Fatigue crack growth rate tests were conducted as a function of temperature, dissolved hydrogen (DH) level, and frequency in a simulated PWR environment. Fatigue crack growth rates increased slightly with increasing temperature in air. However, the fatigue crack growth rate did not change with increasing temperature in PWR water conditions. The DH levels did not affect the measured crack growth rate under the given test conditions. At 316 oC, oxides were observed on the fatigue crack surface, where the size of the oxide particles was about 0.2 μm at 5 ppb. Fatigue crack growth rate increased slightly with decreasing frequency within the frequency range of 0.1 Hz and 10 Hz in PWR water conditions; however, crack growth rate increased considerably at 0.01 Hz. The decrease of the fatigue crack growth rate in PWR water condition is attributed to crack closure resulting from the formation of oxides near the crack tips at a rather fast loading frequency of 10 Hz.

The effect of retained and reversed austenite on the damping capacity in high manganese stainless steel with two phases of martensite and austenite was studied. The two phase structure of martensite and retained austenite was obtained by deformation for various degrees of deformation, and a two phase structure of martensite and reverse austenite was obtained by reverse annealing treatment for various temperatures after 70 % cold rolling. With the increase in the degree of deformation, the retained austenite and damping capacity rapidly decreased, with an increase in the reverse annealing temperature, the reversed austenite and damping capacity rapidly increased. With the volume fraction of the retained and reverse austenite, the damping capacity increased rapidly. At same volume of retained and reversed austenite, the damping capacity of the reversed austenite was higher than the retained austenite. Thus, the damping capacity was affected greatly by the reversed austenite.

In this study, we investigated the precipitation behavior of the R-phase precipitated at the initial stage of aging and its effect on the pitting corrosion of 25%Cr-7%Ni-4%Mo super duplex stainless steel. The R-phase in super duplex stainless steel was mainly precipitated at the interface of ferrite/austenite phases and inside of the ferrite phase during the initial stage of aging, and it was transformed into the σ-phase with an increase in aging time. The ferrite phase was decomposed into a new austenite phase and σ-phase. The R phase was an intermetallic compound, which represented a lower Ni and higher Mo than the matrix, and also had a higher Mo and Cr concentration than the σ phase. With an increasing aging time, the pitting potential Ep was increased slowly by the precipitation of the R-phase, and it was then steeply decreased by the precipitation of the σ-phase. The R-phase was decreased the pitting potential, but its effect was smaller than effect of σ-phase.

In this study, we investigated the precipitation behavior of the R-phase precipitated at the initial stage of aging and its effects on the mechanical properties of 25%Cr-7%Ni-2%Mo-4%W super duplex stainless steel. The R-phase was mainly precipitated at the interface of ferrite/austenite phases and inside of the ferrite phase during the initial stage of aging. It was transformed into the σ-phase with an increase of the aging time. The ferrite phase was decomposed into a new austenite(γ2)phase and the σ-phase by an aging treatment. The R phase was an intermetallic compound showing higher molybdenum and tungsten concentrations than the matrix and also showed higher molybdenum and tungsten concentrations than the σ phase. In the initial stage of aging, precipitation of the R-phase did not change the hardness, the strength and the elongation. The hardness and the strength increased upon a longer aging time, but the elongation rapidly decreased. These results show that the R-phase did not significantly affect the hardness and the strength, though it did influence the elongation.

본 연구에서 고투과도를 갖는 실리카 분리막은 콜로이달 실리카 졸과 고분자형 실리카 졸 두 가지를 DRFF법과SRFF법으로 다공성 금속 지지체 위에 코팅하여 제조되었다. 실리카 졸은 졸-겔법으로 테트라에톡시실란(TEOS)에 의하여 제조되었고, 각각의 졸은 동적광산란법(DLS), 전계방사 주사전자현미경(FE-SEM), 질소 흡착법 등을 이용하여 그 특성을 평가하였다. 다공성 금속 지지체위에 콜로이달 실리카 졸로 중간층을 형성하여 치밀한 구조의 실리카 층을 형성한 후 그 위에 분리층으로 고분자형 실리카 졸을 코팅하여 핀홀을 줄이는 방법으로 기체분리용 분리막을 제조하였다. FE-SEM으로 분리막의코팅 층을 분석한 결과 분리층은 중간층보다 침밀한 구조를 가지고 있음을 확인하였고 기체투과 결과 수소 투과도 (6.63-9.21) × 10-5 mol⋅m-2⋅s-1⋅Pa-1 분포를 보였다.

합성된 스테인레스 스틸에 대한 NATM(New Austria Tunnel Method) 수지의 기계적 특성은 SEM, FT-IR, 인장특성, 그리고 [NCO]/[OH]의 mole %, 입도분석에 의해 측정하였다. 친환경적인 NATM에 관한 관심이 고조됨에 따라 스테인레스 등의 금속에 코팅하는 무용제 도료를 합성하였다. 폴리올, IPDI, 충진제, 실리콘 계면활성제, 촉매 등이 함유된 기존 NATM수지보다 폴리올, MDI, 충진제, 실리콘 계면활성제, 촉매, 가교제가 함유되어 합성된 NATM 수지의 도료가 내구력과 강도가 양호하였다. 견고한 NATM 수지의 기계적 특성은 가교와 [NCO]/[OH]의 mole%가 증가함에 따라 강도가 증가하였다. 결론적으로 NATM의 가교된 미세조직는 스테인레스 스틸 같은 금속물질 코팅에 좋은 물질이다.

The 304 stainless steel powders were prepared by high energy ball milling and subsequently sintered byspark plasma sintering, and the microstructural characteristics and micro-hardness were investigated. The initial size ofthe irregular shaped 304 stainless steel powders was approximately 42 µm. After high energy ball milling at 800 rpmfor 5h, the powders became spherical with a size of approximately 2 µm, and without formation of reaction compounds.From TEM analysis, it was confirmed that the as-milled powders consisted of the aggregates of the nano-sized particles.As the sintering temperature increased from 1073K to 1573K, the relative density and micro-hardness of sintered sampleincreased. The sample sintered at 1573K showed the highest relative density of approximately 95% and a micro-hard-ness of 550 Hv.

전형적인 3-전극 시스템의 순환전압전류법을 사용하여 알킬기를 가진 에탄올아민 용액 중에서 스테인리스에 대한 전류-전압 곡선을 측정하였다. 스테인리스는 작업 전극으로, Ag/AgCl 전극은 기준 전극으로, 그리고 백금선은 상대 전극으로 각각 사용하였다. N-에틸에탄올아민과 N,N-디메틸에탄올아민 용액에서의 스테인리스의 C-V특성은 순환전압전류법으로부터 산화전류에 기인한 비가역 공정으로 나타났다. 부식억제제의 확산계수의 효과는 각각 농도 증가에 따라 감소하였다. 금속의 SEM 이미지로부터 0.5 N의 전해질에서 부식억제제인 N,N-디에틸에탄올아민 (1.0 × 10-³ M)을 첨가한 경우, 구리와 니켈에서 부식억제 효과가 향상되었다.

This study is experimentally investigated whether or not a relationship exists between the mechanical properties anddamping capacity of cold-rolled 316L stainless steel. Deformation-induced martensite was formed with surface relief anddirectionality. With the increasing degree of deformation, the volume fraction of ε- martensite increased, and then decreased,while α'- martensite increased rapidly. With an increasing degree of deformation, tensile strength was increased, and elongationwas decreased; however, damping capacity was increased, and then decreased. Tensile strength and elongation were affectedin the α'- martensite; hence, damping capacity was influenced greatly by ε- martensite. Thus, there was no proportionalrelationship between strength, elongation, and damping capacity.

The present work investigated the dispersion behavior of Y2O3 particles into AISI 316L SS manufactured using laser cladding technology. The starting particles were produced by high energy ball milling in 10 min for pre- alloying, which has a trapping effect and homogeneous dispersion of Y2O3 particles, followed by laser cladding using CO2 laser source. The phase and crystal structures of the cladded alloys were examined by XRD, and the cross section was characterized using SEM. The detailed microstructure was also studied through FE-TEM. The results clearly indi- cated that as the amount of Y2O3 increased, micro-sized defects consisted of coarse Y2O3 were increased. It was also revealed that homogeneously distributed spherical precipitates were amorphous silicon oxides containing yttrium. This study represents much to a new technology for the manufacture and maintenance of ODS alloys.

The coastal area of Republic of Korea is very clean compared to other countries. In this reason, west coastal area of our country is a good place for breeding up a fish such as shrimp. In winter season, the heating system is required for preventing shrimp death caused by freezing in the farm. The heater in the heating system for fishery's farm is operated very severe combating corrosion due to high accumulation by feeding material and high temperature in heated sea water. Almost all manufactured heaters of STS 316L and Ti material are scrapped every year due to heavy corrosion such a general and crevice corrosion. For comparing the general and galvanic corrosion in new heater material, the test material of Zirconium (Zr), Titanium (Ti) and STS 316L are tested by potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), current density-time methods and microscopic examination in a 3.5% NaCl solution. The corrosion potential (Ecor) measured by potentiodynamic polarization for Zr, Ti and STS 316L reveals -198, -250 and -450mV, corrosion current density 0.5, 2.5 and 6.5μA/cm2 respectively. The film resistance measured by EIS are Zr 63,000, Ti 39,700 and 316L 3,150Ω, and the current of Zr-Ti couple is 0.03μA, whereas Zr-316L SS is 0.1μA. According to the result of this experiment in 3.5% NaCl solution, Zr is excellent corrosion resistance material than Ti and STS 316L.

Coatings composited with alumina and Perfluoro alkoxyalkane (PFA) resin were deposited on stainless steel plate (SUS304) to further improve corrosion resistance. Plate (ca. 10μm) and/or nanosize (27~43 nm) alumina used as inorganic additives were mixed in PFA resin to make alumina-fluoro composite coatings. These coatings were deposited on SUS304 plate with wet spray coating and then the film was cured thermally. According to the amount and ratio of the two kinds of alumina having plate morphology and nano size, corrosion resistance of the film was evaluated under strong acids (HF, HCl) and a strong base (NaOH). The film prepared with the addition of 5~10 wt% alumina powders in PFA resin showed corrosion resistance superior to that of pure PFA resin film. However, for the film prepared with alumina content above 10 wt%, the corrosion resistance did not improve with the physical properties, such as surface hardness and adhesion. The film prepared with plate/nanosize (weight ratio = 1/2) alumina especially enhanced the surface hardness and corrosion resistance. This can be explained as showing that the plate and the nanosize alumina dispersed in PFA resin effectively suppressed the penetration of cations and anions due to the long penetration length and fewer defects that accompany the improved surface hardness under a serious environment of 10% HF solution for over 120 hrs.

미세 조직은 SEM, FT-IR 스펙트라, 인장특성, 그리고 [NCO]/[OH]의 mole %, 입도분석에 의해 측정하였다. 친환경적인 NATM에 관한 관심이 고조됨에 따라 스테인레스같은 금속코팅에 더욱더 중요한 열경화 무용제 수지를 합성 하였다. 이 수지는 일반적 도료와 비교하여 매우 강도가 강하고 내구성이 매우 좋다. 폴리우레탄 수지는 폴리올, IPDI, 실리콘 계면활성제, 촉매, 충전제로 구성된다. 폴리우레탄 화합물은 가교제가 첨가된 수지가 가교제가 첨가되지 않은 수지보다 물성이 우수함을 나타냈다. 견고한 폴리우레탄 도료의 기계적 특성은 [NCO]/[OH]와 가교제가 증가함에 따라 강도가 증가하였다. 합성한 도료의 물성 향상은 스테인레스 산업뿐만 아니라 다양한 산업에서 폴리우레탄 고분자 수지가 강구조물의 보수보강에 많은 응용이 기대된다.

This study was carried out to investigate efficacy of aerosol sanitizer with natural antimicrobial and organic acids against Escherichia coli O157:H7, Salmonella Typhimurium and Listeria monocytogenes. The artificially inoculated pathogens on stainless steel coupon were treated with grapefruit seed extract (GFE), acetic acid,citric acid and lactic acid in model cabinet for 5 min. The number of three foodborne pathogens with individual treatment was reduced by 0.34-3.77 log units, treatment with GEF + organic acid was reduced by 1.72-3.89 log units and treatment with GEF + organic acid + alcohol was reduced by 1.46-5.05 log units. By treatment with GEF + lactic acid + alcohol in scale-up model system for 10 min. Populations of E. coli O157:H7, S. Typhimurium and L. monocytogenes were reduced by 3.42, 2.72 and 2.30 log units from the untreated control respectively. From the above result,aerosol sanitizer with natural antimicrobial agents and organic acid can be used as an environmental sanitation method with satisfying the consumer demand on safe food.

Joining of NiO-YSZ to 316 stainless steel was carried out with B-Ni2 brazing alloy (3 wt% Fe, 4.5 wt% Si, 3.2 wt% B, 7 wt% Cr, Ni-balance, m.p. 971-) to seal the NiO-YSZ anode/316 stainless steel interconnect structure in a SOFC. In the present research, interfacial (chemical) reactions during brazing at the NiO-YSZ/316 stainless steel interconnect were enhanced by the two processing methods, a) addition of an electroless nickel plate to NiO-YSZ as a coating or b) deposition of titanium layer onto NiO-YSZ by magnetron plasma sputtering method, with process variables and procedures optimized during the pre-processing. Brazing was performed in a cold-wall vacuum furnace at . Post-brazing interfacial morphologies between NiO-YSZ and 316 stainless steel were examined by SEM and EDS methods. The results indicate that B-Ni2 brazing filler alloy was fused fully during brazing and continuous interfacial layer formation depended on the method of pre-coating NiO-YSZ. The inter-diffusion of elements was promoted by titanium-deposition: the diffusion reaction thickness of the interfacial area was reduced to less than 5 compared to 100 for electroless nickel-deposited NiO-YSZ cermet.

염분분위기에서의 부식은 사용후핵연료의 중간저장 기간 동안 304 스테인레스 강재 건식저장용기의 주 열 화기구들 중 하나다. 본 연구에서는 감소정도가 서로 다른 냉연 304 스테인레스 강 시편들에 0.5wt.%의 염화 나트륨 연무를 분사시키면서 느린 변형속도시험(SSRT)과 중성염 분사시험(NSS)을 85℃와 200℃에서 수행하 였다. 85℃에서 2000 시간 동안 시험한 NSS시편의 무게 변화는 200℃에서 시험한 시편의 무게 변화와 크게 달 랐다. NSS 시편의 85℃에서 무게 감량은 미미하였지만, 냉연 감소율이 증가함에 따라서 무게 변화는 점진적으 로 감소하였다. 85℃와 200℃에서 그리고 염분분사 환경에서 가볍게 냉연 가공된 시편의 SSRT 시험으로부터얻은 항복강도와 극한 인장응력의 값은 공기 중의 값보다 약간 낮았다. 그러나 염분 분위기에서 부식으로 인 한 20% 감소 냉연시편의 강도는 더 이상 변화하지 않았다. 예비결과는 냉연 304 스테인레스 강의 질과 성능이 건식저장용기의 제작을 위한 조건에 맞는다는 것을 증명하였다. 그러나 냉연 스테인레스 강의 장기적인 성능 을 더 잘 이해하기 위해서는 염분분위기에서 이 재질의 부식거동에 관한 더 많은 연구가 필요하다.

Titanium carbonitride is more perspective materials compared to titanium carbide. It can be used in tool industry and special products because of its higher strength, abrasive wear-resistance and especially its strong chemical stability at high temperatures. We produced STS+TiCxNy composite by the spark plasma sintering for higher strength and studied the characteristics. The planar and cross-sectional microstructures of the specimens were observed by scanning electron microscopy. Characterizations of the carbon and nitride phases on the surface of composite were carried out using an X-ray diffractometer. During annealing TiCxNy particles diffusion into STS 430 was observed. After annealing, sintering isolations between particles were formed. It causes decreasing of mechanical strength. In addition when annealing temperature was increased hardness increased. Heterogeneous distribution of alloying elements particles was observed. After annealing composites, highest value of hardness was 738.1 MHV.