Crosslinked poly(methyl methacrylate) particles from 2.4 to 8.1μm in diameter were prepared by homogenized suspension polymerization. The effect of polymerization parameters such as homogenizing speed, homogenizing time and stabilizer concentration on the particle size were examined. Optical diffusion films were prepared with the crosslinked poly(methyl methacrylate) particles. The effect of film thickness, particle size, and particle size distribution on transmittance and haze of optical diffusion film was examined. Transmittance of optical diffusion film increased with increasing particle size and decreasing film thickness. Haze increased with increasing film thickness and decreasing particle size. We also found the existence of an optimum ratio for optical performance when the mixture of small particle and large particle was used.

Sputter Cu(1-4.5at.%Mg) alloy를 100mTorr이하의 산소압력에서 온도를 증가시키며 열처리하였을 때 표연과 계면에서 형성된 MgO의 확산방지막 특성을 살펴보았다 먼저, Cu(Mg)/SiO2/Si 구조의 샘플을 열처리했을 때 계면에서는 2Mg+SiO2→2MgO+Si의 화학반응에 의해 MgO가 형성되는데 이 MgO충에 의해 Cu가 SiO2로 확산되는 것이 현저하게 감소하였다. TiN/Si 기판 위에서도 Cu(Mg)과 TiN 계면에 MgO가 형성되어 Cu(4.5at.%Mg)의 경우 800˚C까지 Cu와 Si의 확산을 방지할 수 있었다. 표면에 형성된 MgO위에 Si을 증착하여 Si/MgO(150 Å)/Cu(Mg)/SiO2/Si구조로 만든 후 열처리했을 때 150 Å의 MgO는 700˚C까지 Si과 Cu의 확산을 방지할 수 있었다. 표면에 형성된 MgO(150 Å)의 누설전류특성은 break down 5V, 누설전류 10-7A/cm2의 값을 나타냈다. 또한 Si3N4/MgO 이중구조에서는 매우 낮은 누설전류밀도를 나타냈으며 MgO에 의해 Si3N4 증착시 안정적인 계면이 형성됨을 확인하였다.

Co/Ti 이중막을 급속열처리하여 형성한 CoSi2에 As+을 이온주입한 후, 500~1000˚C에서 drive-in 열처리하여 매우얇은 n+ p접합의 다이오드를 제작하고 I-V 특성을 측정하였다. 500˚C에서 280초 drive-in 열처리하였을 때, 50nm정도의 매우 얇은접합이 형성되었고, 누설전류가 매우 낮아 가장 우수한 다이오드 특성을 나타내었다. 특히, Co 단일막을 사용한 다이오드에 비해 누설전류는 2order 이상 낮았으며, 이는 CoSi2Si의 계면이 균일하였기 때문이다.

본 연구에서는 여러 기판에 대한 Cu의 확산정도를 알기 위하여 Ta, Nb, Co/Ta이중층 및 Co/Nb 이중층 위에 기화법으로 증착하고 열처리를 실시하였다. 열처리한 Ta막은 열처리하지 않은 Ta막보다 Cu 확산방지막으로서의 성능이 더 떨어지는데, 이것은 열처리에 의하여 Ta막이 결정화되기 때문이다. Cu/Co/Ta/(001)Si 구조에서의 구리 실리사이드 생성온도는 Cu/Co/Ta(001)Si 구조에서의 그것보다 더 높다. 한편, nb의 Cu에 대한 barrier 특성은 Ta와 비슷한 수준이다. 또한 Cu막 도포 이전에 Pd+HF활성화 전처리나 N2플라즈마 전처리를 실시하면, Cu의 핵생성뿐만 아니라 기판에 대한 Cu막의 접착성도 향상된다.

Reactive dc magnetron sputtering 법을 이용하여 증착한 molybdenum mitride 박막의 Cu 확산 방지막 특성을 조사하였다. Cu 확산 방지막으로서 molybdenum nitride 박막의 열적안정성을 관찰하기 위하여 molybdenum nitride 박막 위에 Cu를 evaporation 법으로 증착하고 진공 열처리하였다. Cu/r-Mo2N/si 구조는 600˚C, 30분간 열처리 시까지 안정하였다. 확산 방지막의 파괴는 650˚C, 30분간 열처리 시부터 격자 확산(lattice diffusion)이나 입계(grain boundary)과 결함(defect)을 통한 확산에 의해 나타나기 시작하였고, 이 때 molybdenum silicide과 copper silicide의 형성에 기인된 것으로 생각되었다. 열처리 이후 Cu/r-Mo2N/Si 사이의 상호반응이 증가하였다. 이는 Rutherford backscattering spectrometry, Auger electron spectroscopy 그리고 Nomarski microscopy 등의 분석을 통해 조사되었다.

InP 기판위에 InP와 격자정합된 undoped-InGaAs에서 zine의 확산 특성을 Electrochemical Capacitance-Voltage 법(polaron)과 Secondary Ion Mass Spectrometry(SIMS)로 조사하였다. Metallorganic Chemical Vapor Deposition (MOCVD)를 이용하여 undoped-InGaAs 층을 성장시켰으며 확산방법으로는 Zn3P2 확산원 박막과 Rapid Thermal Annealing (RTA)를 이용하였다. 450-550˚C온도범위에서 30-300초 동안 확산을 수행한 결과 zinc의 확산계수는 D=Doexp(-δE/kT)의 특성을 만족하였으며, Do와 δE는 각각 1.3x105cm2/sec와 2.3eV였다. 얻어진 확산계수는 다른 확산방법을 이용한 값들에 비해 매우 큰 값인데, 이것은 RTA 처리시 빠른 온도 증가에 의한 확산원 박막, 보호막, 그리고 InGaAs 에피층이 가지는 열팽창계수의 차이로인한 응력의 효과에 의한 것으로 생각되며, 이를 sealed-ampoule 법을 사용한 경우의 확산특성과 비교를 통하여 확인할 수 있었다.

Cu와 Si사이의 확산방지막으로 1000Å 두께의 TiN의 특성에 대하여 면저항 측정, 식각패임자국 관찰, X선 회절, AES, TEM 등을 이용하여 조사하였다. TiN 확산방지막은 550˚C, 1시간의 열처리 후에 Cu의 안쪽 확산으로 인해 Si(111)면을 따라 결정결함(전위)을 형성하고, 전위 주위에 Cu 실리사이드로 보이는 석출물들을 형성함으로써 파괴되었다. Al의 경우와는 달리 Si 패임자국이 형성되지 안흔 것으로부터 TiN확산방지막의 파괴는 Cu의 안쪽 확산에 의해서만 일어나는 것을 알 수 있었다. 또한, Al의 경우에는 우수한 확산방지막 특성을 보여주었던 충진처리된 TiN가 Cu의 경우에는 거의 효과가 없는 것을 알 수 있었다. 이것은 Al의 경우에는 TiN의 결정립계에 존재하는 TiO2가 Al과 반응하여 Al2O3를 형성함으로써 Al의 확산을 방해하는 화학적 효과가 매우 크지만, Cu의 경우에는 CuO 또는 Cu2O와 같은 Cu 산화물은TiO2에 비해서 열역학적으로 불안정하기 때문에 이러한 화학적 효과를 기대할 수 없으며, 따라서 충진처리 효과가 거의 없는 것으로 이해된다.

Al과 Si사이에서 Ti의 충진처리가 확산방지막 성능에 미치는 영향에 대해서 조사하였다. TiN의 충진처리는 450˚C의 N2 분위기에서 30분간 열처리함으로써 행하였다. TEM 분석을 통해 갓 증착된 TiN의 결정립 사이에는 약 10-20Å 정도의 고체물질이 없거나 TiN에 비해 밀도가 매우 낮은 공간이 존재함을 알 수 있었다. 또한 충진처리된 TiN의 경우에는 이러한 공간의 폭이 10Å 이하로 줄어듦을 알 수 있었다. RBS와 AES 분석에 의해 갓 증착된 TiN는 dir 7at.% 정도의 산소를 함유하고 있었고, 충진처리된 TiN는 약 10-15at.%의 산소를 함유하고 있었다. 갓 증착된 TiN와 충진처리된 TiN를 확산방지막으로 시험한 결과, 갓 증착된 TiN는 650˚C, 1시간의 열처리 후에 Al 스파이크와 Si 패임자국의 형성으로 이해 파괴되었다. 하지만 충진처리된 TiN의 경우에는 같은 열처리 조건에서 Al 스파이크나 Si 패임자국을 전혀 찾아볼수 없었다. 따라서, TiN의 충진처리가 Al과 Si사이에서 확산 방지막 성능을 크게 향상시켜주는 효과가 있음을 알 수 있었다. 이와 같은 충진처리 효과는 TiN의 결정립계의 간격이 줄어듦에 의해서 빠른 확산 경로인 결정립계를 통한 확산이 감소하는 것에 기인하는 것으로 이해된다.

The tidal current observation was carried out to investigate the characteristics of the circulation and diffusion in the vicinity of Kunsan harbor on March 1415, April 1∼2, and 13∼14, 1988. By harmonic analysis, the semidiurnal tidal current of more the amplitude of vibration was prevailed and its rotary direction was anti-clockwise in this harbor. Apparently constant current which is generated by out flow of Geum river was found to flow from Kunsan inner harbor to Janghang with the speed of about 30㎝/sec. It can be easily considered that deposition of much sand and mud which come from Geum river in Kunsan inner harbor and erosion in Janghang harbor will be occurred respectively. Autocorrelation and diffusion coefficient of each components was calculated to study the some characteristics of diffusion. Correlogram of the east-west component current was regular and nearly the same period as semidiurnal current. But it appeared irregular and considerably small value in the north-south component correlogram. Diffusion coefficient was 4 order in X-axis and 2∼3 order in Y axis in each study station.

진해만은 여름철에 적조가 자주 발생하는 해역으로서 우리나라 남해안 중 해양 오염이 가장 문제시되고 있는 해역중 하나이다. 그러므로 오염된 마산만의 해수가 진해만으로 어떻게 유입, 희석되는가를 알아보고, 만외에서 유입되는 해수의 확산 이동을 조사하기 위하여 대조(1981년 8월 17일)와 소조(1981년 9월 7일) 각 조석에 따라 네 번에 걸쳐 Rhodamine B (중량비 6%) 확산실험을 실시하였다. 그 결과 대조 때 방출 90분 후의 썰물과 밀물 때의 확산계수는 각각 3.0×10 super(3) cm super(2) /sec, 2.8×10 super(3) cm super(2) /sec 이고 소조 때 방출 90분 후의 확산 계수는 밀물 때는 6.2×10 super(2) cm super(2) /sec, 썰물 때는 2.1×10 super(3) cm super(2) /sec로서 소조 때보다 대조 때 더 크게 나타났으며, 다른 해역과 비교해 보면 수영만의 8.2×10 super(2) cm super(2) /sec, 1.12×10 super(3) cm super(2) /sec(Kim: 1981)와 그 값이 거의 비슷하나, 고리에서의 10 super(3) ~10 super(4) cm super(2) /sec(Ro: 1980)보다는 매우 적게 나타났다. 진해만 및 마산만의 경우, 만 입구가 협소하고 남쪽으로 열려 있어서 여름철에 남풍계열의 바람이 강하게 불면 썰물 때라도 표층수가 역류하여 만으로 들어오기 때문에, 특히 소조 때에는 오염물질의 분산이 잘 되지 않고 누적될 가능성이 크게 보인다.

콘크리트의 수화물 및 이와 관련된 특성치들은 재령에 따라 변화하며 이는 염화물 확산성과 큰 관련이 있다. 본 연구에서는 세 가지 수준의 물-결합재 비와 플라이 애시 및 고로슬래그 미분말을 30% 혼입한 콘크리트 대하여 2년간 장기 양생을 수행하였다. 5번의 측정 시점(28일, 56일, 180일, 365일, 730일)에 대하여 촉진실험을 통하여 촉진 염화물 확산계수를 평가하였으며, DUCOM을 통하여 도출된 공극률, 염화물 구속능, 투수계수의 변화와 비교하였다. 염화물 확산성과 투수성의 변화 패턴이 가장 유사하였는데, 이는 투수성이 공극률의 제곱에 비례하기 때문이다. 또한, 각 재령 기간 동안 변화하는 비율을 분석하였는데, 초기 재령(재령 28일~56일)에서 공극률, 투수성 및 염화물 확산성의 변화가 지배적이었고, 낮은 물-결합재 비를 가진 OPC 콘크리트에서는 180일까지 확산성의 변화가 지속적으로 크게 평가되었다.

To establish initial response scenarios for nuclear accidents around the Kori nuclear power plants, the potential for radionuclide diffusion was estimated using numerical experiments and statistical techniques. This study used the numerical model WRF (Weather Research and Forecasting) and FLEXPART (Flexible Particle dispersion model) to calculate the three-dimensional wind field and radionuclide dispersion, respectively. The wind patterns observed at Gijang, near the plants, and at meteorological sites in Busan, were reproduced and applied to estimates of seasonally averaged wind fields. The distribution of emitted radionuclides are strongly associated with characteristics of topography and synoptic wind patterns over nuclear power plants. Since the terrain around the power plants is complex, estimates of radionuclide distribution often produce unexpected results when wind data from different sites are used in statistical calculations. It is highly probable that in the summer and autumn, radionuclides move south-west, towards the downtown metropolitan area. This study has clear limitations in that it uses the seasonal wind field rather than the daily wind field.

In this study, we study the characteristics of thermal diffusion of cement paste at elevated temperature. Results of the experiments can be used to predict the fire damaged temperatures of concrete, and to recommend proper methods for repair and rehabilitation.

In this study, we study the characteristics of thermal diffusion of cement paste at elevated temperature. Results of the experiments can be used to predict the fire damaged temperatures of concrete, and to recommend proper methods for repair and rehabilitation.

본 연구에서는 국내에서 생산되고 있는 콘크리트용 순환 굵은골재를 사용하여 콘크리트의 압축강도 수준(20, 35, 50 MPa)에 따라 순환 굵은골재의 혼입률 변화가 콘크리트의 염화물 확산특성에 미치는 영향을 분석하였다. 실험결과 순환 굵은 골재의 치환율 변화에 따른 유 동성(슬럼프)은 순환골재를 혼입하지 않은 경우에 비해 동등하거나 양호한 유동성을 나타내는 것으로 나타났다. 이러한 영향은 국내에서 생산 되는 순환골재의 양호한 입형이 유동성 개선에 기여한 것으로 판단된다. 또한, 순환 곩은 골재의 치환율 변화에 따른 압축강도는 순환골재 혼 입률이 증가할수록 약 9~10% 감소하는 것으로 나타났다. 그리고 염화물 확산계수는 순환골재 혼입률이 증가함에 따라 최대 144%까지 증가하 는 결과를 나타냈으며 낮은 강도 수준의 콘크리트 일수록 순환골재 활용에 따른 내염성 저하 정도가 큰 것으로 나타났다. 강도가 증가할수록 순 환골재 혼입에 따른 영향은 감소되어, 고강도 영역에서는 일반 콘크리트와 유사한 염화물 확산 특성을 발현하는 것으로 분석되었다. 따라서 순 환골재를 콘크리트용 재료로 대량 활용하기 위해서는 콘크리트의 내염성 개선을 위한 혼화재료의 적용 또는 배합설계상 조정을 통한 강도의 개선 등이 필요할 것으로 판단된다.

In this study, chloride penetration of calcium leached concrete according to mineral admixture ratio were compared with OPC. From the results, it showed that chloride diffusion coefficient in calcium leached concrete were increased as calcium leaching period increase. However, the chloride diffusion coefficient of BFS case showed the better resistance than Fly Ash case. And, the distribution of chloride diffusion coefficient was significantly changed by calcium leaching period.