Al-Cr-Zr nanocomposite metal powders were prepared by mechnical alloying (MA) in order to develop aircraft structure materials with lighter weight and lower cost than the conventional Ti and Ni alloys. The morphological changes and microstrutural evolution of Al-6wt.%Cr-3wt.%Zr nanocomposite metal powders during MA were investigated by SEM, XRD and TEM. The approximately 50m sized Al-Cr-Zr nanocomposite metal powders has been formed after 20 h of MA. The individual X-ray diffraction peaks of Al, Cr and Zr were broadened and peak intensitied were decreased as a function of MA time. The observed Al crystallite size by TEM was in the range of 20 nm, which is a simliar value calculated by Scherrer equation. The microhardness of Al-Cr-Zr nanocomposite metal powders increases alomost linearly with increase of the processing time, reaching a saturation hardness value of 127 kg/ after 20 h of processing. The intermetallic compound phase of in the matrix was identifed by XRD and TEM.

현행 내진설계 규준에서 사용하고 있는 반응수정계수는 설계지진하중과 유사한 지진발생시 구조물이 비선형 거동을 하도록 탄성응답에서 요구되는 밑면전단력 값을 낮추는 계수라 할 수 있다. 따라서 반응수정계수는 하중저감계수(force reduction factor)라고 할 수 있으며, 이러한 값들은 경험적으로 결정된 것이어서 예상지진에 대하여 구조설계자가 설계한 건물이 어느정도의 비선형 거동을 할지는 예측하기가 힘들다. 본 연구에서는 목표가 되는 연성비(target ductility ratio)에 따라 요구되는 밑면전단력의 값을 구하고 이를 규준에서 요구하는 값과 비교할 것이다. 만약 요구되는 값이 규준 값 보다 크다면 이는 구조물이 가지는 부가강도(overstrength)나 잉여력(redundancy)이 담당해야 한다. 모멘트연성골조 건물을 설계한 후 이를 push-over 해석에 의하여 부가강도를 찾아 보아 요구강도와 비교할 것이다.

본 연구는 철근콘크리트 단층 구조물의 구조 부재 위치에 대한 비파괴검사법을 이용한 추정 신뢰도를 알아보기 위해 기둥, 벽체, 보 및 슬래브로 구성된 실험체를 제작하고, 기존 추정식과 비교 과정에서 정확한 분석을 위해 오차율 비교와 모평균 구간 추정을 사용하여 통계적 접근을 통한 신뢰성을 분석하고자 한다. 그 결과, 초음파속도법을 이용하여 압축강도를 추정한 결과와 코어시험 결과를 비교한 전체 평균 오차 율은 18.8%, 반발경도법을 이용하여 압축강도를 추정한 결과와 코어시험 결과를 비교한 전체 평균 오차율은 20.1%가 도출되어 현장 적용성을 확인하였다. 그리고 부재별 신뢰성 부분에서 초음파속도법과 반발경도법을 이용하여 신속하고 효율적인 구조물 안전진단을 하기 위해서 각각 벽체 부재와 보 부재를 중심으로 압축강도 추정 시 신뢰도 높은 결과를 도출되는 것을 확인하였다.

본 연구에서는 단일강섬유와 하이브리드강섬유로 보강된 UHPC의 휨강도 및 연성을 평가하기 위해 세 개의 휨파괴형 보에 대한 4점 가력 실험을 수행하였다. 실험 결과 단일섬유로 보강된 UHPC보다 하이브리드 섬유로 보강된 UHPC가 강도 및 연성 모든 측면에서 더 우수한 구조성능을 보유한 것으로 나타났다. 설계시의 안전성에 대해 평가하기 위하여, K-UHPC 구조설계지침에서 제공하는 방법에 따라 실험 체의 강도와 연성을 평가해본 결과 현재의 재료모델은 강도에 대해서는 보수적으로 평가할 수 있으나 연성에 대해서는 과대평가하는 것으로 나타났다.

철근콘크리트 구조물의 설계 시 구조물의 연성거동을 보장할 수 있도록 한다. 연성거동에 영향을 미치는 주요 인자 중 하나는 철근이다. 철근콘크리트에 사용되는 철근은 KS D 3504에 따라 제작되어지는데, 설계 시 사용되는 철근의 항 복강도는 KS D 3504에서 제시하는 기준 항복강도이다. 항복강도가 달라짐에 따라 구조물의 파괴거동 또한 달라질 수 있다. 본 연구에서는 기준 항복강도와 KS D 3504에서 허용하고 있는 허용 최대항복강도를 적용하였을 때의 구조물의 파괴거동 차이를 비교 및 분석하였다.

이 연구는 상하단 철근의 영향에 따른 철근콘크리트 보의 비틀림 강도를 평가하고자 단면의 상하단 철근의 R값을 변수로 비틀림 실험을 수행하였다. 실험체는 선행연구와 동일한 캔틸레버 형태로 총 2체를 제작하였으며, 1000kN의 액추에이터 2대 를 이용하여 가력을 실시하였다. 실험결과, 상하단 철근의 영향에 따라 비틀림 내력의 차이를 확인하였다.

최근 건축물 붕괴사고 빈도수가 증가하면서 안전진단에 대한 수요가 증가하고, 신뢰도 높은 안전진단기법에 대한 요구가 확대되고 있다. 국토교통부(2018) 자료에 따르면 노후건축물 수에 비해 안전진단관련 전문기관이 부족한 실정이다. 본 연구에서는 초음파속도법을 이용한 압축강도 추정 값과 코어 시험을 이용한 콘크리트 압축강도 측정값을 비교하여 추정오차율 비교와 신뢰도 구간 추정을 하고, 최소인원으로 신속하게 효율적인 구조물 안전진단 기법을 제안하는 것을 목표로 한다.

본 연구는 전단력과 휨을 받는 춤이 작은 중공 SFRC 부재를 대상으로 중공에 따른 웨브폭이 부재의 전단강도에 미치는 영향을 평가하고자 실험 및 해석을 실시하고 기존식과 비교⋅분석하였다. 전체폭에 비하여 웨브폭은 1/2배, 2/3배로 선정하였으며, 전단경간비는 1.5로 계획하였다. 전단실험 결과, 웨브폭이 33% 증가함에 따라 최대전단강도는 10.3~28.0% 증가하였다. 실험체의 전체춤이 1.5배 증가함에 웨브폭이 100mm인 실험체는 전단강도가 29.2% 증가한 반면, 150mm인 실험체는 11.3% 증가에 그쳐, 웨브폭이 적을수록 춤의 증가에 따른 전단강도 증가율이 큰 것으로 나타났다. 이를 볼 때, 웨브폭이 적을수록 강섬유의 기여도가 큰 것으로 사료된다. KCI 기준식이 중공 슬래브의 전단강도를 매우 안전측으로 평가하고 있으며, Shin et al.의 제안식이 실험강도를 비교적 잘 예측하는 것으로 나타났다. 비선형 유한요소 해석으로부터 웨브폭이 2, 3, 6배 증가함에 따라 해석부재의 평균 전단강도는 각각 1.18배, 1.80배, 2.19배로 나타나, 웨브폭의 증가에 비례하여 전단강도가 증가하지 않는 것으로 나타났다.

In this study, the compressive strength and elastic modulus of concrete mixed with electric furnace slag were evaluated. The concrete specimens were prepared using the steel slag as coarse aggregate and heavyweight waste glass as fine aggregate. From the results, compressive strength and the elastic modulus were improved with the addition of electric furnace slag.

The strength and durability of PSC sleepers may deteriorate in the long term due to the cracks generated on the concrete surface, and maintenance is required to improve the strength and usability of sleepers and prolong the service life for a certain period. In this paper, flexural strength tests were carried out on rectangular parallelopiped specimens and real cracked PSC sleepers to evaluate the contribution of the flexural performance for the liquid-type reinforcing materials.

Smart construction materials have recently been interesting to improve the performance of cement composites and concretes. Especially, no repairing system is required for concrete structures by using self healing concrete, which can close cracks on concrete by itself. Mineral admixtures, capsules and bacteria are the most used for self healing concrete technology. In this study, high strength concrete with mineral admixtures were utilized to develop self healing capacity. Comparison with water flow test and image captures were conducted.

In this study, an experimental evaluation was made on the change of the pull - out performance of BFRP concrete interface after repairing cracks on the lower surface of reinforced concrete by using basalt fiber which is environment friendly and heat - resistant compared to glass fiber. The test standard was ASTM D7522 / D7522M, and the influence factor was considered as the crack thickness. Test results showed that the fracture pattern was the same regardless of the crack thickness and the bond stress was measured similarly.

In this study, the shear strength according to the width of the web was assessed by using the Waste styrofoam as hollow material without reprocessing. The concrete's design strength was set to 24MPa and the web width was 50mm, 100mm, and 150mm as variables. Shear strengths of KCI increased from 111.2% to 203.9%.

The purpose of this study is to evaluate the validity of design criteria for the SCP module specified in KEPIC-SNG. The structural performance of the compression members for the SCP module joint types was measured and the characteristics of the compression members were analyzed. As a result, For all specimens, the maximum load exceeded the ultimate strength.

기존의 정수처리 방법으로는 제거되지 않는 물질이 발생함에 고도정수 처리 시설의 도입이 증가하고 있다. 그러나 오존을 이용한 고도정수처리 시설의 내부 방수·방식재는 오존의 산화력에 의해 열화되며 콘크리트까지 영향을 미쳐 내구성 저하의 원인이 된다. 본 연구에서는 내오존성 및 내화학성이 뛰어난 금속 패널을 기존의 시공법 보다 손쉬운 방법으로 시공하기 위한 방법으로 금속용사 공법을 이용하여 수처 리 시설 콘크리트 구조물의 열화를 원천적으로 방지하기 위한 마감공법 개발 연구의 일원으로 용사금속 종류 및 피막의 표면처리 방법에 따른 내오존성 평가를 실시하였으며, 오존처리 후의 부착강도를 평가하였다. 실험결과 용사금속 Ti이 용사 후에도 내오존성이 뛰어난 것으로 나타 났으며 표면처리 방법으로는 테프론계 봉공처리제를 사용하여 마감하는 것이 내오존성 및 부착성능 확보에 가장 적합한 방법이라 판단된다.

이 논문은 압축강도 수준(100, 140, 180 MPa급)에 따른 HPFRCC의 동적충격 인장강도를 평가하였다. 먼저 100, 140, 180 MPa급 HPFRCC의 압축응력-변형률 관계를 분석한 결과 압축강도는 각각 112, 150, 202 MPa로 나타났으며, 압축강도가 높아짐에 따라 탄성계수도 증가하는 경향을 나타내었다. 100, 140, 180 MPa급 HPFRCC의 정적 인장강도는 각각 10.7, 11.5, 16.5 MPa로 나타났으며, 압축강도가 높아질 수록 인장강도도 증가하는 경향을 나타내었다. 반면 100 및 140 MPa급 HPFRCC에서의 인장강도 및 에너지 흡수능력은 압축강도 수준에 따라 큰 차이를 보이지 않았다. 이는 시험체의 규격 및 강섬유의 배열에 영향을 받은 것으로 판단된다. HPFRCC의 동적충격 인장강도를 평가한 결과, 변형률 속도가 10-1/s에서 150/s로 증가할수록 모든 HPFRCC의 인장강도와 동적증가계수는 증가하는 경향을 보였다. 한편 동일한 범위의 변형률 속도에서 HPFRCC의 압축강도가 낮을수록 인장강도에 대한 DIF가 높게 측정되어 효율적인 측면에서는 100 MPa급 HPFRCC가 가장 우수한 것으로 나타났다. 따라서 높은 수준의 인장성능이 요구되는 경우 높은 압축강도를 가지는 HPFRCC를 사용하는 것이 유리하며, 폭발과 같은 고속변형률 속도에서 보다 효율적인 접근을 위해서는 목표 압축강도에 근접한 HPFRCC를 사용하는 것이 바람직한 것으로 판단된다.

In this study, presents the mechanical bond strength properties of mortar using bio polymer in seaweed. The evaluation was based on the method presented in KS F 2762. It was confirmed that the resistance performance all levels of biopolymer using mortar excellent performance with bond strength over 1.0 MPa as defined in KS F 4042 『Polymer-cement mortar for Concrete Structures』.

The purpose of this paper is to assess the effect of surface characteristic of GFRP rebar on concrete-reinforcement bond behavior. For sample preparation, 10 GFRP rebar with two types of surface conditions were used to fabricate 15×15×15cm sized GFRP reinforced concrete. Then, pull-out test was carried out on each concrete samples until the maximum bond strength was achieved. From the test result, it was found that the maximum bond strength at the lattice type is 1.38 times higher than that for unidirectional surface.

In this study, compressive tests were carried out on seamless circular tubular short columns with corrosion-damaged end, and investigated change in compressive strength of columns with local corrosion at the end. Local corrosion was artificially introduced by milling machine, and differed in corrosion depth (0, 1.5, 3, 4.5 mm), corrosion height (0, 20, 60, 120 mm), and corrosion circumference (0, 90, 180, 360˚ ). As a result, the compressive loads were linearly decreased with increasing of corrosion degrees, and a quantitative evaluation for residual compressive strength of seamless circular tubular short column with corrosion-damaged end was suggested by using corroded volume loss ratio.