An ACR/HMMM film was prepared by blending high-solid ACR with curing agent, hexamethoxymethyl melamine (HMMM). An active curing reaction was observed at 170℃. The dynamic viscoelastic Tg of the final film increased with the static viscoelastic Tg of the film. The log damp value, which means a viscoelastic ratio, decreased with the increase in the curing temperature of the film. Physical properties of the films were within a suitable range for films, and by an accelerated weathering resistance test the films were proved weather resistible ones.

Acrylic resin(ACR) was blended with a curing agent, hexamethoxymethylmela-mine(HMMM), in which blending ratio was 70:30. The curing behavior was examined using Rheovibron. Cross-linking reaction started at 170℃ in 2 min of reaction and curing was completed in 10 min. It was found that the extent of cross-linking increased with the content of acetoacetoxyethyl methacrylate monomer in the ACR.

Curing reaction was carried out with the acrylic resin (ACR) [n-butyl acrylate/atyrene/2-hydroxyethyl methacrylate/acetoacetoxyethyl methacrylate (AAEM)] synthesized before and a curing agent, hexamethoxymethylmelamine (HMMM). With rotational rheometer, the effect of catalysts on curing rate of acrylic resin/melamine was examined. Among the four catalysts used, p-toluene sulfonic acid showed the highest reactivity, and the optimum amount of catalyst was 0.5 phr. It was observed that in the ACR/HMMM curing reaction, gelation point was lowered with the increasing the amount of AAEM and HMMM in the ACR.

An acrylic resin was synthesized with several monomers, styrene(St), 2-hydroxyethyl methacrylate(2-HEMA), n-butyl acrylate, methyl methacrylate, and acetoacetoxyethl methacrylate(AAEM) to prepare a high-solid coatings. Then, a high-solid acryl/melamine coatings was prepared by curing the acrylic resin with a curing agent, hexamethoxymethylmelamine(HMMM). The curing behavior of the acrylic resin with HMMM was investigated by the Ozawa method using DSC. For AAEM/HMMM and 2-HEMA/HMMM curing reactions, activation energies were 33.01 and 27.12 kcal/mol and frequency factors were 9.54×1015 and 1.53×1013 min-1, respectively. From the results, it was found out that 2-HEMA showed higher reactivity with the curing agent than AAEM.

우리나라에서는 봄철에 콩과목초를 수확한 후 포장 건조시 목초의 수량 및 품질손실에 관한 연구는 거의 없는 실정이다. 따라서 본 시험은 콩과목초인 알팔파(Medicago sativa L.), 크림손 클로버 (Trifolium incarnatum L.) 및 레드 클로버(Trifolium pratense L.)를 봄철 포장에 건조하였을 때 콩과목초의 수량 및 품질 손실에 관한 정보를 얻기 위하여 수행하였으며 결과는 다음과 같다. 알팔파의 수확시 건물 함량은 15%로 가장 높았으며, 크림손 및 레드 클로버의 건물 함량은 각각 12.4 및 11.5%였다. 이러한 초종간의 건물 함량의 차이는 포장 건조기간 중에 계속 유지되었다. 건물 함량이 80% 이상이 되는데 알팔파는 7일이 소요되었으나, 크림손 및 레드 클로버는 8일이 소요되었다. 크림손 클로버 및 알팔파의 건물당 잎과 줄기의 비는 레드클로버보다 높았으나, 조단백질 함량을 가지고 비교할 때 잎과 줄기 비는 레드 클로버가 크림손 클로버 및 알팔파보다 높았다. 건조기간중 탈엽에 의한 건물 손실률은 알팔파가 크림손 클로버 및 레드 클로버보다 높았으며, 조단백질의 손실률도 초종간의 차이가 같은 경향을 보였다. 생초와 건초의 사료가치 비교에서 생초는 조단백질(CP), 가소화영양소총량(TDN) 및 상대사료가치(RFV)에서 높았고, 건초는 ADF 및 NDF 함량이 낮았다. 이상의 연구결과를 볼 때 봄철(5월 중순)에 포장에서 건조된 건초는 건조기간 중 탈엽에 의한 조단백질의 손실이 높기 때문에 ADF 및 NDF 함량보다는 조단백질 함량에 더 영향을 미치는 것을 알 수 있다.

Two-packaged polyurethane coatings were prepared by blending benzoic acid lactone modified polyester polyol(BLMPs) and HDI-biuret. BLMPs were synthesized by polycondensation of benzoic acid, viscosity depression component, with 1,4-butanediol, adipic acid, and polycaprolactone polyol. Kinematic viscosity of BLMP was gradually decreased with increasing benzoic acid content in BLMP. The low viscosity of modified polyester has an advantage of making a high-solid content coatings. After the film was coated with the prepared polyurethane coatings and cured at room temperature, the various physical properties were measured. They showed good physical properties such as flexibility, impact resistance, cross hatch adhesion, yellowness index, and rust resistance. These advantages are the results of introducing polycaprolactone polyol.

The object of this study were twofold, namely, to study on (1) effect of using ultrasound therapy for curing warts (2) any relation between a cure for warts and onset of warts, as well as subject age. Our subjects, composed of 22 people from age 12 to 49, were assigned to two groups, experimental group and control group. We experimented for 8 session on 12 people in the experimental group by using ultrasound therapy to observe any morphological change in the warts or disappearance of a pain. However, we did not cure warts in the other group, control group. The result of the study are as follows. (1) Ultrasound therapy has an effect on curing warts. (2) Neither condition, onset of warts or subject age, had no influence on a cure for warts.

An experiment was camed out in 1994 to determine the effects of curing periods and preservatives on the characteristics and forage quality of baled alfalfa(Medicago sativa L.) hay after 60 days of storage. The main plots consisted of the curing periods su

Method for the sun curing dehydration of pig excreta by using vinyl house was described. We determined effects of the dehydrated pig excreta on the yields of whole crop corn and proximate chemical composition of whole crop corn. Pig excreta were dehydrate

온실 가스의 대부분을 차지하는 이산화 탄소는 시멘트 제조과정에서 많이 발생한다. 최근에 배출된 이산화 탄소를 활용하기 위한 방안으로 탄산화 양생 기법이 연구 중이다. 탄산화 양생은 굳지않은 콘크리트의 초기 강도 발현을 급속으로 증진 시킨다. 본 연구에선 탄산화 양생의 효율을 높이고 정량적으로 평가를 하였다. (1) 압력 챔버 내 시편에 이산화 탄소를 350 kPa로 가압하여 양생하는 방법, (2) 챔버 내 시편을 이산화 탄소 농도 20%와 상대습도 75±5%의 조건에서 양생하는 방법을 활용하였다. (1)번 양생 기법에서 이산화 탄소 압력 감소량을 모니터링하여 반응한 이산화 탄소 양을 정량적으로 평가하였다. 또한, 시편을 크기별로 달리하여 탄산화 양생이 미치는 영향을 평가하였다.

본 연구에서는 저탄소 친환경 콘크리트의 일반적인 원재료로 널리 알려져 있는 플라이애시, 고로슬래그미분말을 혼합하여 알칼리 활성화 결합재를 제작한 후, 양생 조건에 따른 내구성을 파악하고자, 탈형한 시험체를 15 및 25°C의 해수에 양생 시켜 재령 91일까지의 내구 특성을 살펴보았다. 플라이애시와 고로슬래그미분말의 혼합비에 대해서 일부 혼합에 대해서는 재령 28일에 비해 재령 91일에서 흡수율 증가 및 강도 감소를 나타났지만, 그 이외에는 양생 조건에 관계없이 재령에 따라 흡수율 감소 및 강도 증가를 보여주었다.

본 연구에서는 플라이애시가 90 %만큼 다량치환된 모르타르에 알칼리 활성화를 통한 강도증진을 동일한 양생온도 조건 에서 양생방법 및 유지시간 변화에 따라 비교 분석하고자 하였다. 연구 결과로 플래이애시를 90 % 치환한 경우, 소생재 도 포 후 40℃로 24시간 기중양생시 가장 높은 압축강도를 발휘하였지만, OPC의 압축강도까지 발휘하는 것은 어려울 것으로 분석되었다.

양생조건에 따른 고로슬래그를 혼입한 콘크리트의 염화물 이온 확산계수의 변화를 관찰하기 위하여 GGBFS 혼입율 0%, 30%, 60%로 구분하고 W/B를 40%,50%,60%로, 양생조건을 기중양생과 수중양생으로 시험체를 제작하여 콘크리트 염화물 이온 확산계수 평가를 실시하였다. 평가결과 GGBFS의 치환율이 증가할수록 콘크리트 염화물이온 확산계수는 감소하였지만, 양생조건에 따른 확산계수 편차가 증가하는 것을 확인하였다. 특히 W/B가 증가할수록 그 차이는 증가하였으며. W/B 60% 조건에서 수중양생 대비 기중양생 시험체의 염화물 이온 확산계수는 2배 가까이 증가하는 것을 확인하였다.

본 연구에서는 플라이애시가 다량치환된 모르타르에 알칼리 활성화를 통한 강도증진을 양생온도 및 양생방법 변화에 따라 비교 분석하였다. 연구 결과로 플라이애시를 60 % 과다치환한 경우 소생재 도포 후 40℃의 온도로 48시간 기중양생을 실시한다면 OPC의 28일 압축강도에 근접하게 발휘되는 것이 얻어졌다.

This study was conducted to evaluate the effect of self-sensing performance on strain-hardening cement composite containing CNT by curing age. The mixing amount of CNT was set at 1.0%, and SHCC fibers were mixed with PE 1.0% and steel fiber 0.5%. The electrical resistance measurement for the tensile strain sensing performance was based on AC method and 4 probe methods. Test results indicated that electrical sensitivity of SHCC decreased with an increase in curing age.

최근 산업 활동에 의해 발생하는 CO2에 대한 처리와 산업부산물에 대한 유효처리 및 자원화 방안이 시급히 요구되고 있다. 본 연구는 콘크리트 혼합재료로 활용이 가능한 산업부산물를 대상으로 탄산화 양생에 의한 건설재료로의 적용성 평가를 목적으로 한다. 이러한 목적을 위해 연구용 시멘트(research cement, RC), 고로슬래그 미분말(GGBFS) 및 유동층 보일러 애시(CFBC)를 대상으로 탄산화 양생에 의한 물리·화학적 변화를 비교 검토하였다. 페이스트 내부의 미세조직 변화를 살펴보기 위해 XRD, SEM 분석을 수행하였다. 실험결과 탄산화 양생을 통해 생성된 반응 생성물인 탄산칼슘은 페이스트 내부의 공간을 채우며 밀도가 높은 미세 구조를 형성함을 확인하였다. 또한, CO2 양생시간이 길어짐에 따라 탄산칼슘 결정이 함께 성장하여 밀실한 미세구조를 이루는 것을 확인하였다.

Recently, high-performance and high-fluidity concrete have been studied and developed because high-rised build is constructed. An early-age properties of these concretes have been studied and developed bacause of comparing existed concrete. This study proposed non-destructive method as electrical resistivity measurement, which evaluates setting time of cement-based materials. An assessment of the effect on the setting time was studied on the addition of a superplasticizer to delay the setting time and the curing temperature to promote the setting time. 6th of samples prepared mortar according to adding superplasticizer(PNS) or curing temperature and measured the electrical resistivity during 24 h. As the results, mortars which curing higher temperature were promoted rising time which is setting time in the electrical resistivity, also mortars which adding superplasticizer were retard rising time.

The present study investigates the material and hydration properties of nPOFA mixed cement mortar with early carbonation curing based on the fact that each process contributes to fill capillary pores, to enhance compressive strength and to reduce CO2. Mortar samples were carried out compressive strength test, phenolphthalein test, MIP testt and SEM. Pulverized cement paste was analytically characterized by XRD, TG/DTA, and FTIR analzes. The fabricated specimens were cured for 0,7, and 28 days in the carbonation chamber which set to carbon dioxide concentration of 5%