Barnea manilensis is a bivalve which bores soft rocks, such as, limestone or mudstone in the low intertidal zone. They make burrows which have narrow entrances and wide interiors and live in these burrows for a lifetime. In this study, the morphology and the microstructure of the valve of rock-boring clam B. manilensis were observed using a stereoscopic microscope and FE-SEM, respectively. The chemical composition of specific part of the valve was assessed by energy dispersive X-ray spectroscopy (EDS) analysis. 3D modeling and structural dynamic analysis were used to simulate the boring behavior of B. manilensis. Microscopy results showed that the valve was asymmetric with plow-like spikes which were located on the anterior surface of the valve and were distributed in a specific direction. The anterior parts of the valve were thicker than the posterior parts. EDS results indicated that the valve mainly consisted of calcium carbonate, while metal elements, such as, Al, Si, Mn, Fe, and Mg were detected on the outer surface of the anterior spikes. It was assumed that the metal elements increased the strength of the valve, thus helping the B. manilensis to bore sediment. The simulation showed that spikes located on the anterior part of the valve received a load at all angles. It was suggested that the anterior part of the shell received the load while drilling rocks. The boring mechanism using the amorphous valve of B. manilensis is expected to be used as basic data to devise an efficient drilling mechanism.

Tungsten disulfide (WS2) nanosheets have attracted considerable attention because of their unique optical and electrical properties. Several methods for fabrication of WS2 nanosheets have been developed. However, methods for mass production of high-quality WS2 nanosheets remain challenging. In this study, WS2 nanosheets were fabricated using mechano-chemical ball milling based on the synergetic effects of chemical intercalation and mechanical exfoliation. The ball-milling time was set as a variable for the optimized fabricating process of WS2 nanosheets. Under the optimized conditions, the WS2 nanosheets had lateral sizes of 500–600 nm with either a monolayer or bilayer. They also exhibited high crystallinity in the 2H semiconducting phase. Thus, the proposed method can be applied to the exfoliation of other transition metal dichalcogenides using suitable chemical intercalants. It can also be used with highperformance WS2-based photodiodes and transistors used in practical semiconductor applications.

Korean small and medium sized software companies have tried to export their solutions or services to overseas markets. In 2016, exports of the software industry increased by 6.0% from the previous year, and the value added of the industry was 2.2 times higher than that of the manufacturing industry. From a long-term perspective, it is important to secure a global competitive advantage in order to sustain the export high value-added of the software industry. The obstacles to entry into the overseas market of small to medium enterprises are as follows: first, difficulty in product development and localization of marketing; second, lack of investment for overseas expansion; and finally, competitiveness of software technology. In particular, To overcome such obstacles, Korean small and medium sized software companies should increase the technical perfection and secure software export competitiveness. The paper presents a payment settlement framework enabling adaptive reuse and semiautomatic development of global payment settlement services. The quantitative and qualitative evaluation results are presented with domestic and overseas case studies as follows: Firstly, semi-automatic development is realized successfully by applying the framework. Secondly, it is possible to maintain consistent quality of software and to deliver maintenance services without relying on the internal human resources. Thirdly, it is possible to reduce the project duration of the same development cope to less than 50% by applying the framework. Finally, because it is based on BPMN 2.0, which is a high level design diagram, it is expected that it will be easy to implement through components connection and reduce difficulties in technology transfer and localization. Also, at the time of runtime operation, it will be effective to understand the design idea easily and to carry out additional developments without human resource who participated in the initial project.

Stainless steel is known as a corrosion-resistant material and this superior ability could be a desired property for a pinhole aperture operated in a corrosive environment and thereby be able to maintain both smoothness and a perfect circular shape in order to achieve precise beam alignment. Laser drilling has widely been preferred when placing holes into stainless steel due to its non-contact method of machining. In addition, this method is capable of performing delicate machining while inducing relatively low amounts of heat in the affected zone in comparison with other traditional machining techniques such as punching. Laser drilling is also beneficial for specimens having a thin thickness since manufacturing tolerances are minimal in this case. In this paper, we have attempted to produce holes of various diameters in 10 m thick stainless steel foil by using a femtosecond laser trepanned method. We have demonstrated these to be of perfect circular shape and adhering to low tolerance manufacturing by adjusting the beam parameters. In addition, holes with various diameters have been made by employing previously selected machining parameters and the viability of pinhole apertures fabricated by laser drilling have been evaluated.

이 연구는 10가지의 보호처분 중 1호처분을 받아 청소년회복센터에 위탁되어 있는 보호소년의 사회복귀 의지에 영향을 미치는 요인을 파악하고자 하는 목적을 가지고 수행되었다. 청소년회복센터는 청소년 교정 분야에 새롭게 도입된 시설이기 때문에 보호소년의 경험을 토대로 한 연구는 소년보호에서 매우 중요한 의미를 가진다. 이를 위한 연구방법은 청소년회복센터 11개소에 위탁되어 있는 보호소년 90명을 대상으로 설문조사하였다. 그 결과를 살펴보면 다음과 같다. 먼저, 보호소년의 인구사회학적 배경에 따른 사회복귀 의지는 차이가 없었다. 비행이라는 동질성과 아직은 미성숙한 청소년이라는 특성이 반영된 결과라 볼 수 있다. 다음으로 보호소년의 사회복귀 의지에 영향을 미치는 요인들 간의 관계를 알아보았다. 행동변화(r=0.523), 시설생활긍정(r=0.473), 자아존중감(r=0.414), 교육프로그램만족(r=0.396) 순으로 정적인 관계가 있는 것으로 나타났다. 이러한 각 요인들은 보호소년의 사회복귀 의지에 유의미한(p=000)영향을 미치며, 사회복귀 의지를 예측하는데 34.2%(R²(수정))의 설명력을 갖는 것으로 나타났다. 각 변수별 영향력은 자아존중감(β=0.476), 행동변화(β=0.350), 구성원관계(β=-0.336), 시설생활긍정(β=0.260), 학교재학여부(β=-0.150) 순으로 유의미한 영향을 미치는 것으로 나타났다. 즉 비행초기의 시설보호 비행청소년에게 필요한 프로그램은 자아 수준을 높일 수 있는 자아존중감프로그램과 행동변화를 위한 프로그램이 필요한 것으로 나타났다. 또한 학교를 다니지 않는 보호소년의 사회복귀 의지를 강화하기 위한 직업훈련 및 진로프로그램을 강화할 필요가 있다.

장님마디톡토기는 토양생태계에서 오염물질의 독성영향을 평가하기 위한 국제 공인 표준시험종으로 제안되고 있다. 토양생태계 먹이사슬에서 중요한 역할을 수행하는 톡토기의 특성에 따라 다양한 연구가 시도되고 있으며, 더 민감한 독성영향 종말점이 제시되고 있는 실정이다. 본 연구에서는 대표적인 토양오염물질인 중금속의 생태독성영 향을 평가하기 위하여 장님마다톡토기의 도약능을 이용하였다. 장님마디톡토기는 표준시험법에 따라 중금속 오염토 양에 만성노출되었으며, 이후 생존개체를 수집하여 도약능 평가를 수행하였다. 톡토기의 도약은 일시적인 화학스트레 스를 이용하여 유도되었으며, 이를 회피하기 위한 운동능을 컴퓨터 프로그램을 통해 기록하여 평가하였다. 중금속 오염토양에 노출된 개체는 도약을 통한 회피 경로가 단순화되었으며, 도약 횟수와 길이가 중금속 농도에 따라 통계적으로 유의하게 감소하였다. 이는 중금속 오염토양에서 톡토기의 회피능력이 감소할 수 있음을 의미하며, 생태독성을 평가하기 위한 종말점이 될 수 있을 것이라 판단된다.

최근 한국의 소년사법에서 우려할 만한 현상 가운데 하나가 재범률의 증가이다. 6호 처분은 40년간 중간단계 처우로서 운영되어왔지만, 과연 6호 처분이 소년범의 재비행 예방에 기여하고 있는지에 대한 연구는 미흡하다. 6호 처분 시설들이 과거와는 다르게 새로운 프로그램을 도입하는 등 변화를 하고 있다는 시점에서 새로운 관심과 연구들이 필요하다. 이 연구는 기존의 시설 내 처우가 주는 낙인효과(labelling effect)와 범죄배양효과(crime breeding effect)을 극복하자는 6호 처분의 목적에 근거하여, 6호 처분의 프로그램이 과연 입소자의 재범태도에 영향을 미치고 있는지 살펴보았다. 이를 위해, 가족요인, 학교요인, 또래요인, 과거 판결횟수 등 입소 전 과거 생활과 재범태도에 영향을 미칠 가능성이 높은 입소 후 행동변화를 추가하여 프로그램이 재범태도에 영향을 미치는지를 살펴보았다. 또한 재범태도에 영향을 미치는 요인들과의 경로를 통해 프로그램 효과를 탐색하였다. 연구결과를 살펴보면, 주요 변인을 중심으로 회귀분석을 실시한 결과 가족애착과 또래애착, 프로그램만족도만이 유의미하게 나타났다. 친구들과의 애착관계가 잘 형성되어 있을수록, 가족과의 애착이 클수록, 프로그램만족도가 높을수록 재범태도에 긍정적인 영향을 미치고 있었다. 더불어 재범태도에 영향을 미치는 요인들 간의 경로는 어떠한 지 분석해본 결과, 프로그램 만족도만이 재범태도에 직접효과와 간접효과를 가지고 있었다. 위의 결과를 토대로 지역사회 내 수용처우 입소자들이 재범을 하지 않겠다는 의지 혹은 태도를 높이기 위해서는 입소자를 위한 프로그램강화와 실질적인 차원에서의 프로그램 효과성을 높일 수 있는 정책과 제도적 장치가 필요함을 알 수 있었다. 또한 한국의 현실에 근거한 지역사회 내 수용시설 프로그램 개발, 운영, 관리, 평가 등에 대한 연구들도 마련되어야 할 것이다.

해양보호구역 일부 지역을 포함하고 있는 서천 유부도 해안과 순천만 그리고 다도해해상국립공원 여수 안도 등에 해양쓰레기가 다량 표착하고 있다. 이곳에 표착해 있는 해양쓰레기는 해류와 바람 및 조류 등의 영향으로 유입되고 있는 것으로 조사되었다. 연구지역 중 유부도는 서해로 흐르는 금강하구에 위치하고 있으며, 계절별 희귀철새들이 대규모로 날아오는 국내최대 철새도래지다. 이곳에 폐그물과 낚싯줄 같은 플라스틱류가 다량 표착해있었다.

영광 주변해역에서 꽃게의 갑폭조성, 상대성장, 성비와 외포란량을 조사하였다. 조사해역에서 출현한 꽃게는 총 658개체(수컷:305, 암컷:353)로 나타났다. 조사기간 동안 수온과 염분의 변화 양상은 수온은 5.9-27.3℃의 범위를 나타내었으며, 염분 농도의 경우 28.1-31.6 psu의 범위를 각각 나타내었다. 두흉갑폭(CW)과 갑장(CL)의 관계와 두흉갑폭(CW)과 전중량(TW)의 관계식의 경우 암컷의 경우 CL = 1.3073 CW + 25.684(R2=0.791), TW=0.0061CW2.4231(R2=0.801)로 나타났고, 수컷의 경우 CL = 1.3652 CW + 22.495(R2= 0.741), TW=0.0068CW2.400(R2=0.749)로 나타났다. 꽃게의 성비의 경우 수컷과 암컷의 출현비율이 평균 0.86 : 1로 나타났다. 외포란량의 경우 암컷의 크기가 증가함에 따라 포란량은 증가함을 알 수 있었다.