In this study, Rebar of SD500, SD600 is applied to the designed or constructed in domestic underground parking. Analyzed the variation of the rebar according to the strength of the rebar and the construction cost of the change. Most of underground parking appear reduction of Rebar ratio. In this case, the load acting on the underground parking garage is large. So, Rebar placing is dominated by element's stress. Therefore, Large amounts material of slabs, beams and foundations are reduced. In case of columns and wall, Ratio of Material reduction is less than former. Because Splice and Anchorage of rebar amounts are increased and Hoop and horizontal rebar amounts are fixed. Percentage of rebar of the column and wall are 15%. So, Showed a less impact on the reduction of total material.

In this study, prediction of later-age compressive strength of ultra-high strength concrete, based on the accelerated strength of concrete cured in hot water was investigated. Comparing other acceleration method, hot water curing method is relatively easy and intuitive to use in the real construction site. The amount of time for evaluation of the concrete strength using the hot water curing method in KS and JIS is too long to predict the strength of the ultra-high strength concrete that are used in the tall building structure. For that reason, curing temperature of 40, 50, 60℃ 3 levels were examined to shorten the amount of time for the evaluation of the strength. When curing in warm water, different strength characteristics are verified from the experiment. In case of F3 substituting 30% fly ash in combination, because of the curing temperature sensitivity of fly ash, differences of strength expression velocity was verified according to the curing temperature at the same age. In case of B4 substituting 40% ground granulated blast furnace slag, there were no big strength expression velocity differences of the specimen cured in 3 different level of curing temperature(40, 50, 60℃). The results show reliable accuracy by regression relation between 28day strength cured by standard curing method and accelerated strength of concrete cured in warm water.(y=1x-0.0002 R2=0.9866) As a result, the feasibility of 3day-prediction was confirmed using warm water curing method with accelerated strength of concrete cured for three days in warm water.

Strength bar has merits in workability improvement, construction time shortening and connection details to be easy. But, lap splice length tends to be longer. In this study, high strength threaded bar will be reviewed whether it is appropriate in domestic standards by KCI concrete structural criteria and propose the mechanical splice.

이 연구에서는 프리스트레싱용 고강도 강연선의 정착장치 중 강연선을 직접 정착하는 앵커헤드(anchor head)에 대해 거 동특성을 분석하고, 앵커헤드의 제원을 결정하는 단계에 있어서 해석적 검토에 요구되는 프로세스에 대해 정립하였다. 앵 커헤드는 쐐기와의 접촉(contact)을 통해 강연선으로부터의 힘이 전달되고 거동변화에 따라 접촉상태 또한 변하게 된다. 이 를 고려한 상세 거동분석을 위해 쐐기와 헤드 사이의 접촉(contact)조건을 설정하였으며, 앵커헤드의 비선형 재료모델을 적 용하여 기하 및 재료 비선형성을 고려한 구조해석을 수행하였다. 해석결과로부터 다음의 결과를 얻을 수 있었다. 앵커헤드 의 거동은 앵커헤드와 쐐기 간의 상호거동에 크게 영향을 받기 때문에 초기 설계단계부터 상대 영향을 고려해야 한다. 쐐 기홀(wedge hole)의 배치는 층배열(layered) 보다는 원형배열(circular)이 보다 응력분배에 효과적이고, 쐐기홀의 간격을 증 가시키고 헤드 하면 구멍의 크기를 줄여 구멍사이 강재의 두께를 다소 늘이는 것이 구조거동에 효과적이다.

광펄스 기술은 광범위한 파장의 강한 빛을 짧은 시간동안 조사하여 미생물을 사멸시킴으로서 식품을 살균하는 새로운 비가열 살균 기술로서 주목받고 있다. 본 연구에서는 막걸리를 회분식 방법으로 광펄스 처리하여 살균 효과를 살펴보고, 저장 중의 품질 변화에 대하여 살펴보았다. 광펄스 처리 후 막걸리는 처리하지 않은 막걸리에 비해 2 log cycle 정도의 생균수의 감소를 보였으며, 균수는 1.8-2.7×104 CFU/mL 정도였다. 저장 기간 중 생균수는 4oC에서는 처리구와 무처리구 모두 효모, 세균 및 젖산균의 수가 약간 감소하는 경향을 보였으며, 저장 후 4주간 큰 변화가 없었다. 그러나 30oC에서는 광펄스 처리하지 않은 막걸리의 경우 106정도 수준에서 7일간 일정하게 유지되었으며, 처리구는 2일 정도 후에 무처리구와 비슷한 생균수를 나타내었다. 저장기간 중 품질 변화를 보면 pH는 저장 온도와 상관없이 무처리구와 처리구 모두 약간 감소하는 경향을 보였으나 적정산도는 4oC에서는 일정하게 유지가 되었으나 30oC에서는 무처리구의 경우 2일 후부터 급격한 증가를 보였지만 처리한 시료의 경우에는 저장 6일 후까지 큰 증가를 보이지 않았다. 그리고 환원당의 경우에는 저장 온도에 따라 차이는 있으나 처리구와 무처리구 모두 저장기간동안 지속적으로 감소하였다. 이상의 결과로 보아 막걸리를 적절한 조건으로 광펄스 처리하였을 경우 품질변화를 최소화하고 생균수와 적정산도의 증가를 지연시킬 수 있을 것으로 생각된다.

Research into the development of high strength (1 GPa) and superior formability, such as total elongation (10%), and stretch-flangeability (50%) in hot-rolled steel was conducted with a thermomechanically controlled hot-rolling process. To improve the overall mechanical properties simultaneously, low-carbon steel using precipitation hardening of Ti-Nb-V multimicroalloying elements was employed. And, ideal microstructural characteristics for the realization of balanced mechanical properties were determined using SEM, EBSD, and TEM analyses. The developed steel, 0.06C-2.0Mn-0.5Cr-0.2(Ti + Nb + V), consisted of ferrite as the matrix phase and second phase of granular bainite with fine carbides (20-50 nm) in both phases. The significant factor of the microstructural characteristics that affect stretch-flangeability was found to be the microstructural homogeneity. The microstructural homogeneity, manifest in such characteristics as low localization of plastic strain and internally stored energy, was identified by grain average misorientation method, analyzed by electron backscattered diffraction (EBSD) and hardness deviation between the phases. In summar, a hot-rolled steel having a composition 0.06C-2.0Mn-0.5Cr-0.2(Ti + Nb + V) demonstrated a tensile strength of 998 MPa, a total elongation of 19%, and a hole expansion ratio of 65%. The most important factors to satisfy the mechanical property were the presence of fine carbides and the microstructural homogeneity, which provided low hardness deviation between the phases.

The flat type automotive cross members with high strength steel have advantages in light weight and fewer parts compared to the hump type cross members. But the complex part shape of the flat type cross member and the poor formability of high strength steel make it difficult to form the parts without forming defects, such as splits and wrinkles. The purpose of this study is to develop the flat type automotive cross member with high strength steel. For that purpose, drawing processes are evaluated using PAM-STAMPTM and proper draw die and blank designs are proposed. Using the proposed die and blank design, the flat type upper and lower cross member could be formed successfully without forming defects.

In case of general concrete, autogenous shrinkage is about 10% of the drying shrinkage. Therefore it was not considered significant to be a subject matter about managing the crack control and design. It was reported that cracks can be generated from the autogenous shrinkage. Because of the low W/B rate and the high unit binder of the high strength concrete. In this study, autogenous shrinkage and drying shrinkage are examined which is the main reason of the cracks of the high strength concrete based on the previous studies. Comparing the data from this study and previous studies, we developed the shrinkage reduced concrete using shrinkage reducing agent. The purpose of this study is to provide the data for reducing and managing the column shortening of the high strength concrete structures.

In this study, prediction of later-age compressive strength of ultra-high strength concrete, based on the accelerated strength of concrete cured in hot water was investigated. Comparing other acceleration method, hot water curing method is relatively easy and intuitive to use in the real construction site. The amount of time for evaluation of the concrete strength using the hot water curing method in KS and JIS is too long to predict the strength of the ultra-high strength concrete that are used in the tall building structure. For that reason, curing temperature of 40, 50, 60˚c 3 levels were examined to shorten the amount of time for the evaluation of the strength. As a result, the feasibility of the three days hot water curing method was confirmed.

The shock absorber base assembly is one of the parts in the shock absorber equipment that controls the vehicle movement. It absorbs the shock and vibration to guarantee riding stability and comfort. It demands strength, reliability and strict airtightness

화학적 안정성이 양호하고, 제막조건이 온화한 재료인 poly(vinylidene fluoride) (PVDF)를 주재료로 사용하여 용매, 첨가제, 혼합고분자 및 제막조건의 변화에 따른 고강도 친수성 정밀여파(microfiltration, MF) 중공사 분리막의 실험에 의해 고찰하였다. 제조된 MF 중공사막의 막성능은 평균 공경 0.3 μm, 인장강도 42kgf/㎠, 순수 투과유량은 600 LMH을 얻었다. 제막과정에서 다양한 첨가제의 막성능을 검토한 결과는 순수투과유량과 제거율에 상당한 영향을 미치고 있음을 알 수 있었다. MF막의 친수성을 개선하기 위해 소수성 PVDF와 상호 용해성 이 좋은 친수성 poly(methyl methacrylate) (PMMA)를 혼합하여 투과성능과 제거율을 개선한 우수한 친수성 MF막을 제조할 수 있었다.

High-performance concrete (HPC) is a new terminology used in concrete construction industry. Several studies have shown that concrete strength development is determined not only by the water-to-cement ratio but also influenced by the content of other conc

Recently, practical application of high tension bar is attempted. The main object of using high tension bar is strengthening of material property and decreasing of steel amount. If using high tension bar which is not a definite yield strength，according to strain ratio of high tension bar tensile and compressive dominate mode ciearly, there being a possibility dividing becoming difficult. Specially, Providing steel ratio of balanced destruction is very difficult. In this study, high tension bar to apply to flexural member and the behavior experiment bending after one, will consider high tension bar the application possible standard of existing.

High-performance concrete(HPC) is a new terminology used in concrete construction industry. Several studies have shown that concrete strength development is determined not only by the water-to-cement ratio but also influenced by the content of other concrete ingredients. HPC is a highly complex material, which makes modeling its behavior a very difficult task. This paper aimed at demonstrating the possibilities of adapting artificial neural network (ANN) to predict the comprresive strength of HPC. Mahalanobis Distance(MD) outlier detection method used for the purpose increase prediction ability of ANN. The detailed procedure of calculating Mahalanobis Distance (MD) is described. The effects of outlier compared with before and after artificial neural network training. MD outlier detection method successfully removed existence of outlier and improved the neural network training and prediction perfomance.

Shock absorber base assembly is one of the parts in shock absorber equipment which control the vehicle movement and absorb the shock and vibration to realize the stability and the comfort for the riding. This part demand hardness, reliance and rigorous density of the welded section because it is a resist pressure container which needs durability by being filled with gas and oil. However, the present engineering needs much time, high cost and shows low production rate due to the eight processes which are spot welding, reinforcement welding(MAG), prior process of base cap and tube for the precision and pressing etc. In this study we will analyze the problem of the processes for the base assembly and suggest an engineering to improve the problem innovatively using frictional welding. As the result of experiment by frictional welding using frictional heat, its hardness for the joining section became high and its precision showed excellence. Therefore we can expect the curtailment for the welding processes, the reduction of cost and excellent joining function.

Existing non-destructive test for evaluation of concrete compressive strength may show deviation in results analysis due to deterioration of precision by strength calibration and dry or humid condition by age, so there needs be testing method to determine long term structural internal force by collecting specimen with no damage of structure and measuring compressive strength through destruction test. This research applied to mock-up member the compressive strength evaluation method using joint separation mold that can plan and produce specimen cured in the same composition environment as concrete structure by attaching arbitrary(joint separation) to the form before concrete piling, and as a result, the management specimen was contrary to the hydration temperature of the member or was affected by external atmospheric temperature, however the joint separation specimen connected to structure and managed in the same environment showed a temperature curve similar to the member and decrease in temperature difference. Additionally, from initial age, with the compressive strength of joint separation specimen most similar to core strength，stable compressive strength can be evaluated up to design criteria strength 100MPa, so the method is proposed as an evaluation technique that can confirm highly reliable concrete quality.

As architectures have recently become high-risers and mega-structured, stable high strength products have been ensured. Accordingly, use of precast concrete accouplement has been increased in order to facilitate air compression and rationalize construction. Since external rising by the steam heating and internal rising by the accumulation of cement hydration heat for the temperature of members, precast concrete members with large cross-section used for high-rise mega-structure's columns and beams may exhibit different temperature history compared to the precast concrete members for wall and sub-floor with relatively small cross-sections. Therefore, this study aims to elucidate the characteristics of temperature history of mass concrete members cast with high-strength concrete for precast concrete application. In this study, large cross-sectional precast concrete mock-up, unit cement quantity, and temperature histories in manufacturing precast concrete member under different curing condition were inclusively investigated.

Recently, as architectural concrete structures become high-rise and megastructured, concrete become high-strengthened and, by ensuring products of more stability, and rationalization of construction are required.large cross-sectional precast concrete members such as columns show large temperature increase in manufacturing process not only by external heating but also by concrete itself's hydration heating. Therefore, it is expected that specimen for management to predict strength and compression strength of precast concrete member shows different strength characteristics. Conceming this, in order to suggest strength characteristics of high strength mass concrete suitable for precast concrete application, this study comprises the inclusive investigations on the relations between core strength and the strength characteristics per member cross-section dimensional value and per water-bonding material ratio value.

본 연구에서는 고강도 고내구성 시멘트콘크리트 포장을 위하여 도출된 배합 콘크리트의 굳지않은 콘크리트 특성, 강도발현 특성, 염소이온의 투수특성 및 동결-융해에 대한 저항성 등의 역학적 내구적 특성을 분석하였다. 제시된 배합의 목표스럼프와 공기량은 적절한 혼화제의 사용으로 확보가 가능하나, 혼화제의 적정사용량은 충분한 현장배합실험을 통하여 구하여야 할 것이다. 단위시멘트량을 증가한 경우 일반적으로 강도가 증가하였으며 특히 재령 28일 이후의 강도가 지속적으로 증가하는 양상을 나타내었다. 휨강도는 그 특성상 단위시멘트량을 증가하더라도 뚜렷한 효과는 나타나지 않았다. 염소이온 침투저항성도 단위시멘트량보다는 재령에 따른 영향을 더 크게 받는 것으로 나타났다. 공기량에 가장 많은 영향을 받는 동결-융해 저항성은 각 실험변수에 대한 시험체를 공기량이 3% 이하 및 이상인 경우에 대하여 그리고 동결시 수돗물을 사용한 경우와 현장의 열악한 환경을 모사하기 위하여 4%의 NaCl 용액을 사용한 경우로 구분하여 실시하였다. 공기량에 상관없이 수돗물을 사용한 경우에는 동결-융해반복회수가 300회까지 상대동탄성계수나 표면의 손상이 거의 발생하지 않았다. 4% NaCl 용액을 사용한 경우에는 단위시멘트량이 현재의 한국도로공사의 표준배합인 경우 손상이 발생하였으며, 단위시멘트량이 동결-융해 저항성에 미치는 영향이 큰 것으로 나타났다. 따라서, 동결-융해에 대한 저항성을 충분히 확보하는 고내구성의 시멘트콘크리트 포장을 위해서는 단위시멘트량을 현재의 수준보다 증가시키는 것이 유리한 것으로 판단되며, 실험결과로부터 이러한 요구성능을 발휘하기 위해서는 단위시멘트량을 400kg/m3 이상으로 할 것을 권장한다.

국내에서 시멘트콘크리트 포장이 차지하는 비율이 증가하는 수준에 비하여 이의 기술적인 발전은 상대적으로 뒤쳐져 있다고 할 수 있다. 또한, 사용기간의 증가와 함께 여러 가지 기술적인 문제점도 부각되고 있는 실정이다. 이에 본 연구에서는 외국의 콘크리트포장 배합의 특성을 분석하고 이를 기초로 한국의 실정에 부합하는 장수명의 고강고 고내구성의 콘크리트 포장의 최적배합을 도출하고자 하였다. 단위시멘트량, 잔골재율(S/a), 그리고 물-시멘트(W/C)비 등을 변수로 하여 배합에 대한 실험적 연구를 수행하였다. 장기적인 공용수명을 확보하고 고강도 고내구성의 포장을 위하여 우선적으로 단위시멘트량을 375kg/m3, 400kg/m3, 425kg/m3 수준으로 증가시킬 것을 권장한다. 또한, 최적배합표는 포장타설 장비를 활용하여 포설하므로 슬럼프 40mm로 결정하였고, 동결융해 방지를 위하여 공기량을 5%로 결정하였다. 또한 시공 시 재료 수급의 원활함을 위하여 굵은골재 최대 치수를 25mm로 결정하였다. 도로의 장수명을 위한 고강도 배합을 위해 낮은 W/C비와 단위시멘트량의 증가가 요구되는데, 예비실험 결과 공기연행제와 폴리카본산고성능 AE감수제를 사용하여 W/C비를 0.4까지 낮추어도 증가된 단위시멘트량에 대하여 충분히 목표 슬럼프를 가지는 배합이 가능한 것으로 나타났다. 예비 실험 결과 S/a를 0.34까지 낮추어도 골재의 분리 등 문제를 보이지 않고 충분히 배합이 가능하였으며, 이는 단위 시멘트페이스트 양의 증가로 인한 점착력 증가와 워커빌리티의 향상에 의한 것으로 판단된다.