닌 고차전단변형(Higher order Shear Deformable plate Theory : HSDT)의 필요성에 대해 언급하였다.

The mechanical behavior of concrete-filled glass fiber reinforced polymer columns is affected by various factors including concrete strength, stiffness of tube, end confinement effect, and slenderness ratio of members. In this research the behavior of slender columns was examined both experimentally and analytically. Experimental works include 1) compression test with 30cm long glass fiber composite columns under different end confinement conditions, 2) uni-axial compression test for 7 slender columns, which have various slenderness ratios.Short-length stocky columns gave high strength and ductility revealing high confinement action of FRP tubes.The strength increment and strain change were examined under different end confinement conditions.With slender columns, failure strengths, confinement effects, and stress-strains relations were examined.Through analytical work, effective length was computed and it was compared with the amount of reduction in column strength, which is required to predict design strength with slender specimens.This study shows the feasibility of slender concrete-filled glass fiber reinforced polymer composite columns.

복합재료(FRP)는 재료적 고비강도, 고내구성 등으로 인하여 건설분야에 널리 사용되고 있어, 본 연구에서는 인발성형된 FRP 바닥판의 형상최적설계를 수행하였다. 최적설계의 정식화에서 목적함수는 단위모듈의 체적을 최소화하도록 하였으며, 설계변수는 바닥판 단면의 기하적 치수와 재료적 물성을 사용하였다. 반면 바닥판의 성능을 최대한 효율적으로 설계하기 위하여 설계 제약조건으로 처짐규정, 재료파괴 기준, 좌굴하중, 바닥판 최소두께와 응력을 사용하였다. 단면형상의 효율적 결정과 시공성을 고려하여 구조적 보조부재를 포함하지 않는 튜브 모양의 형상으로 제한하였으며, 최적화 알고리즘은 Index기법을 적용하여 수렴성을 극대화한 개선된 GAs를 사용하였다. 상용 프로그램인 ABAQUS를 사용하여 3차원 유한요소해석을 수행하였고, 구조해석 결과를 최적화 과정에 필요한 제약조건으로 활용하고, 민감도 분석을 수행하였다. 본 연구를 통하여 개발한 최적화 프로그램을 검증하기 위하여, 40m의 지간, 폭 12.14m에 주형 간격이 2.5m인 단순교를 대상으로 하였으며, 도로교 설계 기준을 만족하는 DB-24하중을 적용하였다. 복합재료의 재료로 E-glass섬유를 사용하였으며, 최적설계를 수행한 결과 인발성형공법에 의한 실용적인 단면을 제안하였다.

The processes of manufacturing FRP sewage disposal tanks are very dangerous and hazardous jobs for workers because of large size and heavy weight of the tank, toxic fiberglass dust, nasty smell, and dangerous tools such as hand-grinders. This paper introduces an automatic manufacturing system of the FRP sewage disposal tank to enhance the safety of workers. The system consists of 3 components: the FRP body rotation jig, the automatic manhole cutting machine, the automatic sanding processing machine. The safety of workers and working environment are greatly improved, because the dangerous jobs are automatized and the toxic fiberglass dust is automatically collected. Also, the productivity is greatly improved and the cost is reduced.

Steel, concrete and their combination materials are the most 6commonly used materials for civil engineering structural systems such as buildings, bridge structures and other structures. Recently, however, fiber reinforced polymer (FRP) composites, a relatively new composite material made of fibers and polymer resins, have been gradually used in structural systems as an alternative structural material. This paper describes a comparison of design strength equations for steel column and FRP composite column based on design philosophies. The safety factors used in allowable stress design (ASD) are relatively higher in FRP structural design than steel structural design. Column critical stress equations of FRP composites column from an experimental study can be represented by Euler elastic buckling equation at the long-range of slenderness, and an exponential form at the short-range of slenderness as defined in Load and Resistance Factor Design (LRFD) of steel column. The column strength of steel and FRP composite columns in large slenderness is independent of material strength, this result verified the elastic buckling equation as derived by Eq. (15) and Eq. (5).

SMC(Sheet molding compound)욕조 생산시 발생하는 폐 FRP를 보강재로서 재활용하기 위하여 불포화 폴리에스테르 매트릭스 수지에 보강하고 보강재와 매트릭스 수지의 계면 결합력을 증진시키기 위하여 보강재를 실란계 커플링제[3-methylacryloxyviny1 silane (MAOS)]로 전 처리하여 복합재를 제조하고 기계적 물성 및 계면현사에 대하여 관찰하였다. 보강률이 20wt%인 복합재의 굴곡강도 및 굴곡탄성률이 각 각 110MPa, 8.0GPa로 가장 우수하였으며 커플링제(MAOS)의 노동가 0.50wt%인 복합재의 굴곡강도 및 굴곡탄성률은 약 10%정도 향상되어 각 각 120MPa, 9.2GPa을 나타내었다. 또한 주사전자현미경 관찰 결과 보강재를 커플링제(MAOS)로 처리한 복합재의 보강재와 매트릭스 수지는 물리, 화학적을 잘 결합하여 보강재와 매트릭스 수지의 계면에서 pull out현상이 확인되지 않았으며 크랙도 발생하지 않았다.

The purpose of this study is to investigate the freeze - thaw behavior of FRP reinforced concrete structures. Under the same conditions, two FRP reinforced beam specimens were made, and one speciemen was subjected to freezing and thawing. Then a four-point bending experiment was conducted. As a result, it was analyzed that the load values of reinforced specimens after freezing and thawing appear less at the same displacement in displacement-load behavior.

In this study, an experiment was conducted to evaluate the behavior of fiber reinforced concrete beam according to GFRP(Glass Fiber Reinforced Polymer)sheets and based on previous specimens and directly compare the fiber reinforcing effect. As a result, all specimens, regardless of the cross section shape, had an increase in torsional capacity and similar behavior compared to previous study.

This research presents effectiveness of fiber-reinforced polymer column jacketing system for a non-ductile reinforced concrete building frame constructed before the 1970s. To investigate the retrofit effects, a series of full-scale dynamic tests for the retrofitted test frame was conducted, and the dynamic responses were compared to those of the non-retrofitted test frame. The effectiveness of the retrofit system was investigated in terms of response reductions, damage mechanisms and drift concentration factors.