The fabrication of Fe alloy-40 wt.%TiC composite materials using spark plasma sintering process after ball-milling was studied. Raw powders to fabricate Fe alloy-TiC composite were Fe alloy, and activated carbon. Fe alloy powder was Distaloy AE (4%Ni-1%Cu-0.5%Mo-0.01%C-bal.%Fe) made by Hoeganes company with better toughness and lower melting point. These powders were ball-milled in horizontal attrition ball mill at a ball-to-powder weight ratio of 30 : 1. After that, these mixture powders were sintered by using spark plasma sintering apparatus for 5 min at in vacuum atmosphere under torr. DistaloyAE-40 wt.%TiC composite was directly synthesized by dehydrogenation and carburization reaction during sintering process. The phase transformation of as-milled powders and sintered materials was confirmed using X-ray diffraction (XRD) and transmission electron microscope (TEM). The density and harness materials was measured in order to confirm the densification behavior. In case of DistaloyAE-40 wt.%TiC composite retained for 5 min at , it has the relative density of about 96% through the influence of rapid densification and fine TiC particle reinforced Fe-based composites materials.

Bulk metallic glass (BMG) composite was fabricated by consolidation of milled metallic glass composite powders. The metallic glass composite powder was synthesized by a controlled milling process using the Cu-based metallic glass powder blended with 30 vol% Zr-based metallic glass powders. The milled composite powders showed a layered structure with three metallic phases, which is formed as a result of mechanical milling. By spark plasma sintering of milled metallic glass powders in the supercooled liquid region, a fully dense BMG composite was successfully synthesized.

Using Spark Plasma Sintering process (SPS), consolidation behavior of gas atomized alloys were investigated via examining the microstructure and evaluating the mechanical properties. In the atomized ahoy powders, fine particles were homogeneously distributed in the matrix. The phase distribution was maintained even after SPS at 723 K, although particles were newly precipitated by consolidating at 748 K. The density of the consolidated bulk Mg-Zn-Y alloy was . The ultimate tensile strength (UTS) and elongation were varied with the consolidation temperature.

Using spark plasma sintering process (SPS), Ti-6Al-4V alloy powders were successfully consolidated without any contamination happened due to reaction between the alloy powders and graphite mold. Variation of microstructure and mechanical properties were investigated as a function of SPS temperature and time. Compared with hot isostatic pressing (HIP), the sintering time and temperature could be lowered to be 10 min. and , respectively. At the SPS condition, UTS and elongation were about 890 MPa and 24%, respectively. Considering the density of 98.5% and elongation of 24%, further improving the tensile strength would obtain by increasing the SPS pressure.

The microstructure and mechanical properties of hot-pressed composites with a different sintering temperature have been studied. The size of matrix grain and Cu dispersion in composites increased with increase in sintering temperature. Fracture toughness of the composite sintered at high temperature exhibited an enhanced value. The toughness increase was explained by the thermal residual stress, crack bridging and crack branching by the formation of microcrack. The nanocomposite, hot-pressed at , showed the maximum fracture strength of 707 MPa. The strengthening was mainly attributed to the refinement of matrix grains and the increased toughness.

Ni based() bulk metallic glass(BMG) powders were produced by a gas atomization process, and ductile Cu powders were mixed using a spray drying process. The Ni-based amorphous powder and Cu mixed Ni composite powders were compacted by a spark plasma sintering (SPS) processes into cylindrical shape. The relative density varied with the used SPS mold materials such as graphite, hardened steel and WC-Co hard metal. The relative density increased from 87% to 98% when the sintering temperature increased up to in the WC-Co hard metal mold.

The microstructure and mechanical property of hot-pressed nanocomposites with a different temperature for atmosphere changing from to Ar have been studied. When the atmosphere changed from to Ar gas at , the hot-pressed composite was characterized by inhomogeneous microstructure and low fracture strength. On the contrary, when the atmosphere changed at a lower temperature of , a more homogeneous microstructure and higher fracture strength was observed.

Refractory materials, such as W and Mo, are very useful elements for use in high-temperature applications. But it is not easy to fabricat pure W and Mo with very high density and retaining very fine grain size because of their high melting point. In this paper, a newly developed method named as resistance sintering under ultra high pressure was use to fabricate pure fine-grained W and Mo. The microstructure was analysis by SEM. The sintering mechanism is primary analyzed. Basic physical property of these sintered pure W and Mo, such as hardness, bend strength, are tested.

High-purity and super-hard nano-polycrystalline diamond has been successfully synthesized by direct conversion from high-purity graphite under static pressures above 15 GPa and temperatures above . This paper describes research findings on the formation mechanism of nano-structure and on the contributing factor leading to high hardness.

Considering the idea that some properties, especially the mechanical properties of at ambient temperature can be improved by adding of some substitutional/interstitial elements, our goal was to obtain these materials starting from mechano-composites powders. In this aim, using mechanical alloying techniques three type of mechano-composite powders starting from elemental powders were obtained. Then, by reactive sintering in argon atmosphere at temperature over , alloyed materials were realized. This paper presents our research results regarding the microstructural aspects and phase formation in obtained materials.

The shrinkage variation of Low Temperature Cofired Ceramics(LTCC) limits the size of the substrates that impose limitations on embedded passive components. This paper focuses on the method of minimizing or controlling planar shrinkage and reducing distortion during firing. The laminated sheets of alumina and glass were sintered at varying temperature, and depending on the amount of the glass ceramics. When the sintered of multi-layer structure with , the glass infiltrated entirely into layer at the temperature of about or higher.