The high-solid coatings were prepared by blending the synthesized acrylic resin in the previous paper and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, 60℃ specular gloss, cross-hatch adhension, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. From a viscoelastic measurement using a rigid-body pendulum, curing was accelerated with the Tg value. With the increase in Tg, log damp value was lowered and dynamic viscoelasic Tg of a cured film was increased.

Synthesis gas is commercially produced by a steam reforming process. However, the process is highly endothermic and energy-consuming. Thus, this study was conducted to produce synthesis gas by the partial oxidation of methane to decrease the energy cost. Supported Ni catalysts were prepared by the impregnation method. To examine the activity of the catalysts, a differential fixed bed reactor was used, and the reaction was carried out at 750~850℃ and 1 atm. The fresh and used catalysts were characterized by XRD, XPS, TGA and AAS. The highest catalytic activity was obtained with the 13wt% Ni/MgO catalyst, with which methane conversion was 81%, and H2 and CO selectivities were 94% and 93%, respectively. 13wt% Ni/MgO catalyst showed the best MgNiO2 solid solution state, which can explain the highest catalytic activity of the 13wt% Ni/MgO catalyst.

A copolymer 〈HSAs : EA/EMA/2-HEMA/AAEM) which is an acrylic resin containing 70% solid content was synthesized by the reaction of monomers, including ethyl acrylate, ethyl methacrylate, and 2-hydroxyethyl methacrylate with a functional monomer, such as acetoacetoxyethyl methacrylate, which may give improvements in cross-linking density and physical properties of films. The physical properties of prepared acrylic resins, HSA containing AAEM, are as follows : viscosity, 203~550cps ; Mn, 2590~2850 ; and conversion, 82~89%, respectively. It was found from the plotting of Tg versus viscosity and Tg versus molecular weight that viscosity increased with Tg while number averaged molecular weight decreased with increasing Tg.

Electrical properties of carbon filler/PVdF [poly(vinylidene fluoride)] composite were investigated as a funtion of carbon filler/PVdF ratio in the range of 0.2~0.5. Three kinds of comercialzied conductive carbon blacks such as Hiblack 41Y, KE300J, and KE600J, and carbon nanofibers prepared by the catalytic chemical vapor deposition of C2H4 over Ni-Cu catalysts were used as the carbon fillers. The electrical conductivity of carbon filler/PVdF composites were in the range of 0.65 to 13.5 S/cm depending the fillers' electrical conductivity ranging from 5.6 to 23.1 S/cm. Among the carbon fillers used, the KE600J carbon black showed the highest conductivity both in the composite and filler itself because of its high degree of graphitization due to the high-temperature thermal treatment and its high surface area due to the activation treatment.

Two-component polyurethane flame retardant coatings (ATTBC) were prepared by blending polyisocyanate (TDI-adduct) with ATTBs mentioned at the previous paper. Most of the physical properties of the flame retardant coatings were comparable to those of non-flame retardant coatings. Especially, the hardness, impact resistance, and accelerated weathering resistance were remarkably improved with the increase of the content of 1,4-butanediol. Coatings containing 10 and 15 wt% 1,4-butanediol, ATTBC-10C and ATTBC-15C, were not flammable in vertical flame-retardancy test. Their char area recorded 1.1~11.6 cm2 in 45˚ eckel burner method.

To prepare alkaline degreasing agents(SADAs), tetrasodium pyrophosphate(TSPP), Na2CO3, Tetronix T-701 (T-701), Na-dioctyl sulfosuccinate(303C), Demol C, and MJU-100A were blended. The prepared degreasing agents were tested with steel specimens and the results were as follows. The degreasing powers of SADA-6(Na2CO3 50g/TSPP 25g/T-701 10g/303C 15g/Demol C 12g/MJU-100A 8g/water 130g mixture) for press-rust preventing oil were 98% and 99% degreasing at 4wt%, 70 ℃ and 90 ℃, respectively; for quenching oil, the degreasing power of SADA-6 was 92% degreasing at 4wt% and 70 ℃. From these results, it was proved that the SADA-6 exhibits a good degreasing power. Foam heights measured immediately after foaming by Ross & Miles method and Ross & Clark method at 6wt% and 60 ℃ were 16mm and 40mm, respectively. SADA-6 was proved a good low foaming degreasing agent.

An intermediate, tetramethylene bis (orthophosphate), was prepared by the esterification of pyrophosphoric acid and l,4-butanediol. Then pyrophosphoric-containing modified polyesters (ATTBs) were synthesized by polycondensation of tetramethylene bis(orthophosphate), trimethylolpropane, adipic acid, and l,4-butanediol. The content of l,4-butanediol was varied from 10 to 20wt% for the reaction. The increase of the amount of l,4-butanediol in the synthesis of ATTBs resulted in increase in average molecular weight and decrease in kinematic viscosity owing to the excellent flowability and reactivity of l,4-butanediol.

Acidic degreasing agent(AADA) was prepared by blending sorbitol, Newpol PE-68, Na-dioctyl sulfosuccinate, Tetronix T-70l, MJU-100A, n-octanoic acid, and phosphoric acid, The physical properties of AADA tested with aluminum specimen showed the following results ; when 3wt% AADA-5 was performed at 70℃, the degreasing rate was 95% which is comparitively good, and the percentage of etching was 0.277% which was found to be less than that of commercialized product. when 20wt% of AADA-5 was added at 65℃, the percentage of derusting was 91% and the good defoaming effect proved by following low foaming power tests respectively : Ross and Miles, and Ross and Clark methods.

Environmental friendly acrylics/urea high-solid paints (BEHCU) were prepared through the curing reaction of acrylics resin(BEHC) containing 70wt% of solids content and butylated urea curing agent. BEHC was synthesized by addition copolymerization of caprolactone acrylate(CLA), 2-hydroxypropyl methacrylate(2-HPMA), ethyl methacrylate, and n-butyl acrylate. The addition polymerization of these monomers, especially including flexible CLA monomer and 2-HPMA monomer with OH funtional group, under appropriate reaction conditions resulted in polymers with controlled glass transition temperature(Tg) and crosslinking density. The molecular weight(Mw) of these polymers(BEHCs) was 2940~3240 and polydispersity (Mw/Mn) was in the range of 1.61~1.72. The viscosity and the molecular weight of these acrylic resins increased with increasing Tg. The coated films were prepared using curing reaction between BEHC resin and butylated urea curing agent at 100℃ for 30 minutes. Our experimental resulted showed that enhancement of the coating properties such as adhesion, flexibility, impact resistance, water resistance, and abrasion resistance could be expected through introducing CLA component in acrylic resin for the high-solid content acrylics/urea coatings.

In order to prepare a softener, alkyl imidazoline salt, fatty carbamide salt, and fatty polyamide salt were synthesized first, and then the synthesized salts were blended. The prepared softeners were applied to acrylic fibers, and then several properties were tested. As a result, the prepared softeners show good softening and lubricating properties, and they also show a little antistatic property. Through bending resistance tests and measurements of feeling change of acrylic fibers treated with the softeners, it was proved that the prepared softeners are durable softeners.

Environmental friendly acrylic/urea high-solid paint(MUHC) were prepared through the curing reaction of acrylics resin(EBHC) containing 70wt% of solids content and butylated urea curing agent. The synthesis of EBHC Was done at 150℃ for 6 hours, and the results were obtained as follows : Mn=1830~2190, Mw 3290~4000, Mw/Mn=1.80~1.83 viscosity=110~352 cps, and conversion=82~92%. After the film was coated with MUHC, the various physical properties were measured. They showed that enhancement of the coating properties such as adhesion, flexibility, abrasion resistance, impact resistance, and water resistance could be expected through introdl1cing caprolactone acrylate component in acrylics resin for the high-solids content acrylics/urea coatings.

Fatty polyamide that gives softness, lubrication and bulky property and alkyl imidazoline that gives durable softness and antistatic property were synthesized. then, an O/W-type durable softener (DSN) was prepared by the emulsion of the synthesized fatty polyamide and alkyl imidazoline. Emulsion stability of the DSN was good, and the mixed HLB value was 11.2. From the measurement of softness, lubrication, antistatic property, bending resistance, and color fastness, it was proved that the prepared DSN was a good durable softener for nylon.

[Ga]-MFI and H-ZSM-5 catalysts were synthesized under atmospheric pressure and used in the propylene aromatization. The effect of temperature on the product distribution was also investigated. The catalytic activities of the prepared catalysts were compared with the commercialized H-ZSM-5 which was converted from NH4-ZSM-5. In the propylene aromatization, product distribution does not depend on the ratio of Si/Ga2 with [Ga]-MFI catalyst, but depend on the ratio of Si/Al2 with H-ZSM-5 catalyst [Ga]-MFI catalyst shows better dehydrogenation and alkylation activities than H-ZSM-5 catalyst The addition of Ga to H-ZSM-5 catalyst increases the conversion of propylene, selectivity to aromatics, and alkylation. In the propylene aromatization, the selectivity to aromatics slightly increased with increasing temperature with [Ga]-MFI catalyst, while slightly decreased with increasing temperature with H-ZSM-5 catalyst

A silicone softner (SS-5), a permanent press (PP) finish, was prepared by blending silicone oil KF-96 (as a lubricating component) and beef tallow hardened oil (as a softening component) which was synthesized from fatty polyamide salts. The prepared SS-5 and the PP finishing resin were applied to PP finishing cotton cloth and P/C gingham sample by one-bath method. The properties such as crease recovery, tear strength, and bending resistance were tested. The samples treated with SS-5 and PP finishing resin showed improved properties when comparing with the untreated ones, with the ones treated only with PP finishing resin, with ones treated with commercial PP finishing softners and PP finishing resin. The grades of fabric samples treated with 3% SS-5 were fifth grade in the bending resistance test.

Two PU flame-retardant coatings, 2,3-DBPO/N-l00 (DBPON) and 2,3-DBPO/IL (DBPOI), were prepared by curing 2,3-dibromo modified polyester (2,3-DBPO) with isocyanate curing agent Desmodur N-l00 (or Desmodur IL) at room temperature. The physical properties and flame-retardancy of the two coatings were tested and compared. As a result, the pot-life, yellowness index, lightness index difference, 60˚ specular gloss, cross-hatch adhesion, viscosity, and accelerated weathering resistance of DBPON were better than those of DBPOI; the fineness of grind of the two coatings were the same; and the drying time, hardness, and abrasion resistance of DBPOI were better than those of DBPON. The flame retardancy of the flame-retardant coatings increased with the content of the flame retarding component, 2,3-dibromopropanoic acid (2,3-DBP); and the LOI values of the two coatings were in a range of 27~29% when the content of 2,3-DBP was 30wt%.

Our study is aimed at proposal of systematic verification method of molecular structure using measuring method of selective ionic determination and spectrometry on 34 kinds of surfactants such as sodium dodecyl sulfate(SDS) which are most widely used today. In the IR spectrum, unsaturated fatty acids reveal themselves by HC= at 3000~3020cm-1, and intensity of 720cm-1 depends on carbon length of alkyl group. Also ethylene oxide(EO) adducts exhibit weak characteristic bands by -CH2-CH2-O at 1350, 1100 and 950cm-1. Isethionate can be distinguished from diester succinate by intensity ratio of 1740 and 1200cm-1 spectrums, the ratio of latter is close to 1 due to 2 carboxylate radical in diester succinate. Quaternary ammonium salts exhibit characteristic band of C4N+ at 1000-900㎝-1. In the case of dialkyl dimethyl ammonium salts in quaternary ammonium surfactants, the spectrum of 3000cm-1 by N-CH3 collapses to a very weak band at 3020cm-1. In ammonium heterocyclic derivatives, pyridinium salts show characteristic bands at 1640 and 1460cm-1, while imidazolinium salts exhibit characteristic band at 1620-1610cm-1. In the characteristic spectrum at 1080-1050cm-1 on OH radicals of the alkyl esters, primary alcohol appears as weak band and the 2 bands show in almost same intensity when primary and secondary alcohols exist together in one molecule. Also, alkyl ester of polyhydric alcohols appears as various broad band.

An ACR/HMMM film was prepared by blending high-solid ACR with curing agent, hexamethoxymethyl melamine (HMMM). An active curing reaction was observed at 170℃. The dynamic viscoelastic Tg of the final film increased with the static viscoelastic Tg of the film. The log damp value, which means a viscoelastic ratio, decreased with the increase in the curing temperature of the film. Physical properties of the films were within a suitable range for films, and by an accelerated weathering resistance test the films were proved weather resistible ones.

Aqueous urethane dispersion resin begins to assume commercial importance due to increasing environmental awareness of VOC in coating industry. Moreover there have been strong industrial needs for the development of reactive-type polyurethane flame retardant coatings. In this study, chlorinated polyester polyols were synthesized by two step polycondensation reaction using mono chloroacetic acid, adipic acid, trimethylol propane, and 1,4-butanediol. In the next step polyurethane dispersion was prepared using these chlorinated polyester polyols and isophorone diisocyanate with dimethylol propionic acid(DMPA) and trimethylamine. The structure of chlorinated polyol was characterized by GPC, FT-IR and NMR. Particle size and its distribution were examined in terms of various dispersion parameters including molecular weight and composition of polyol, amount of DMPA, and NCO/OH ratio, etc. The effect of chlorinated polyols on flammability was also evaluated.

Due to its low density, good mechanical properties and chemical inertness, glassy carbon(GC) has been studied for appications in several fields. A raw thermosetting resin of furanic resin was polymerized with a curing agent of p-toluenesulfonic acid monohydrate. The maximum yield of GC was obtained at the curing agent content of 1.0 wt% in furanic resin. In order to make thick GC, the affect of graphite filler addition to the furanic resin was investigated. The density and electrical resitivity of GC after graphitization were 1.45 g/cm3 and 47 ×10-4 Ω · cm respectively and the amorphous structure of GC was confirmed by XRD profiles with very broad peaks comparable to those of graphite at 206˚ and 45˚.