In this work, norepinephrine (NE) was determined by an electrochemical sensor represented by a carbon paste electrode boosted using nitrogen-doped porous carbon (NDPC) derived from Spirulina Platensis microalga anchored CoFe2O4@ NiO and 1-Ethyl-3-methylimidazolium acetate (EMIM Ac) ionic liquid. The morphological characteristics of the catalyst were recorded by field emission scanning electron microscope (FE-SEM) images. Moreover, the electrochemical behavior of norepinephrine on the fabricated electrode was checked using various voltammetric methods. All tests were done at pH 7.0 as the optimized condition in phosphate buffer solution. The results from linear sweep voltammetry revealed that the electro-oxidation of norepinephrine was diffusion, and the diffusion coefficient value was obtained by chronoamperometry (D⁓6.195 × 10– 4). The linear concentration of the modified electrode was obtained from 10 to 500 μM with a limit of detection of 2.26 μM using the square wave voltammetry (SWV) method. The sensor selectivity was investigated using various species, and the results from stability and reproducibility tests showed acceptable values. The sensor's efficiency was tested in urine and pharmaceutical as real samples with recovery percentages between 97.1% and 102.82%.

Interest in the use of semiconductor-based photocatalyst materials for the degradation of organic pollutants in a liquid phase has grown, due to their excellent performance and response to the light source. Herein, we fabricated a NiO-SiCTiO2 ternary structured photocatalyst which had reduced bandgap energy, with strong activation under UV-light irradiation. The synthesized samples were examined using XRD, SEM, EDX, TEM, DRS, EIS techniques and photocurrent measurement. The results confirmed that the two types of metal oxides were well bonded to the SiC fiber surface. The junction of the new photocatalyst exhibited a large number of photoexcited electrons and holes. The holes tended to oxidize the water and form a hydroxyl radical, which promoted the decomposition of methylene blue. The close contact between the 2D SiC fiber and metal oxide semiconductors expanded the scope of absorption wavelength, and enhanced the usability of the ternary photocatalyst for the degradation of methylene blue. Among three synthesized samples, the NiO-SiC-TiO2 showed the best photocatalytic effect, and was considered to have excellent photoelectron transfer due to the synergy effect between the metal oxide and SiC.

The presence of dyes in water is the most popular problem recently, so the current study was directed towards the synthesis of an effective material consisting of NiO and MWCNTs. The NiO/F-MWCNTs nanocomposite was synthesized using a simple hydrothermal method after functionalization of MWCNTs using sulfuric acid and nitric acid and utilized as an efficient surface to adsorption of malachite green dye from polluted water. The nanocomposite sample was characterized using several techniques are X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Thermogravimetric analysis (TGA), Field emission scanning electron microscopy (FESEM), High- resolution transmission electron microscopy (HRTEM), Brunauer–Emmett–Teller (BET) surface area analysis, Barrett-Joyner-Halenda (BJH) analysis and Energy dispersive X-ray (EDX). The analytical results showed that the prepared nanocomposite is of good crystalline nature with a particle size of 25.43 nm. A significant specific surface area was 412.08 m2/ g which indicates the effective impact of the nanocomposite in the adsorption of malachite green (MG) dye. On the other hand, the effect of adsorbent dose, temperature, acidic function and contact time on the adsorption efficiency of dye was studied. The kinetics of dye adsorption were also investigated employing two kinetic models, pseudo-first-order model and pseudo-second-order model. Finally, the thermodynamic functions were determined to identify the type of the reaction and the spontaneity of the process.

This work reported the electrochemical and photoelectrochemical (PEC) properties of a new photoelectrode based on hematite Co-Fe2O3@NiO, a photoactive semiconductor, was prepared using a process involving a combination of the co-precipitation and microwave-assisted synthesis of Fe2O3, Co-Fe2O3 and Co-Fe2O3@NiO, respectively. The obtained products were characterized by X-Ray powder Diffraction (XRD), Scanning Electron Microscope (SEM), Energy Dispersive X-ray analysis (EDX), Ultraviolet–Visible (UV–vis) analysis, Fourier Transform Infrared spectroscopy (FT-IR). X-ray diffraction (XRD) pattern of the sample determined the crystal structure of α-Fe2O3 nanoparticles. The SEM image shows spherical nanoparticles. FTIR spectrospy spectrum confirmed the phase purity and chemical bond for the sample. Optical studies show a variation of band gap from 2.118 to 2.07 eV. The electrochemical and photoelectrochemical (PEC) performance of the films were examined by cyclic voltammetry, linear sweep voltammetry and chronoamperometry. The electrochemical oxidation of water achieved by Cobalt-doped Fe2O3@ GCE modified electrode exhibited the current density of 21 mA/g at 0.5 V vs. SCE for 5 at% of Co and reveals enhanced specific capacitance of 352.11 F/g. The catalytic performance of urea oxidation was measured by cyclic voltammetry on Co-Fe2O3@NiO nanoparticles modified glassy carbon electrode (GCE) in alkaline medium. The electrode Co-Fe2O3@NiO without annealing showed a peak current density of 1.59 mA/cm2 at 0.1 M urea in 1.0 M NaOH, which was 3.6 fold higher than that of Co-Fe2O3@NiO with annealing. In another part, this work reported the photoelectrochemical (PEC) properties of photoanode prepared by spin coating. The highest photocurrent 0.042 mA/cm2 at 0.5 V Vs SCE was obtained for 5% Co-Fe2O3@NiO while the photocatalytic oxidation of urea.

Nitrogen-doped carbon dots (N-CDs), derived from the biomass (anthocyanin), are the novel additive to the nanocarbon materials, which is expected to bring a wide spectrum of novel applications. Moreover, metallic oxides are emerging for their unique potential for electrocatalysis. Herein, we report the synthesis of N-CDs for the selective detection of Fe3+ with a limit of detection of 2.57 μM in the range of 5–60 μM using ethylenediamine and H2O2 by a hydrothermal method. The obtained N-CDs displayed a spherical morphology with a particle size range of 2–7 nm and emitted blue luminescence at 394 nm under excitation at 319 nm. Meanwhile, we have demonstrated the fabrication of cost-efficient electrocatalysts for oxygen evolution reaction (OER) in an alkaline medium, employing N-CDs. Owing to the successful incorporation of N-CDs into NiO nanospheres, the resulting N-CDs/NiO with large surface areas, fast charge transfer, and increased conductivity vastly improved the catalytic activity. Remarkably, the optimal of N-CDs/NiO composite requires the overpotential of only 380 mV at a current density of 10 mA cm− 2 and a relatively low Tafel slope of 57.96 mV dec− 1 compared with pure NiO. These results open up a facile route for the application of N-CDs and offer prospects for CD-metal hybrids as high OER catalysts in electrochemical energy devices.

Oxygen evolution reaction (OER) is an essential step at an anode in electrochemical water-splitting process and requires efficient electrocatalysts to reduce overpotentials. Although precious metal-based materials, such as RuO2, IrO2 and their hybrids with other components, performed excellently as OER electrocatalysts, their high cost has limited practical applications. Consequently, earth-abundant metal components including Fe, Co, and Ni have been investigated as alternatives. In this work, the hybridization of Ni-containing species with conductive carbon-based materials was used to prevent aggregation of active species and improve electrochemical catalytic performance. A new hybrid material composed of NiO nanoparticles and N-doped carbon materials was prepared. The NiO particles with a narrow size distribution were well dispersed on the surface of carbon-based materials. The hybrid showed improved electrocatalytic performance for OER than single components of NiO and N-doped carbon materials.

정공 수송 층 (HTL)은 PSC의 효율 및 안정성을 증가시키기 위해 페로브스카이트 태양 전지 (PSC)에서 중요한 역할을 한다. 본 연구에서, 우리는 PSCs에서 HTL 스핀 코팅 및 블레이드 코팅 방법으로 니켈 산화물 구리 산화물 (NiO-CuO) 나노 입자 (NPs) 박막을 준비하였다. 스핀 코팅 및 블레이드 코팅 된 NiO-CuO 필름의 필름 특성은 원자력 현미경 (AFM)을 사용하여 조사하었고, 장치 성능에 대한 효과는 J-V 특성, 양자 효율 및 광 강도의 Voc 의존성을 사용하여 조사하었다. 결과적으로, 스핀 코팅으로 15.28 % 효율, 블레이드 코팅으로 11.18 % 효율을 달성하였다.

In this study, freeze drying of a porous Ni with unidirectionally aligned pore channels is accomplished by using a NiO powder and camphene. Camphene slurries with NiO content of 5 and 10 vol% are prepared by mixing them with a small amount of dispersant at 50℃. Freezing of a slurry is performed at -25℃ while the growth direction of the camphene is unidirectionally controlled. Pores are generated subsequently by sublimation of the camphene during drying in air for 48 h. The green bodies are hydrogen-reduced at 400℃ and then sintered at 800℃ and 900℃ for 1 h. X-ray diffraction analysis reveals that the NiO powder is completely converted to the Ni phase without any reaction phases. The sintered samples show large pores that align parallel pores in the camphene growth direction as well as small pores in the internal walls of large pores. The size of large and small pores decreases with increasing powder content from 5 to 10 vol%. The influence of powder content on the pore structure is explained by the degree of powder rearrangement in slurry and the accumulation behavior of powders in the interdendritic spaces of solidified camphene.

Needle-like NiO protecting layers on NiCrAl alloy foam, used as support for hydrogen production, are introduced through electroplated Ni and subsequent microwave annealing. To improve the stability of the NiCrAl alloy foam, oxygen concentration of microwave annealing to form a needle-like NiO layer with good chemical stability and corrosion resistance is controlled in a range of 20 and 50 %. As the oxygen concentration increases to 50 %, needle-like NiO forms a dense coating layer on the NiCrAl alloy foam; this layer formation can be attributed to accelerated growth of the (200) plane. In addition, the increased oxygen concentration causes increased NiO/Ni ratio of the resultant coating layer on NiCrAl alloy foam due to improved rate of the oxidation reaction. As a result, the introduction of dense needle-like NiO layers formed at 50 % oxygen concentration improves the chemical stability of the NiCrAl alloy foam by protecting the direct electrochemical reaction between the electrolyte and the foam. Thus, needle-like NiO can be proposed as a superb protecting layer to improve the chemical stability of NiCrAl alloy form.

The present study demonstrates the effect of raw powder on the pore structure of porous W-Ni prepared by freeze drying of camphene-based slurries and sintering process. The reduction behavior of WO3 and WO3-NiO powders is analyzed by a temperature programmed reduction method in Ar-10% H2 atmosphere. After heat treatment in hydrogen atmosphere, WO3- NiO powder mixture is completely converted to metallic W without any reaction phases. Camphene slurries with oxide powders are frozen at −30 oC, and pores in the frozen specimens are generated by sublimation of the camphene during drying in air. The green bodies are hydrogen-reduced at 800 oC and sintered at 1000 oC for 1 h. The sintered samples show large and aligned parallel pores to the camphene growth direction, and small pores in the internal wall of large pores. The strut between large pores, prepared from pure WO3 powder, consists of very fine particles with partially necking between the particles. In contrast, the strut densification is clearly observed in the Ni-added W sample due to the enhanced mass transport in activation sintering.

This study reports an environment-friendly synthetic strategy to process nickel oxide nanocrystals. A mesoporous nickel oxide nanostructure was synthesized using an environmentally benign biomimetic method. We used a natural rambutan peel waste resource as a raw material to ligate nickel ions to form nickel-ellagate complexes. The direct decomposition of the obtained complexes at 700 oC, 900 oC and 1100 oC in a static air atmosphere resulted in mesoporous nickel oxide nanostructures. The formation of columnar mesoporous NiO with a concentric stacked doughnuts architecture was purely dependent on the suitable direct decomposition temperature at 1100 oC when the synthesis was carried out. The prepared NiO nanocrystals were coated on cotton fabric and their antibacterial activity was also analyzed. The NiO nanoparticle-treated cotton fabric exhibited good antibacterial and wash durability performance.

Flower-like nickel oxide (NiO) catalysts were coated on NiCrAl alloy foam using a hydrothermal method. The structural, morphological, and chemical bonding properties of the NiO catalysts coated on the NiCrAl alloy foam were investigated by field-emission scanning electron microscopy, scanning electron microscopy-energy dispersive spectroscopy, Xray diffraction, and X-ray photoelectron spectroscopy, respectively. To obtain flower-like morphology of NiO catalysts on the NiCrAl alloy foam, we prepared three different levels of pH of the hydrothermal solution: pH-7.0, pH-10.0, and pH-11.5. The NiO morphology of the pH-7.0 and pH-10.0 samples exhibited a large size plate owing to the slow reaction of the hydroxide (OH−) and nickel ions (Ni+) in lower pH than pH-11.5. Flower-like NiO catalysts (~4.7 μm-6.6 μm) were formed owing to the fast reaction of OH− and Ni2+ by increased OH− concentration at high pH. Thus, the flower-like morphology of NiO catalysts on NiCrAl alloy foam depends strongly on the pH of the hydrothermal solution.

A commercial NiO (green nickel oxide, 86 wt% Ni) powder was reduced using a batch-type fluidized-bed reactor in a temperature range of 500 to 600 oC and in a residence time range of 5 to 90 min. The reduction rate increased with increases in temperature; however, agglomeration and sintering (sticking) of Ni particles noticeably took place at high temperatures above 600 oC. An increasing tendency toward sticking was also observed at long residence times. In order to reduce the oxygen content in the powder to a level below 1 % without any sticking problems, which can lead to defluidization, proper temperature and residence time for a stable fluidized-bed operation should be established. In this study, these values were found to be 550 oC and 60 min, respectively. Another important condition is the specific gas consumption rate, i.e. the volume amount (Nm3) of hydrogen gas used to reduce 1 ton of Green NiO ore. The optimum gas consumption rate was found to be 5,000 Nm3/ton-NiO for the complete reduction. The Avrami model was applied to this study; experimental data are most closely fitted with an exponent (m) of 0.6 ± 0.01 and with an overall rate constant (k) in the range of 0.35~0.45, depending on the temperature.

NiO catalysts/Al2O3/FeCrAl alloy foam for hydrogen production was prepared using atomic layer deposition (ALD)and subsequent dip-coating methods. FeCrAl alloy foam and Al2O3 inter-layer were used as catalyst supports. To improve thedispersion and stability of NiO catalysts, an Al2O3 inter-layer was introduced and their thickness was systematically controlledto 0, 20, 50 and 80nm using an ALD technique. The structural, chemical bonding and morphological properties (includingdispersion) of the NiO catalysts/Al2O3/FeCrAl alloy foam were characterized by X-ray diffraction, X-ray photoelectronspectroscopy, field-emission scanning electron microscopy and scanning electron microscopy-energy dispersive spectroscopy. Inparticular, to evaluate the stability of the NiO catalysts grown on Al2O3/FeCrAl alloy foam, chronoamperometry tests wereperformed and then the ingredient amounts of electrolytes were analyzed via inductively coupled plasma spectrometer. We foundthat the introduction of Al2O3 inter-layer improved the dispersion and stability of the NiO catalysts on the supports. Thus, whenan Al2O3 inter-layer with a 80nm thickness was grown between the FeCrAl alloy foam and the NiO catalysts, it indicatedimproved dispersion and stability of the NiO catalysts compared to the other samples. The performance improvement can beexplained by optimum thickness of Al2O3 inter-layer resulting from the role of a passivation layer.

The synthesis of NiTi alloy powders by hydrogen reduction and dehydrogenation process of NiO and TiH2 powder mixtures is investigated. Mixtures of NiO and TiH2 powders are prepared by simple mixing for 1 h or ball milling for 24 h. Simple-mixed mixture shows that fine NiO particles are homogeneously coated on the surface of TiH2 powders, whereas ball milled one exhibits the morphology with mixing of fine NiO and TiH2 particles. Thermogravimetric analysis in hydrogen atmosphere reveals that the NiO and TiH2 phase are changed to metallic Ni and Ti in the temperature range of 260 to 290oC and 553 to 639oC, respectively. In the simple-mixed powders by heat-up to 700oC, agglomerates with solid particles and solidified liquid phase are observed, and the size of agglomerates is increased at 1000oC. From the XRD analysis, the presence of liquid phase is explained by the formation and melting of NiTi2 intermetallic compound due to an exothermic reaction between Ni and Ti. The simple-mixed powders, heated to 1000oC, lead to the formation of NiTi phase but additional Ni-, Ti-rich and Ti-oxide phases. In contrast, the microstructure of ball-milled powders is characterized by the neck-grown particles, forming Ni3Ti, Ti-oxide and unreacted Ni phase.

NiO catalysts were successfully coated onto FeCrAl metal alloy foam as a catalyst support via a dip-coating method. To demonstrate the optimum amount of NiO catalyst on the FeCrAl metal alloy foam, the molar concentration of the Ni precursor in a coating solution was controlled, with five different amounts of 0.4 M, 0.6 M, 0.8 M, 1.0 M, and 1.2 M for a dip-coating process. The structural, morphological, and chemical bonding properties of the NiO-catalyst-coated FeCrAl metal alloy foam samples were assessed by means of field-emission scanning electron microscopy(FESEM), scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS), X-ray diffraction(XRD), and X-ray photoelectron spectroscopy(XPS). In particular, when the FeCrAl metal alloy foam samples were coated using a coating solution with a 0.8 M Ni precursor, well-dispersed NiO catalysts on the FeCrAl metal alloy foam compared to the other samples were confirmed. Also, the XPS results exhibited the chemical bonding states of the NiO phases and the FeCrAl metal alloy foam. The results showed that a dip-coating method is one of best ways to coat well-dispersed NiO catalysts onto FeCrAl metal alloy foam.

Cu-Ni alloys with unidirectionally aligned pores were prepared by freeze-drying process of CuO-NiO/cam-phene slurry. Camphene slurries with dispersion stability by the addition of oligomeric polyester were frozen at -25˚C,and pores in the frozen specimens were generated by sublimation of the camphene during drying in air. The green bod-ies were hydrogen-reduced at 300˚C and sintered at 850˚C for 1h. X-ray diffraction analysis revealed that CuO-NiOcomposite powders were completely converted to Cu-Ni alloy without any reaction phases by hydrogen reduction. Thesintered samples showed large and aligned parallel pores to the camphene growth direction, and small pores in the inter-nal wall of large pores. The pore size and porosity decreased with increase in CuO-NiO content from 5 to 10 vol%.The change of pore characteristics was explained by the degree of powder rearrangement in slurry and the accumulationbehavior of powders in the interdendritic spaces of solidified camphene.

Recently, self-propagating high-temperature synthesis (SHS), related to metallic and ceramic powder inter- actions, has attracted huge interest from more and more researchers, because it can provide an attractive, energy-efficient approach to the synthesis of simple and complex materials. The adiabatic temperature Tad and apparent activation energy analysis of different thermit systems plays an important role in thermodynamic studies on combustion synthesis. After establishing and verifying a mathematic calculation program for predicting adiabatic temperatures, based on the thermo- dynamic theory of combustion synthesis systems, the adiabatic temperatures of the NiO/Al aluminothermic system dur- ing self-propagating high-temperature synthesis were investigated. The effect of a diluting agent additive fraction on combustion velocity was studied. According to the simulation and experimental results, the apparent activation energy was estimated using the Arrhenius diagram of ln(v/Tad)~1/Tad based on the combustion equation given by Merzhanov et al. When the temperature exceeds the boiling point of aluminum (2,790 K), the apparent activation energy of the NiO/ Al aluminothermic system is 64 ± 14 kJ/mol. In contrast, below 2,790 K, the apparent activation energy is 189 ± 15 kJ/ mol. The process of combustion contributed to the mass-transference of aluminum reactant of the burning compacts. The reliability of the simulation results was experimentally verified.

We have examined the co-doping effects of 1/2mol% NiO and 1/4mol% Cr2O3 (Ni:Cr=1:1) on the reaction,microstructure, and electrical properties, such as the bulk defects and the grain boundary properties, of ZnO-Bi2O3-Sb2O3 (ZBS;Sb/Bi=0.5, 1.0, and 2.0) varistors. The sintering and electrical properties of Ni,Cr-doped ZBS, ZBS(NiCr) varistors werecontrolled using the Sb/Bi ratio. Pyrochlore (Zn2Bi3Sb3O14), α-spinel (Zn7Sb2O12), and δ-Bi2O3 were detected for all ofcompositions. For the sample with Sb/Bi=1.0, the Pyrochlore was decomposed and promoted densification at lowertemperature by Ni rather than by Cr. A homogeneous microstructure was obtained for all of the samples affected by α-spinel.The varistor characteristics were not dramatically improved (non-linear coefficient, α=5~24), and seemed to formZni..(0.17eV) and Vo.(0.33eV) as dominant defects. From impedance and modulus spectroscopy, the grain boundaries werefound to have been divided into two types, i.e., one is tentatively assigned to ZnO/Bi2O3 (Ni,Cr)/ZnO (0.98eV) and the otheris assigned to a ZnO/ZnO (~1.5eV) homojunction.

Nickel oxide was doped with a wide range of concentrations (mol%) of Aluminum (Al) by solvothermal synthesis;single-phased nano powder of nickel oxide was generated after calcination at 900oC. When the concentration of Al dopant wasincreased, the reduced intensity was confirmed through XRD analysis. Lattice parameters of the synthesized NiO powder weredecreased after treatment of the dopant; parameters were increased when the concentration of Al was over the doping limit(5mol% Al). The binding energy of Ni2+ was chemically shifted to Ni3+ by doping Al3+ ion, as confirmed by the XPS analysis.The tilted structure of the synthesized NiO with 5mol% Al dopant and the polycrystalline structure of the Ni0.75Al0.25O wereobserved by HR-TEM analysis. The electrical conductivity of the newly synthesized NiO was highly improved by Al dopingin the conductivity test. The electrical conductivity values of the commercial NiO and the synthesized NiO with 5mol% Aldopant (Ni0.95Al0.05O) were 1,400s/cm and 2,230s/cm at 750oC, respectively. However, the electrical conductivity of thesynthesized NiO with 10mol% Al dopant (Ni0.9Al0.1O) decreased due to the scattering of free-electrons caused by the largenumber of impurity atoms; the electrical conductivity of Ni0.9Al0.1O was 545s/cm at 750oC.