Tungsten nanopowders were produced by the method of wires electrical explosion in the different gases. The study of phase and dispersed composition of the powders was carried out. The influence of electrical parameters such as the value of energy input in wire and the arc stage of the explosion was discussed. The factors that make for decreasing the particles size are the lower pressure of surrounding gas and the use of addition of chemically reactive gas.

The purpose of this research was to analyze the effects of the increase of the femoral anteversion angle on the unbalanced quadriceps femoris muscle causing the increase of the valgus force on the knee joints and patellofemoral pain syndrome by comparing with the group that shows the smaller femoral anteversion angle. The method for the research was to compare the femoral muscle's activity while the subjects were maintaining the knee joint flexed isometrically for 10 seconds. The evaluation tool for femoral muscle's activity was QEMG-4 (model LXM 3204). The results were as followings. Firstly, in case of the experimental group, the muscle strength of the vastus lateralis muscle was strong while the rectus femoris and vastus medialis were weak. In these facts, we can see the statistically meaningful difference in vastus medialis muscle activity. Secondly, in the muscle activity analysis for vastus lateralis and medialis of the two groups, we could see the vastus lateralis muscle was strong in anteversion wider for experimental group while the vastus medialis muscle contracted far more stronger in anteversion smaller for control group. From these results, we can see the significant differences in muscle recruitment between the two groups. Above results show that if the anteversion becomes wider, vastus medialis muscle will become seriously weaker, on the other hand, vastus lateralis act stronger.

Dispersion-strengthened copper with was produced by ball-milling and spark plasma sintering (SPS).Ball-milling was performed at a rotation speed of 300rpm for 30 and 60min in Ar atmosphere by using a planetary ball mill (AGO-2). Spark-plasma sintering was carried out at for 5min under vacuum after mechanical alloying. The hardness of the specimens sintered using powder ball milled for 60min at 300rpm increased from 16.0 to 61.8 HRB than that of specimen using powder mixed with a turbular mixer, while the electrical conductivity varied from 93.40% to 83.34%IACS. In the case of milled powder, hardness increased as milling time increased, while the electrical conductivity decreased. On the other hand, hardness decreased with increasing sintering temperature, but the electrical conductiviey increased slightly

Cu- nanocomposite powders were synthesized by combining high-energy ball-milling of Cu-Ti-B mixtures and subsequent self-propagating high temperature synthesis (SHS). Cu-40wt.% powders were produced by SHS reaction and ball-milled. The milled SHS powder was mixed with Cu powders by ball milling to produce Cu-2.5wt.% composites. particles less than 250nm were formed in the copper matrix after SHS-reaction. The releative density, electrical conductivity and hardness of specimens sintered at were nearly 98%, 83%IACS and 71HRB, respectively. After heat treatment at 850 to for 2 hours under Ar atmosphere, hardness was descedned by 15%. Our Cu- composite showed good thermal stability at eleveated temperature.

Maghemite and hematite nanospheres were synthesized by using the Sol-gel technique. The structural properties of these nanosphere powders were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM), and pore size distribution. Hematite phase shows crystalline structures. The mean particle size that resulted from BET and XRD analyses were 4.9 nm and 2 nm. It can be seen from transmission electron microscopy that the size of the particles are very small which is in good agreement with the FESEM and the X-ray diffraction. The BET and pore size method were employed for specific surface area determination.

Nanoscale Al powder with thin layer of alumina was produced by Wire Electric Explosion (WEE) process. Spark-Plasma Sintering (SPS) was performed for the produced powder to confirm the effectiveness of SPS like so-called 'surface-cleaning effect' and so on. Crystallite size and alumina content of produced powder varied with the ratio of input energy to sublimation energy of Al wire (): Increase in () resulted in the decrease of crystallite size and the increase of alumina content. Shrinkage curve during SPS process showed that the oxide surface layer could not be destroyed near the melting point of Al. It implied that there was not enough or no spark-plasma effect during SPS for Al/Alumina powder.

Mechanically-alloyed NiAl powder was sintered by Spark-Plasma Sintering (SPS) process. Densification and behavior mechanical property were determined from the experimental results and analysis ,such as changes in linear shrinkage, shrinkage rate, microstructure, and phase during sintering process, Victors hardness, and transver.ie-rupture-strength (TRS). Above 97% relative density was obtained after sintering at 115 for 5 min. Crystallite size determined by the Scherrer method was approximately 50 nm. From the X-ray diffraction analysis it was confirmed that the sintered bodies were composed mainly of NiAl phase together with NiAl phase. Measured Vickers hardness and TRS value were 55510 and 139375 MPa , respectively.

The mechanical alloying effect has been studied on the three Cu-based alloy systems with a positive heat of mixing. The extended bcc solid solution has been formed in the Cu-V system and an amorphous phase in the Cu-Ta system. However, it is round that a mixture of nanocrystalline Cu and Mo Is formed in the Cu-Mo system. The neutron diffraction has been employed at a main tool to characterize the detailed amorphization process. The formation of an amorphous phase in Cu-Ta system can be understood by assuming that the smaller Cu atoms preferentially enter into the bcc Ta lattice during ball milling.

The various properties such as the electric current distribution, resonant frequency and radiation patterns of open-ended meander slot antenna placed on a small ground plane, are investigated to give the help in performing antenna design. Based upon these characteristics, the designed antenna which is only 22mm(0.06λg) in height and 31mm(0.09λg) in width can operate at the 433 MHz with the measured radiation efficiency of 8% and end-fire radiation pattern. These properties make the antenna suitable for the handheld device such as the wireless remote controller.

환경호르몬(내분비계 장애물질)이 하등동물의 생식기 및 생식 기능 이상을 초래한다는 최근보고는 포유동물도 그 영향하에 있음을 암시한다. 따라서 2-bromopropane(2-BP)이 생쥐 차산자의 성별에 미치는 영향과 성 분화 과정 중에 발현되는 유전자를 조사하였다. 생쥐를 2-BP로 3주일 동안 주입한 암수를 4종류 조합으로 교배시 킨 후 태어난 새끼들의 성별을 이유시기에 결정하였다. 성관련 유전자들은 수태 후 10일에 어미 생쥐를 희생시켜 RT-PCR

This study was carried out to map Bphl and bph2 gene in Mudgo and Sangju13 (Oryza sativa L.) respectively conferring resistance to brown plan-thopper (BPH) and to establish the marker-assisted selection (MAS) system. Bulked seedling (grown for 20 days) test was conducted with the 73 F4 lines derived from a cross between Nagdongbyeo and Mudgo for Bphl and with 53 BC3F5 lines derived from the Milyang95/Sangju13 cross for bph2. Bph1 was mapped between RG413 and RG901 on chromo-some 12 at a distance of 7.5 cM from RG413 and 8.4 cM from RG90l. A recessive gene bph2 was located near RZ76 on chromosome 12 at a distance of 14.4 cM. Bphl and bph2 were linked to each other with a distance of about 30 cM. An RFLP marker, RG413 linked to Bphl, was converted to an STS marker to facilitate the marker-assisted selection. BPH resistant genotypes could be selected with 92% accuracy in a population derived from a line of NM47-B-B.