Based on the study of strength development characteristics of Ground granulated blast-furnace slag(GGBFS), it was found that the use of GGBFS as a admixture was advantageous in terms of long-term strength. Therefore, GGBFS can be a replacement for the Flyash which is currently used in the NPP.

This study examines the strength properties use of talc as a substitute for OPC-GGBFS cement. The test was carried out by replacing the plain mix(OPC : GGBFS = 50 : 50) with talc at the rate of 0~100%. The OPC contents was constant in all mixtures. The mixtures replaced GGBFS with talc. The results showed that the compressive strength and bending strength decreases with an increase in talc contents.

This study evaluates the material performance of slump value and compressive strength of the concrete which was made by recycled sand and blast furnace slag powder(BFSP). The main variables are replacement ratio of BFSP. As a result, it was evaluated that more detailed evaluation is needed in long-term strength development and the compensation of slump value to the replacement ratio of BFSP.

Using of the ground granulated blast furnace slag as the substitutes of cement mixtures is increasing. This is used about 40% as the substitutes commercially but recently there are several tests used the maximum 80%. When used as the substitutes of cement mixtures which can improve the durability, the watertightness and the sulfate resistance but there is reduced the concrete quality due to early strength reduction and the drying shrinkage increase. Therefore it is very important to make the curing environment which helps early hydration activation vigorously. In this study, the hydrate characteristics replacing the maximum 80% of ordinary portland cement with blast furnace slag powder and using the alkali activator to increase early hydration activation were considered and analyzed by the XRD, TG-DTA, SEM, From these tests results, the use of the alkali activator had the increase of the calcium hydroxide according to ages and the reach time reduced about 1 min. and 9 min. for the first and second peak respectively. The effects on the hydrate characteristics of using the alkali activator were not significant.

알칼리활성화 슬래그-레드머드 시멘트는 알칼리활성화 시멘트 연구의 일환으로서 시멘트 조성에서 알칼리자극제, 고로슬래그와 레드머드로 구성되어져 있으며, 포틀랜트 시멘트를 사용하지 않는 클링커 프리 시멘트(Clinker Free Cement)를 의미한다. 본 논문에서는 포틀 랜트 시멘트를 전혀 사용하지 않고 고분자 유기화합물인 재유화형 분말 폴리머를 혼입한 알칼리활성화 슬래그 시멘트에 레드머드의 대체율을 달리하여 강도특성, 기공특성 등을 기존 포틀랜트 시멘트와 비교 평가하였다. 그 결과 알칼리활성화 시멘트에 레드머드를 대체할 경우 C-S-H 광물상과 에트린가이트가 주요 수화생성물로 포틀랜트 시멘트와 비교하여 조직이 치밀하고 대체율 10%까지는 압축강도 및 휨강도가 증가하 였다.

혐기성 고정상 반응기는 충전된 담체의 표면적에 미생물을 부착시켜 고효율 반응을 유도하는 반응기이다. 혐기성 고정상 반응기는 기본적인 부유성장식 공정인 CSTR반응기보다 상대적으로 짧은 체류 시간(HRT)에서 고농도의 유기물을 처리하는데 유용하다. 본 연구에서는 포항의 제철 공장에서 채취한 고로 슬래그를 담체로 이용한 상향류식 혐기성 고정상 반응기를 CSTR반응기와 비교해서 짧은 HRT에서 미감수를 처리하는데 적용하였다. 또한 높은 유기물 부하율 조건에서 혐기성 고정상 반응기의 공정 효율과 담체로써 고로 슬래그의 이용가능성에 대해 연구하였다. 쌀은 아시아의 대부분 나라에서 주식으로 먹고 있고, 쌀 이용 시 세척하는 과정에서 주요 폐기물로써 미감수가 대량 배출된다. 미감수는 높은 유기물 함량과 가용성 때문에 생물학적 분해가 쉽고, 혐기 소화에 의한 바이오 가스 생성에 적합하다. 본 실험의 반응기는 희석한 미감수(6.2 g COD/L)를 기질로 하여 HRT 10일에서 0.7일까지 점차적으로 감소시켜 운전하였다(유기물 부하율 기준 0.6 - 8.6 g COD/L·d). 운전 조건의 변화와 함께 유기물 제거율, 메탄 발생량, 메탄 수득율 등의 공정 인자가 변화하였고, HRT 3.4일에서 최대의 메탄 수득율(0.33 L/g COD)을 얻었다. HRT 3.1일에 추가적으로 denaturing gradient gel electrophoresis(DGGE)분석법을 이용하여 미생물 군집분석을 수행하였다.

고로슬래그는 선철 과정 중 고로에서 발생되는 대표적인 부산물이다. 이러한 고로슬래그는 건설재료 중심으로 다방면에 사용되고 있으며, 그 사용량은 급격하게 증가하는 추세이다. 일반적으로 시멘트 혼합재로 사용되는 슬래그는 급랭슬래그이며, 동일 조성을 갖는 서랭 슬래그라 하더라도 자유에너지가 낮아 물질 자체가 안정하여 반응성이 매우 낮기 때문이다. 급랭(수쇄) 슬래그는 준안정 상태로 존재하기 때문에 외부의 자극에 따라 쉽게 새로운 반응 생성물 또는 수화물로 변화하는 특징을 갖는다. 그러나, 슬래그 자체의 활성화가 초기에 손쉽게 이루어지지 않아, 시멘트 초기 강도저하 및 응결 지연 등을 일으키는 단점을 갖고 있다. 이러한 이유에서 시멘트 자극제로서 석고류(황산염 등)가 일반적으로 사용되고 있으며, 이는 슬래그의 5% 수준이다. 일반적으로 슬래그 자극제로서 슬래그시멘트의 초기 강도 보완을 위해 천연무수석고가 사용되고 있으며, 이는 고가의 수입산(태국, 중국)에 전량 의존하고 있다. 이에 대한 방안으로 화력 발전소의 산업부산물인 배연탈황석고를 일부 사용하고 있으나, 초기 강도 보완이라는 목적을 충분히 달성할 수 없는 실정이다. 배연탈황석고 사용으로 인한 초기 강도 개선을 위해 황산염과 알칼리 성분인 CaO 성분이 다량 함유된 열병합발전소 Fly-Ash와 유리생산공정의 부산물인 망초를 알칼리자극제로 혼합 사용하여, 수입에 의존하던 천연무수석고의 대체 사용으로 고부가가치자원화 및 천연 자원의 절약 또한 가능하다. 수쇄슬래그는 물과의 반응이 매우 느리게 진행되지만 알칼리 분위기에서는 수화활성을 나타내므로, 재활용 가능한 열병합발전소 Fly-Ash 및 폐기되는 망초를 활용함으로써 고로슬래그의 알칼리 자극제로 이용 가능하다. 따라서 본 연구에서는 슬래그 자극제 개발에 따른 슬래그 활성화 조건 도출과 수입산 천연무수석고 대체 사용 방안으로 화력발전소 배연탈황석고, 열병합발전소 Fly-ash, 유리산업의 망초를 기본 원료로 하는 석고 대체재(혼합석고) 개발을 실시하고자 한다.

제강 슬래그는 제철 공정 중 쇳물에 녹아있는 불순물을 제거하는 공정에서 발생하는 슬래그로, 불순물과 생석회(CaO), 석회석(CaCO3) 등과의 반응으로 생성된다. 슬래그의 발생량은 원료 및 공정에 따라 그 차이가 있으나 1톤 조강 시 약 470kg이 발생하며, 국내 제강 슬래그의 발생량은 한 해 약 830만톤 정도이다. 제강슬래그에는 칼슘의 성분이 다량으로 함유되어 있어 콘크리트 등 건설원료로 사용이 가능하지만, 이를 사용하기 위해서는 장시간의 숙성 과정이 필요하기 때문에 처리 및 재활용할 수 있는 방안이 필요하다. 광물탄산화는 산업폐기물을 이용하여 이산화탄소 고정 및 탄산염을 생성하는 기술로, 이를 제강 슬래그에 적용하는 연구가 진행되고 있다. 본 연구에서는 광물탄산화 방법중의 하나인 간접 탄산화 방법을 통해 제강 슬래그로부터 탄산칼슘을 제조하고 그 특성을 평가하였다. HCl을 이용하여 제강 슬래그 내 칼슘을 추출하였으며, NaOH 및 CO2 가스를 이용하여 탄산칼슘을 제조하였다. 추출의 경우 반응 온도에 의한 효과는 크지 않은 반면, HCl 농도 및 고액비의 영향을 받았으며, HCl의 농도가 높을수록 낮은 순도의 탄산칼슘이 생성되었다. 최적 조건에서 칼슘 추출 효율은 89%로 나타났으며, 98% 이상의 순도를 가진 탄산칼슘을 생성하는 것이 가능하였다.

Performance Evaluation was conducted for analyzing fundamental properties of warm-mix asphalt mixture using 100% steel slag. This study tested and compared asphalt mixture used three types of asphalt binder and two types of aggregate.

The study is compressive strength of 110MPa PHC pile using ground granulated blast furnace slag to NAC, AC curing method. In the result, 20% of ground granulated blast furnace slag could be substituted for cement in PHC pile concrete.

This paper was examined the durability properties of concrete using rapid cooling slag as fine aggregate for concrete. The results of experiments, concrete using rapid cooling slag showed that durability properties was equal to concrete using normal fine aggregate.

This paper presents the quantitative evaluation of migration diffusion coefficient considering an effect of cold joint. This also contains an effect of mineral admixture on chloride diffusion coefficient and the interaction of cold joint for chloride diffusion is experimentally investigated. The effect of mineral admixture is very effective to resistance to chloride penetration even if concrete has cold joint section.

Recently, the environmental issues are emerging as one the most Compressive strength of concrete using blast furnace slag is decreased when cured at low temperature. To apply slag concrete in winter, we perform the experiment about alkali-activated slag concrete cured at low temperature.

In experimental results, the prediction equation for 28 day-strength of GGBF slag concrete could be produced through the linear regression analysis of early strength and 28 day-strength. In order to acquire the reliability, all mixture were repeated as 3 times and each mixture order was carried out by random sampling. The prediction equation for 28 day-strength of GGBF slag concrete by 1 day strength won the good reliability.

본 연구는 혼합 활성화제에 의한 알칼리 활성화 슬래그 시멘트(AASC)의 역학적 특성에 관한 연구이다. 사용된 활성화제는 황산칼슘(CaSO4, 이하 CS), 황산나트륨(Na2SO4, 이하 SS) 및 수산화나트륨(NaOH)이다. 황산염은 슬래그 중량의 2.5, 5.0, 7.5 및 10.0%로 치환하여 사용하였으며, NaOH는 2M 및 4M 농도의 수용액으로 사용하였다. 본 연구에서는 황산염(CS 및 SS) 치환율에 따른 배합(4가지 배합)과 2M 및 4M의 각각의 NaOH 수용액에 치환된 황산염을 혼합하여 시험체를 제작하였다. 시험체는 총 24가지의 배합에 따라 페이스트로 제작되었으며, 물－결합재 비는 0.5로 하였다. 경화된 시험체에 대해서 압축강도, 휨강도, 초음파속도(UPV), 흡수율 및 XRD 분석을 수행하였다. CS의 활성화제를 사용한 경우는 7.5% CS 치환율, 2M NaOH 수용액+ 5.0% CS 치환율 및 4M NaOH 수용액+ 5.0% CS 치환율의 시험체에서 최고의 압축강도를 나타내었다. 또한, SS의 활성화제를 사용한 경우는 10.0% SS 치환율, 2M NaOH + 7.5% SS 치환율 및 4M NaOH + 2.5% SS 치환율에서 최고의 압축강도 발현을 나타내었다. 휨강도, UPV 및 흡수율은 압축강도 발현 결과와 유사한 경향을 나타내는 것을 알 수 있었으며, XRD 분석결과 시험체 내에 생성된 반응물질은 ettringite, CSH 및 실리케이트계 수화물인 것으로 나타났다. AASC에서 황산염과 NaOH의 혼합 사용은 황산염의 단독 사용의 경우와 비교하여 일정 수준의 농도 범위에서 강도를 향상시키고 조직을 치밀화 시키는 등의 긍정적인 영향을 미치는 것으로 판단된다.

본 연구에서는 반응성 피복소재인 제올라이트, 몬모릴로나이트, 제강슬래그의 피복두께에 따른 오염된 해양퇴적물 내 중금속 용출 차단 효율을 평가하였다. 실험결과, As의 용출차단에는 제올라이트, 몬모릴로나이트, 제강슬래그 모두 효과적이지 못하였다. 제올라이트는 Cr 용출 차단에 부정적인 영향을 미치는 것으로 나타났지만, 몬모릴로나이트 5 cm 피복은 Cr 용출 차단에 매우 효과적이었다. As 및 Cr과는 대 조적으로 Cd, Ni, 그리고 Pb은 미피복 퇴적물에서 조차 용출되지 않았다. Cu와 Zn은 피복 조건에 따른 영향이 가장 뚜렷한 중금속이었다. Cu 의 용출은 몬모릴로나이트 피복 두께 1 cm 이상 그리고 제올라이트 피복 두께 3 cm 이상에서 효과적으로 차단되었다. 해양퇴적물에서 Zn의 용출은 모든 피복 물질에서 효과적이었다. 본 연구를 통해서 제올라이트, 몬모릴로나이트, 제강슬래그를 오염된 해양퇴적물에서 Cr, Cu, Zn의 용출 차단을 위한 효과적인 피복소재로 활용할 수 있을 것으로 판단된다.

본 연구에서는 슬래그를 다량 치환한 콘크리트의 동결융해 저항성능에 미치는 미세공극의 영향을 검토하였다. 콘크리트는 용선예비처리슬래그가 포함된 고로슬래그 미분말을 0, 40, 70 % 치환하여 제조하였으며 압축강도 특성 및 동결융해 저항성능과 미세공극을 검토하였다. 또한 설계기준강도와 목표공기량을 설정하고, 동결융해 작용에 따른 열화를 확인하기 위하여 재령 14일의 낮은 압축강도로 인한 내력저하를 유도하였다. 실험결과, 설계기준강도를 유사하게 설정하고 목표공기량을 확보하였음에도 불구하고 콘크리트의 미세공극 분포가 상이한 결과를 나타내었다. GGBS70 시험체는 동결융해를 받지 않은 초기 0사이클에서 10~100 nm 크기의 공극량이 가장 적어 공극 내 동결할 수 있는 물의 양이 적을 것으로 판단된다. 이러한 이유로 다른 시험체에 비해 동결팽창압력이 상대적으로 작기 때문에 동결융해 저항성능이 우수한 것으로 판단된다.

Converter slag is discharged as by-product from steel making process. Its chemical composition is similar to that of blast furnace slag. Therefore its recyclability is high. But actually it was not widely recycled relatively. We studied to prepare insulating brick with it for enhancing the recyclability. We discussed mixing ratio of melting slag and converter slag and also additional amounts of Al-dross and NaOH as affecting factors. According to our results, 0.195 W/mK of thermal conductivity and 3.02 MPa of compressive strength were obtained at the following condition mixing ratio 60 : 40, aluminum dross 1.5wt%, NaOH 5.6wt%. It seemed that the thermal conductivity of prepared brick was decreased with increasing amount of Al-dross and NaOH. It is satisfied with the standard of insulating fire bricks (KS L3301).

본 연구는 MgO를 0~16% 사용한 알칼리 활성화 슬래그 시멘트 (AASC)의 강도와 건조수축 특성에 관안 연구이다. 고로슬래그 미분말 (GGBFS)는 KOH를 활성화제로 사용하였고, 활성화제의 농도는 2M과 4M이다. MgO는 GGBFS의 중량에 대해 치환하였고 물-결합재 비 (w/b)는 0.5이다. 실험결과, 높은 MgO 치환율은 높은 수화반응으로 모든 재령에서 높은 압축강도를 나타내었다. 압축강도와 초음파속도 (UPV)는 MgO의 양이 증가함에 따라 증가되었다. AASC의 건조수축은 MgO의 양이 증가함에 따라 감소하였다. SEM 결과를 통해 높은 양의 MgO 시험체는 치밀한 반응 생성물질이 만들어 진 것을 확인할 수 있다.

As environmental concerns become a critical issue in the sustainability of the steel industry, manufacturing of various kinds of glass-ceramics and related functional materials recycled from post-mortem slags has become an important topic of research. The slag composition, which was reduced and cooled using this secondary treatment is affected by the operating parameters and thermo-physical properties of the slag, and thus can provide the potential for utilization in highly value-added products such as Portland cement and high-alumina cement. To increase the applications of the reduced slag product, a new cement material as well as slag aggregates from the EAF slags were developed by controlling the composition and morphology through novel methods.