본 논문은 절연유 불포함 재활용 가능 전력케이블 절연체에 동일배열 폴리프로필렌(IPP) 기반 열가소성 폴리올레핀 엘라스토머(TPO) 나노복합체 사용 가능성을 문헌적으로 고찰한 리뷰논문이다. 2010년 IPP 기반 나노복합 유전체는 파워 커패시터 연구에서 유전손실을 제외한 고전압 특성이 크게 향상되었다. IPP 기반 TPO 나노복합체 사용 자동차 외장부품 연구에서는 나노충전제 최대 3 wt% 함유로 전력케이블 절연체의 필수특성인 저온 충격성을 비롯한 기계적 특성향상이 보고 되었다. 특히 유전손실의 원천인 상용화제 사용의 최소화 기술이 보고되어, 3 wt% 이하 나노충전제 함유 IPP 기반 TPO의 전기적 특성조사가 필요하다.

Effects of ethylene-propylene diene monomer (EPDM)/polypropylene (PP), zinc oxide, stearic acid, and clay on the combustive properties based on EDPM/PP were investigated. The EDPM/PP/clay nanocomposites was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). It was found that the specific mass loss rate (SMLR) in the nanocomposites decreased due to the fire resistance compared with unfilled EDPM/PP, while the nanocomposites showed the higher total heat release (THR), higher CO production release, and higher specific extinction area (SEA) than those of virgin EPDM/PP. The stearic acid for softening ruber increased the THR and amount of smoke by itself, combustible.

Compatibility and properties of PP/N66 blends with or without PP-g-MAH as a compatibilizer were investigated by DSC, SEM and universal testing machine. Morphological studies revealed that PP and N66 were incompatible and addition of PP-g-MAH was very effective to enhance the compatibility between PP and N66. The compatibilization effect between N66 and PP-g-MAH was based on the reaction between the amine end group of N66 and anhydride group in PP-g-MAH. The crystallization and melting behavior of PP/N66 blends were investigated and the results of analyses for enthalpy changed were discussed. The Izod impact strength could be improved by optimizing the compatibilizer concentration. Tensile strength, elongation at break, notched Izod impact strength were increased with using compatibilizer, however, both the compatibilized and the noncompatibilizer blends did not show any big difference in the flexural modulus.

In this study, by using oleic acid and polypropylene glycol, good natured antifoaming agent for suitable electronics process under the alkaline conditions were synthesized. For the synthesized mono and diesters, acid value, hydroxyl value was measured, and identified by FT-IR and 1H-NMR spectroscopy. Surface properties such as surface tension, critical micelle concentration(cmc) for diluted aqueous solution was measured, and tested the antifoaming properties according to the difference of alkyl chain length, various concentration, temperature and pH. The surface tension of synthesized antifoaming agent, PPMO(Polypropylene glycol monooleate) was 24.3 dyne/cm, PPDO(Polypropylene glycol dioleate) was 23.7 dyne/cm. By increasing of the alkyl chain length, surface tension was decreased slightly, and showed good antifoaming properties at 0.06 wt% concentration and 50℃, pH 11. These synthesized compounds are expected to apply as a suitable antifoaming agents in the semiconductor and the PCB(Printed Circuit Board) manufacturing process.

The combustion reaction of polypropylene was investigated using a thermogravimetric technique under an air atmosphere condition at several heating rates from 10 to 50℃/min. To obtain information on the kinetic parameters, the dynamic thermogravimetric analysis curve and its derivative were analyzed by a variety of analytical methods such as Kissinger, Friedman, Freeman-Carroll, Chatterjee-Conrad, Ozawa and Coats-Redfern methods. The comparative works for the kinetic results obtained from various methods should be performed to determine the kinetic parameters, because there are tremendous differences in the calculated kinetic parameters depending upon the mathematical method taken in the analysis.

In this paper, internal thermal stresses of the cementitious matrix were evaluated by incorporating polypropylene fibers. By using the temperature heating method specified in KS F 2257-1, the temperatures by a depth were measured. Thermal stress was calculated based on Kodur's thermal stress formula. Different thermal stress behaviors were observed depending on amount of PP fiber. Thas, it will become fundamental data to analyze the thermal stresses behavior of structure members subjected to higher temperature.

The chemical kinetics of the steam reforming of the pyrolysis oil of polypropylene (PP) over a ruthenium-based catalyst has been examined as a function of pyrolysis oil and steam partial pressures at various temperatures. The activation energy of steam reforming over Ru/Al2O3 catalyst is 136 kJ/mol, and the reaction orders of pyrolysis oil and steam are 0.42 and 0.24, respectively. Fitting the experimental data to the Langmuir?Hinshelwood expression shows that the steamreforming reaction probably proceeds via the dissociative adsorption of pyrolysis oil and steam on two different sites.

The mechanical properties of high temperature mortar reinforced by polypropylene fibers were investigated in this paper. Ordinary portland cement was used as basic binder and the effect of the replacement of fly ash, slag, silica fume and graphite for Ordinary portland cement was investigated.

팽이버섯은 타 작물에 비해 수확 후 호흡률이 높아 갈변, 경도감소, 부패 등이 수확 즉시 진행되는 작물이다. 이러한 팽이버섯을 장기간 유통하기 위해 가장 많이 적용되는 방법은 진공 포장하여 저온 저장하는 것이다. 본 연구에서는 팽이버섯의 포장 후 유통기간을 연장에 더욱 적합한 진공필름을 선발하기 위해 20μm두께의 PE+PP, OPP 및 LDPE 필름으로 진공 포장하여 유통온도인 10℃의 저온에서 2주간 저장하였다. 일반적으로 많이 적용되는 LDPE 필름이 갈변, 줄기신장, 호흡률 급변, 조직 연화와 같은 변질이 포장 후 7일 이내로 가장 빠르게 진행되었다. 또한 OPP 필름보다 PE+PP가 수일 더 일찍 해체되기 시작하여 갈변 현상이 먼저 발생하였다. 최종적으로 OPP 필름이 안정된 호흡률과 외부색도, 신장억제 현상이 유지되어 LDPE 필름 포장군의 저장 7일차에 발생된 부패율보다 7일이 지연된 저장 14일차에 나타났다.

This research investigated the pullout behavior of high strength polypropylene fibers. Test results showed that the frictional bond between polypropylene fiber and cement matrix of water to binder ratio 0.23 is 0.2 MPa

본 실험은 인공 배지를 사용하여 채소류의 생육반응을 알아보고 EPP소재 화분에 적합한 가볍고, 보수성이 우수한 배지를 선발하기 위하여 실시하였다. 고형율은 배지A가 27.4%였으며 배지B~E는 10% 정도였다. 공극율은 B~E의 경우 90% 정도로 A의 72.6%보다 유의하게 높았다. A의 함수량은 63.6g 이었으나 B~E는 70g 이상으로 유의하게 높았다. B의 pH는 5.6으로 가장 높았으며 그 다음으로 C, D, E 순이었다. EC의 경우 A가 2.16ds/m 으로 가장 높았으며 B~E의 경우 0.43ds/m 이하로 매우 낮았다. 사용한 배지의 물리성은 변하지 않았다. 엔다이브의 엽수는 D, E에서 19.2장으로 가장 많았다. 상추의 엽장과 엽폭은 B~E에서 각각 19cm, 11cm 정도로 배지 간에 차이는 없었으나 배지 A의 14.7cm, 9.1cm보다 유의하게 증가하였다. 엽수와 근장의 경우 유의차는 없었지만 잎의 크기와 마찬가지로 B~E가 A 보다 많은 것으로 나타났다. 머스타드의 엽장은 B~E가 A에 비해 통계적으로 유의하게 큰 것으로 나타났다. 토마토의 초장은 C~E에서 50cm 정도로 A에 비해 유의하게 생장이 증가하였다. 개화일은 D가 7월 28일로 가장 빨랐으며 그 다음이 E로 7월 30일이었다. 과실수는 유의한 차이는 없었으나 E가 8개로 가장 많았다. 이상의 결과로 보아 본 실험에서 조제한 배지는 기존의 원예상토에 비해 가볍고 보수성이 우수하였다. 또한 식물의 생육과 배지의 물리화학적인 특성을 고려할 때 엔다이브, 상추, 머스타드, 토마토의 재배에 적합한 배지는 E(코코피트:피트모스:수태=2:5:3)로 판단되었다.

폴리비닐알코올 섬유와 폴리에틸렌 섬유 등의 합성 섬유는 고연성 섬유보강 시멘트 복합재료를 제조하는데 성공적으로 사용되고 있다. 폴리프로필렌 섬유 역시 복합재료를 제조하는데 사용되고 있지만, 고연성을 구현하는 목적보다는 고온에 노출된 콘크리트의 내화 성능 향상 목적으로 사용되고 있다. 이 연구에서는 폴리프로필렌 섬유로 보강된 시멘트 복합재료의 성능을 향상시키는 방법에 대하여 논하고자 한다. 폴리프로필렌 섬유보강 시멘트 복합재료의 성능을 평가하기 위하여 5가지 배합을 결정하였다. 1종 보통포틀랜드시멘트 (OPC)와 OPC를 다량 치환한 플라이애시를 결합재로 사용하였고 물-결합재 비는 0.23~0.25이다. 또한 부피비로 2%의 폴리프로필렌 섬유가 사용되었으며, 연성을 향상시킬 목적으로 폴리스틸렌 비드가 사용되었다. 슬럼프, 밀도, 압축강도, 1축 인장 실험을 포함한 일련의 실험을 수행하였으며, 실험결과, 파괴역학, 마이크로역학, 통계이론을 이용하여 폴리프로필렌 섬유보강 시멘트 복합재료의 성능을 향상할 수 있는 것으로 나타났다.

Spite of the several advantages of durability and economic characteristics, such as civil engineering and construction materials, which is widely used as a mortar and concrete, and the tensile strength of fragility and brittleness due to local damage caused. This mechanical shortcoming ensure ductility and brittle complement the various fibers used in concrete and mortar has been developed in order to improve the energy absorption capacity, and increase the use of multiple structures in the form of.Now widely used in the polypropylene fiber polypropylene and affordable, excellent chemical stability and durability, but mainly use the nature of water and mix well so the fluorinated surface hydrophilic polypropylene fibers that can be granted through the processing unit,to overcome this.

폴리프로필렌섬유보강 시멘트 복합재료와 구조용 합성섬유의 부착특성을 평가하였다. 폴리프로필렌섬유는 0.10%, 0.15% 및 0.20%의 체적비로 적용하여 dog-bone 시험을 실시하였다. 구조용 합성섬유와 폴리프로필렌섬유보강 시멘트 복합재료 사이의 부착강도는 폴리프로필렌섬유의 혼입률이 증가할수록 증가하였으나 0.20% 이상이 되면 감소하였다. 또한 폴리프로필렌섬유의 첨가는 계면인성과 마찰저항을 증가시킨다. 인발시험 후 구조용 합성섬유 표면의 미소구조 분석은 폴리프로필렌섬유의 혼입률이 증가할수록 긁힘 현상이 증가하였다.