Geopolymer is a term covering a class of synthetic aluminosilicate materials with potential use in a number of areas, but mainly as a replacement for Portland cement. In this study, geopolymers with fly ash and meta kaolin were prepared using KOH as an alkali activator and water glass. The effect of water glass on the microstructures and the compressive strength of the geopolymer was investigated. As the amount of water glass increased, the dissolved inorganic binder particles in the geopolymers increased due to polymerization, resulting in a dense microstructure. The meta kaolin-based geopolymer showed a better extent of polymerization and densification than that of the fly ash-based geopolymer. XRD data also suggested that polymerization in meta kaolin-based geopolymers should be active resulting in the formation of an amorphous phase with an increasing amount of water glass. The compressive strength of the geopolymer was also dependent on the amount of water glass. The compressive strength of the geopolymers from both fly ash and meta kaolin increased with an increasing amount of water glass because water glass improved the extent of polymerization of the inorganic binder and resulted in a dense microstructure. However, the addition of water glass to the geopolymer did not seem to be effective for the improvement of compressive strength because the meta kaolin-based geopolymer mainly consisted of a clay component. For this reason, the fly ash-based geopolymer showed a higher value of compressive strength than the meta-kaolin geopolymer.

본 연구는 일정한 실험조건 하에서 골심지 시료에 따른 골 성형 실험을 행하여 골심지에 의한 하이로골의 발생과 골판지상자의 압축강도의 관계에 대하여 조사하였다. 골판지의 골 높이가 낮은 골(low corrugation)의 비율이 많은 골심지 그레이드는 장력 변동의 저항에도 약하며 골심지의 이탈력에 의한 강탈(stealing)이 일어나기 쉽고, 결과적으로 낮은 골 비율이 높아졌으며, 골심지 두께 편차가 큰 골심지는 골 성형 시에 슬립현상을 발생하기 쉽기 때문에 불규칙한 골을 연속 형성하는 경향이 있었다. 또한 골심지의 그레이드에 따른 하이로골 분포비율의 실험결과 일반적 경향으로는 그레이드가 높은 골심지일수록 낮은 골 비율이 적었다. 골 성형된 골판지 시트의 두께의 경우는 원지 평량과의 상관성은 적고 골심지 두께와 상관하며(y = 3.9732x+4.2712, R2 = 0.8142), 골심지의 밀도에 역상관한다(y = -3.1213x+6.8736, R2 = 0.9919). 하이로골 중에서 낮은 골 분포를 크게 나타낸 골심지 재료의 골판지로 만든 골판지상자의 압축강도가 현저히 낮고 골심지 시료의 그레이드에 따라 13%의 차이가 있었으며 압축강도의 편차도 골심지의 시료에 따라 21%로 크며, 골심지 골은 원지의 두께 및 밀도 등 물리적 특성치의 변동과 관계한다.

Existing non-destructive test for evaluation of concrete compressive strength may show deviation in results analysis due to deterioration of precision by strength calibration and dry or humid condition by age, so there needs be testing method to determine long term structural internal force by collecting specimen with no damage of structure and measuring compressive strength through destruction test. This research applied to mock-up member the compressive strength evaluation method using joint separation mold that can plan and produce specimen cured in the same composition environment as concrete structure by attaching arbitrary(joint separation) to the form before concrete piling, and as a result, the management specimen was contrary to the hydration temperature of the member or was affected by external atmospheric temperature, however the joint separation specimen connected to structure and managed in the same environment showed a temperature curve similar to the member and decrease in temperature difference. Additionally, from initial age, with the compressive strength of joint separation specimen most similar to core strength，stable compressive strength can be evaluated up to design criteria strength 100MPa, so the method is proposed as an evaluation technique that can confirm highly reliable concrete quality.

콘크리트에서 강도는 콘크리트의 물리적 특성을 평가할 수 있는 중요한 인자중 하나이며 압축강도의 경우 실험의 편리함과 범용성으로 인해 널리 사용되고 있다. 콘크리트는 재료와 양생조건 등에 따라 압축강도가 달라지며, 특히 동일 재료라 하더라고 양생조건에 따라 강도는 변한다. 그러므로 현장에서 시공한 콘크리트의 강도를 알기위해서는 현장과 동일한 양생조건에 놓여야만 정확하게 강도를 측정할 수 있다. 그러나 현실적으로 밤낮으로 변화하는 현장의 양생조건을 실내에서 묘사하기란 쉽지가 않다. 또한 실제 콘크리트 포장의 강도를 측정하기 위해 포장체에 코어를 뚫기 때문에 손상이 가해지는 걸 피할수는 없다. 이러한 한계를 극복하기 위해 이미 비파괴 기법에 대한 다양한 연구가 진행되어 왔으며 그중 탄성파를 이용해 이미 콘크리트의 압축강도와 탄성파 속도와의 상관관계가 높음이 입증되었다. 본 연구에서는 양생조건에 따른 압축강도와 전단파 속도의 상관성을 분석하기 위해 동일 시멘트 페이스트를 3가지 서로 다른 양생온도에서 재령별 압축강도와 탄성파 속도의 변화를 측정했으며, 이 두 변수간의 상관관계를 파악하였다. 그 결과 양생온도는 재령별 압축강도증진과 탄성파 속도증가에 각각 영향을 미치는 것으로 나타났으나, 압축강도와 전단파 속도와의 상관관계에는 영향을 미치지 않는 것으로 나타났다.

An evaluation of the concrete strength has very important meaning in the maintenance and the structural safety. The reliability of ferroconcrete building is weakening and enlarging the life is strongly demanded due to the early deterioration of concrete. Like this social demand, concrete strength presumption is being indirectly executed using the result in parallel with the concrete pouring by material age. This data is usually different as concrete poured practically and the way of hardening and curing. Although existing concrete strength presumption formula is proposed, the material used and the concrete strength is different. And as a matter of remicon, the concrete strength varies according to the site and the way of curing. So the objective of this research is strength evaluation of the structural body concrete according to the concrete pouring and curing temperature change seasonally after using the system which evaluates the structural body concrete strength which is applied the transparent junction-separation mold that is presented. Also there is an objective to present the fundamental data for the constructional quality technique proposal of the structural body concrete developed in relation to field specimen and the strength evaluation method by non-breaking.

심층혼합처리공법에서 원지반과 개량재에 의해 형성되는 혼합처리토에 산업폐기물중 하나인 폐타이어와 기존 토목공사에서 섬유보강재로 사용되고 있는 강섬유를 혼합하여 보강재 및 개량재의 혼합비에 따른 개량체의 압축강도 특성을 파악하기위해 실내실험을 실시하였다. 개량재(시멘트, 시멘트계 고화재)의 경우는 건토중량에 대한 혼합비를 5%, 10%, 15%로 하였으며, 보강재(폐타이어, 강섬유)의 경우는 건토중량에 대한 혼합비를 0.5%, 1%, 2%로 하였다. 그 결과 개량재의 혼합비가 증가함에 따라 일축압축강도는 증가하였으며, 보강재를 첨가한 경우에는 폐타이어분말의 입자크기와 강섬유의 형상비가 작을수록 강도가 크게 나타났으며, 첨가량이 많아질수록 강도가 저하되는 경향이 나타났다.

Non-sintering cement was manufactured with briquette ash. Alkali activator for compression bodies used a NaOH solution. In order to apply alkali-activated briquette ash and the non-sintering cement to concrete, several experimental studies were performed. It was necessary to study the binder obtained by means of a substitute for the cement. This study concentrated on strength development according to the concentration of NaOH solution, the curing temperature, and the curing time. The highest compressive strength of compression bodies appeared as 353kgf/cm2 cured at 80˚C for 28 days. This result indicates that a higher curing temperature is needed to get a higher strength body. Also, geopolymerization was examined by SEM and XRD analysis after the curing of compression bodies. According to SEM and XRD, the main reaction product in the alkali activated briquette ash is aluminosilicate crystal.

콘크리트 압축강도는 신설된 콘크리트 포장과 공용중인 콘크리트 포장의 품질관리 인자로 매우 중요하게 여겨져 왔다. 다양한 배합설계를 이용하는 실험실이나 도로포장 시공 현장처럼 동일배합으로 지속적으로 시공하는 경우에도 압축강도는 콘크리트의 강도 평가용으로 많이 제작하여 측정하고 있는 실정이다. 하지만 동일배합에 동일다짐을 한 압축강도 공시체라 하더라도 강도시험시 오차가 발생하는 것이 현실이다. 이는 수동으로 재하속도나 변위를 조절하는데서 기인한 압축강도시험 장비의 오차일수 있고 공시체의 편심으로 인한 강도차이 등으로 인한 오차가 발생할 수 있다. 또한 시공현장에서 동일한 배합의 재령별 압축강도를 매 시공때 마다 조사할 경우 수많은 공시체 제작이 필요하며 이에 따른 인력과 비용이 발생하게 된다. 이러한 반복적 압축강도 시험을 대체하기 위한 수단으로 비파괴를 이용한 압축강도 추정이 필요로 하게 된다. 본 연구에서는 다양한 비파괴 실험 방법 중에서 탄성파를 이용하였으며 그 중에서 구속조건에 따라 크게 영향이 없는 전단파 속도를 이용하여 콘크리트 압축강도를 재령별로 추정하였다. 그 결과 전단파 속도와 압축강도의 상관관계는 매우 우수한 것으로 나타났다.

최근의 건물의 동향을 보면 아름다움을 강조하여 비틀리고, 경사지고, 테이퍼형태를 가지고 있다. 이러한 건물에 대응하는 구조시스템으로 대형 대각가새 구조시스템이 등장하였다. 이 구조시스템은 건축적인 요구사항을 만족하면서 구조물량 절감의 가능성이 있지만 다수의 부재가 만나는 접합부에 대한 구조성능 평가가 필요하다. 이에 본 연구에서는 H형 단면을 이용한 대형 대각가새 구조시스템의 접합부에 대한 단조가력 실험을 수행하였으며 하중 및 변형능력을 평가하였다. 주요 변수로는 부위별로 용접방법 및 웨브의 이음길이를 적용하였다. 실험결과 완전용입용접에 대하여 국부적으로 부분용입용접을 사용한 경우와 비교해 보면 구조성능에는 차이가 없었고, 웨브의 중첩길이는 웨브사이 이격거리에 100%에 해당하는 길이가 필요함을 알 수 있었다.

This study is basic experiment for estimating influence of strength by curing temperature of concrete's heat of hydration and estimate relationship of compressivε strength development by initial curing temperature factor, and then asume temperature factor which influence compressive strength development and for showing basic document of quality control. According to the result of cement mortar by the curing temperature factor high-curing temperature shows high strength on 3 day compare with low curing-temperature, shows higher strength than the piece of high curing temperature.

Because of building higher story and larger buildings, and because current concrete, a basic construction material, needs higher strength rather than normal strength, the use of high-strength concrete becomes more widely spread. High-strength concrete shows very high temperature increase due to inside heat of hydration different from normal-strength concrete, and because mass concrete under low temperature shows temperature stress due to temperature difference between inner and outer parts, it is known or reported that there is a significant difference between the compressive strength of srtucture and that of specimen for management, and between the compressivestrength of circular specimen made by standard underwater curing and structure concrete Therefore, in this research, an adiabatic curing box was manufactured which can provide hydration heat hysteresis of high strength mass concrete members and similar hydration heat hysteresis, using insulating materials, as a easy and exact method to manage compressive strength of rnass concrete member under low temperature, and the features of concrete member and those of specimen for management were compared.

Porous and porous surfaced Ti-6Al-4V implant compacts were fabricated by electro-discharge-sintering (EDS) of atomized spherical Ti-6Al-4V powders with a diameter of , The solid core formed in the center of the compact after discharge was composed of acicular Widmanstatten grains, The hardness value at the solid core was much higher than that at the particle interface or particles in the porous layer, which can be attributed to both heat treatment and work hardening effects induced from EDS, The compressive yield strength was in a range of 19 to 436 MPa which significantly depends on both input energy and capacitance, Selected porous-surfaced Ti-6Al-4V implant compacts with a solid core have much higher compressive strengths compared to the human teeth and sintered Ti dental implants.

콘크리트 포장의 품질관리 항목 중에서 압축 강도는 매우 중요한 인자로 여겨져 왔다. 압축 강도 값을 얻기 위해 현장에서 코아를 채취하여 이를 품질관리의 기준으로 사용하였다. 그렇지만, 코아를 채취하는 것은 많은 인력과 시간을 필요로 하며 실제로 현장의 품질관리를 정확히 추정하는데 많은 어려움이 있다. 또한 포장의 설계 방법도 탄성계수에 근거한 역학적-경험적 방법이 도입되고 있다. 이러한 현장의 품질관리 문제점을 해결하고, 포장설계와의 연계를 위해 비파괴 실험방법이 도입되고 있다. 다양한 비파괴 실험 방법 중에서 이론적으로 탄성계수를 추정할 수 있는 방법은 Wave Propagation방법이므로 본 연구에서는 Wave Propagation 방법을 도입하였다. 본 연구에서는 현장의 품질관리를 수행하는 방법 중의 일환으로 실내에서 제작한시편의 압축 강도와 비파괴 방법으로 얻은 탄성 계수와의 상관성을 검토하였으며, 비파괴 방법으로 얻은 탄성 계수로부터 압축 강도를 추정 할 때 배합별 특성에 대한 분석을 실시하였다. 비파괴 실험에서 구한 탄성계수와 압축강도와의 상관성은 매우 우수한 것으로 판명되었으며, 골재의 종류별로 상관성이 서로 상이하게 나타남을 알 수 있었다.

본 연구는 철근콘크리트 단층 구조물의 구조 부재 위치에 대한 비파괴검사법을 이용한 추정 신뢰도를 알아보기 위해 기둥, 벽체, 보 및 슬래브로 구성된 실험체를 제작하고, 기존 추정식과 비교 과정에서 정확한 분석을 위해 오차율 비교와 모평균 구간 추정을 사용하여 통계적 접근을 통한 신뢰성을 분석하고자 한다. 그 결과, 초음파속도법을 이용하여 압축강도를 추정한 결과와 코어시험 결과를 비교한 전체 평균 오차 율은 18.8%, 반발경도법을 이용하여 압축강도를 추정한 결과와 코어시험 결과를 비교한 전체 평균 오차율은 20.1%가 도출되어 현장 적용성을 확인하였다. 그리고 부재별 신뢰성 부분에서 초음파속도법과 반발경도법을 이용하여 신속하고 효율적인 구조물 안전진단을 하기 위해서 각각 벽체 부재와 보 부재를 중심으로 압축강도 추정 시 신뢰도 높은 결과를 도출되는 것을 확인하였다.

본 연구에서는 플라이애시가 90 %만큼 다량치환된 모르타르에 알칼리 활성화를 통한 강도증진을 동일한 양생온도 조건 에서 양생방법 및 유지시간 변화에 따라 비교 분석하고자 하였다. 연구 결과로 플래이애시를 90 % 치환한 경우, 소생재 도 포 후 40℃로 24시간 기중양생시 가장 높은 압축강도를 발휘하였지만, OPC의 압축강도까지 발휘하는 것은 어려울 것으로 분석되었다.

본 연구는 콘크리트 구조물의 균열 및 유지보수에 대한 문제점을 개선시키기 위한 연구의 일환으로 자기치유형 고상캡슐 (PCC)의 대체율에 따른 모르타르 플로우 및 압축강도를 측정·분석 하였다.