Ti-Cu-Ni-Sn quaternary amorphous alloys of Ti50Cu32Ni15Sn3, Ti50Cu25Ni20Sn5, and Ti50Cu23Ni20Sn7 composition were prepared by mechanical alloying in a planetary high-energy ball-mill (AGO-2). The amorphization of all three alloys was found to set in after milling at 300rpm speed for 2h. A complete amorphization was observed for Ti50Cu32Ni15Sn3 and Ti50Cu25Ni20Sn5 after 30h and 20h of milling, respectively. Differential scanning calorimetry analyses revealed that the thermal stability increased in the order of Ti50Cu32Ni15Sn3, Ti50Cu25Ni20Sn5, and Ti50Cu23Ni20Sn7.

TiC-and Ti(C,N)-based cermets are excellent in semi-and final finishing of work piece during cutting operations. Typical microstructure of the cermets is a core/rim structure. The undissolved Ti(C,N) cores contribute to their high hardness while the rim phases, (Ti,M1,M2)(C,N)-type solid solutions, play great roles in enhancing the toughness. In this paper, various ultrafine pre-mixed MeC-Ni powders were synthesized and the powders were sintered or hot pressed after mixing in order to control the size and volume fractions of core and rim phases in the system. This paper will present the factors determining the microstructure along with mechanical properties.

This paper presents the influence of the compositions of sintered Ti-Ni alloys on their thermo-mechanical properties. The Ti-Ni alloys having various compositions from 50at%Ni to 51at%Ni were sintered using elemental Ti and Ni powders by a pulse-current pressure sintering equipment. The deformation resistance in stress-strain curves increased with an increase in Ni content. In the case of Ti-50at%Ni, tensile strength and elongation were more than 500 MPa and 7%, respectively. The increase in Ni content also makes the transformation temperatures lower. The deformation resistance at a test temperature change from 293K and 353K in isothermal tensile test increased with elevating test temperature.

Ti-Zr-Ni coatings deposited by low vacuum plasma spray technique consisted of nanometer-sized 1/1 cubic approximant and TiZrNi Laves phases as well as a low volume fraction of phase. The shift of composition during deposition of the quasicrystalline powders and the presence of phases are believed to be responsible for the reduced corrosion performances evaluated by means of electrochemical tests in a Hanks' Balance Salt Solution at .

TiNi bodies were produced from (Ti＋Ni) powder mixture by spark-plasma sintering procerg. The sintering behavior was investigated through the measurement of change in density, densification rate, phase analysis and microstructure. Irrespective of heating rate, sintered bodies with above 97％ relative density could be obtained. TiNi with B2 structure was confirmed as the major phase and , unreacted Ti, Ni as the second phase. Increase in heating rate suppressed a formation of intermediate phase during sintering process. Increase in holding time at sintering temperature led to a compositional homogenization.