        검색결과 329

        101.
        2017.04 KCI 등재 서비스 종료(열람 제한)
        Powder mine wastes cause secondary environmental problems from dust flying around villages. It is necessary to recycle to prevent this secondary pollution and to use its beneficial contents. Magnesium and iron may play a role like that of aluminum in geopolymer forming. In this study, therefore, we analyzed the compressive strength of geopolymer prepared from melting slag (MS) and high-magnesium iron mine waste (MW). The compressive strength increased by increasing the mixing ratio of MS and decreasing the L/S ratio. The optimal properties were obtained at a mixing ratio of MS to MW of 5 : 5, molar ratio of SiO2/Na2O of 1.8, and L/S ratio of 0.2. Under these conditions, the compressive strength at 28 days was 112.5 MPa. According to the FT-IR analysis, a geopolymer structure was identified. As a result, we confirmed the possibility of geopolymer forming from MS and MW.
        102.
        2017.04 서비스 종료(열람 제한)
        This paper investigates the strength properties of ground granulated blast furnace slag(GGBFS) with magnesium sulfate(MgSO4). GGBFS was replaced with 1, 2, 3, 4, and 5% MgSO4 by weight. Mixtures of sodium hydroxide(NaOH) and sodium silicate(Na2SiO3) were used as the alkaline activator; a mixture of 5% NaOH and 5% Na2SiO3, and a mixture of 10% NaOH and 10% Na2SiO3 by slag weight. The added activators were dissolved in the water, and the weight ratio of water to slag was 0.45. This study was performed using compressive strength testing, ultrasonic pulse velocity(UPV), water absorption and X-ray diffraction(XRD). In this study, the strength of hardened samples decreases with increasing MgSO4 content. In addition, the water absorption of samples increases and UPV decreases, with the increase of MgSO4 content. Brucite, gypsum and M-S-H(magnesium silicate hydrate) are present in the XRD patterns of the hardened samples.
        103.
        2017.04 서비스 종료(열람 제한)
        The purpose of this study was to evaluate flowability of engineered cemetitious composite(ECC) Using blast furnace slag and fly ash as a binder in mixture. From the test result, flowability value of all ECC mixtures show good flowability and self compacting performance.
        104.
        2017.04 서비스 종료(열람 제한)
        In general, polymer cement mortars that is made from organic polymer dispersion and cement have good workability compared with ordinary cement due to ball-bearing acting of polymer particles in cement mortar. The purpose of this study is to evaluate the workability of cement mortar according to adding of admixtures such as polymer dispersions, blast-furnace slag and fly ash. From the test results, the flow of polymer-modified mortars is increased with increasing polymer-cement ratio, and also is a little improved according to adding of fly ash compared to blast-furnace slag.
        105.
        2017.04 서비스 종료(열람 제한)
        From the test results, it was found that the compressive strength and the resistance of chloride ion penetration were evaluated the slag content of the concrete for bridge pavement. Compressive strength test results showed that initial strength was decreased as slag replacement ratio increased. The chlorine ion penetration performance increased with increasing strength.
        106.
        2017.04 서비스 종료(열람 제한)
        In this study, it was developed geopolymer concrete of alkali-activated using the mixed fly ash and blast furnace slag. and it was developed the interlocking block using the developed geopolymer concrete. In addition, the bending strength and water absorption rate of the interlocking block was tested by KS standard. The test results were as follows. The water adsorption ratio of the BSF4 specimen was under 10%, and the flexural strength of that was over 5MPa
        107.
        2017.03 KCI 등재 서비스 종료(열람 제한)
        As the amount of slag generated annually increases, attempts to recycle slag as high value products are underway in order to develop an efficient resource recycling industry based on slag and derive economic benefits as well. However, the application of electric arc furnace (EOS) slag as construction material is practically limited because of the unstable substances included in it, such as free CaO.(EOS contains a small amount of free CaO, but several limitations still exist. Slag is stored for more than 3 months depending on the quantity of slag, which leads to additional economic loss. In this study, the amount of free CaO present in EOS is quantitatively evaluated to examine its qualities as a potential construction material and verify its application as concrete material. The quantitative analysis of free CaO present in EOS is performed using ethylene glycol. The free CaO contents of EOS samples were found to be below 0.5%. This satisfies the criteria specified in KS F 4571, which states that the CaO content should be below 40% and CaO/SiO2 ratio should be below 2.0. In addition, it was confirmed that free CaO content difference appears to be dependent on the aging period and storage position.
        108.
        2017.01 KCI 등재 서비스 종료(열람 제한)
        This paper investigates the strength properties of ground granulated blast furnace slag(GGBFS) with magnesium sulfate(MgSO4). GGBFS was replaced with 1, 2, 3, 4, and 5% MgSO4 by weight. Mixtures of sodium hydroxide(NaOH) and sodium silicate(Na2SiO3) were used as the alkaline activator; a mixture of 5% NaOH and 5% Na2SiO3, and a mixture of 10% NaOH and 10% Na2SiO3 by slag weight. The added activators were dissolved in the water, and the weight ratio of water to slag was 0.45. This study was performed using compressive strength testing, ultrasonic pulse velocity(UPV), water absorption and X-ray diffraction(XRD). In this study, the strength of hardened samples decreases with increasing MgSO4 content. In addition, the water absorption of samples increases and UPV decreases, with the increase of MgSO4 content. Brucite, gypsum and M-S-H(magnesium silicate hydrate) are present in the XRD patterns of the hardened samples.
        109.
        2017.01 KCI 등재 서비스 종료(열람 제한)
        The purpose of this study was to evaluate flowability of engineered cemetitious composite(ECC) Using blast furnace slag and fly ash as a binder in mixture. From the test result, flowability value of all ECC mixtures show good flowability and self compacting performance.
        110.
        2017.01 KCI 등재 서비스 종료(열람 제한)
        In general, polymer cement mortars that is made from organic polymer dispersion and cement have good workability compared with ordinary cement due to ball-bearing acting of polymer particles in cement mortar. The purpose of this study is to evaluate the workability of cement mortar according to adding of admixtures such as polymer dispersions, blast-furnace slag and fly ash. From the test results, the flow of polymer-modified mortars is increased with increasing polymer-cement ratio, and also is a little improved according to adding of fly ash compared to blast-furnace slag.
        111.
        2017.01 KCI 등재 서비스 종료(열람 제한)
        From the test results, it was found that the compressive strength and the resistance of chloride ion penetration were evaluated the slag content of the concrete for bridge pavement. Compressive strength test results showed that initial strength was decreased as slag replacement ratio increased. The chlorine ion penetration performance increased with increasing strength.
        112.
        2017.01 KCI 등재 서비스 종료(열람 제한)
        In this study, it was developed geopolymer concrete of alkali-activated using the mixed fly ash and blast furnace slag. and it was developed the interlocking block using the developed geopolymer concrete. In addition, the bending strength and water absorption rate of the interlocking block was tested by KS standard. The test results were as follows. The water adsorption ratio of the BSF4 specimen was under 10%, and the flexural strength of that was over 5MPa.
        113.
        2016.10 서비스 종료(열람 제한)
        By analyzing the flexural capacity of shotcrete mixture with blast furnace slag and confirmed the suitability as subsea tunnel support of the long-term repeated soaked in chloride-ion slag shotcrete. As a result, the shotcrete mixture with slag is excellent evaluated in terms of flexural capacity compared with existing shotcrete.
        114.
        2016.10 서비스 종료(열람 제한)
        The purpose of the present study is to investigate some effects of concrete according to addition of blast furnace slag and sulfuric alkali-activator. Blast furnace slag was used at 30~80% replacement by weight of cement, and liquid sulfur having NaOH additives was chosen as the alkaline activator. In order to evaluate characteristics of blast furnace slag concrete with sulfuric alkali activators, compressive strength test, carbonation test were performed.
        116.
        2016.10 서비스 종료(열람 제한)
        In this study, we tried to review the potential of commercialization of the developed product of aerated concrete and floor mortar used in the construction of residential buildings such as apartment buildings. As a result, it was analyzed that the difference was negligent in terms of the depth of subsidence, though the developed product was good enough in terms of compressive strength and economic efficiency.
        117.
        2016.09 KCI 등재 서비스 종료(열람 제한)
        본 연구에서는 경량기포 콘크리트를 이용한 육성용 토양골재의 적용성을 평가하기 위해서 고로슬래그 기반 기포콘크리트의 총 8 배합과 인공토양골재를 제조하였다. 고로슬래그 기반 기포콘크리트 배합의 주요변수는 단위결합재량으로서 100에서 800 kg/m3으로 변화하 였다. 경량기포콘크리트는 플로우, 슬러리 및 절건 밀도와 재령별 압축강도를 측정하였으며, 파쇄된 인공토양골재는 pH, 입도분포, 투수계수, 양이온치환용량(CEC), 유기물함유량(C/N비)을 측정하였다. 측정결과 경량기포콘크리트의 플로우, 슬러리 및 절건밀도와 재령별 압축강도는 단위결합재량이 증가함에 따라 증가하였다. 경량기포콘크리트의 단위결합재량이 500 kg/m3 이상인 배합의 28일 압축강도는 4 MPa 이상이었 다. 인공토양골재에 3일 이상의 15% 희석된 제1인산암모늄의 수용액침지는 pH를 저감시키는데 효과적이었다. 또한 제조된 인공토양골재는 양이온 치환용량(CEC) 측면에서 상급으로 평가되었지만 C/N비 측면에서는 조경시방서를 만족시키지 못하였다.
        118.
        2016.09 KCI 등재 서비스 종료(열람 제한)
        철근 콘크리트 구조물의 철근에 대한 부식을 발생시키는 다양한 유해 열화인자 중 염화물 이온(Cl-)은 침투로 인한 확산속도가 빠 르고, 철근에 직접적으로 관여하여 부식을 야기시켜 매우 중요한 열화원인이다. 대형 콘크리트 구조물의 타설에서 불가피하게 발생하는 콜드 조인트는 전단력에 취약하여, 이는 내구적 열화에 대한 피해를 증가시키는 경향을 보인다. 본 연구에서는 콜드조인트를 가진 OPC(Ordinary Portland Cement) 콘크리트와 GGBFS(Ground Granulated Blast Furnace Slag) 염화물 촉진 실험으로 염화물 확산계수를 정량적으로 평가하였 다. GGBFS 콘크리트에서는 6.6×10-12 m2/sec의 확산계수가 측정되었는데. 이는 OPC 콘크리트에 비하여 약 30% 수준의 낮은 확산계수값을 나 타내었으며, 콜드조인트를 가진 콘크리트에서도 비슷한 경향이 관측되었다. OPC 건전부 콘크리트에 비하여 GGBFS 콘크리트의 염화물 확산 계수는 건전부에서 0.30배, 콜드조인트부에서 0.39배 정도의 우수한 염해 저항성을 나타내었다.
        119.
        2016.04 서비스 종료(열람 제한)
        Converter slag contains free-CaO and free-MgO that has a problem causing a breakdown in the water and reaction. To solve this problem, it was treated the aging process that is inserting a converter slag aggregate in water before placing concrete. As a result, aging process was very effective in the compressive strength of the concrete.