In this paper, initial value problem for dynamical astronomy will be established using parabolic cylindrical coordinates. Computation algorithm is developed for the initial value problem of gravity perturbed trajectories. Applications of the algorithm for the problem of final state predication are illustrated by numerical examples of seven test orbits of different eccentricities. The numerical results are extremely accurate and efficient in predicating final state for gravity perturbed trajectories which is of extreme importance for scientific researches as well as for military purposes. Moreover, an additional efficiency of the algorithm is that, for each of the test orbits, the step size used for solving the differential equations of motion is larger than 70% of the step size used for obtaining its reference final state solution.

Multi-walled carbon nanotube-poly methyl methacrylate (MWNT/PMMA) nanocomposite has been prepared by in situ polymerization of MMA dispersed with MWNTs. The MWNTs were functionalized by nitric acid and sulfuric acid treatment, and this was confirmed by FTIR spectrometer. The solution mixture of MWNTs and MMA was partially polymerized at 80℃, followed by the addition of AIBN and polymerization at 50℃. The MWNT-PMMA composite was prepared by casting the pre-polymer on the glass plate, and the optical properties have been studied using UV-vis spectrometer. The acid treated MWNTs were well dispersed in MMA with fairly good dispersion stability, while flocculation and sedimentation was observed from raw MWNTs in MMA.

In the present work, the influence of the ball-milling time, milling atmosphere and weight ratio of ball to powder on characteristics of was studied. Results show that, the grain sizes of the and CuO in the ball-milled powder mixture were significantly decreased with increasing the milling time. Those of each oxide ball-milled in Argon and Hexane atmosphere for 30 and 20 hour were about 98 and 84 nm, respectively. After milling of 20 hour in Hexane as PCA, the powder had a homogeneously mixed structure and the average size of powders was determined to about 230nm.

We studied formation of nanostructured -Cu composites under shock wave conditions. We investigated the influence of preliminary mechanical activation (MA) of Ti-B-Cu powder mixtures on the peculiarities of the reaction between Ti and B under shock wave. In the MA-ed mixture the reaction proceeded completely while in the non-activated mixture the reagents remained along with the product . titanium diboride. The size of titanium diboride particles in the central part of the compact was 100-300 nm.

The creep behavior of Al-5vol.% SiC composite was investigated. The composite powder was produced by mechanical milling and hot extruded at at ratio of 16:1. A creep test was carried out at a constant load at 598, 648, and 673 K. Using the steady-state equations, the threshold stress and the stress exponent of the creep as a function of temperature were determined. The stress exponent was found to be 3 at the temperature of 673 K and 8 at 598 and 648 K. The dependency of the threshold stress to temperature obeys the Arrhenius relationship with the energy term of .

Al-8Fe-2Mo-2V-1Zr alloys were prepared by the gas atomization/hot extrusion and the melt spinning/hot extrusion. For the gas atomized and extruded alloy, equiaxed grains with the average size of 400 nm and finely distributed dispersoids with their particle sizes ranging from 50nm to 200nm were observed. For the melt spun and hot extrusion processed alloy, refined microstructural feature consisting of equiaxed grains with the average size of 200nm and fine dispersoids with their particle sizes under 50nm appeared to exhibit a difference in microstructure. Strength of the latter alloy was higher than that for the former alloy up to elevated temperatures.

The present paper is a parameter study of zinc flake production using a Simoloyer CM01 horizontal high energy rotary ball mill. The manufactured flakes have a dimension in thickness (t) < 1μm and diameters (d) 5-100 μm, consequently a ratio d/t up to 200. The flake geometry is mainly controlled by the variation of process parameters such as rotary speed of the rotor, ratio of powder/ball charge, load ratio of the system, process temperature, operating model and the quantity of process control agent (PCA). The Zn flakes were characterized by SEM, tap densitometry, laser diffraction and water coverage measurement.

This research reports for the successful consolidation of Al2O3 powder with retained ultra-fine structure using MPC and sintering. Measurements in the consolidated Al2O3 bulk indicated that hardness, fracture toughenss, and breakdown voltage have been much improved relative to the conventional polycrystalline materials. Finally, optimization of the compaction parameters and sintering conditions will lead to the consolidation of Al2O3 nanopowder with higher density and even further enhanced mechanical properties.