PURPOSES : Given that large-scale repair works of expressway bridge pavements have high maintenance cost and long traffic blocking time, the thin overlay method that maintains the existing pavement is attracting attention. In this study, because the bridge thin overlay has not been introduced in Korea yet, the basic physical properties of the epoxy thin overlay, which is mainly used for the bridge thin overlay, were investigated, and the skid resistance and bond performance were analyzed. METHODS : Basic physical property tests were performed on each of the epoxy binders, aggregates, and mixtures used in epoxy thin overlay. They were also compared and reviewed against foreign standards. The epoxy binders were tested for viscosity, gel time, and thermal compatibility. The aggregates were tested in terms of water absorption, specific gravity, and gradation. The compressive and flexural strengths of the mixtures were investigated. The epoxy thin overlay has the possibility of detachment of aggregates, so the skid resistance was tested according to the paving phase. In addition, to investigate the bond performance, which is the most important performance of the epoxy thin overlay, the bond strength test was performed by varying the moisture condition and treatment condition of the existing layer surface. RESULTS : The basic physical properties of the materials used in the epoxy thin overlays satisfied foreign standards except for the gradation of aggregates. The skid resistance did not satisfy the standard when the epoxy was exposed, whereas the skid resistance did satisfy the standard when the aggregates were exposed, even after the abrasion test. The bond strength of the epoxy thin overlay satisfied the standard in all cases. The bond strength was the highest when the relative humidity of the existing layer surface was 60%. CONCLUSIONS : The materials of epoxy thin overlay that could be obtained in Korea satisfied the basic physical property standards except for aggregate gradation. Given that the aggregate gradation could be adjusted, it can be concluded that the epoxy thin overlay could be introduced in Korea. In addition, it was confirmed that the skid resistance and bond strength of the epoxy thin overlay were high enough to be used in general road conditions. It was determined that the existing layer surface should maintain an optimal relative humidity of approximately 60% because the moisture condition affects the bond strength.

In this study, the fatigue properties of press die steel, such as SKD11, and three high-durability die steel for the cold forming of ultra-high-strength steel sheets are evaluated. Specimens for fatigue, tensile, and hardness tests are manufactured through the heat treatment recommended by steelmakers and ultra-high precision processing. The general mechanical properties and fatigue properties are derived from hardness, tensile, and fatigue tests for four die steel. The tensile and fatigue properties of die steel derived through the tests are compared and analyzed. In particular, the correlation between the fatigue limit and the general mechanical properties such as tensile strength and elongation is analyzed, which allows relational expressions to be obtained through regression analysis. Finally, the study confirms that applying high-durability die steel is necessary for improving the die life in the manufacturing of press dies for ultra-high-strength steel sheets.

The bead geometry according to the welding conditions was analyzed through the laser fillet welding experiment of 9% Ni steel, and the relationship between the shear strength and the five bead geometry measured by selecting the main bead geometry of the fillet weld was analyzed. Among the welding conditions, the welding conditions that directly affect the penetration depth are welding speed and laser power, and the working angle and beam position have a great influence on the formation of leg of vertical and horizontal members. The bead shape, which greatly affects the shear strength, is the horizontal member length, neck thickness, and weld length, and has a proportional relationship with the shear strength. As a result of confirming the relationship between shear strength and bead shape through the derivation of the trend line, it was confirmed that the length of the vertical member, whose R2 value was 0.92, was most closely related to the shear strength.

건축 및 토목 구조물의 대표 재료인 콘크리트의 핵심지표인 구조 성능을 개선하기 위해 많은 연구가 진행되고 있다. 아울러 구조물의 크기가 커질수록 강도가 높은 고기능 콘크리트의 필요성이 높아지고 있으며, 특히 내구성과 내후성이 우수한 콘크리트 재료의 개발이 필요한 실정이다. 따라서, 본 연구에서는 강섬유와 함께 파라-아라미드 원사를 이용하여 피복 및 꼬임, 원사 데니어 및 섬유 길이에 대한 차별화된 원사가공을 적용한 복합재료인 슈퍼섬유를 콘크리트에 혼입하여 구조적인 성능을 평가하고자 하였다. 본 연구를 통해 최적화된 슈퍼 섬유로 보강된 슈퍼 콘크리트는 도로, 교량, 상수도 및 하수도 등 기존 SOC 의 수리 및 보강에 적용될 유망한 성장 기술 분야가 될 것으로 예상된다.

소나무림에서 간벌 강도에 따른 황소비단그물버섯의 균사집단과 genet의 특징에 관하여 알아보고자 34%, 45%, 60%의 강도별 간벌이 이루어진 소나무 목재생산림에서 2018년 발생한 황소비단그물버섯을 대상으로 SSR(Simple sequence repeat) 분석을 실행한 결과 발생한 자실체의 개체수는 34% 간벌지역이 104개체로 다른 처리구 비하여 약 60~100개체 이상 많았다. 34% 간벌 지역에서 발생 균사집단의 형태는 임목을 기준으로 크게 약 5 m 직경의 원형의 형태로 발생하였고 일부 자실체는 바위 위에 약 3~4 cm 두께로 깔려진 낙엽위에 발생하기도 하였다. 45% 간벌 지역에서는 자실체가 6~7 m 범위에서 벌채된 그루터기를 포함하여 무작위적으로 분포되어 있었다. 60% 간벌 지역에서는 입목과 입목 사이에 6 m 길이의 폭이 좁은 타 원형이나 선형의 형태로 발생하였다. 대조구에서는 총 2 개의 자실체가 입목의 근원부 주위에서 발생하였다. 각 처리구에서 SSR 분석결과 Sb-CA1과 Sb-CA3의 maker만이 잡종성을 확인 할 수 있었으며 그 결과 34% 간벌 처리구에서 발생한 황소비단그물버섯은 60% 간벌 처리구에 비하여 He/Ho의 값이 1정도 낮았다. 34% 간벌 처리구에서는 총 20개의 genet이 확인되었고 genet의 크기는 평균 14±11 m 2 였다. 단일 자실체로 형성된 genet은 전체 genet 의 60% 였다. 45% 간벌 처리구에서는 총 6개의 genet이 확인되었고 평균 크기는 11±12 m 2 였다. 단일 자실체로 형성된 genet은 전체 genet의 50% 였다. 60% 간벌 처리구에서는 총 10개의 genet이 확인되었고 genet의 크기는 평균 1.1±0.8 m 2였다. 단일 자실체로 형성된 genet은 전체 genet의 70%로 나타나 간벌의 강도가 작을수록 균사 생장에 의한 genet의 크기는 더 크며 간벌 강도가 클수록 단일 genet의 형성율이 증가되었다.

Cured-in-place-pipe(CIPP) is the most adopted trenchless application for sewer rehabilitation to extend the life of the existing sewer without compromising both direct construction and indirect social costs especially applied in the congested urban area. This technology is globally and domestically known to be the most suitable for partial and full deteriorated pipe structure rehabilitation in a sewer system. The typical design of CIPP requires a significant thickness of lining to support loading causing sewage flow interruption and increasing material cost. This paper presents development of a high strength glass fiber composite lining material for the CIPP application and structural test results. The test results exhibit that the new glass fiber composite lining material has 12 times of flexural strength, 6.2 times of flexural modulus, and 0.5 Creep Retention Factor. These test results can reduce lining design thickness 35% at minimum. Even though taking into consideration extra materials such as outer and inner films for actual field applications, the structural capacity of the composite material significantly increases and it reduces 20 percent or more line thickness as compared to the conventional CIPP. We expect that the newly developed CIPP lining material lowers material costs and minimizes flow capacity reduction, and fully replaceable to the conventional CIPP lining materials.

This paper aims at investigating the adhesive property at damage analysis according to the shape of the DCB test specimen made of Titanium, Dualumin as the high strength nonferrous metals. In this analysis, all three specimens had the lower holes bound by the cylinder support and the top holes were elongated with the rate of 6mm/min. The study results show that the longer the load block of DCB specimens, the more reliable and durable they are. It is utilized as the basic data at investigating the damage properties of adhesives in DCB specimens made of high strength nonferrous metals.

본 연구에서는 딸기 재배온실의 최적 환경 구현에 필요한 시스템 선정을 위한 기초자료로 활용할 목적으로 딸기의 엽온을 측정하여 분석하였다. 그 결과는 다음과 같다. 실험 온실의 최대, 평균 및 최소 광투과율은 각각 64.9%, 58.3% 및 48.5%로 나타났다. 그리고 엽온은 재배시기나 처리구별 및 환기의 유무 등에 따라 다르게 나타나는 경향을 보였다. 실험기간 동안 상하 잎의 엽온과 기온의 편차는 –2.4∼3.7℃정도의 범위로 나타났다. 정식 직후에 엽온과 기온과의 차이가 3.7℃정도로써 가장 큰 차를 보였고, 생육이 왕성한 시기에도 전체적으로 엽온이 약간 높은 경향을 보이긴 하지만 엽온이 –2.4∼-2.3℃정도 낮은 경우도 있었다. 그리고 재배후기에는 엽온과 기온 간에는 거의 차이가 없는 것으로 나타났다. 엽온과 일사량 및 주변공기와 결정계수가 각각 0.4567 및 0.8826정도로써 일사량보다 엽온은 주변공기의 온도에 더 민감한 것을 알 수 있었다. 엽기온차와 옥외 수평면 일사량, 평균 및 최소 상대습도와의 상관관계가 거의 없는 것으로 나타났다.

This study deals with the effects of austempering time on the microstructure and mechanical properties of ultrahigh strength nanostructured bainitic steels with high carbon and silicon contents. The steels are composed of bainite, martensite and retained austenite by austempering and quenching. As the duration of austempering increases, the thickness of bainitic ferrite increases, but the thickness of retained austenite decreases. Some retained austenites with lower stability are more easily transformed to martensite during tensile testing, which has a detrimental effect on the elongation due to the brittleness of transformed martensite. With increasing austempering time, the hardness decreased and then remained stable because the transformation to nanostructured bainite compensates for the decrease in the volume fraction of martensite. Charpy impact test results indicated that increasing austempering time improved the impact toughness because the formation of brittle martensite was prevented by the decreased fraction and increased stability of retained austenite.

Small fishing vessels are manufactured using FRP. Various studies have been conducted to increase the strength of the composite material by mixing alumina powder with resin. Tensile tests and flexural strength tests are conducted to examine the effect of alumina powder on the strength of GFRP. In the current study, resin/alumina composites at different alumina contents (i.e., 0, 1, 5, and 10 vol%) have been prepared. The physical and mechanical properties of the prepared composites have been investigated. From the results, the tensile strength of the specimen with alumina powder mixed in at 10% shows the highest value of 155.66 MPa. The tensile strength of the specimen mixed with alumina powder increases with the amount of alumina powder impregnated. In the flexural strength test, the flexural strength of neat resin without alumina powder has a highest value of 257.7 MPa. The flexural modulus of ALMix-5 has a highest value of 12.06 GPa. Barcol hardness of ALMix- 10 has a highest value of 51. We show that alumina powder leads to decreasing cracks on the surface and decreasing length area of delamination.

본 연구는 합천호에서 2002~2017년까지 16년간의 장기간 동안 수질변수를 이용하여 부영양화 특성, 경험적 모델분석 및 몬순강도에 따른 수질변이 특성을 분석하였다. 장기간의 연별 수질 분석에서 합천호는 중영양 ~부영양 상태로 분석되었고, 계절별 수질분석에서 부영양화 현상은 하절기 이후 심화되는 것으로 나타났다. 장기간의 수질변이 특성은 유역의 점오염원 및 비점 오염원이 크게 변하지 않는 상황 하에서 매년 강우 사상 (집중 강우 vs. 약한 강우) 및 계절적인 강우강도에 의해 조절되는 것으로 분석되었다. 총인(TP), 총질소(TN), 생물학적 산소요구량(BOD) 및 이온 농도변화는 건기해(Dry year)와 홍수해 (Wet year)의 비교분석에서 뚜렷한 차이를 보여 영양염류, 유기물 농도 및 이온농도 변동에 가장 중요한 역할을 하는 것으로 분석되었다. 특히, 수질 변수 중 매년 영양염 지표(TP, TN), 유기물 지표(BOD, COD), 총 부유물질 농도 및 1차생산력의 지표 (Chl-a)는 강수량과 정상관관계를 보였다. 녹조의 지표인 Chl-a 농도는 총인, 총질소, 및 BOD와 높은 상관관계를 보여, 타 호수처럼 영양염의 과도한 증가시기에 Chl-a농도가 낮아지는 특성과는 차이를 보였다. Log-전환된 총질소, 총인 및 Chl-a에 대한 경험적 모델(Empirical model) 분석에 따르면, Chl-a 농도는 인(phosphorus) 농도에 의해 1차적으로 조절되며, 질소(N)농도는 유의한 영향을 주지 않는 것으로 나타났다. 이는 Log10TN, Log10TP, Log10CHL의 상류, 중류, 하류구간에 대한 공간적 회귀분석에서 총인과 Chl-a는 p <0.005의 유의적인 상관관계를 나타내었으나 총질소와 Chl-a는 p > 0.005의 결과를 보여, 녹조번성에 대해 인(P)이 핵심역할을 하는 것으로 분석 되었다. 또한, 총질소와 총인 모두 Chl-a와 댐에 가까운 하류구간(Lacustrine zone)에 비해 상류구간(Riverine zone)에서 더 유의적인 결과를 보여, 상류역에서 무기성 부유물의 농도의 영향에 의한 광제한 효과(Light limitation)가 거의 나타나지 않는 것으로 분석되었다.

PURPOSES: The objective of this study is to evaluate the properties of high-performance concrete and compare them with the properties of ternary blended cement (OPC 60% : BFS 30% : FA 10%) as applied to all-in-one bridge decks. High-performance concrete modified with styrene-butadiene latex (SB latex) was evaluated for strength development and durability through its compressive strength and chloride ion diffusion coefficient. METHODS: The compressive strength test was conducted according to KS F 2405, and the average value of the three specimens was used as the result at each stage. The chloride ion diffusion test was performed at 28 days, 56 days, and 365 days according to NT BUILLD 492. The chloride ion penetration test was conducted according to ASTM C 1202. RESULTS: For the compressive strength of the high-performance concrete, the blast furnace slag 40% replacement (BFS40) mixture had the most similar results to those of the ternary blended cement. The BFS40 mixture exhibited a lower compressive strength at 3 days than the latex modified concrete (LMC) mixture used for the bridge deck pavement, whereas it exhibited a 3.7-9.8% higher compressive strength at 7 days. In addition, the BFS40 mixture had the lowest diffusion coefficient, which was 49.1~59.0% lower than that of the LMC mixture. Mixing with latex tended to decrease in charge passed compared to Plain which is only used ternary blended cement, and showed excellent watertighness (rated “very low”), which is lower than 1,000 coulombs in all mixtures with latex. CONCLUSIONS : The BFS40 mixture exhibited excellent compressive strength, chloride ion permeability resistance, and the lowest chloride ion diffusion coefficient although it included a small amount of latex, which makes it more expensive than the current LMC mixture. It is believed that it is possible to secure excellent economic efficiency and durability by using lesser latex than that in the LMC mixture and using a mixture of the blast furnace slag instead.