The effects of mechanical alloying conditions on the formation of Mn-sulfide powders were analyzed. Impeller rotating speed, lubricant coating and added amounts of process control agent(stearic acid) were selected as a process control factor. MnS compounds are synthesized in 3 hours by mechanical alloying at the alternative milling condition. Discontinuous rotating speed of 1200rpm for 4 minutes and 1000rpm for 1 minute shows more effects on the compound formation of MnS. After coating of lubricant on the wall, elementary Mn and sulfur were partially remained by mechanical alloying. The friction effects of the wall and grinding media on the powders are significantly important to form the compound of MnS.

본 연구는 보행주기 동안 정상인과 당뇨병성 족부궤양 환자의 족관절 운동역학적 변수와 족관절 근육들의 근활성도에 차이가 있는지 알아보기 위하여 실시하였다. 본 연구의 대상자는 당뇨병성 족부궤양이 있는 환자 9명(남자: 6명, 여자: 3명)과 성, 연령, 체중으로 짝짓기(matching)시킨 대조군 9명이었다. 3차원 동작분석기, 힘판, 표면 근전도를 이용하여, 보행주기 동안 족관절의 관절가동범위, 모멘트(moment), 일률(power), 그리고 내측가자

반무한 호소의 동적 모델링을 위한 역학적 집중변수모델을 제안하였다. 깊이가 일정한 2차원 반무한 호소의 전달경계의 정해를 구하였다. 정해의 거동특성을 주파수 영역과 시간 영역에서 조사하였다. 고유진동수와 합성곱 적분의 핵함수인 베셀 함수의 모양 등과 같은 해의 주요 특성이 변하지 않도록 질량, 감쇠기, 스프링 계수를 구한다. 최종 집중 변수 모델은 각각의 고유값에 대해 2개의 질량, 1개의 스프링, 2개의 감쇠기로 구성된다. 적용 예제를 통하여 새로운 집중변수모델이 댐-호소계의 시간 영역 해석에 효율적으로 사용될 수 있음을 확인하였다.

일반적으로 기계부품의 설계는 부품의 설계, 해석, 그리고 시제품에 대한 성능변화를 통해서 수행된다. 이와 같은 방식의 설계는 여러 번의 시행착오에 따른 개발경비와 개발기간이 많이 소요되고 각 단계를 수행시킬 전문인력도 필요하므로 현재 산업현장에서 요구되는 신속하고 저렴한 제품개발에 적합하지 않다. 이를 해결할 수 있는 한 가지 방법으로 각 개발과정을 하나의 시스템에서 제어할 수 있는 통합시스템을 개발하는 것이다. 이런 통합시스템은 특정 제품에 대한 전용시스템이 될 가능성이 크지만 통합시스템을 구축하는 기법은 일반적인 제품들에 대해서도 적용이 가능하다. 본 논문에서는 자동차의 부품 중에서 좌석의 프레임 설계를 수행하는 통합시스템을 구축한다. 자동차 좌석은 법규에 규정되어 있는 강도와 강성을 만족해야 하므로 본 통합시스템에서는 정적조건 강도시험인 헤드레스트 테스트를 통해서 좌석을 설계한다. 그리고 통합시스템은 UNIX환경에서 C언어를 이용해 좌석 모델의 생성과 정적 성능평가를 수행할 상용프로그램들을 제어하며, 그래픽 환경은 Motif로 구현한다.

졸-겔공정을 이용하여 SiO2 및 TEOS에 유기 고분자로서 PDMS가 도입된 PDMS/SiO2 xerogel을 제조하고 촉매로서 HCI과 NH4OH를 이용한 2 step acid/base catalyzed공정에 의해 SiO2 및 PDMS/SiO2 xerogel의 기공 크기 및 분포를 제어하였다. 촉매로서 HCl이 첨가된 SiO2 및 PDMS/SiO2 xerogel에서 PH는 2.3~2.5, gel화 시간 12~13일, xerogel의 모양은 Pellet형태를 나타내나 HCl/NH4OH 몰비가 증가하면 pH 및 gel화 시간은 급격히 감소하고 xerogel의 모양도 pellet형과 column형으로 뚜렷하게 구분된다. 이는 반응의 최종용액이 산성이면 가수분해속도가 축합속도보다 빠르게 진행되어 9el화에 오랜 시간이 소요되어 pellet형의 Xerogel이 되나 약산성에서는 축합속도가 가수분해속도보다 빠르게 되어 gel화 시간은 빨라지고 column형의 xerogel이 되기 때문이다 SiO2 및 PDMS/SiO2, xerogel의 표면적 및 평균기공크기는 HCl/NH4OH 몰비가 증가함에 따라 각각 400→600(m2/g)과 15→28Å 으로 변화하고 단일 기공크기분포를 갖는다. 이는 초기에 HCl에 의해 가수분해된 종이 NH4OH에 의해 축합속도가 촉진되어 silica의 골격구조가 낮은 온도에서 규칙적으로 형성되고 열처리에 의해 균일한 기공으로 되었기 때문이다.

This paper presents the relevance between GMFM and the spatiotemporal parameters of gait in children with cerebral palsy. Twenty-one children ( months) with cerebral palsy participated in this study. GMFM was performed and spatiotemporal parameters of gait were measured by foot print gait analysis. A correlation analysis was used to investigate the correlation between GMFM scores and spatiotemporal parameters of gait. A linear regression analysis was employed to find how much each gait spatiotemporal parameters could be predicted from GMFM scores. The total GMFM scores was significantly correlated with walking speed, cadence, and stride length. Dimensions D (standing) and E (walking, running, and jumping) were more significantly correlated with gait spatiotemporal parameters than dimensions A (lying and rolling), B (sitting), and C (crawling and kneeling). The GMFM scores were useful for predicting spatiotemporal parameters. However, it is difficult to predict the status of gait development using GMFM scores because GMFM scores and gait spatiotemporal parameters are only measured as quantities not qualities. In the field, it is easily found that many children with cerebral palsy are unable to walk in any way. Consequently, gait analysis cannot be performed in many cases. Therefore, it is more reasonable to investigate the influence of GMFM on spatiotemporal parameters, rather than vice versa.

소프트 콘돼트렌즈를 처방할 때 사용하는 시험렌즈용 소프트 콘택트렌즈의 소독방 법은 방법이 간편하며 소독효과가 확실하고 무엇보다 콘택트렌즈의 기하학적 형태에 변화를 주지 않는 방법으로 선택되어야 하나， 소프트 콘택트렌즈의 관리방법과 사용 횟수에 따른 렌즈의 기하학적언 디자인의 변화 등에 관한 연구는 미홉한 실정이므로 본 연구에서는 일정한 변수를 갖는 제 I 그룹렌즈 및 제 W 그룹렌즈를 대상으로 열소 독， 화학소독， 멸균， 전자파소독을 반복 시행하면서 이에 따라 나타나는 콘택트렌즈의 기하학적 변수 변화값을 측정하여 다음과 같은 결과를 얻었다. 세척과 소독방법에 따라 콘택트렌즈의 형태변화를 관찰한 결과 제 I 그룹렌즈는 세 척과 열소독， 화학소독， 멸균， 전자파소독을 30 회 반복 시행할 때까지 콘택트렌즈의 전반적인 형태가 잘 유지되었으며 콘택트렌즈의 변수에 변화가 관찰되지 않았으나， 제 N 그룹렌즈에서는 열소독과 멸균， 전자파소독에 의해 렌즈의 형태가 왜곡되었고 굴 절 력， sagittal value, 직 경 모두에 변화가 나타났다 각 변수의 변화값은 임 상적 인 허 용값 수준으로 나타났으나 콘택트렌즈의 모뜬 변수에 변화가 초래되었기 때문에 콘 택트렌즈의 피팅상태와 착용감에 영향을 줄 것으로 생각된다. 따라서 제 I 그룹 시험 렌즈의 경우에는 멸균볍을 포함한 모든 소독방법이 시험렌즈의 소독방법으로 가능하 다고 생각되며， 제 W 그룹 시험렌즈의 경우에는 콘택트렌즈 변수 변화가 가장 적은 화 학소독방법이 적합할 것으로 생각된다.

합리적인 기기의 활률론적 지진위험도 평가를 위해서는 모델의 동특성에 대한 보다 현실적인 정보가 제공되어야 한다. 이 연구에서는 심한 비선형 동적 거동을 보일 것으로 예상되는 철제 전기 캐비넷의 동특성 시험결과 및 분석 절차를 제시하였다. 특히, 이 연구에서는 가진 강도의 크기에 따른 동특성의 비선형 집중분석하고, 그 비선형성의 원인을 고찰하였다. 시험 결과 및 이 논문에 제시된 분석 절차를 이용하여 시험체의 동특성이 효과적으로 도출될 수 있으며, 대상 시험체는 가진 강도에 따라 심한 비선형 거동을 함을 입증하였다. 비선형성의 원인은 일반적인 재료 비선형이라기 보다는 각 부품들의 마찰력과 기하학적인 비선형성에 기인함을 발견하였다. 또한, 캐비넷 형식의 기긱에 대한 합리적인 내진안전성 평가를 위해서는 각 방향별로 서로 다른 감쇠값을 적용할 것을 추천하였다. 또한, 캐비넷 형식의 기기에 대한 합리적인 내진안전성 평가를 위해서는 각 방향별로 서로 다른 감쇠값을 적용할 것을 추천하였다.

Monodisperse polymer particles have many industrial applications such as surface coatings for metal panels, chromatographic media, spacers for liquid crystal display panel, and fillers for cosmetics, etc.. Micron-size monodispersed poly(methyl methacrylate) particles were prepared by dispersion polymerization in methanol medium in the presence of poly(vinyl pyrrolidone) and 2,2'-azobis(isobutyronitrile) as steric stabilizer and initiator, respectively. Effects of polymerization parameters, such as monomer and initiator concentration, stabilizer type and concentration, solvent composition on average particle size and size distribution were studied.

이 논문은 탄성지반위에 놓인 원호형 곡선보의 자유진동에 관한 연구이다. 회전관성 및 전단변형을 고려하여 두 개의 매개변수로 표현되는 탄성지반위에 놓인 원호형 곡선보의 자유진동을 지배하는 미분방정식을 유도하고, 이를 수치적분기법과 시행착오적 행렬값탐사법이 결합된 수치해석기법으로 해석하였다. 회전-회전, 회전-고정 및 고정-고정의 단부조건을 갖는 곡선보의 최저차모드 3개의 고유진동수를 산출하였다. 곡선보의 수평높이 지간길이비, Winkler 지반계수, 전단지반계수에 따른 고유진동수 변화를 분석하였으며, 회전관성 및 전단변형의 영향을 고찰하였다.