The MIM technology is an alternative process for fabricating near net shape components that usually uses gas atomised powders with small size (< 20 μm) and spherical shape. In this work, the possibility of changing partially or totally spherical powder by an irregular and/or coarse one that is cheaper than the former was investigated. In this way, different bronze 90/10 components were fabricated by mixing three different types of powder, gas and water atomised with different particle sizes, in order to evaluate how the particle shape and size affect the MIM process.

조사후 핵연료 가열(PIA장비)를 이용한 고연소도 UO2 사용후 핵연료의 산화 및 가열후 미세조직의 변화를 관찰하였다. 울진 2호기에서 한국원자력연구소 조사후시험시설로 이송된 국산 경수로용 고연소도 사용후 핵연료는 봉평균 연소도가 57,000 MWd/tU-rod avg.이였다. 본 시험에 사용된 시편은 국부연소도 65,000 MWd/tU UO2 소결체의 고형체 200 mg을 사용하였다. 본 시편을 사용후 핵 연료 가열(PIA) 시험장비를 이용하여 핫셀 내에서 3시간의 산화시험과 연속적으로 까지 가열하였다. 결정립경계까지의 산화를 위하여 에서 헬륨 50 ml, 표준공기 100 ml를 흔합한 산화분위기로 3시간을 유지하였다. 핵분열기체 방출거동을 알기위해 시험 전과정중에 85Kr의 방출량을 베타 측정기와 감마 측정기를 이용하여 실시간으로 측정 하였다. 가열시험이 종료된 후 전자주사현미경을 이용하여 미세구조의 변화를 관찰하였다. 시험결과 가열하는 동안 핵분열생성물은 UO2기지의 결정립경계와 표면으로 이동된 것을 관찰하였다. 이 시편은 환원과정을 통하여 재구조화 되었고, 정도의 결정립크기를 가진 것으로 나타났다.

Recently, membrane can be prepared by two methods, phase inversion and electrospinning techniques. Phase inversion technique is a conventional but commercially preparation membrane. The most versatile of preparation in this technique is immersion of the cast film into nonsolvent bath, causing dense top layer with a finger-like pattern in the sub layer membrane. The membrane pore size getting from phase inversion is in the range of micro or submicrometer. As a result, it can be used as microfiltration and ultrafiltration applications. A new technique, electrospinning, is introduced for membrane preparation. Nonwoven nanofibrous mat or nanofibrous membrane is obtained. In this technique, electrostatic charge is introduced to the solution jet, causing a thin fiber with high surface area; hence it can be used in the applications where high surface area-to-volume or length-to-diameter ratios are required. Moreover, the pore size can be controlled by controlling the time of electrospinning. Hence, it can be used as a filter for filtering microparticles as well as nanoparticles.

본 연구는 한우 수정란의 체외생산에 있어서 효율과 품질의 향상을 위해서, 미성숙 난포란을 회수하는 난소의 형태와 배양 용기로서 straw의 효과를 검토하였다. 난소의 형태에 따른 수정율은 전 군에서 70.3∼84.1%로서 비슷한 경향이었다. 8세포기 및 배반포기 발달율은 황체와 난포가 모두 존재하지 않는 대조군이 가장 높았다. 배반포의 inner cell mass(ICM), trophectoderm(TE), total cell number(TCN) 및 ICM/TCN 비율은 낭종군과 퇴행황체군이 다른군에 비하여 높은 경향이었다. 체외성숙에 이용하는 배양용기에 따른 수정율은 0.5 ㎖ straw 군이, 8세포기 발달율은 대조군이 가장 높았으나, 배반포기 발달율은 23.1∼30.7％로서 각 군 간에 비슷한 경향이었다. 한편 각각의 배양 용기에서 유래된 배반포의 ICM, TE, TCN 및 ICM/TCN 비율은 유사한 경향이었다.

Multi-walled carbon nanotubes (CNTs) were prepared by microwave plasma chemical vapor deposition (MPCVD) using various combination of binary catalysts and methane precursor. The maximum yield (10.3 %) of CNTs was obtained using a methane-hydrogen-nitrogen mixture with volume ratio of 1:1:2 at 1000 W of microwave power. As the microwave power increased up to 1000 W, the deposition yield of CNTs raised from 4.1 % to 10. 3 %. However, the prepared CNTs at 800 W showed the more crystalline structure than those prepared at 1000 W. The prepared CNTs over different binary catalysts had various structural conformations such as aligned cylinder, bamboo, and nanofibers. The Id/Ig value of CNTs overFe-Fe/Al2O3, Co-Co/Al2O3, and Co-Cu/Al2O3 were in the range of 0.89~0.93. Among the various binary catalysts used, Fe-Co./Al2O3 showed the highest yield.

Film properties of monodispersed model composite latexes with particle size of 190 nm, which consist of n-butyl acrylate as a soft phase monomer and methyl methacrylate as a hard phase monomer with different morphology was examined. Five different types of model latexes were used in this study such as random copolymer particle, soft-core/hard-shell particle, hard-core/soft-shell particle, gradient type particle, and mixed type particle. Tensile strength and tensile elongation at break of final films were evaluated. Those properties can be interpreted in terms of PBA/PMMA phase ratio and their morphology. The interfacial adhesion strength was also evaluated using 180˚ peel strength measurement and cross hatch cutting test.

Multi-walled carbon nanotubes (CNTs) were prepared by thermal chemical vapor deposition (CVD) and microwave plasma chemical vapor deposition (MPCVD) using various combination of binary catalysts with four transition metals such as Fe, Co, Cu, and Ni. In the preparation of CNTs from acetylene precursor by thermal CVD, the CNTs with very high yield of 43.6 % was produced over Fe-Co/Al2O3. The highest yield of CNTs was obtained with the catalyst reduced for 3 hr and the yield was decreased with increasing reduction time to 5 hr, due to the formation of FeAl2O4 metal-aluminate. On the other hand, the CNTs prepared by acethylene plasma CVD had more straight, smaller diameter, and larger aspect ratio(L/D) than those prepared by thermal CVD, although their yield had lower value of 27.7%. The degree of graphitization of CNTs measured by Id/Ig value and thermal degradation temperature were 1.04 and 602℃, respectively.

Film forming behavior of monodispersed model composite latexes with particle size of 190 nm, which consist of n-butyl acrylate as a soft phase monomer and methyl methacrylate as a hard phase monomer with different morphology was examined. Five different types of model latexes were used in this study such as random copolymer particle, soft-core/hard-shell particle, hard-core/soft-shell particle, gradient type particle, and mixed type particle. The film forming behavior was evaluated using pseudo on-line measurements of the cumulative weight loss, the UV transmittance, and the tensile fracture energy. Each stages of film formation I, II were not sensitive to the morphology of model latexes, but stage-ill was largely dependent on the morphology of model latexes. The chain mobility of polymer which composed the shell component was found to dominantly determine the behavior of film forming stage-III.

균일한 밀집구조를 지니는 투명한 폴리설폰 필름이 용매를 사용한 표면처리를 통해 개질되었다. 개질은 고분자 필름을 디메털포름아마이드 용매에 1 sec간 담그고 이를 비용매 욕조에 침지시켜 이루어졌다. 개질 전 투명하였던 필름은 개질 후 횐색을 띠며, 많은 기공이 표면에 형성되었다. 비용매로서 물을 사용하였을 때가 이소프로파놀을 사용하였을 때 보다 표면의 불균일도가 증가하였다. 개질된 필름을 사용하여 방사성핵종으로 오염된 지역으로부터 오염물을 채취하였을 때 일반적으로 사용되는 필터페이퍼를 사용하는 것보다 우수한 채취 효율을 보여주었다. 개질된 필름 중에서는 비용매로 물을 사용한 경우 이소프로파놀을 이용한 필름보다 오염물의 채취 효과가 좋은 것으로 나타났다. 한편, 개질된 필름은 고분자 필름의 양쪽 겉표면만을 변화시켜, 필름의 내부는 고유한 밀집도를 유지함으로써, 필터페이퍼 또는 유리섬유를 사용한 오염물 제거 과정에서 나타날 수 있는 매체의 기공을 통한 2차적 오염을 방지하는 효과가 있다.