A laser glass cutting system using a femto-second laser was evaluated for Flat Panel Display (FPD) glass. A theoretical analysis of the ablation threshold and depth is described using an explicit analytic form. Experiments for clean and deep grooves were performed using a 3W femto-second laser, and the relationships between the input energy and the scribing depth as well as the threshold energy are presented. Mechanical breaking after the scribing process was carried out and the results are compared with a theoretical method. It was found that a two-sided LCD panel glass can be cut clearly using the laser cutting method. The methodology was found to be very effective as a mass-production cutting system.

김제시 만경읍에 위치한 5,000㎡ 규모의 토마토 유리 온실에서 담배가루이의 분포 특성을 조사하였다. 유리온실을 66개(11×6)의 구획으로 나누고 구획 별로 토마토 한 주를 임의로 선택한 다음, 각 결과소지 바로 위에 있는 우상복엽에서 한 잎을 절취하여 현미경을 이용하여 검경하였다. 선택된 잎은 상부에서부터 차례로 번호를 부여하였다. 대체로 1번 잎은 신초 부위, 2번 잎은 한 개 이상의 꽃이 핀 결과소지의 바로 위쪽, 3번 잎은 꽃이 모두 만개하였거나 한 개 이상의 과실이 형성되기 시작한 결과소지 바로 위쪽에서 선택되었으며, 주당 평균 7개의 잎을 조사하였다. 조사기간은 2008년 1월 초부터 4월 초까지이며, 1~2주 간격으로 총 10회에 걸친 조사가 이루어졌다. 조사 기간 동안 담배가루이의 밀도가 기하급수적으로 증가하였기 때문에, 6회 조사 직후인 3월초에 스피로메시펜을 처리하여 방제하였다. 약제처리 직후 담배가루이 알의 밀도는 급격하게 감소하였지만, 약충의 밀도는 일시적인 증가추세를 유지하였다. 담배가루이의 토마토 주내 분포는 잘 분화된 층위구조를 보였는데, 알은 3번 잎에서 가장 많았고, 1령 약충은 4~5번 잎에서 가장 많았으며, 나머지 약충과 번데기ㆍ탈피각은 6~7번 잎에서 가장 많았다. 온실 전체의 담배가루이 밀도 분포 또한 안정적인 구조를 유지하였는데, 조사를 시작할 때 담배가루이 밀도가 높았던 곳이 조사 종료시점까지도 높은 밀도를 유지하였다. 한편 담배가루이는 이웃한 열로 확산되어 옮겨가기 보다는 같은 열의 작업경로를 따라 확산되는 경향을 보였다.

막 구조는 형태의 다양성, 막의 가벼움과 내구성, 투광성 및 균질성 때문에 현대 건축물에 다용하게 사용되어 새로운 건축세계를 열어가고 있다. 본 논문은 대공간 건축 구조물에 주로 사용되는 유리섬유 막 재료의 역학적 특성에 대한 연구이다. 현재 주로 사용되는 건축용 막 재료의 종류에는 PVC, PVF, PVDF, PTFE, ETFE 막재들이 있다. 본 연구에서는 이러한 건축용 막재료에 대한 역학적 시험 방법을 정립하고, PTFE 코팅 유리섬유 막재에 대한 인장강도, 인열강도 및 반복하중 시험 등을 실시하여 건축용 막 재료의 역학적 특성을 분석하고자 한다.

전통적인 유리병 부식 공정에서는 공정 투입 전 유리병을 홀더에 장착하는 수작업으로 인해 작업자들의 노동강도가 매우 크고, 부식에 사용되는 불산의 증발로 인한 위험 요소가 매우 크게 나타나고 있다. 본 연구에서는 기존의 병부식 공정을 자동화해주는 로터리 방식 부식 장비와 병을 홀더플레이트에 자동으로 장입하고 부식 후에 탈거하는 메커니즘 개발하고 시제품을 제작하여 이의 성능과 효과를 평가하였다. 그 결과로 노동집약적인 병 장입작업을 자동화하여 힘든 장입작업을 하던 작업자의 노동강도를 덜어줄 수 있었고, 불산으로부터 작업자를 이격시켜서 잠재적인 산업재해를 예방하여 작업환경을 개선하였다.

일반적으로 순환유동층 열교환기에서 최적의 운전과 설계에 대한 지식은 아직 잘 알려져 있지 않다. 입자 유동에 관한 기초적 지식이 부족하기 순환유동층 열교환기를 최적 설계하는 데에는 아직 제한적이다. 그러므로 본 연구에서는 순환하는 물속에 고체입자(유리)가 유동하는 수평 원형관에서 압력강하와 마찰계수에 대해 실험적으로 측정한다. 고체입자의 직경은 3 mm와 4 mm를 각각 취급하였고 레이놀즈수의 범위는 10,000에서 45,000이었다. 연구 결과 4 mm 직경의 입자가 3 mm의 입자보다 마찰계수가 더 컸다. 그리고 고체입자의 농도가 낮은 경우에서는 마찰계수는 고체입자의 농도보다 유체속도에 의해서 더 영향이 컸다. 그러나 입자의 농도가 큰 운전조건에서는 고체입자의 농도도 마찰계수에 큰 영향을 주었다.

Pretreatment of eliminating FFA is needed to make biodiesel from animal fat recovered from leather wastes because its acid value is high. This study was carried out to investigate the influence of 4 different pretreatment methods, which are heterogeneous catalyst method, ion exchange resin method, low pressure.high temperature method, and alkali method on the eliminating FFA and fatty acid composition. The results showed that the rate of eliminating FFA increased in the order of alkali method > catalyst method > low pressure high temperature method > ion exchange method. In the case of pretreatment of alkali method using NaOH, the rate of eliminating FFA appeared more than 86% regardless of acid value. Therefore, it was considered that alkali method using NaOH was the most effective in the view of economical and productive aspects, taking it into account that the acid value of animal fat recovered from fleshing scrap generated during leather making processes was 7 to 8.

The purpose of this study was to compare the efficiency of slow freezing with that of vitrification method for the cryopreservation of human embryos. Human embryos were derived from in vitro fertilization (IVF) or intracytoplasmic sperm injection (ICSI) and the mixed solution of propanedial (1.5, 1.0, 0.5M PROH) and sucrose (0.1M), ethylene glycol (7.5, 15%), dimethyl sulfoxide (7.5, 15% DMSO), sucrose (0.5, 1.0M) and SPS (Serum Protein Substitute) was used for a cryoprotectant for slow freezing and vitrification solution, respectively. Rates of recovery after thawing, morphological normality, post-thaw viability, arrest, morphological abnormality and preimplantation development were compared between two protocols. After freezing-thawing, recovery and survial rate of slow freezing was (88.6% and 73.4%), whereas vitrification was (99.2% and 96.2%) (p<0.05). The arrest rate of slow freezing was significantly lower compared with those of vitrification(8.7% vs 29.9%) (p<0.05). Preimplantation development to the 2-cell (83.8% vs 67.7%), 4-cell (69.0% vs 47.2%) and 8-cell (62.4% vs 37.8%) stages 24, 48 and 72 h after thawing, respectively, were higher in the slow freezing than the vitrification. After slow freezing and vitrification of human embryo at 2-8cell stage, the rate of recovery rate, survival rate and partial damage rate were 92.0% vs 100%, 80.4% vs 96.2% and 52.2% vs 19.0%, respectively. And partial damage rate was significantly lower than those of slow freezing method (p<0.05). These results demonstrate that a slow freezing using PROH is more efficient than a vitrification for cryopreserving the human zygotes, although the vitrification yielded better recovery, survival and partial damage of frozen-thawed 2-8 cell stage embryos than slow freezing method.

The effects of fillers on the mechanical and thermal properties of glass/novolac composites have been studied. The matrix polymer and reinforcement were novolac type phenolic resin and milled glass fiber, respectively. Three different fillers, such as calcium carbonate, aluminum oxide, and wood powder were used for glass fiber reinforced plastic(GFRP) manufacture. Gravity, moisture content, tensile and flexural strength were measured to analyze the mechanical properties of GFRP and the final composites was burned in the electronic furnace at 1000℃ to confirm thermal properties GFRP containing aluminium oxide shows the highest thermal stability with 32% of weight loss at 1000℃ for one hour. GFRP containing calcium carbonate shows the maximum flexural strength (146 MPa), but that containing wood powder dose the highest tensile strength (65 MPa). Conclusively, we found that the characteristics of final composites strongly depend on several factors, such as types of materials, contents and chemical affinity of fillers. Therefore, it is very important to set up the combination of fillers for GFRP manufacturing to improve both mechanical and thermal properties at the same time.

초 록 유리화공정 고온영역에서의 방사성 배기체 유동해석을 해석하기 위하여 상용 수치해석 범용 툴인 FLUENT를 이용하여 적용성을 검토하여 보았다. 수치해석을 통하여 유리화공정 원형설비에 영향을 미치는 인자를 파악하였는데, 저온용응로, 배관냉각기 및 고온필터 등의 세 단계로 나누어 해석을 수행하였다. 저온용융로의 경우 폐기물 처리용량에 따른 해석과 저온용융로 내부 과잉산소 공급 비에 따른 연소지연 가능성에 대한 수치해석을 수행하였다. 배관냉각기의 경우에는 각종 수치 모델 및 외벽 열전달계수를 확보하였으며 또한 방사성 핵종의 거동을 모사할 수 있는 수치적 기업을 검토하였다. 이러한 방법론을 적용하여 핵종의 열교환기 내부에서의 응고 특성에 대하여 고찰하였다. 수평 유입형식의 인입관이 있는 일반적인 형상과 유입구가 필터 내부에 수직으로 있는 고온필터의 수치해석을 통하여 인입관의 위치에 따른 고온필터의 작동 특성을 비교하였다. Appropriate numerical models for the simulation of off-gas flow in hot area of the vitrification plant have been developed in this study. The models have been applied to analyze the effect of design parameters of real plant and numerical analyses have been performed for CCM(Cold Crucible Melter), pipe cooler and HTF(High Temperature Filter). At first, the effect of excess oxygen and the ratio of oxygen distribution on combustion characteristics in the CCM has been studied. Next, solidification behavior of radio nuclide in the pipe cooler has been numerically modeled and scrutinized. Finally, flow pattern in accordance with the location of off-gas entrance of the HTF has been compared.

  The powder blasting process has become an important machining technique for the cost effective fabrication of micro devices. This process is similar to sand blasting, and effectively removes hard and brittle materials. A large number of investigations o