CdS/CuInSe2태양전지의 광흡수층인 CuInSe2박막을 In2Se3와 Cu2Se 이원화합물을 precursor로 하여 진공증발법으로 제조하였고 특성을 분석하였다. 먼저 유리기판위에 0.5μm 두께의 In2Se3를 susceptor온도를 변화시켜가면서 증착한 결과 400˚C에서 가장 평탄하고 치밀한 박막이 형성되었다. 그 위에 Cu2Se3를 진공증발시켜 증착함으로써 in-situ로 CuInSe2박막을 형성시키고 In2Se3를 추가로 증발시켜 CuInSe2박막내에 존재하는 제 2상인 Cu2Se를 제거시켰다. 이 경우 susceptor온도가 700˚C 일때 미세구조가 가장 좋은 CuInSe2박막이 형성되었으며 약 1.2μm 두께에서 약 2μm의 결정립크기와 (112) 우선배향성을 가졌다. 추가 In2Se3양이 증가함에 따라 CuInSe2박막의 조성편차보상으로 hole 농도가 감소하고 전기 비저항이 증가하였고, optical bandgap은 거의 일정한 값인 1.04eV의 값을 가졌다. Mo/유리기판 위에 증착한 CuInSe2박막도 유리기판 위에 증착한 박막과 비슷한 미세구조를 가졌으며, 이 박막을 토대로 ZnO/CdS/CuInSe2/Mo 구조를 갖는 태양전지 구현이 가능할 것으로 생각된다.

The purposes of this studies were to investigate the effect of dietry Se levels and alcohol administration on the lipid hyperoxidation and the lipid metabolism in the rat. Seventy two male rats of Sprague-Dawley Strain weighting about 58∼62g were divided into 12groups. The dietary Se levels were 10, 0.4 and 0㎎, and the dietary α-tocopherol levels were 150 and 0㎎ per ㎏ diet, respectively. Alcohol-administrated groups received drinking water solution containing 10% of ethanol from the 3-weeks of experimental periods. The obtained experimetal results are summarized as follows. 1. Food intake, body weight gain and food efficiency ratio were significantly lower in H-, L- and alcohol administrated groups(-A) by administrated Se and alcohol in diet. The weight of liver and spleen tended to be greater in H- and alcohol administrated groups. 2. The glutathione values in liver tend to be lower in alcohol or Vit. E administrated groups than nonadministrated groups. Also there were higher in H- and L- than C-groups, but the increasing range decreased due to administrated alcohol. The lipid peroxide values in liver were significantly higher in alcohol groups, and L- and tocopherol groups were higher values. Specially the increasing of lipid peroxide values were significantly effected by alcohol in low Se and Vit. E groups. 3. The contents of total glyceride in plasma were higher in alcohol groups, there were significantly higher values in alcohol administrated groups under low Se and Vit. E groups. The contents of total cholesterol and HDL-cholesterol in plasma were significantly higher in alcohol groups. 4. The contents of total lipid in liver were higher alcohol groups, and slightly higher values in low Se groups(L-groups) than other groups, also higher values in low Vit. E groups. Those of total glyceride in liver were significantly higher in alcohol groups, appeared highest values when alcohol was administrated in low Se and Vit. E groups. The increasing of total glyceride content was significantly effected by alcohol in low Se groups than that in C-groups.

한반도 동남부에서 가장 규모가 큰 마이오세 포항분지의 남서부를 대상으로 상세한 지질도 작성과 지질구조를 분석하여 분지 발달사를 해석하였다. 포항분지 남서부는 북북동 방향의 분지 내 지구내지루에 의해 기하와 변형사가 서로 다른 서쪽의 보문구역과 동쪽의 오천구역으로 나누어진다. 보문구역은 포항분지 초기 확장 이후 거의 변형되지 않은 반면, 오천구역은 충전물의 퇴적 이후에도 후기 변형이 지속·중첩된 지역이다. 따 라서 보문구역은 포항분지 최초 확장 형식에 대한 중요한 정보를 제공한다. 보문구역은 북북동 방향의 정단 층들과 북북서(북서) 방향의 우수향 주향이동단층 분절들이 지그재그로 이어진 서편 경계단층에 의해 침강이 주도되었으며, 이 경계단층은 남쪽으로 한반도 동남부 마이오세 지각변형의 서쪽 한계선이며 우수향 주향이 동성 주변위대로 알려진 연일구조선과 연결된다. 따라서 포항분지는 17-16.5Ma 경 활동을 시작한 연일구조 선 북쪽 말단에 우향스텝 형태로 생성된 북북동 방향의 정단층 또는 사교이동단층에 의해 서북서-동남동 방 향으로 확장된 횡인장단층말단분지로 최초 침강된 것으로 해석된다. 이로 인해 보문구역에는 서쪽으로 갈수록 분 지의 깊이가 더 깊어지는 북북동 방향의 비대칭 지구 또는 반지구가 생성되었다. 이후 포항분지의 확장과 변 형은 오천구역을 포함하는 보다 동편 지역으로 이동하였다.

The purpose of this paper is to show that if ‘-ise’, ‘-se’ and ‘-i’ are treated as allomorphs. Since ‘-i’ attached to numerals and classifiers in the numeral quantifier constructions can be supposed to have adverbiality, the numerals and classifiers associated with such an element can be introduced in vP. Furthermore, we attempt to prove that nominative case marking can be deleted in the constructions. For the purpose of this paper, we investigate the analyses by several scholars on the allomorphy, finding out that ‘-i’ can be an abbreviation of ‘-ise’, a nominative case marker and affix. Within the vP, as ‘honca(se)’ functions as an adverbial phrase, if ‘seys-i(se)’ and ‘seymyeng-i(se)’ also do so, we can explain why phrases like ‘seymyeng-i’ can be in the vP. In addition, we examine nominative case ellipsis phenomenon in the light of Hong's generalization that case markers are optional to arguments in the complement position but obligatory to arguments in the spec positions, rethinking the possibility of the ellipsis of nominative case makers.

The removal characteristics of As and Se ions from aqueous solution by hexadecyl trimethyl ammonium bromide (HTMAB) modified anthracite (HTMAB-AT) were investigated under various conditions of contact time, pH and temperature. When the pH is 6, the zeta potential value of anthracite (AT) is 24 mV and on the other hand, the zeta potential value of the HTMAB-AT is +44 mV. It can be seen that the overall increase of about 60 mV. Increasing the (+) potential value indicates that the surface of the adsorbent had a stronger positive charge, so adsorption for the anion metal was increased. The isotherm data was well described by Langmuir and Temkin isotherm model. The maximum adsorption capacity was found to be 7.81 and 6.89 mg/g for As and Se ions from the Langmuir isotherm model at 298 K, respectively. The kinetic data was tested using pseudo first and pseudo second order models. The results indicated that adsorption fitted well with the pseudo second order kinetic model. The mechanism of the adsorption process showed that adsorption was dependent on intra particle diffusion model according to two step diffusion. The thermodynamic parameters(ΔGo, ΔHo, and ΔSo) were also determined using the equilibrium constant value obtained at different temperatures. The thermodynamic parameters indicated that the adsorption process was physisorption, and also an endothermic and spontaneous process.

찰옥수수, 단옥수수, 초당옥수수 등은 종실에 전분이 저장되는 과정에서 돌연변이가 발생하여 전분의 구성에 차이를 일으키며 이들의 유전자들 상호간에는 상위성이 존재한다. 배유의 저장전분에 관여하는 유전자 중에서 brittle1(bt1), brittle2(bt2), shrunken1(sh1), shrunken2(sh2), sugary1(su1), sugary2(su2), sugary enhancer(se)들은 전분 합성을 억제하고 amylose extender(ae), dull(du), floury(fl), opaque2(o2), waxy(wx)들은 배유 내에 전분의 구성 및 구조 등을 변경한다. 전분합성을 억제하는 유전자들은 전분의 구성을 변경하는 유전자에 상위성을 가지며 그들의 작용을 피복한다. 이들의 사실을 기초로 본 시험은 단옥수수(se) 유전자와 찰옥수수(wx) 유전자를 함께 가지는 자식계통을 만들어 육종 소재로 활용하고자 수행하였다. 2011년에 se 유전자를 가진 자식계통과 wx 유전자를 가진 자식계통을 상호 교배하여 F1 종자를 만들고 2012년 이들을 자식(selfing)시켰다. 멘델에 유전법칙에 따라 유전자형은 Se_Wx_:Sesewxwx:seseWx_:sesewxwx가 9:3:3:1로 분리되고 표현형 분리비는 이들 유전자 간의 상위성에 따라 일반옥수수, 단옥수수, 찰옥수수가 9:4:3으로 표현된다. 이들 분리1세대(S1) 종자를 White light transilluminator (LCF-900-470V, Ultra Violet Products)를 이용하여 찰옥수수의 표현형을 나타내는 종자를 골라 2013년 4월 중순에 파종하였다. 앞으로 이들을 자식(selfing)시켜 분리2세대 종자를 수확하고 단옥수수의 형질을 나타내는 것을 분리하면 이들은 찰옥수수(wx)와 단옥수수(se)의 유전자를 동시에 가지는 double mutant일 것으로 사료되며 분자마커 및 검정교배를 통해 유전자들을 확인할 수 있을 것으로 생각된다.

최근 의료영상분야에서 형광체와 광도전체 물질을 이용한 디지털 평판형 X선 영상검출기가 폭넓게 이용되고 있다. 본 연구는 CsI:Na 형광체층과 광민감도가 우수한 비정질 셀레늄(a-Se)층의 이중 접합구조로 구성된 변환구조 설계를 위한 몬테카를로 시뮬레이션과 X선에 대한 광학적 및 전기적 반응특성을 조사하였다. 먼저 CsI:Na의 발광스펙트럼과 a-Se의 광흡수 스펙트럼을 측정하여 X선에 의한 신호 변환특성을 분석하였다. 또한, 인가전기장의 함수에 따른 X선 민감도을 측 정하여 상용화된 a-Se(500㎛)의 직접변환 검출기와 비교 평가하였다. 측정결과로부터, 10 V/μm에서 CsI:Na(180 ㎛)/a-Se(30㎛) 변환센서의 X선 민감도는 7.31 nC/mR-cm2 이고, a-Se(500㎛) 검출기는 3.95nC/mR-cm2로 약 2배 정 도 높은 값을 보였다.

본 연구는 셀레늄 함유 녹두 생산을 위해 셀레늄의 효과적인 처리방법과 이행특성 등을 구명하고자 수행하였다. 1. 셀레늄 3.5, 7, 14, 28mg/l 를 개화기에 엽면살포구 1, 2차 수확 종실의 셀레늄 함량은 각각 0.41~3.96mg/kg, 0.27~2.38mg/kg로 엽면살포 농도에 비례하여 많았으나 1차 수확 종실이 2차 수확 종실에 비해 52~71% 많았다. 반면에 무처리구 1, 2차 수확 종실의 셀레늄 함량은 모두 0.02mg/kg로 같아 함량이 매우 적었다. 2. 셀레늄(7mg/l) 2회나 3회 엽면살포구 1~3차 수확 종실의 셀레늄 함량은 균일한 반면 1회 엽면살포구는 1차 수확 종실의 셀레늄 함량이 2, 3차 수확종실에 비해 각각 56, 67%많았다. 3. 셀레늄 2.05mg/kg이 함유된 녹두 종실에서 자엽의 셀레늄 함량은 2.99mg/kg으로 종피보다 단위 중량당 38% 많고, 녹두나 물을 생산하였을 경우 셀레늄 함량은 5.51mg/kg인 반면 나물 부산물인 종피는 0.78mg/kg 이었다. 4. 본 연구에 이용된 셀레늄의 엽면살포 농도 및 횟수에 따른 녹두 생육과 수량은 유의차가 없었다.

본 연구에서는 a-Se 기반 디지털 X-선 영상장치의 저대조도 특성을 평가하기 위하여 contrast-detail 곡선 해석을 수행하였다. 본 실험에 사용된 X-선 영상장치는 픽셀크기가 139㎜×139㎜이고 유효면적이 46.7㎝×46.7㎝인 a-Si TFT 기판 위에 500㎜ 두께의 광전도체가 코팅된 구조를 갖고 있다. Contrast-detail 곡선을 측정하기 위하여 우선 주어진 촬영조건(즉, 40, 50, 60, 70, 80 kVp, and 16 mA.s)에서 상용 팬톰 인 CDRAD 2.0을 사용하여 X-선 영상을 획득한 후, 그 영상으로부터 IQFinv 인자를 사용하여 그 특성을 최종 평가하였다. 평가된 IQFinv 값은 주어진 광 플루언스(즉, 1.8×105, 5.9×105, 11.3×105, 19.4×105, and 29.4×105 photons/㎟)에서 각각 24.4, 35.3, 39.2, 41.5, 43.4으로 광 플루언스가 증가할수록 점진적으 로 증가하였으며 이는 광 플루언스가 증가할수록 영상의 가독성이 향상됨을 나타낸다.

울릉분지 남부 대륙붕 석유탐사 시추공에서 회수된 사암 내에서 산출되는 녹니석-스멕타이트 혼합층 점토광물에 대하여 광물학적 및 화학적 연구를 수행하였다. X-선 회절분석과 화학분석 결과에 의하면 이 점토광물은 녹니석과 스멕타이트가 1:1 비율로 구성된 이팔면체형의 녹니석-스멕타이트 혼합층광물, 즉 토수다이트이다. 이 토수다이트는 Li가 풍부한 토수다이트로서 열수변질대에서 보고되는 토수다이트와 거의 동일하다. 이것은 토수다이트가 산출되는 지역은 열수변질과 관련된 열적 영향을 받았음을 지시한다. 실제로 이 시추공이 있는 지역은 단층과 습곡이 많이 발달되어 있고 구조적으로 변형되어 있다. 이와 같은 점을 고려할 때 하부로부터 열수가 올라와서 사암 내의 토수다이트의 생성에 기여했을 것으로 생각된다.