Crosslinked poly(methyl methacrylate) particles from 2.4 to 8.1μm in diameter were prepared by homogenized suspension polymerization. The effect of polymerization parameters such as homogenizing speed, homogenizing time and stabilizer concentration on the particle size were examined. Optical diffusion films were prepared with the crosslinked poly(methyl methacrylate) particles. The effect of film thickness, particle size, and particle size distribution on transmittance and haze of optical diffusion film was examined. Transmittance of optical diffusion film increased with increasing particle size and decreasing film thickness. Haze increased with increasing film thickness and decreasing particle size. We also found the existence of an optimum ratio for optical performance when the mixture of small particle and large particle was used.

Ultra-thin films of amphiphillic squarylium dye were prepared on the hydrophillic substrate by Langmuir-Blodgett(LB) technique. In this study, the photoelectric properties of a amphiphillic squarylium dye LB film was investigated. The visible light(λ = 684nm ) of xenon lamp was illuminated on the amphiphillic squarylium dye LB films and light absorptivity and photoconductivity were observed. The photoconductivity was nearly constant regardless of nominal layer number. The photoelectric properties of the amphiphillic squarylium dye LB films with bottom electrode showed better than that top electrode.

We studied electrochemical characteristics of Langmuir-Blodgett(LB) films by using cyclic voltammetry with a three-electrode system. An Ag/AgCl as a reference electrode, a platinum wire as a counter electrode and LB film-coated indium tin oxide(ITO) as a working electrode were used to study electrochemical characteristics at a various concentration of NaClO4 solution. LB films were reduced from initial potential to -1350 mV, continuously oxidized to l650mV and returned to the initial point. The scan rate was l00mV/s. The monolayer surface morphology of the LB film have been measured by Atomic Force Microscope(AFM). As a result, We comfirmed that the microscopic properties of LB film by AFM showed the good orientation of momolayer molecules and the thickness of monolayer was 3.5-4.lnm. The cyclic voltammograms(CV) of the ITO-coated glass showed the peak potentials for the reduction-oxidation reation. LB films of 4-octyl-4'-(5-carboxypentamethyleneoxy) azobenzene(8A5H) / L-α-phosphayidyl choline, dilauroyl(DLPC) seemed to be irreversible process caused by only the oxidation current from the cyclic voltammogram. The current of oxidatation increased at cyclic voltammogram by increasing 8A5H density in LB films. The diffusivity(D) of LB films increased with increasing of a 8A5H amount and was inversely proportional to the concentration of NaClO4 solution.

Thin Ag films deposited onto substrates by DC magnetron sputtering and thereafter annealed ,it temperatures 100-50 are investigated by scanning tunneling and atomic forte microscopy. It is shown that the film surface topography and microstructure are considerably changed as a result of annealing. To provide a quantitative estimation of the surface topography changes of Ag films the surface fractal dimension was calculated. Elasticity and hardness of the films are studied by a nanoindentation technique. The films are found to have value of elastic modulus close to that of bulk silver while their hardness and yield stress are essentially higher.