        701.
        1997.12 KCI 등재 구독 인증기관 무료, 개인회원 유료
        intermetallics containing 0-6 wt% of Cu were made by reactive sintering (RS) under vacuum using elemental powder mixtures (Process 1), electro-pressure sintering (EPS) using RS'ed materials (Process2), and EPS using elemental powder mixtures (Process 3). Relatively low dense titanium silicides were gained by process 1, in which porosity decreased with increasing Cu content. For example, porosity changed from 42 to 19.4% with the increase in Cu content from 0 to 6 wt%, indicating that Cu is a useful sintering aid. The titanium silicides fabricated by Process 2 had a higher density than those by Process 1 at given composition, and porosity decreased with increasing Cu content. For example, porosity decreased from 38 to 6.8% with the change in Cu content from 0 to 6 wt%. A high dense titanium silicides were obtained by Process 3. In this Process, porosity decreased a little by Cu addition, and was almost insensitive to Cu content. Namely, about 9 or 7% of porosity was shown in 0 or 1-6 wt% Cu containing silicides, respectively. The hardeness increased by Cu addition, and was not changed markedly with Cu content for the silicides fabricated by Process 3. This tendency was considered to be resulted from porosity, hardening of grain interior by Cu addition, and softening of grain boundary by Cu-base segregates. All these results suggested that EPS using elemental powder mixtures (Process 3) is an effective processing method to achieve satisfactorily dense titanium silicides.
        4,000원
        702.
        1997.12 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Engine valve-shaped TiAl-Mn intermetallics containing 43.5 to 47.5at%Al (Mn/Al=0.036) are successively fabricated by reactive sintering the elemental powder mixtures near-net shaped by extrusion and die forging. A duplex structure consisted of lamellar grains and equiaxed grains is developed for all compositions, and the areal fraction of the lamellar grains(or equiaxed grains) decreases (or increases) with increasing Al content. As Al content increased, the elongation increases with accompanying decrease in yield strength and ultimate tensile strength at both room temperature and 80. This indicates that the suitable composition is Ti-45at%Al-1.6at%Mn in considering the balance of ambient and elevated tensile properties. The reactive-sintered Ti-45Al-1.6Mn alloy shows superior oxidation resistance not only to the plasma arc melted one but also to the heat resistance steel STR35(representative exhaust valve head material for automotive engine). The reactive-sintered Ti-45Al-1.6Mn alloy coated with an oxidizing scale exhibits a better wear resistance than induction hardened martensitic steel STR11(representative exhaust valve tip material for automotive engine).
        4,000원
        703.
        1997.11 KCI 등재 구독 인증기관 무료, 개인회원 유료
        It is well known that the metallo-phthalocyanine(MPcs) are sensitive to toxic gaseous molecules such as NO2 and also chemically and thermally stable. Therefore, lots of MPcs have been studied for the potential chemical sensor for NO2 gas using quartz crystal microbalance or electrical conductivity. In this study, 2,3,9,10,16,17,23,24-[octa-(dodecyloxy)] copper phthalocyanine and 2,3,9,10,16,17,23,24-[octa-(octyloxy)] copper phthalocyanine were synthesized and their possibility of LB film preparation were tested. It was confirmed by using FT-IR, DSC, NMR, UV-Vis absorption spectroscopy and Elemental Analysis that CuPc derivatives were successfully synthesized. From the π-A characteristics and limiting areas of two CuPc derivatives it was found that the preparation of LB films with these CuPc derivatives is possible.
        4,000원
        704.
        1997.09 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        비정질 금속 Co66F e4Ni B14S i15 의 표면층 제거에 대한 자기임피턴스 효과는 시료의 길이방향에 평행한 일축자기장에 대하여 측정하였다. MIR(Magnetoimpedance Ratios)은 비정질 금속의 두께가 얇아짐에 따라 감소하고, 전류에 비례하여 증가하는 경향을 나타내었다. 인가전류 주파수에 대한 MIR과 자기장의 감도는 모든 시료에서 주파수에 비례하여 증가하며 수 MHz 부근에서 최대값을 가지고 점차 감소하는 경향을 나타내었다. 시료의 표면층제거에 기인한 이방성자기장의 변화는 MI RMax을 나타내는 외부 자기장을 감소시키지만, MIR은 표면층 제거에 따른 부피효과에 기인하여 감소하였다....
        4,000원
        705.
        1997.09 KCI 등재 구독 인증기관 무료, 개인회원 유료
        4,000원
        706.
        1997.09 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Joining of AIN ceramics to W and Cu by active-metal brazing method was tried with use of (Ag-Cu)-Ti alloy as insert-metal. Joints were produced under various conditions of temperature, holding time and Ti-content in (Ag-Cu) alloy Reaction and microstructural development in bonded interface were investigated through observation and analysis by SEM/EDS, EPMA and XRD. Joint strengths were measured by shear test. Bonded interface consists of two layers: an insert-metal layer of eutectic Ag- and Cu-rich phases and a reaction layer of TiN. Thickness of reaction layer increases with bonding temperature, holding time and Ti-content of insert-metal. It was confirmed that the growth of reaction layer is a diffusion-controlled process. Activation energy for this process was 260 KJ/mol which is lower than that for N diffusion in TiN. Maximum shear strength of 108 MPa and 72 MPa were obtained for AIN/W and AIN/Cu joints, respectively. Relationship between processing variables, joint strength and thickness of reaction layer was also explained.
        4,000원
        707.
        1997.09 KCI 등재 구독 인증기관 무료, 개인회원 유료
        In most of sintered metal powder compacts, the sintered density distribution is controlled to be as high and uniform as possible to ensure the required mechanical properties. In general, the density distribution in the compacts is not uniform and not easy to measure. In the present study, a method for measuring the density distribution was developed, based on the indentation force equation by which the hardness and the relative density were related. The indentation force equation, expressed as a function of strength constant, workhardening coefficient and relative density, was obtained by finite element analysis of rigid-ball indentation on sintered powder metal compacts. The present method was verified by comparing the predicted density distribution in the sintered Fe-0.5%C-2%Cu compacts with that obtained by experiments, in which the density distribution was directly measured by machining the compacts from the outer surface progressively.
        4,000원
        709.
        1997.08 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Tris(8-hydroxyquinoline)-aluminum complex(AlQ3) having greenish luminescent characteristics was synthesized and it was confirmed with UV-Vis absorption spectroscopy, elemental analysis, and FT-IR spectroscopy that AlQ3 was successfully synthesized. Thin films of AlQ3 having multilayer structure were prepared by spin coating method and vacuum evaporation technique. Photopluminescent characteristics of these films were investigated by Luminescence spectroscopy and Current-Voltage(I-V) characteristics of these films were also investigated.
        4,000원
        710.
        1997.07 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        LI2형 결정구조를 갖는 Ni-20at.%AI-10at%Fe 금속간화합물에 boron, zirconium 과 hafnium을 최고 0.5at.% 까지 첨가하여 항복강도, 연성, 파괴 등 기계적 성질의 변화를 인장시험과 X선분석 및 XPS분석 등을 통하여 관찰하였다. Ni-20at.% AI-10at.% Fe금속간화합물에 boron을 첨가하였을 때는 연신율의 현저한 증가가 나타났으나 zirconium이나 hafnium첨가의 경우에는 별다른 효과가 나타나지 않았다. Ni-20at.%AI-10at%Fe 금속간화합물의 경우, boron의 양이 증가할수록 인장연신율이 증가하였으며 0.1at.%의 boron을 첨가한 경우 최고 48.5%의 상온인장연신율을 나타내었다. 첨가물을 넣지 않은 경우와 zirconium과 hafnium을 첨가한 경우, 파괴모드는 입계파괴의 형태를 나타내었으나 boron을 첨가한 경우에는 파괴모드가 입계파괴에서 입내파괴로 변화되었다. XPS분석을 통하여 boron이 입계에 편석된 것을 관찰할 수 있었으며 이는 이미 제시된 여러가지 해석들과 일치하는 결과이다. 이로부터 boron의 첨가에 따른 인장연신율의 증가는 boron의 입계편석거동과 관련이 있음을 알 수 있다.
        4,000원