Spherical Ag powder was prepared in the system of by wet chemical reduction method. The size of Ag powder was increased as the reaction temperature and the concentration of reducing agent was decreased in the constant concentration of dispersion agent. Optimum conditions of producing Ag powder having of D50 was 1M of , 0.5M of , 1.5g of Gelatine in the room temperature.

Powder library of pseudo four components Li-Ni-Co-Ti compounds were prepared for exploring the composition region with the single phase of the layer-type structure by using combinatorial high-throuput preparation system "M-ist Combi" based on electrostatic spray deposition method. The new layer-type compounds were found wider composition region than the previous report. This process is promising way to find multi component functional materials.

Ag powder was prepared from by wet chemical reduction method using various reduction agent system involving , (AgCl) and Ag complex ion aqueous solution. The pure Ag powder could be prepared regardless of reaction system but the particle shape and distribution were affected very much according to the kind of reduction agents and reaction systems. The optimum reaction system for the preparation of the silver powder having the uniform particle shape and size distribution was Ag complex ion aqueous solution-reduction agent system and in particular, and as a reduction agent leaded the more uniform particle shape and size distribution

The bi-materials composed of and its composite reinforced with SiC particles were prepared by ball-milling and subsequent sintering process. The size of powder in Al-Mg/SiCp mixture decreased with increasing ball-milling time, it was saturated above 30 h when the ball and powder was in the ratio of 30 to 1. Both powders mixture and mixture were compacted under a pressure of 350MPa and were bonded by sintering at temperatures ranging from 873K to 1173K for 1-5h. At 873k, the sound bi-mate-rials could not be obtained. In contrast, the bi-materials with the macroscopically well-bonded interface were obtained at higher temperatures than 873K. The length of well-bonded interface became longer with increasing temperature and time, indicating the improved contact in the interface between unreinforced Al-Mg part and Al-Mg/SiCp composite part. The relative density in the bi-materials increased as the sintering temperature and time increased, and the bi-materials sintered at 1173K for 5h showed the highest density.

An aqueous solution of a commercial liquid synthetic detergent for kitchen use was photodecomposed in the presence of titanium dioxides powder under an atmosphere of air at room temperature. Titanium dioxides were prepared by sol-gel method from titanium iso-propoxide at different R ratio(H2O/titanium iso-propoxide) and calcined at 500℃. All titanium dioxides were characterized by XRD, BET surface area analyzer and UV-VIS spectrometer. The surface area of titanium dioxides prepared at R ratio=6 appeared higher volume about 20% than commercial TiO2 catalysts. XRD patterns of titania particles were observed mixing phase together with rutile and anatase type. Titanium dioxides prepared by sol-gel method show higher activity about 6% than commercial TiO2 catalysts on the photocatalytic degradation of a commercial liquid synthetic detergent for kitchen. The concentration of the detergent decreased to about 90% of its initial value at illumination times of 2 hour. Illumination for 30 minutes decreased the concentration of oxygen to about one-fifth of the initial value.

Submicron nickel powders were prepared from aqueous solution under hydrothermal condition. The experimental conditions including the types of protective agents, concentration of the solution and the pH were studied in detail. Starting concentration of nickel ion is a dominant factor affecting particle size. It was shown that the subsequent addition of Poly Vinyl Pyrrolidone(PVP) and Sodium Dodecyle Sulfate(SDS) can help to disperse the nickel powder. X-ray diffraction and SEM were employed to characterize the products.

Alkaline powder cleaning agents (APCAs) were prepared by blending of Na2CO3 tetrasodium pyrophosphate (TSPP). sodium orthosilicate (Na-OSi), Na-dioctyl sulfosuccinate (303C), Demol C, and MJU-100A (100A). The physical properties of APCAs tested with steel specimen showed the following results. The cleaning powers of APCA-6 (Na2CO3 250g/TSPP 70g/Na-OSi 40g/303C 60g/Demol C 50g/100A 30g mixture) for press-rust preventing oil was 97% and 98% degreasing at 2wt%, 70℃ and 90℃, respectively; for Quenching oil, the cleaning power of APCA-6 was 95% degreasing at 2wt% and 70℃. From the results, it was ascertained that APCA-6 exhibited a good cleaning power. Also low foaming power tests proved that the APCA-6 maintained good defoaming effect.