우리는 마이카, boron nitride, bismuthoxychloride와 같은 판상 분체에 ZnO 나노입자를 코팅한 고 기능성 무기 분체를 합성하였다. 본 실험에서 우리는 수열침전법을 이용하여 합성 분체를 합성하였다. 출발물질은 ZnCl2를 사용하였고 침전제로는 hexamethylenetetramine(HMT)와 urea를 사용하였다. 본 실험의 반응변수로는 출발물질의 농도, 침전제 및 반응온도를 변화시켜 실험하였다. 합성물의 형태, 결정성 및 UV-차단능은FE-SEM, XRD, FT-IR, TGA-DTA, in vitro SPF 테스트를 활용해 분석하였다. 본 실험의 결과, 나토입자 크기를 갖는 ZnO는 동일한 최적의 합성조건하에서 다양한 판상 분체의 종류에 관계없이 균일하게 코팅되었다.

To co-fire with commercial LTCC (Low Temperature Co-fired Ceramic) materials at , different contents of were added to the (BZN) ceramics. According to the test results, the cubic phase of BZN was transformed into orthorhombic in all the test materials. phase was formed in test materials with of addition. The phase transformation of cubic BZN was controlled during the synthesis process with excess ZnO content. The Cubic and orthorhombic phases of BZN could coexist and be sintered densely at .

Pulsed Current Sintering (PCS) process possesses some problems that need to be resolved. We, therefore aims at understanding phenomena of PCS process by presenting some basic data on in situ sintering behavior of PCS. Special graphite mold equipped with thermo couple and electrodes were designed to measure the temperature, electric current and voltage inside the powder during PCS process. We apply three types of raw materials, especially for ZnO as semiconductor, Al2O3 as non-conductor and WC as good conductor. The electric current and voltage were measured for each powder during PCS process. In addition, their electric resistance properties were calculated.

Thermoelectric conversion efficiency of thermoelectric elements can be increased by using a structure combining n-type and p-type semiconductors. From the above point of view, attention was directed at ZnO as a candidate n-type semiconductor material and investigations were made. As the result, a dimensionless figure of merit ZT close to 0.28 (1073K) was obtained for specimens produced by the PCS (Pulse Current Sintering) method with addition of specified quantities of , CoO, and to ZnO. It was found that the interstitial in the ZnO restrains the grain growth and CoO acts onto the bond between grains. The influence of the inclusion of and CoO onto the sintering behavior also was investigated.

The influence of the internal current for the ZnO ceramics on the sintering behavior by pulse current sintering (PCS) method was investigated. To clear the dependence of inner current on the sintering behavior of ZnO ceramics, direct measurement of electric resistance of ZnO specimen under sintering by SPS device was carried out. It was observed that electric resistance of specimen decreases with increase in the temperature. The electric resistance begins to decrease from the low temperature of . The internal structure of sintered ZnO ceramics changed by the control of the internal current in the specimen using plate.