The study was conducted to evaluate the latent heat properties of cement mortar with different contents of phase change material (PCM). The paraffin PCM with melting point of 44℃ used in this study. PCM was added in the mixture with contents ranged from 0 to 30%. Test results indicated that the heat storage performances of cement mortar were improved with increasing the content of PCM.

본 연구는 저온환경에서 경화가 가능한 알루미나시멘트 및 아질산염을 사용한 보수용 시멘트 모르타르의 기초성능을 평가하고자 하였다. 이를 위해 국내 건설현장에서 사용되고 있는 보수용 모르타르를 조사 및 선정하였으며, 이를 대상으로 알루미나시멘트, 아질산염을 치 환하여 혼입량 조절에 따른 실험평가를 실시하였다. 그 결과, 알루미나시멘트, 아질산염을 보수용 모르타르에 치환하여 사용할 경우 초기 강도 발현이 증진되었다. 또한 내화학성이 개선되었고 수축거동이 감소하였으며 동결융해에 대한 저항성이 증대되었다. 알루미나시멘트와 아질산 염을 2:1의 비율로 7.5% 치환하여 외부구조물에 시공한 결과 표면상태가 5개월 이상 양호하게 유지되었으며, 실제 외부구조물에 사용성이 우 수한 것으로 판단된다.

In general, polymer cement mortars that is made from organic polymer dispersion and cement have good workability compared with ordinary cement due to ball-bearing acting of polymer particles in cement mortar. The purpose of this study is to evaluate the workability of cement mortar according to adding of admixtures such as polymer dispersions, blast-furnace slag and fly ash. From the test results, the flow of polymer-modified mortars is increased with increasing polymer-cement ratio, and also is a little improved according to adding of fly ash compared to blast-furnace slag.

This paper investigates the effect of amount of Paraffin-encapsulated phase change material (PCM) on the thermal energy storage of cement mortar for developing energy saving concrete. The PCM with melting point of 44℃ was used in this study. The added amounts of PCM in the cement mortar were 0, 10, 20 and 30% of cement weight. The results indicated that the heat storage properties of cement mortar was improved with increasing contents of PCM.

In general, polymer cement mortars that is made from organic polymer dispersion and cement have good workability compared with ordinary cement due to ball-bearing acting of polymer particles in cement mortar. The purpose of this study is to evaluate the workability of cement mortar according to adding of admixtures such as polymer dispersions, blast-furnace slag and fly ash. From the test results, the flow of polymer-modified mortars is increased with increasing polymer-cement ratio, and also is a little improved according to adding of fly ash compared to blast-furnace slag.

This paper investigates the effect of amount of Paraffin-encapsulated phase change material (PCM) on the thermal energy storage of cement mortar for developing energy saving concrete. The PCM with melting point of 44℃ was used in this study. The added amounts of PCM in the cement mortar were 0, 10, 20 and 30% of cement weight. The results indicated that the heat storage properties of cement mortar was improved with increasing contents of PCM.

본 논문은 바탕면의 함수조건에 따른 보수재료로서 MKPC의 인발 부착강도, 전단 부착강도, 계면 부착강도를 폴리머 시멘트 모르 타르, 에폭시 모르타르와 비교 분석하였다. 그 결과 MKPC는 PC 및 MKPC와 비교하여 바탕면 함수조건에 따른 부착성능의 변화가 상대적으 로 작은 것으로 나타났다. 또한 MKPC의 경우 절건 바탕면에서의 부착성능은 무기계 보수재료인 폴리머 시멘트 모르타르와 비교하여 우수한 특성을 지니고 있으며, 습윤 바탕면에서의 부착성능은 폴리머 시멘트 모르타르와 유사한 수준을 보이고 있으나 에폭시 모르타르와 비교하여 우수한 특성을 지니는 것으로 나타났다.

In this research, the adverse effect of various oils when the mortar including fly ash was submerged into the oils. From the experimental results, the highest length and mass changing rates were observed when the mortar was submerged into the biodiesel and in the case of relative dynamic elastic modulus, soy oil and biodiesel caused the most decreasing. Additionally, the mortar with fly ash was influenced more than ordinary Portland cement when it submerged into the oil.

Recently, a Multi-Walled Carbon Nano Tube(MWCNT) is widely used to increase mechanical strength of the cementitious composite material. In this study, a dilution of MWCNT aqueous solution(from wt 2.0%, 1.5% to wt 1.0%) is a main parameter. A compressive strength of diluted CNT cement mortar is maximum 4.7% larger than that of a pure CNT cement mortar. The result indicates that the diluted MWCNT aqueous solution of the MWCNT cement mortar makes very little differences of the compressive strength.

In this study, Corrosion behavior in mortar was observed by the passage of time by using EIS method. As a result of EIS experiment, equivalent circuit and changes of Impedance parameter could be observed. In addition, it was confirmed that impedance of rebar in mortar and corrosion rate according to the amount of NaCl were different.

알칼리활성화 슬래그-레드머드 시멘트는 알칼리활성화 시멘트 연구의 일환으로서 시멘트 조성에서 알칼리자극제, 고로슬래그와 레드머드로 구성되어져 있으며, 포틀랜트 시멘트를 사용하지 않는 클링커 프리 시멘트(Clinker Free Cement)를 의미한다. 본 논문에서는 포틀 랜트 시멘트를 전혀 사용하지 않고 고분자 유기화합물인 재유화형 분말 폴리머를 혼입한 알칼리활성화 슬래그 시멘트에 레드머드의 대체율을 달리하여 강도특성, 기공특성 등을 기존 포틀랜트 시멘트와 비교 평가하였다. 그 결과 알칼리활성화 시멘트에 레드머드를 대체할 경우 C-S-H 광물상과 에트린가이트가 주요 수화생성물로 포틀랜트 시멘트와 비교하여 조직이 치밀하고 대체율 10%까지는 압축강도 및 휨강도가 증가하 였다.

본 연구에서는 칼슘알루미네이트 시멘트(CAC) 모르타르의 수화생성물, 강도, 흡수율, 표면전기 저항성 및 염소이온 침투저항성을 실험적으로 고찰하였다. CAC 모르타르의 성능은 보통포틀랜드 시멘트(OPC) 모르타르의 성능과 상호 비교되었다. 실험 결과에 따르면, CAC 모르타르의 주요 수화생성물은 C2AH8 및 CAH10으로 조사되었으며, 압축 및 부착강도는 OPC 모르타르에 비하여 우수하게 나타났다. 뿐만 아 니라, 표면전기 저항성 및 염소이온 침투저항성도 대체적으로 좋은 결과를 나타냄으로서, CAC의 우수한 성능도 확인하였다. 그러나, CAC 모 르타르의 흡수율은 초기재령부터 OPC 모르타르에 비하여 다소 크게 나타남으로써, CAC 경화체의 표면흡수 성능을 개선하기 위한 연구가 더 필요할 것으로 판단된다. 반면, CAC 및 OPC 혼용배합 모르타르의 역학적 성능은 CAC 모르타르에 비하여 대체적으로 다소 떨어지는 것으로 조사됨으로써, CAC계 경화체 제조시 주의가 요구된다.

This study was intended to estimate the effect of adding stone dust into cement mortar on the rheological properties. it was found that higher the content of stone dust decrease the yield stress but there was no noticeable correlation between stone dust dosage and the plastic viscosity.

Due to the increasingly serious environmental problems presented by waste tires, the feasibility of using elastic and flexible tire-rubber particles as aggregate in concrete is investigated in this study. Tire-rubber particles is composed of tire chips, crumb rubber, and a combination of tire chips and crumb rubber. Experimental work of Waste Rubber Particle Reinforced Mortar(WRPRM) have been conducted in the form of cube specimens [50mm x 50mm x 50mm], beam specimens [40mm x 40mm x 160mm] mixed with 0%, 5%, 10%, 15%, 20%, 25% of rubber particle. We executed test for compression strength test, bending strength test on 7 days, 14days, 28days and percentage of moisture content test on 28days after initial curing. In this study, We studied the initial strength of WRPRM. But, in order to understand the reinforcing effect of the rubber particles, we need to execute a test of Waste Rubber Particle Reinforced Concrete(WRPRC).

최근 선진국을 중심으로 MWCNT(Multi-walled carbon nanotube)의 우수한 기계적 성질을 이용한 시멘트 모르타르의 압축강도 향상 연구가 활발하다. 그러나 국내에서 MWCNT 모르타르와 관련된 연구는 국외에 비해 상당히 미미한 실정이다. 따라서 본 연구에서는 MWCNT 수용액을 시멘트 모르타르에 적용하여 MWCNT 모르타르의 압축강도 증진 효과를 분석하고자 한다. 실험 매개변수는 최적의 MWCNT 모르타르 제작법 도출을 목적으로 강도시험에 큰 영향을 미칠 것으로 예상되는 물시멘트비, 재령일, MWCNT의 농도로 선정하였다. 물시멘트비는 0.4, 0.5, 0.6으로 변화시켰고 재령일은 7일, 14일 28일로 구분하였으며 MWCNT수용액의 농도는 2.0wt%로 선정하였다. MWCNT 모르타르에 혼입한 MWCNT 수용액의 분산은 계면활성제와 초음파로 처리하였으며, 증류수를 기반으로 제작 하였다. 실험결과 물시멘트비 0.4, 0.5, 0.6일 때 일반 시멘트 모르타르의 압축강도보다 MWCNT 모르타르의 압축강도가 각각 최대 35%, 20%, 25% 높게 측정되었다. MWCNT 모르타르의 압축강도가 일반 시멘트 모르타르의 압축강도보다 높은 이유는 모르타르의 수화 과정에서 MWCNT의 우수한 기계적 성질이 모르타르 내부의 결합력을 증진시켜 주는 것으로 분석되었다.

Two main parameters were examined such as CSA content and polymer-binder ratio to find effects on the strength, water absorption, chloride ion penetration depth, carbonation depth, length change and chemical resistance of polymer-modified mortar with CSA and EVA polymer powder (EVAPP). As results, compressive, flexural, tensile, adhesive strengths, and length change of the polymer-modified mortar with CSA and EVAPP increases with increasing CSA content and polymer-binder ratio, although the water absorption, chloride ion penetration depth, and carbonation depth decrease with increasing polymer-binder ratio and CSA content, and also the chemical resistance decreases. Such strength and durability development is attributed to the high tensile strength of EVA polymer and the improved bond between cement hydrates and aggregates because of the addition of EVAPP and CSA.

As global warming is higher by CO2, most of countries have an effort to develop CO2 reducing technology like a CO2 sequestration and a CO2 curing method using cement based materials. In this study, CO2 uptake rate and compressive strength were investigated when CO2 curing method was applied in cement mortar. The CO2 uptake rate was ranged from 10.1% to 11.6% by mass measurement method and from 6.2% to 16.3% by TGA method. This means that mass measurement method by electronic scale is more accurate than TGA method to estimate CO2 uptake rate. The early compressive strength of 1 hour CO2 curing specimens was higher than that of 1 hour atmospheric curing specimens, but lower than that of 5 hours steam curing specimens. 3 days and 7 days compressive strength of specimens by atmospheric curing and steam curing were increased both. But compressive strength of 1 hour CO2 curing specimens was lower than that of other two curing methods.

In this study, manufactured of cement mortar using high early strength cement(10 ~ 50 wt%) and blast furnace slag powder(50 ~ 90 wt%), according to compressive strength and flexural strength of hardened cement mortar. XRD and SEM were evaluated utilizing the initial cement hydration properties.

Experiments were divided into two parts; one part is to understand the basic properties of high flowable VA/VeoVa-modified cement mortar with different polymer cement ratio (P/C) and the weight ratio of fine aggregate to cement (C:F) and the other part is to investigate the effect of surface water spread on the concrete substrate on adhesion in tension. To understand the basic performance, the specimens were prepared with proportionally mixing VA/VeoVa redispersible powder, ordinary portland cement, silica sand, superplasticizer and viscosity enhancing agent. Here, P/C were 10, 20, 30, 50 and 75% and C:F were 1:1 and 1:3. As the change of P/C and C:F unit weight, flow test, crack resistance and adhesion in tension were measured. Three specimens with good adhesion properties were selected among specimens with different P/C and C:F. The effect of surface water evenly sprayed on concrete substrate on adhesive strength is investigated. The results show that surface water on concrete substrate increases the adhesion in tension of high flowable VA/VeoVa-modified cement mortar and additionally improves the flowability compared to the non-sprayed case.

석탄화력 발전의 부산물 중에서 플라이애쉬는 콘크리트 혼화재료로서 많은 공학적 장점을 가지고 있으므로 다양하게 활용되고 있다. 그러나 바텀 애쉬를 포함한 나머지 부산물 등은 주로 매립되어 공학적 활용성이 떨어진다. 본 연구에서는 매립된 부산물인 매립회 (PA: Pond Ash)를 이용하여 시멘트 모르타르를 제조하였으며, 매립회 시멘트 모르타르의 공학적 특성을 평가하였다. 이를 위해 두 매립지로부터 유연탄 및 무연탄 매립회를 채취하였으며, 2가지 물-시멘트 비 (0.385, 0.485)와 3가지 잔골재 치환률 (0%, 30%, 60%)을 고려하여 시공성, 역학성능, 내구성능을 평가하였다. 흡수율이 높은 무연탄 매립회의 경우, 적절한 시공성, 우수한 강도발현과 내구성능을 확보하였는데, 매끈한 표면과 내부의 풍부한 자유수로 인해 조직구조가 치밀한 시멘트 모르타르가 제조되었기 때문이다. 매립회 중에서도 우수한 성능을 가진 무연탄 매립회의 경우 일반 잔골재의 성능을 확보하고 있으므로, 자원의 재활용이 가능하리라 판단된다.