ZnO micro/nanocrystals at large scale were synthesized through the thermal evaporation of Al-Zn mixtures under air atmosphere. The effect of synthetic temperature and time on the morphology of the micro/nanocrystals was examined. It was found that the temperature and time affected the morphology of the ZnO crystals. At temperatures below 900 oC, no crystals were synthesized. At a temperature of 1000 oC, ZnO crystals with a rod shape were synthesized. With an increase in temperature from 1000 oC to 1100 oC, the morphology of the crystals changed from rod shape to wire and granular shapes. As the time increased from 2 h to 3 h at 1000 oC, tetrapod-shaped ZnO crystals started to form. XRD patterns showed that the ZnO crystals had a hexagonal wurtzite structure. EDX analysis revealed that the ZnO crystals had high purity. It is believed that the ZnO nanowires were grown via a vapor-solid mechanism because no catalyst particles were observed at the tips of the micro/nanocrystals in the SEM images.

본 연구에서는 지도학의 주요 개념인 투영법과 축척에 관한 미국 학부생들의 이해 상태를 조사하였다. 첫째, 투영법 개념을 테스트하는 인터뷰에서 지도학의 비전문가인 학생들은 두 지점 사이의 대권항로가 지도상에서 직선으로 나타나지 않는 이유에 대해 항공 교통 통제 및 비행기 충돌방지, 높은 산과 같은 장애물 회피, 환승, 코리올리의 힘 때문이라는 네 가지 유형의 반응을 보였다. 본 조사에 참여한 학생들은 투영법에 따른 대권항로의 다양한 표현 형태를 제대로 이해하지 못하였다. 둘째, 축척에 대해서는 기존 연구에서 널리 알려진 대축척, 소축척 개념의 혼동이 가장 흔하게 나타나는 오해였다. 대부분의 학생들이 대축척 지도에서 사용된 ‘대’자라는 용어 때문에 대축척 지도가 넓은 지역을 표현한 지도라고 생각하였다. 그리고 축척이라는 개념 자체를 제대로 인지하지 못하는 학생들도 있었다. 이 연구는 투영법과 축척이라는 두 가지의 중요한 지도학적 개념에 대해 학생들의 이해 상태를 실증적으로 조사했다는 점에서 의미가 있다. 이 연구 결과는 추후 지도 관련 정보 디자인이나 효과적인 지리교육 전략 개발 등을 위한 기초 자료가 될 수 있을 것이다.

In order to fabricate the porous Al₂O₃ with dispersion of nano-sized Cu particles, freeze-drying of cam-phene/Al₂O₃ slurry and solution chemistry process using Cu-nitrate are introduced. Camphene slurries with 10vol% Al₂O₃ was frozen at -25˚C. Pores were generated by sublimation of the camphene during drying in air. The sinteredsamples at 1400 and 1500oC showed the same size of large pores which were aligned parallel to the sublimable vehiclesgrowth direction. However, the size of fine pores in the internal walls of large pores decreased with increase in sinteringtemperature. It was shown that Cu particles with the size of 100 nm were homogeneously dispersed on the surfaces ofthe large pores. Antibacterial test using fungus revealed that the porous Al₂O₃/1vol% Cu composite showed antifungalproperty due to the dispersion of Cu particles. The results are suggested that the porous composites with required porecharacteristics and functional property can be fabricated by freeze-drying process and addition of functional nano par-ticles by chemical method.

Freeze drying of a porous Cu-Sn alloy with unidirectionally aligned pore channels was accomplished by using a composite powder of CuO-SnO2 and camphene. Camphene slurries with CuO-SnO2 content of 3, 5 and 10 vol% were prepared by mixing with a small amount of dispersant at 50˚C. Freezing of a slurry was done at -25˚C while the growth direction of the camphene was unidirectionally controlled. Pores were generated subsequently by sublimation of the camphene during drying in air for 48 h. The green bodies were hydrogen-reduced at 650˚C and then were sintered at 650˚C and 750˚C for 1 h. XRD analysis revealed that the CuO-SnO2 powder was completely converted to Cu-Sn alloy without any reaction phases. The sintered samples showed large pores with an average size of above 100μm which were aligned parallel to the camphene growth direction. Also, the internal walls of the large pores had relatively small pores. The size of the large pores decreased with increasing CuO-SnO2 content due to the change of the degree of powder rearrangement in the slurry. The size of the small pores decreased with increase of the sintering temperature from 650˚C to 750˚C, while that of the large pores was unchanged. These results suggest that a porous alloy body with aligned large pores can be fabricated by a freeze-drying and hydrogen reduction process using oxide powders.

이 연구의 목적은 GIS(Geographic Information Systems) 학습에서 성별과 전공 차이가 공간적 습관의 자기 평가에 어떤 영향을 미치는지를 살펴보는 것이다. 많은 연구자들이 GIS가 학생들의 공간적 사고 향상을 위한 효과적인 도구가 될 수 있다고 주장했지만 GIS 학습과 공간적 습관의 상관관계에 대한 논의는 부족했다. 이 연구는 GIS 학습이 공간적 습관 향상에 도움이 된다는 기존 연구를 확장하여 성별과 전공의 영향에 대해 고찰하였다. 이 연구의 주요 결과는 다음과 같다. 첫째, 공간적 습관을 측정하는 SHOMI(Spatial Habits of Mind Inventory)의 총점에서 성별 차이가 발견되지 않았다(사전, 사후 테스트 각각 점수). 그러나 남녀 모두 GIS 학습 후 공간적 관점의 적용 정도가 높아졌다(사전, 사후 테스트 점수 차이). 공간적 습관의 향상 정도를 하위 영역으로 구분해서 살펴보았을 때에는 영역별로 남녀의 향상에 차이가 있었다. 둘째, 전공의 차이는 성별 차이보다 그 영향력의 정도가 컸다. GIS 학습 집단에서 성별 차이가 없었던 이유는 GIS 수업에 참여한 여학생들의 전공이 대부분 지리학 혹은 지리학과 관련된 것이어서 일반적인 여학생 집단을 대표하지 못했기 때문인 것으로 보인다.

ZnO thin films co-doped with Mg and Ga (MxGyZzO, x+y+z=1, x=0.05, y=0.02 and z=0.93) were preparedon glass substrates by RF magnetron sputtering with different sputtering powers ranging from 100W to 200W at a substratetemperature of 350oC. The effects of the sputtering power on the structural, morphological, electrical, and optical propertiesof MGZO thin films were investigated. The X-ray diffraction patterns showed that all the MGZO thin films were grown asa hexagonal wurtzite phase with the preferred orientation on the c-axis without secondary phases such as MgO, Ga2O3, orZnGa2O4. The intensity of the diffraction peak from the (0002) plane of the MGZO thin films was enhanced as the sputteringpower increased. The (0002) peak positions of the MGZO thin films was shifted toward, a high diffraction angle as thesputtering power increased. Cross-sectional field emission scanning electron microscopy images of the MGZO thin filmsshowed that all of these films had a columnar structure and their thickness increased with an increase in the sputtering power.MGZO thin film deposited at the sputtering power of 200W showed the best electrical characteristics in terms of the carrierconcentration (4.71×1020cm−3), charge carrier mobility (10.2cm2V−1s−1) and a minimum resistivity (1.3×10−3Ωcm). A UV-visible spectroscopy assessment showed that the MGZO thin films had high transmittance of more than 80% in the visibleregion and that the absorption edges of MGZO thin films were very sharp and shifted toward the higher wavelength side, from270nm to 340nm, with an increase in the sputtering power. The band-gap energy of MGZO thin films was widened from3.74eV to 3.92eV with the change in the sputtering power.

정량적인 강수량 추정은 기상학 수문학적 연구와 활용에 가장 중요한 요소 중 하나이다. 본 논문에서는 정량적 강수량 추정을 위하여 레이더 강우의 지리통계적 오차 구조 함수를 공동크리깅에 적용하여 레이더 강우강도를 조정하였다. 레이더 강우강도의 오차는 공동크리깅의 주변수로서 지상 우량계와 레이더의 강우강도의 차이로 산출되었다. 지상 우량계 강우장은 공동크리깅의 이차변수로서 정규크리깅에 의해 산출되었다. 레이더 강우강도의 오차 분포는 실험적 베리오그램으로 결정된 이론적 베리오그램을 공동크리깅에 적용하여 생성되었고, 레이더 강우강도 조정을 위하여 레이더 강우강도의 오차 분포를 레이더 강우장에 적용하였다. 본 연구의 검증을 위하여 국지적으로 호우가 발생하였던 2009년 7월 6일에서 7일까지의 강우 사례를 선정하였다. 오차가 조정된 1시간 레이더 누적강우량과 지상 우량계 누적강우량의 상관성은 조정 전에 비하여 0.55에서 0.84로 향상되었고, 평균제곱근오차는 7.45에서 3.93 mm로 조정되었다.

썩덩나무노린재(Halyomorpha halys Stal)는 다양한 과수와 콩류를 가해하는 해충으로 제주도에서는 감귤 과실을 흡즙하여 반점 형성부터 낙과에 이르기까지 극심한 피해를 입히는 해충이다. 썩덩나무노린재는 수확기에 근접하여 발생하여 방제여부 결정에 어려움을 초래하므로 이들 밀도와 흡즙 시기에 따른 노지감귤 낙과 및 저온저장시 부패율을 검정하여 화학방제의 필요성 여부를 검토하는 데 이용하고자 하였다. 실험 곤충은 2009년 실험실에서 수립된 계대사육 개체군을 이용하였으며 두 곳의 노지감귤 포장에서 2011년 9월에는 과실당 각 0.1, 0.2, 1마리, 10월에는 과실당 0.5마리가 되도록 접종하였다. 2010년에는 수확한 과실에 각 1, 2마리씩 접종하여 24시간 보관하였다. 가해한 과실들은 수확과 동시에 낙과율을 조사한 후 대조구와 함께 저온 (2010년: 5℃, 2011년: 4℃) 에서 45-50일간 보관하여 부패율을 확인하였다. 그 결과 9월에 피해를 입은 경우 썩덩나무노린재의 밀도가 과실당 1마리일 때 낙과율이 76.08 ± 5.74%로 높게 나타났다. 접종 밀도가 감소할수록 그에 따른 낙과율은 감소하여 과실당 0.2, 0.1마리일 때는 대조와 유의차가 없었다. 수확 후 저온저장했을 때 부패율은 2.00~13.89%로 나타났으나 대조와는 차이가 없었다. 가해시기별 감귤 과실의 낙과 및 부패율을 조사한 바, 10월에 썩덩나무노린재를 과실당 0.5마리 접종한 경우는 낙과율이 7.78 ± 4.34%, 부패율이 8.37 ± 4.40%로 대조와 유의차가 없었다. 수확기 과실에 접종한 경우는 저장 45일 후에도 부패과가 거의 나타나지 않았다 (0.00~0.03%).

도로를 주행하는 차량들을 구분하는 차종자료는 도로 및 포장의 설계와 관리 등 여러 분야에서 기초자료로 활용되고 있다. 본 연구에서는 차종구분에 차량높이라는 분류기준을 적용하기 위해 주행하는 차량의 높이를 계측할 수 있는 방법을 고안하고 현장에 장비를 설치한 후 실험을 통해서 차량길이와 차량최고높이 자료를 획득하였다. 차량높이 측정과 동시에 동영상을 촬영하여 국토해양부 12종 차종분류에 의거하여 차종분류 기준값을 작성하였다. 영상을 통해 작성된 차종자료 기준값과 측정된 차량길이와 차량높이를 토대로 판별함수를 이용한 차종분류값을 서로 비교한 결과 88.6%의 차종정확도를 확인하였다. 이를 통해 차량높이라는 분류기준을 적용하여 차종분류에 활용할 수 있는 방안을 제시하였다.

As a starting material, BCP (biphasic calcium phosphate) nano powder was synthesized by a hydrothermal microwave-assisted process. A highly porous BCP scaffold was fabricated by the sponge replica method using 60 ppi (pore per inch) of polyurethane sponge. The BCP scaffold had interconnected pores ranging from 100 μm to 1000 μm, which were similar to natural cancellous bone. To realize the antibacterial property, a microwave-assisted nano Ag spot coating process was used. The morphology and distribution of nano Ag particles were different depending on the coating conditions, such as concentration of the AgNO3 solution, microwave irradiation times, etc. With an increased microwave irradiation time, the amount of coated nano Ag particles increased. The surface of the BCP scaffold was totally covered with nano Ag particles homogeneously at 20 seconds of microwave irradiation time when 0.6 g of AgNO3 was used. With an increased amount of AgNO3 and irradiation time, the size of the coated particles increased. Antibacterial activities of the solution extracted from the Ag-coated BCP scaffold were examined against gram-negative (Escherichia coli) and gram-positive bacteria (Staphylococcus aureus). When 0.6 g of AgNO3 was used for coating the Ag-coated scaffold, it showed higher antibacterial activities than that of the Ag-coated scaffold using 0.8 g of AgNO3.

차량의 동적하중이 도로상에 작용하는 위치를 계측하기 위한 원더링 계측용 사선센서의 적정 설치각도를 제안하였다. 이를 위해서 테이프스위치 센서를 이용하여 원더링 계측용 장비를 개발하였고, 개발된 장비와 실험차량을 이용하여 평가용 자료를 수집하였다. 수집자료 분석 결과, 사선센서의 설치각도가 커질수록 원더링 수집자료의 오차가 감소하였고, 이러한 오차의 감소는 통계적으로도 의미가 있는 것으로 분석되었다. 그러나 사선센서를 30˚ 이상으로 설치할 경우, 탠덤축의 제원상의 이유로 인해 오류자료가 수집되는 것을 확인할 수 있었다. 따라서 본 연구에서는 국내 차량제원 등을 종합하여 원더링 계측용 사선센서의 적정 설치각도를 20˚~25˚로 제안하였다.