Ni and NiO particles were made by a combustion synthesis process. The characteristics of synthesized powders were investigated with various kinds and amounts of fuels such as urea, citric acid and glycine. Ni phase particles without NiO phase were obtained through combustion synthesis process in air atmosphere with-out further calcinations process, when the content of glycine was 2.44 times of the stoichiometric ratio in the precursor solution. Primary particle sizes of synthesized Ni and NiO particles were about 20∼30 nm.

Fe-Al계 금속간화합물이 FACS (Field-Activated Combustion Synthesis) 법에 의해 제조되었다. 이 계의 반응에 있어서 조성 (Fe:Al=3 : 1,2 : 1, 1 : 1.1 : 2, 1 : 3) , 성형압력 (150, 250, 350MPa), 저항 등이 조사되었는데. Al의 몰비, 성형압력, 전기장의 세가가 증가함에 따라서 연소온도와 연소속도는 증가하였다. 또한 이 계에 있어서 전류적용방식에 따른 반응에 대한 영향이 조사되었다. 전기장이 적용되지 않는 경우, 반응이 일어나기 위해서는 예열이 필요하였고, 예열을 하였을 경우라도 그 반응은 불안정연소파를 나타내어 완전한 반응이 이루어지지 않았다. 생성물은 X-ray, SEM, EDXS를 사용하여 그 구조와 조성을 관찰하였다

This study was conducted on the properties of exhaust emissions of diesel oil and fish oil blended with diesel oils using a direct injection diesel engine at different loads, and on the conditions of carbon deposits of diesel oil and 40% blend oil in the combustion chamber after 20 hours operation at 1]2 load. The properties of exhaust emissions by fish oil blended with diesel oils showed no significant difference with diesel oil. However, soot emissions decreased, increasing the ratio of fish oil. Carbon deposits by fish oil blended with diesel oils were high level compared with diesel oil, which might be overcome by preheating of fuel oil and operating conditions.

The effect of the mechanical alloying of elemental Mo and Si powders on the combustion densification behavior of MoSi was investigated. The ignition temperature of the combustion reaction of the mechanically alloyed powder was measured to be significantly lower than that of the powder mixture prepared by the low energy ball milling process. The densification of the products after the combustion reaction under compressive pressure from the mechanically alloyed powders, however, was found to be poorer than that of the products from the ball milled powder.

착체증합법 및 연소합성법에 의해 Zn0.994Mn0.006Ga2O4녹색형광체 분말을 합성하였으며, 이들의 분말 및 발광특성을 XRD, SEM, BET, PL 등을 사용하여 조사하였고, 이를 고상반응법에 의하여 합성한 시료와 비교하였다. 착체중합법과 연소합성법에 의해 합성한 시료는 각각 500˚C와 400˚C에서 단일 스피텔 상이 생성되었으며, 이들의 입자크기는 고상반응에 의해 합성된 분말에 비하여 작았다. 한편, 착체중합법에 의하여 합성한 분말의 발광강도는 열처리 온도가 900˚C일 때, 연소합성법에서는 반응온도가 400˚C일 때 각각 최대값을 나타내었다.

장경비가 큰 탄화규소를 탄소와 규소간의 고온연소반응으로 제조하기 위하여 공정변수에 따른 연소거동과 미세조직의 변화를 조사하였다. 연소합성된 생성물은 주로 β-SiC이며 연소반응이 충분히 진행되지 못하였을 경우에는 미량의 잔류 반응물과 α-SiC가 관찰되었다. 생성된 탄화규소의 평균입도는 약 5μm로 작았으며, 1300˚C 이상의 예열 조건에서 장경비가 30이상인 탄화규소를 합성할 수 있었다. 압분 강도가 69MPa인 분말의 성형체에서 평균 연소 온도와 평균 전파 속도는 각각 약 1425˚C와 2.1mm/sec 범위이며, 연소 온도는 흑연 분말을 사용하였을 경우가 탄소 섬유를 사용한 경우보다 약 10˚C 높았다. 연소 반응을 임의로 중단시킨 시편의 계면을 EDX와 Auger 전자 현미경으로 분석한 결과 상호 확산층이 관찰되지 않았다. 이는 탄화규조의 연소합성이 용해-석출 모델에 의하여 진행됨을 시사한다. 예열 온도에 따른 연소 반응 중의 온도 분포를 유한 요소법으로 해석함으로써 2500˚C의 초기 연소 개시 온도에 대하여 예열 온도 300˚C에서는 연소파가 거의 전파할 수 없으며 예열 온도가 1300˚C에서는 시료 내부에 자체 전파가 가능한 2000˚C이상의 온도 구역이 존재함을 알았다.

Titanium cabide, TiC-x mole% Al composites, and functionally-graded materials (FGMs) of TiC-x mole% Al were synthesized by an electrothermal combustion (ETC) method. TiC-70 mole% Al composite was not ignited by indirect tungsten coil heating, but can be synthesized by an electrothermal combustion. The velocity of the combustion wave decreased with increasing addition of Al and increased with an increase in the applied electric field. Functionally-graded TiC-Al materials were made from reactant layers with compositions of Ti+C+x moles Al with x ranging from zero to 70 by an electrothermal combustion. In the FGM products a nearly linear change in composition in the graded region was observed in samples with 0 x 70 with x being the mole% Al.

This paper gives a controller design method by Linear Matrix Inequality(LMI) for internal combustion engine with Continuously Variable Transmission(CVT) which satisfies the given H∞ control performance and robust stability in the presence of physical parameter perturbations. To the end, the validity and applicability of this approach are illustrated by simulation in the all engine operating regions.

The combustion characteristics of diesel oil and fish oil blended with diesel oils were investigated at various blending rate of fish oil in diesel engine and constant volume combustion bomb. The evaporation and combustion duration of diesel oil and fish oil blended with diesel oils were respectively different high and low temperature. The dependence of ignition delay on the temperature was different in high and low temperature ranges which were divided at the 773K. The ignition delay become longer than that of diesel oil as the blending rate of fish oil increases, and its difference were larger at different loads. The densityof smoke was lower as the blending rate of fish oil increases, and the rate offuel consumption showed no significant difference between diesel oil and fish oil blended with diesel oils.

연소화염법을 이용한 다이아몬드 박막합성은 기판의 표면상태에 크게 의존한다. 특히 탄소결합상이 기판에 조재하는 경우 다이아몬드 핵생성과 성장은 크게 영향을 받는다. 본 연구에서는 일정한 흡입가스비율(R=O2/C2H2)과 기판온도 조건의 연소화염법을 이용하여 몰리브덴 기판위에 다리아몬드박막을 합성하는 과정에서 박막의 핵생성에 미치는 기판 탄소화합물의 영향을 조사하였다. Mb 금속기판표면에 형성된 탄화물로는 Mo2C상과 soot를 택하여 박막합성 전에 Mo기판상에 형성시켰다. Mo 금속기판표면에 형성된 탄화물(Mo2C)상에는 다이아몬드 핵생성과 입자성장이 촉진되어 가장 조대한 양질의 다이아몬드 입자가 형성되었다. 이것은 탄화물상이 반응가스중의 탄소의 확산을 저지함과 동시에 핵생성의 필요한 잠복기간을 감소키켰기 때문이다. 그러나 soot를 구성하는 미세한 탄소결합상들이 다이아몬드 핵생성 장소로 작용하여 결과적으로 다이아몬드 수밀도가 가장 크게 관찰된 반면, 입자성장은 Mo2C기판에 비해 작았다.

연소화염법을 이용한 다이아몬드 박막합성시 기판표면온도 및 온도분포에 가장 크게 작용하는 공정변수는 탄화수소량을 결정하는 산소/아세틸렌 가스의 혼합비(R=O2C2H2)이다. 본 연구에서는 혼합가스비율 변화 (R=0.87-0.98)에 따른 기판표면온도 및 온도분포를 측정하고, 이들 변수에 따른 다이아몬드 박막의 생성 및 결정형상의 변화과정을 SEM관찰, Raman 분광분석 및 X-선 회절 분석을 통해 조사하였다. 혼합가스비율의 증가에 따라 다이아몬드의 생성입자 수밀도는 감소하였고, 이와 동시에 결정형상도 (111)면과 (100)면이 혼재된 cobo octahedron형에서 octahedron인 (111)면으로 변화되었다. 한편, 기판온도증가에 따라 생성입자의 수밀도가 증가하고 성장속도도 빨라져 조대한 결정을 얻었으며, 생성된 입자형성은 (111)면애 지배적이다가 (100)결정면이 점차 많아지는 양상을 나타내었다.

예연소실식 디젤기관에 있어서 박용부하운전조건에 따른 연소특성을 규명하기 위해 예언소실의 압력데이터를 single-zone, single-chamber의 열역학적 해석에 적용하여 연소해석을 행한 결과 다음과 같은 결론을 얻었다. 1) 부하가 증가함에 따라 최고압력이 상승하고 그 위치가 크랭크각도상 후진되었다. 2) 착화 지연시간은 부하에 관계없이 거의 일정하고, 부하가 증가할수록 가연 혼합기 형성에 소요되는 흡열량은 겉보기로 감소하였다. 3) 예혼합 연소단계의 열발생 양상은 부하에 관계없이 거의 비슷하고, 예혼합 연소시간은 부하가 증가할수록 짧아졌다. 4) 부하가 증가함에 따라 예혼합 연소량은 다소 증가하나 일정 연공비 이상에서는 거의 일정했다. 5) 예혼합 연소분율은 부하가 증가함에 따라 감소했다.(이 논문의 결론부분임)

The combustion characteristics, ignition delay, p-t, dp/dt, Q-t of diesel oil and fish oil blended diesel oils was investigated according to pressure and temperature in a constant volume combustion bomb. The results are as follows: 1) The influence of temperature and pressure on the ignition delay was almost constant in high temperature, regardless of the blending rates, and the ignition delay was shortest in the 60% blend. 2) The maximum pressure was high in order of with pure diesel oil, with the 20% blend and the 60% blend. 3) The rate of pressure rise was high in order of with pure diesel oil, with the 20% blend and the 60% blend. The rate of maximum pressure rise was significantly higher with pure diesel oil than with two blends. 4) The amount of accumulative heat release was large in order of with pure diesel oil, with the 20% blend and the 60% blend.

In this paper, the behaviour of cavitation erosion, influence of corrosion and corrosion control on slide bearing metals for internal combustion engine were investigated, and this experiment was done by the vibratory cavitation erosion tester. The main results obtained are as follows: 1. With decreasing the space between horn and specimen, the weight loss and its rate increased step by step. But the weight loss and its rate of 0.2mm space decreased conversely more than that of 0.4mm space at early stage. 2. The weight loss and its rate with change of pH were appeared to the order of pH2>pH12>pH7>pH4. And the weight loss and its rate at pH 4 decreased at best. 3. The weight loss and its rate by cavitation erosion for bearing metals were shown to the order of W.M7>W.M1>K.M4. 4. There appeared mainly small pit hole at pH2, and appeared the pit of netting thread type at pH12 by the results of the damaged surfaces at pH2 and pH12 environments that were sensitive to cavitation erosion. 5. With increasing the viscosity of lubricating oil, the weight loss rate by cavitation erosion became dull at the space below 0.5mm. 6. The protective efficiency of cavitation erosion-corrosion is superior inhibitor of chormate(25 ppm) to cathodic protection.