To examine the practical potentials of V-ties to provide a confinement to a strengthening jacket section of existing reinforced concrete members, direct bond tests were conducted under a parameter of the V-tie details. Test results showed that V-ties with headed-end had a higher bond strength than those with the other details.

In this study, cement mortar (KS F 4042) used for repairing concrete structures was evaluated for compressive strength and bond strength according to the mixing ratio of polymer. From the experimental results, it was confirmed that as the polymer content increases, the bond strength properties increase, but the compressive strength decreases slightly at a certain rate.

The purpose of this study is to investigate the bond characteristics of deformed steel bar for concrete with bamboo activated carbon. Pullout test was conducted for specimens with various replacement ratio (0%, 10%, 20%) of bamboo activated carbon. Test results show that it need to use a concrete with a replacement ratio of bamboo activated carbon of 10% or less to retain proper bond strength.

In this study, cement mortar (KS F 4042) used for repairing concrete structures was evaluated for compressive strength and bond strength according to the mixing ratio of polymer. From the experimental results, it was confirmed that as the polymer content increases, the bond strength properties increase, but the compressive strength decreases slightly at a certain rate.

According to social needs, eco-friendly material for concrete structures has been developed in recent years. Hwang-toh is one of the eco-friendly architectural material and hwang-toh has been used by partial or complete replacement of portland cement. Pullout tests on deformed steel reinforcing bars with non-activated hwangtoh concrete are conducted in this paper. Experimental results, average bond strength of non-activated hwangtoh concrete was appeared to 7.3 MPa.

This study aimed to describe the mechanism and reaction characteristics of the adhered mortar removal of recycled aggregate (RA) using microwave irradiation (700 W) and a mixed solution of HCl and H2O2. The HOCl concentration increased to 29.7 M at 35oC and 40 min of reaction time without RA in the mixed solution, which shows that HCl reacts with H2O2 to form HOCl and water. However, after nitrogen purging, the HOCl concentration decreased to 2.71 M in 20 min, which proves indirectly that HOCl reacts with HCl to form Cl2 and water. The HOCl concentration decreased from 29.7 M to 1.88 M at 35oC in 40 min with RA in the mixed solution, and the Ca2+ concentration increased to 9,750 mg/L, which demonstrates indirectly that mortar mainly composed of Ca(OH)2 reacts with Cl2 to form Ca(OCl)2 and CaCl2. The reaction rate (k) with microwave heating was about 2.3 times faster than that with conventional heating, and k at a reaction temperature of 50oC was about 1.3 times faster than that at 35oC. The treated RA was improved in density, water absorption, abrasion loss, and absolute volume.

This study is the adhesion strength of the sprayed metal in accordance with a proportion ratio of the Zn-Al. Results showed the most excellent adhesion strength for metal spraying Al100 For the metal spraying Zn100, ZnAl85, ZnAl95 exhibited a similar level of adhesion strength results.

The purpose of this paper is to evaluate bond capacity of steel fiber reinforced concrete. Test variables were compressive strength of concrete and steel bar diameter and a total of six specimens in order to examine the discrepancy in bond resistance due to each variable. The specimens were tested by using universal testing machine in displacement control mode. From the test results, it can be seen that the bond strength increased with increasing diameter of steel bar for the same compressive strength of concrete. Also, the higher strength concrete is, the higher bond strength can be found in the test. Significant slip resistance inducing greater bond strength can be observed in the specimens with large diameter steel bar. All the specimens failed in splitting failure after its maximum load and compressive stress of concrete predominated in bond capacity.

A series of tests on the bond characteristics between new and old concrete were carried out. Main test variables are type and amount of mineral admixtures, treatment method of the interface and type of waterstops. The test results showed a slightly increased bond strength when applying mineral admixtures and the interface was treated rough and dry.

용융아연도금(galvanizing)은 콘크리트 구조물의 철근 부식 문제를 해결하기 위해 사용된다. 용융아연도금 철근 콘크리트 보의 부착강도 영향에 대한 자료는 거의 없는 실정이다. 따라서, 이 연구의 목적은 용융아연도금철근이 콘크리트 보의 부착강도에 미치는 영향을 파악하는 데 있다. 용융아연도금철근을 사용한 부재와 일반철근을 사용한 부재의 구조실험을 통하여 겹침이음 거동과 부착강도 특성을 비교하였다. 실험변수로써 철근의 용융아연코팅 유무, 철근 직경과 겹침이음 길이를 고려하였다. 용융아연도금 철근콘크리트 보의 균열 및 파괴 특성을 파악하였다. 용융아연도금철근 콘크리트 보의 겹침이음부 휨 거동특성은 일반철근 콘크리트 보의 겹침이음부 휨거동과 유사한 것으로 나타난다. 또한, 용융아연도금철근의 사용은 일반철근을 사용할 때에 비해 콘크리트 보의 부착강도에 불리한 영향을 미치지는 않는 것으로 나타났다.

본 연구에서는 모노파일지지구조의 고성능 그라우트연결부의 부착거동을 다루고 있다. 강관파일 연결부의 일체화를 위하여 섬유보강 고성능 그라우트를 개발하였으며, 재령 7일 압축강도 125MPa와 직인장강도 7.5MPa를 나타내었다. 축하중을 받는 상태에서의 그라우트의부착거동을 평가하기 위하여 강관파일에 그라우트를 충진하여 부착실험을 수행하였으며, 그 결과를 기존의 설계기준과 분석하였다. 실험변수는 섬유혼입율 (0%, 0.5% and 0.9%), 섬유의 형상비 (60 and 80)와 전단키의 높이와 간격의 비 (0.013 and 0.056)로 선정하였다. 실험결과 최대부착강도는 30.8MPa로 관찰되었으며, 섬유 혼입율보다는 전단키의 높이와 간격의 비가 부착강도에 영향을 미치는 것으로 분석되었다.

In this study, bonding property between the hardened concrete and sulfur polymer was evaluated by pull out test. The test results were shown that moisture condition on the concrete decreased the bonding strength between concrete and sulfur polymer.

The bond performance of Latex modified concrete(LMC) is excellent when compared with conventional pavement concrete. But LMC have a several problems. In order to improve the problem of LMC, Remicon latex modified concrete(Remicon LMC) was developed. In this study, the surface scaling resistance and bond properties of Remcion LMC containing extra admixture was compared with latex ratio. From the results, when latex and admixture were mixed in concrete, bond strength was improved. And, the surface scaling resistance of Remicon LMC was quite good comparing to LMC. The surface scaling resistance of Remicon LMC mixed latex ratio 8% more showed the equivalent capacity of LMC.

The most commonly used material of construction structures is steel. In this study, Epoxy-based coating materials and Ceramic-based coating materials durability were investigated. Exposed water immersion, chloride immersion, temperature changes, freezing and thawing for severe environments to simulate and environmental conditions are showed degraded in epoxy-based coating materials.

기존의 많은 연구자들이 철근과 콘크리트 사이의 부착특성에 영향을 주는 다양한 변수에 대하여 연구해왔으며, 특히 최근에는 고강도철근의 등장과 더불어 부착강도의 증진을 위한 연구가 다수 진행 중이다. 철근과 콘크리트 사이의 부착특성은 두 이질재료 사이의 계면조건이 중요한 역할을 하게 되는데, 이 중에서 특히 철근의 마디형상은 계면조건에 가장 큰 영향을 미치게 된다. 본 연구에서는 철근과 콘크리트 사이의 부착거동을 분석할 수 있는 상용 비선형 유한요소프로그램을 사용하여 철근의 마디형상에 따른 부착특성에 대하여 연구하였다.해석에 사용된 부착모델은 2차원 평면응력요소를 사용하였으며, 주요 해석변수로는 마디각, 마디높이, 마디간격 및 마디면적비이다. 해석결과, 마디각은 30~60도인 범위에서 부착력이 우수한 것으로 나타났으며, 마디높이는 일정구간까지는 부착강도가 증가하나 철근직경의 12%를 초과하면 전단파괴를 유발하여 오히려 부착강도가 감소되고, 마디간격에 대한 효과는 상대적으로 크지 않은 것으로 나타났다. 마디의높이와 간격을 하나의 지표로 제시할 수 있는 마디면적비는 부착강도의 변화를 효과적으로 나타낼 수 있는 것으로 분석되었으며, 마디면적비는 0.15 이하에서 최대의 효율을 나타내는 것으로 분석되었다. 특히 대형마디(교차마디형상)를 가진 철근인 경우, 타 변수보다 우수한 효율을 나타내어 부착강도 증진효과가 커지는 것으로 평가되었다.

최근 ‘먹는 물’에 대한 인식이 높아지고 양질의 물에 대한 요구가 이어짐에 따라 정수처리 시설은 수처리 시설을 확대하고 있다. 이에따라 수처리시설에 적용되는 콘크리트 구조물 내부 방수⋅방식재의 개발 및 기준 마련의 필요성이 높아지면서 최근 활발한 연구가 진행중이다. 하지만, 주로 상도의 내구성 향상에 집중된 연구의 한계성으로 콘크리트 표면과 하도 (프라이머)와의 부착력에 대한 연구가 부족한실정이다. 이에 본 연구에서는 수처리시설의 내부 방수⋅방식재로서 사용되는 프라이머와 콘크리트 표면간의 부착력을 확인하고, 콘크리트 표면 상태 (건조 상태, 습윤 상태, 수압상태)에 따른 부착강도 및 특성에 대하여 알아보고자 한다.

FRP 보강근을 사용한 경량콘크리트 구조체는 부식방지 및 자중감소의 효과를 동시에 기할 수 있는 이점이 있어서 추후 그 활용이 기대될 수 있다. 그러나 경량콘크리트와 FRP 보강근을 사용하여 보강근의 내부슬립 없이 외력에 저항할 수 있는 구조체를 만들기 위해서는 경량콘크리트와 FRP 보강근 사이의 부착특성을 파악하는 것이 대단히 중요하다. 그동안 보통콘크리트와 FRP 보강근 사이의 부착거동에 대하여는 많은 연구가 있어 왔으나 경량콘크리트와 FRP 보강근 사이의 부착거동에 대하여는 현재까지 연구결과가 대단히 부족한 실정이다.따라서 본 연구에서는 경량콘크리트와 보강근 표면에 나선형태의 이형을 갖는 GFRP 보강근 사이의 부착특성을 조사하였다. 비교목적으로 보강근 종류, 콘크리트 종류, 경량콘크리트 강도종류의 실험변수를 고려하여 인발실험체들을 제작하고 실험을 행하였다. 실험분석 결과, 보통콘크리트와 철근을 사용한 실험체의 부착강도를 1.0으로 하였을 때 경량콘크리트와 나선형태의 이형을 갖는 GFRP 보강근을 사용한 실험체의 부착강도는 0.49로 나타났다.

콘크리트는 건설재료 중 가장 많이 사용되는 재료이다. 그러나 황산염(sulfate)등의 산성에 노출되어 있는 콘크리트는 열화가 촉진되어 콘크리트 구조물의 기능을 상실하게 된다. 이러한 열화를 방지하기 위해 에폭시 등의 표면보호재를 사용하고 있지만, 표면보호재로 정유산업의 부산물인 유황폴리머를 이용하게 된다면 유황폴리머의 뛰어난 내산성을 활용한 양질의 표면보호재를 확보할 수 있을 것으로 예상된다. 또한, 유황폴리머는 대부분 정유산업의 부산물로 발생되므로 산업부산물 처리효과도 기대할 수 있다. 그러나 현재 유황폴리머에 대한 연구는 활발히 이루어지지 않은 실정이며, 특히 도포공법의 경우 국내에서는 연구가 전혀 이루어지지 않은 실정이다. 따라서 본 연구에서는 유황폴리머의 도포공법(spray)에 적용하기 위한 기초연구를 수행하였고, 특히 도포되는 유황폴리머의 두께에 따른 부착강도를 측정하여 국내기준에 적합한지 평가하였다. 유황폴리머의 두께에 부착강도 평가를 위하여 유황폴리머를 ｢KS F 4936｣ 콘크리트 보호용 도막재에 규정되어 있는 시험용 모르타르 밑판(70×70×20 mm)에 각각 0.5 mm, 1 mm, 1.5 mm (±0.1 mm) 의 두께로 도포하였다. 도포 전 시험용 모르타르 밑판의 4방향 평균 두께와 유황폴리머가 경화된 이후 4방향의 평균두께를 측정하여 그 차이를 도포된 유황폴리머의 두께로 산출하였다. 도포 완료 후 7일간 온도(20 ± 2℃) 및 습도(65 ± 10%)를 일정하게 유지하여 양생한 후 만능시험기를 사용하여 부착강도를 측정하였다. 그 결과 0.5 mm 이상일 때 1.3 MPa의 부착강도를 나타내었으며, 1 mm, 1.5 mm의 조건에서는 각각 1.8 MPa, 2.2 MPa의 부착강도를 나타냈다. 이상의 결과로 도포한 유황폴리머의 두께가 증가할수록 부착강도가 증가하는 것으로 나타났으며, 0.5 mm 이상의 두께에서는 표면보호재로 사용할 수 있는 부착강도(1.0 MPa)를 만족하는 것으로 나타났다.

The purpose of this study is to evaluate bond strength between sulfur polymer coating material and old concrete. The melted sulfur polymer was sprayed on surface of the concrete which is controlled by four types of temperature such as 0, 30, 50 and 100 ℃. The test result showed that the higher the temperature degree of concrete surface, the higher bond strength be obtained.

Experiments were divided into two parts; one part is to understand the basic properties of high flowable VA/VeoVa-modified cement mortar with different polymer cement ratio (P/C) and the weight ratio of fine aggregate to cement (C:F) and the other part is to investigate the effect of surface water spread on the concrete substrate on adhesion in tension. To understand the basic performance, the specimens were prepared with proportionally mixing VA/VeoVa redispersible powder, ordinary portland cement, silica sand, superplasticizer and viscosity enhancing agent. Here, P/C were 10, 20, 30, 50 and 75% and C:F were 1:1 and 1:3. As the change of P/C and C:F unit weight, flow test, crack resistance and adhesion in tension were measured. Three specimens with good adhesion properties were selected among specimens with different P/C and C:F. The effect of surface water evenly sprayed on concrete substrate on adhesive strength is investigated. The results show that surface water on concrete substrate increases the adhesion in tension of high flowable VA/VeoVa-modified cement mortar and additionally improves the flowability compared to the non-sprayed case.