In this study, we fabricated Nd2Fe14B hard magnetic powders with various sizes via spray drying combined with reduction-diffusion process. Spray drying is widely used to produce nearly spherical particles that are relatively homogeneous. Thus, the precursor particles were prepared by spray drying using the aqueous solution containing Nd salts, Fe salts and boric acid with the target stoichiometric composition of Nd2Fe14B. The mean particle sizes of the spray-dried powders are in the range from one to seven micrometer, which are adjusted by controlling the concentra- tions of precursor solutions. After debinding the as-prepared precursor particles, ball milling was also conducted to con- trol the particle sizes of Nd-Fe-B oxide powders. The resulting particles with different sizes were subjected to subsequent treatments including hydrogen reduction, Ca reduction and washing for CaO removal. The size effect of Nd-Fe-B oxide particles on the formation of Nd2Fe14B phase and magnetic properties was investigated.

A novel route to prepare Nd-Fe-B magnetic particles by utilizing both spray drying and reduction/diffu- sion processes was investigated in this study. Precursors were prepared by spray drying method using the aqueous solu- tions containing Nd salt, Fe salt and boric acid with stoichiometric ratios. Precursor particles could be obtained with various sizes from 2 to 10 µm by controlling concentrations of the solutions and the average size of 2 µm of precursors were selected for further steps. After heat treatment of precursors in air, Nd and Fe oxides were formed through desalt- ing procedure, followed by reduction processes in Hydrogen (H2) atmosphere and with Calcium (Ca) granules in Argon (Ar) successively. Moreover, diffusion between Nd and Fe occurred during Ca reduction and Nd2Fe14B particles were formed. With Ca amount added to particles after H2 reduction, intrinsic coercivity was changed from 1 to 10 kOe. In order to remove and leach CaO and residual Ca, de-ionized water and dilute acid were used. Acidic solutions were more effective to eliminate impurities, but Fe and Nd were dissolved out from the particles. Finally, Nd2Fe14B magnetic particles were synthesized after washing in de-ionized water with a mean size of 2 µm and their maximum energy prod- uct showed 9.23 MGOe.

본 연구는 '후지' 품종에 대한 수분수로서 이용가능성을 확인하기 위하여 꽃사과 11품종의 특성 및 자가불화합성 유전자형을 분석하였다. 꽃사과 품종의 개화기는 '후지'에 비하여 개화시기가 2~7일 정도 빨랐고 화분발아율도 'Virginia'(74.4%) 외에 다른 꽃사과 품종들은 85.6~98.0%로 높은 결과를 보였다. '후지' 품종에 꽃사과 화분을 인공수분시킨 결과 착과율이 자연방임의 65.4%에 비해 'Adam's'는 76.8%로 11.4% 높았고, 나머지 품종들은 86~100%로 20.4~34.4% 높은 결과를 보였다. 꽃사과 화분으로 결실된 '후지' 품종의 종자수는 자연방임으로 결실된 과실에 비하여 13.8~42.3% 향상되었고, 과중은 346.7~376.8g으로 7.4~16.7% 정도 향상되었다. 과형지수는 무처리구 과실은 0.82로 비정형과 기준이었는데 비해 'Manchurian', 'Hopa A', 'Virginia', 'Prunifolia', 'Spectabilis' 등을 인공수분한 경우 0.87~0.88로 정형과 기준에 도달하였다. PCR분석을 통한 꽃사과 품종의 자가불화합성 유전자형을 확인한 결과 'Manchurian', 'Virginia', 'Sentinel', 'Adam's', 'Asiatica', 'Yantaishagou', 'Hanyaehanakaidou'에서 S3, S5, S9, S10, S20, S26이 확인되었고, 염기서열 분석을 통해 S5('Manchurian', 'Virginia')와 S9('Yantaishagou')가 보고된 자가불화합성 유전자형과 일치하였다.

This study is carried out to develop the new process for the fabrication of ultra-fine electrodes on the flexible substrates using superhydrophobic effect. A facile method was developed to form the ultra-fine trenches on the flexible substrates treated by plasma etching and to print the fine metal electrodes using conductive nano-ink. Various plasma etching conditions were investigated for the hydrophobic surface treatment of flexible polyimide (PI) films. The micro-trench on the hydrophobic PI film fabricated under optimized conditions was obtained by mechanical scratching, which gave the hydrophilic property only to the trench area. Finally, the patterning by selective deposition of ink materials was performed using the conductive silver nano-ink. The interface between the conductive nanoparticles and the flexible substrates were characterized by scanning electron microscope. The increase of the sintering temperature and metal concentration of ink caused the reduction of electrical resistance. The sintering temperature lower than resulted in good interfacial bonding between Ag electrode and PI film substrate.

In the present study, we systematically investigated the effect of Mn addition on nitrogenation behavior and magnetic properties of Sm-Fe powders produced by reduction-diffusion process. Alloy powders with only single phase were successfully produced by the reduction-diffusion process. The coercivity of powder rapidly increased during nitrogenation and reached the maximum of 637 Oe after 16 hours. After further nitrogenation, it decreased. In contrast, the coercivity of powder gradually increased during nitrogenation for 24 hours. The coercivity of powder was higher than that of powder at the same condition of nitrogenation. It was considered that the Mn addition facilitates the nitrogenation of powder and enhances the coercivity.

본 연구는 2년간 '홍로'/M.9 및 '후지'/M.9 품종의 적과를 위한 석회유황합제 및 어유와의 혼합처리 효과를 조사하기 위해 진행하였다. '후지' 1년 차에 있어, 만개 시 석회유황합제 1% 또는 2% 처리는 대조구에 비해 정과 및 액과의 유과수를 감소시켰다. 하지만 2차년도에는 석회유황합제 1% 또는 2% 단용처리에서는 정과 유과수의 차이를 나타내지 않았다. 다만 석회유황합제 1%의 3회 처리에서는 1차년도와 2차년도 모두 유의적인 적과효과를 나타내었다. 석회유황합제 1%의 다중처리는 '홍로'에서 가장 효율적인 적과효과를 나타내었다. 1차년도의 경우, 석회유황합제 1%의 2회 또는 3회 살포가 효과적인 적과효과를 보였으며, 2차년도에서는 석회유황합제 1% 1회처리를 제외하고는 모두 유의적인 적과효과를 나타내었다. 첨가된 어유의 경우 대부분의 경우 석회유황합제의 적과효과를 강화하지 않았다. 본 시험에 사용된 모든 처리구는 과실의 동녹 형성에 악영향을 미치지 않았으며, 또한 '후지' 및 '홍로'의 과실 중량, 경도, 가용성고형물 및 적정산도와 같은 과실품질에 영향을 미치지 않았다.

연구결과의 요약 및 논의 본 연구에서는 농식품의 주요 소비자판매처인 대형할인점과 대형슈퍼마켓을 대상으로 품질 및 고객서비스만족과 구매의 경제적 가치만족이 점포신뢰와 재구매의도에 미치는 영향력을 장기관계지향고객과 단기거래지향고객으로 분류하여 검증하였다. 분석결과, 대형할인점의 장기관계지향고객의 경우 품질 및고객서비스만족은 점포신뢰에 그리고 구매의 경제적가치만족은 점포신뢰와 재구매의도에 영향을 주었고, 점포신뢰는 재구매의도에 영향을 주는 것으로 나타난 반면 단기거래지향고객의 경우 구매의 경제적가치만족 만이 점포신뢰에 영향을 주는것으로 확인되었다. 그러나 대형마트 장기간 관계지향고객에서는 구매의 경제적가치만족이 점포신뢰에 영향을 줌으로써재구매의도를 형성한 반면 단기지향고객에서는 구매의 경제적가치만족과 점포신뢰가 동시에 재구매의도에 영향을 주는 것으로 확인되었다. 이상의 연구결과를 바탕으로 다음과 같은 논의를 할 수 있다. 첫째, 대형할인점의 경우 장기관계지향고객은 점포 내 제품의 품질과 고객서비스 수준 그리고 구매 시경제적 가치 등 모든 요소를 고려하여 점포에 대하여 만족하게 되며, 또한 점포가 이들 만족요인을 고객에게 제대로 제공할 때 이용하는 점포에 대하여 신뢰하고 재구매의도를 강력하게 나타난다는 것을 알 수 있다. 따라서 장기간 관계지향고객에게는 점포에 대한 만족수준을 높이는 것이 중요하다. 구체적으로는 최신 정보기술(information technology)을 활용하여이용 고객의 데이터베이스를 구축하고, 개인화된 고객의 특성과 구매행동에 관한 정보를 축적하여 관계지향고객을 선정 한후 이들에게 제품 및 서비스에 대한 정보 및 가격과 판매촉진에 관한 정보를 DM(direct mail)이나 홈페이지에 적극적으로제시함으로써 점포이미지를 높이고 표적고객의 욕구를 충족시켜 점포에 대한 신뢰와 반복구매를 높일 수 있다. 그러나 단기거래지향고객은 구매 시 단지 가격구조나 판촉행사를 통한경제적 가치만을 고려하기 때문에 제조업체 브랜드(national brand)보다는 유통업체 브랜드(private brand)상품을 제시하여가격매력성을 높이고, 시간대별 판촉행사를 통해 고객의 점포에 대한 신뢰를 유도할 필요가 있다. 둘째, 대형슈퍼마켓에서는 관계지향고객이나 거래지향고객 모두가 구매의 경제적가치만을 우선적으로 고려하므로 가격정책에 역점을 둘 필요가 있다. 그러나 장기관계지향고객은 점포신뢰를 통해 반복구매의도를 형성하지만 단기거래지향고객은 직접적으로 재구매의도를 나타내므로 고객의 성향에 따라 분류하여 관리할 필요가있다. 즉 관계지향고객에게는 가격정책을 통하여 점포신뢰를꾀하여야 할 것이며, 거래지향고객에게는 판촉행사나 저가격정책 등으로 직접적인 반복구매를 유도해야 할 것이다.

This paper describes the manufacturing process of tilting pad gas bearing with a diameter of 5 mm and a length of 0.5-1 mm for power MEMS (Micro Electomechanical Systems) applications. The bearing compacts with nanopowder feedstock were prepared by Ni-metal mold with 2-mold system using LIGA process. The effect of the manufacturing conditions on sintering properties of nanopowder gas bearing was investigated. In this work, Fe-45 wt%Ni nanopowder with an average diameter of 30-50 nm size was used as starting material. After mixing the nanopowder and the wax-based binders, the amount of powder was controlled to obtain the certain mixing ratio. The nanopowder bearing compacts were sintered with 1-2 hr holding time under hydrogen atmospheres and under temperatures of to . Finally, the critical batch of mixed powder system was found to be 70% particle fraction in total volume. The maximum density of the sintered bearing specimen was about 94% of theoretical density.

Nondestructive instrumented indentation test is the method to evaluate the mechanical properties by analyzing load - displacement curve when forming indentation on the surface of the specimen within hundreds of micro-indentation depth. Resistance spot welded samples are known to difficult to measure the local mechanical properties due to the combination of microstructural changes with heat input. Particularly, more difficulties arise to evaluate local mechanical properties of resistance spot welds because of having narrow HAZ, as well as dramatic changed in microstructure and hardness properties across the welds. In this study, evaluation of the local mechanical properties of resistance spot welds was carried out using the characterization of Instrumented Indentation testing. Resistance spot welding were performed for 590MPa DP (Dual Phase) steels and 780MPa TRIP (Transformation Induced Plasticity) steels following ISO 18278-2 condition. Mechanical properties of base metal using tensile test and Instrumented Indentation test showed similar results. Also it is possible to measure local mechanical properties of the center of fusion zone, edge of fusion zone, HAZ and base metal regions by using instrumented indentation test. Therefore, measurement of local mechanical properties using instrumented indentation test is efficient, reliable and relatively simple technique to evaluate the tensile strength, yield strength and hardening exponent.

체리는 과실성숙기 강우로 인해 해에 따라 열과가 심하게 발생하여 재배 상 문제가 되고 있어 해(2004~2007)에 따른 강우와 열과발생과의 관계와 체리 '좌등금'의 과실표면 관찰 및 과실 크기에 따른 열과반응을 알아본 결과는 다음과 같다. 과실의 열과 형태는 과경부, 과정부 및 측면 열과로 관찰되었고 발생양상은 해에 따라 다르게 나타났는데, 2004년은 과정부열과가 2005~2007년은 과경부열과가 많았다. 열과발생이 많았던 2004년(31.8%)과 2006년(28.6%)은 열과 발생이 낮았던 해에 비하여 5월 상순 강우량이 현저히 많았다. '좌등금'의 과피조직 특성중 아표피층은 유과기인 만개후 15일에는 2~3층 이었고 성숙기인 만개후 35일에는 1~2층으로 매우 얇았으며 열과가 많이 일어나는 과경부에는 큐티클층이 그리고 과정부에는 꽃이 탈락되어 생긴 코르크에서 미세균열 현상이 관찰되었다. 과실크기별 구분하여 물에 침지하였을 때 큰 과실(6g 이상)에서 작은 과실(4.5g 이하)에 비하여 열과반응 시간이 빨랐고 열과율도 높았다.

To produce alloy powders with only SmFe single phase by reduction-diffusion (R-D) method, the effect of excess samarium oxide on the preparation of Sm-Fe alloy powder during R-D heat treatment was studied. The quantity of samarium oxide was varied from 5% to 50% whereas iron and calcium were taken 0% and 200% in excess of chemical equivalent, respectively. The pellet type mixture of samarium, iron powders and calcium granulars was subjected to heat treatment at 1100 for 5 hours. The R-D treated pellet was moved into deionized water and agitated to separate Sm-Fe alloy powders. After washing them in deionized water several times, the powders were washed with acetic acid to remove the undesired reaction products such as CaO. By these washing and acid cleaning treatment, only 0.03 wt% calcium remained in Sm-Fe alloy powders. It was also confirmed that the content of unreacted -Fe in SmFe matrix gradually decreased as the percentage of samarium oxide is increased. However, there was no significant change above 40% excess samarium oxide.

석면에 의한 피해를 소송에 의해서만 해결하려고 하면 인과관계의 입증의 어려움, 장기간에 걸친 석면폐의 발병으로 인하여 시효의 완성이나 발병 사실 조차 알지 못하게 되는 난점, 그리고 무엇보다 이러한 소송을 한다고 해도 소송비용이 과다하거나 소송기간이 길어지면 피해자에게 2중의 고통을 준다는 점 등이 석면피해소송이 노정하는 단점들로 지적된다.미국에서는 석면으로 인하여 건강을 침해당한 자들이 석면관련제품의 제조사를 상대로 제조물책임에 기한 손해배상을 청구하고 있는데 이 배상청구소송에 의해 많은 기업이 막대한 손해배상금을 마련하지 못해 파산한 경우가 많았다고 하고, 일본의 경우도 석면피해에 대한 구제는 일반 민사법상의 불법행위책임에 기한 손해배상청구소송의 형태로서 나타나고 있는데 이러한 소송에는 원고인 피해자측이 석면에의 노출과 발병과의 사이에 인과관계가 존재한다는 것을 입증해야 하는 어려운 점 등이 있었다. 이러한 제도상의 결함을 보완하기 위해서 미국과 일본은 소송 이외의 구제방안을 마련하는 노력을 하였는데 그 중 가장 유력한 방안이 특별법을 제정하여 석면피해를 보상의 개념으로 접근하여 구제하는 것이었다.이러한 특별법에서는 불법행위로 인한 석면피해소송에서 관건이 되고 있는 석면노출과 발병사이의 인과관계를 피해자가 입증하지 않더라도 보상을 받을 수 있는 길을 열어 놓고 있고 또한 피해보상금은 국가, 지방자치단체, 기업 등 여러 주체가 분담해서 갹출한 재원으로 기금을 조성해서 사용하기 때문에 석면피해의 구제에 큰 도움을 줄 수 있을 것이다.

우리나라에서는 지난 7월에 정부기관에 대한 무차별적인 DDoS공격을 받아서 정보통신망 시스템에 장애를 야기하여 사회기능이 일시 마비된 경우도 있었다. 해킹을 비롯하여 악성 바이러스 및 봇 등 사이버테러에 의하여 정보통신망을 안전하게 보호하기 위한 법제도적 문제점을 시정하기 위하여 독일의 정보통신망보호법제의 주요 내용과 정보보안업무를 담당하는 행정조직과 기관이 가지는 규제의 종류와 정보보안과 관련한 자율규제 등을 검토하여 우리나라 관련 법제의 개정에 그 시사점을 찾고자 하는 것이 본 연구의 목적이다.독일의 경우 정보보안기관은 민간부문과 공공부문간 수평적으로 긴밀하게 협력하도록 되어 있다. 우리나라도 이러한 세계적인 정보보안정책의 추세에 맞추어서 정보통신망의 안전성 보호를 위해서 정부가 일방적으로 정보를 독점하는 형태에서 정부, 민간이 상호 공동의 대응체계를 갖출 수 있도록 법적 제도적 장치가 필요하다고 할 것이다.또한 정보통신망의 안전성에 관한 자율규제에 있어서도 인터넷서비스 자율규제기구의 국제협력지원을 강화하여 국내 인터넷서비스기업의 글로벌 경쟁력확보를 위해 정부가 주도적으로 해외 주요국 자율규제기구와의 협력추진 및 지원을 아끼지 말아야 할 것이다. 그리고 정부는 인터넷 이용자보호 및 자율규제 활성화를 위해 자율규제에 적극적으로 참여하는 사업자에게 다양한 혜택을 부여하여야 하고 사업자는 자율규제활동에 적극적으로 참여하여 정부와의 신뢰를 구축함으로써 기업의 사회적 역할과 책임을 수행하여야 할 것이다.

Lubricant-based nanofluids were prepared by dispersing carbon nanoparticles in gear oil. In this study, the effects of the particle size, shape and dispersity of the particles on the tribological properties of nanofluids were investigated. Dispersion experiments were conducted with a high-speed bead mill and an ultrasonic homogenizer, and the surfaces of the nanoparticles were simultaneously modified with several dispersants. The effective thermal conductivity of the nanofluids was measured by the transient hot-wire method, and the tribological behaviors of the nanofluids were also investigated with a disk-on-disk tribo-tester. The results of this study clearly showed that the combination of the nanoparticles, the deagglomeration process, the dispersant and the dispersion solvent is very important for the dispersity and tribological properties of nanofluids. Lubricant-based nanofluids showed relatively low thermal conductivity enhancement, but they were highly effective in decreasing the frictional heat that was generated. For nanofluids containing 0.1vol.% graphite particles in an oil lubricant, The friction coefficient in the boundary and fluid lubrication range was reduced to approximately 70% of the original value of pure lubricant.