The characteristics of ceramics were influenced by the additives and the heat treatment that controls the microcrack behavior at grain boundaries. The effect of additives on ceramics were investigated in terms of mechanical properties and thermal expansion at high temperature. The were synthesized at , and for 2h by reaction sintering. The formation of phase was increased by additives that enhanced the volume of the microcrack that can lead to low thermal expansion. The mechanical properties of the stabilized ceramics were increased remarkably at , and due to the oneset of mechanical healing of grain-bondary microcracks at a high temperature. The amount of microcrack was decreased at lower sintering temperature that causes the increase of mechanical properties at high temperature.

The sol-gel technique has been studied to fabricate a homogeneous Fe-Mo/MgO catalyst. Ambient effects (air, Ar, and H2) on thermal decomposition of the citrate precursor have been systematically investigated to fabricate an Fe-Mo/MgO catalyst. Severe agglomeration of metal catalyst was observed under thermal decomposition of citrate precursor in air atmosphere. Ar/H2 atmosphere effectively restricted agglomeration of bimetallic catalyst and formation of highly-dispersed Fe-Mo/MgO catalyst with high specific surface-area due to the formation of Fe-Mo nanoclusters within MgO support. High-quality thin-multiwalled carbon nanotubes (t-MWCNTs) with uniform diameters were achieved on a large scale by catalytic decomposition of methane over Fe-Mo/MgO catalyst prepared under Ar-atmosphere. The produced t-MWCNTs had outer diameters in the range of 4-8 nm (average diameter ~6.6 nm) and wall numbers in the range of 4-7 graphenes. The as-synthesized t-MWCNTs showed product yields over 450% relative to the utilized Fe-Mo/MgO catalyst, and indicated a purity of about 85%.

The particle size of MgO was examined as a function of the Na content in Mg(OH)2 powders and the calcination temperature. Mg(OH)2 suspension was obtained by dropwise precipitation of Mg(NO3)2·6H2O and NaOH solutions. The suspension was diluted by varying the dilution volume ratio of distilled water to Mg(OH)2 suspension to change the Na salt concentration in the suspension. Mg(OH)2 slurry was filtered and dried at 60˚C under vacuum, and then its Mg(OH)2 powder was calcined to produce MgO with different amount of Na content at 500~900˚C under air. Investigation of the physical and chemical properties of the various MgO powders with dilution ratio and calcination temperature variation was done by X-ray diffraction, transmission electron microscopy, BET specific surface area and thermal gravimetric analysis. It was observed that MgO particle size could depend on the condition of calcination temperature and dilution ratio of the Mg(OH)2 suspension. The particle size of the MgO depends on the Na content remaining in the Mg(OH)2 powder, which powder was prepared by changing the dilution ratio of the Mg(OH)2 suspension. This change increased as the calcination temperature increased and decreased as the dilution ratio increased. The growth of MgO particle size according to the increase of temperature was more effective when there was a relatively high content of Na. The increase of Na content lowered the temperature at which decomposition of Mg(OH)2 to MgO took place, thereby promoting the crystal growth of MgO.

최근 화석에너지의 남용으로 인한 지구온난화문제가 인류가 해결해야 할 지상과제로 대두되고 있으며, 본 연구는 이러한 에너지문제의 해결에 도움이 될 수 있는 고온축열탱크의 개발과 그 성능특성에 관한 내용이다. 지금까지 이에 관한 연구는 그다지 활발하지 않았으며, 특히 고온축열탱크에 관한 연구는 매우 드문 실정이다. 본 연구의 목적은 비교적 열물성이 양호하며 가격이 저렴한 물질인 MgO를 현열축열재로 사용하는 고온축열탱크의 개발이다. 이를 위하여 분말 상태의 MgO를 이용하여 축열벽돌을 제작하고, 실험적 방법을 통하여 MgO를 축열재로 사용하는 고온축열탱크의 성능특성에 관하여 연구하였다. 본 연구를 통하여 현열축열재인 MgO의 고온축열 및 방열성능을 확인하였다.

The autothermal reforming reaction of methane was investigated to produce hyd rogen with Ni/CeO2-ZrO2, Ni/Al2O3-MgO and Ni-Ru/Al2O3-MgO catalysts. Honeycomb metalli c monolith was applied in order to obtain high catalytic activity and stability in autothermal r eforming. The catalysts were characterized by XRD, BET and SEM. The influence of various catalysts on hydrogen production was studied for the feed ratio(O2/CH4, H2O/CH4). The O2/CH4 and H2O/CH4 ratio governed the methane conversion and temperature profile of reactor. Th e reactor temperature increased as the reaction shifted from endothermic to exothermic reactio n with increasing O2/CH4 ratio. Among the catalysts used in the experiment, the Ni-Ru/Al2O3-MgO catalyst showed the highest activity. The 60% of CH4 conversion was obtained, and th e reactor temperature was maintained 600℃ at the condition of GHSV=10000h-1 and feed ratio S/C/O=0.5/1/0.5.

Magnesium hydroxide sulfate hydrate whiskers (, abbreviated 513 MHSH) were prepared using hydrothermal reaction with magnesium oxide (MgO) and magnesium sulfate () as the starting materials. The effects of the molar ratio of /MgO and amount of were studied. As a result, 513 MHSH whiskers co-existed with hexagonal plate at low concentration of . The molar ratio of /MgO was 7:1, uniform 513 MHSH whiskers were formed without impurity such as . Appropriate amount of has affected to formation of high quality MHSH. Their morphologies and structures were determined by powder X-ray diffraction (XRD) scanning electron microscopy (SEM) and thermo-gravimetric analyzer (TGA).

For the present paper, we prepared MgO/MWCNT/TiO2 photocatalyst by using multi-walled carbon nanotubes(MWCNTs) pre-oxidized by m-chlorperbenzoic acid (MCPBA) with magnesium acetate tetrahydrate (Mg(CH2COO)2·4H2O)and titanium n-butoxide (TiOC(CH3)34) as magnesium and titanium precursors. The prepared photocatalyst was analyzed byX-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) analysis. The decompositionof methylene blue (MB) solution was determined under irradiation of ultraviolet (UV) light. The XRD results show that theMgO/MWCNT/TiO2 photocatalyst have cubic MgO structure and anatase TiO2 structure. The porous structure and the TiO2agglomerate coated on the MgO/MWCNT composite can be observed in SEM images. The Mg, O, Ti and C elements can bealso observed in MgO/MWCNT/TiO2 photocatalyst from EDX results. The results of photodegradation of MB solution under UVlight show that the concentration of MB solution decreased with an increase of UV irradiation time for all of the samples. Also,the MgO/MWCNT/TiO2 photocatalyst has the best photocatalytic activity among these samples. It can be considered that theMgO/MWCNT/TiO2 photocatalyst had a combined effect, the effect of MWCNT, which could absorb UV light to create photo-induced electrons (e−), and the electron trapping effect of MgO, which resulted in an increase of the photocatalytic activity of TiO2.

Unreported dielectrics based on the binary system of MgO-SiO2 were investigated as potential candidates for microwave dielectric applications, particularly those demanding a high fired density and high quality factors. Extensive dielectric compositions having different molar ratios of MgO to SiO2, such as 2:1, 3:1, 4:1, and 5:1, were prepared by conventional solid state reactions between MgO and SiO2. 1 mol% of V2O5 was added to aid sintering for improved densification. The dielectric compositions were found to consist of two distinguishable phases of Mg2SiO4 and MgO beyond the 2:1 compositional ratio, which determined the final physical and dielectric properties of the corresponding composite samples. The increase of the ratio of MgO to SiO2 tended to improve fired density and quality factor (Q) without increasing grain size. As a promising composition, the 5MgO.SiO2 sample sintered at 1400 ˚C exhibited a low dielectric constant of 7.9 and a high Q × f (frequency) value of ~99,600 at 13.7 GHz.

In this study, porous electrospun carbon fibers were prepared by electrospinning with PAN and MgCl2, as a MgO precursor. MgO was selected as a substrate because of its chemical and thermal stability, no reaction with carbon, and ease of removal after carbonization by dissolving out in acidic solutions. MgCl2 was mixed with polyacrylonitrile (PAN) solution as a precursor of MgO with various weight ratios of MgCl2/PAN. The average diameter of porous electrospun carbon fibers increased from 1.3 to 3 μm, as the MgCl2 to PAN weight ratio increased. During the stabilization step, MgCl2 was hydrolyzed to MgOHCl by heat treatment. At elevated temperature of 823 K for carbonization step, MgOHCl was decomposed to MgO. Specific surface area and pore structure of prepared electrospun carbon fibers were decided by weight ratio of MgCl2/PAN. The amount of hydrogen storage increased with increase of specific surface area and micropore volume of prepared electrospun carbon fibers.

Composites of gadolinium-doped ceria/magnesia(CGO/MgO) were synthesized and characterized for the electrolytes of intermediate temperature solid oxide fuel cells. XRD and SEM results revealed that composite electrolytes consisted of their own phases after sintering at 1400˚C without noticeable solid solution of Mg into CGO. As the MgO content increased, the total electrical conductivity decreased, which might be attributed to the decrease of grain boundary conductivity, possibly due to the lowering of the continuity of the CGO grains and blocking effects of the insulating MgO phase. The space charge effect may not be a significant factor to affect the electrical conductivity of the CGO/MgO composites.

The effects of an addition of ZrO2 on the microstructure and electrical properties of MgO films as a protective layer for AC plasma display panels were investigated. MgO + a 200 ppm ZrO2 protective layer prepared by e-beam evaporation exhibited a secondary electron emission coefficient (γ) that was improved by 21% compared to that of a pure MgO protective layer. The relative density and Vickers hardness increased with a further addition of ZrO2. These results suggest that the discharge properties and optical properties of MgO protective layers are closely related to the relative density and Vickers hardness. The good optical and electrical properties of γ, at 0.080, a grain size of 19 μm and an optical transmittance of 91.93 % were obtained for the MgO + 200 ppm ZrO2 protective layer sintered at 1700˚C for 5 hrs.

Innovative SMC with low iron loss was made from iron powders with evaporated MgO insulation coating. The coating had greater heat-resistance than conventional phosphatic insulation coating, which enabled stress relieving annealing at higher temperature. Magnetic properties of toroidal samples (OD35mm,ID25mm, t5) were examined. The iron loss at 50Hz for Bm = 1.5T was lower 50% of conventional SMC and was almost the same with silicon iron laminations(t0.35). It became clear that MgO insulation coating has enough heat resistance and adhesiveness to powdersurface to obtain innovative SMC with low iron loss.

The vacuum infiltration method is one of the composite producing methods. There are several parameters in composite production by vacuum infiltration. One of them is particle size of reinforcement in particulate reinforced composites. In this study, MgO powder and Al were used as reinforcement and matrix respectively. MgO powders with different size and amount to give same height were filled in quartz tubes and liquid metal was vacuum infiltrated into the MgO powder under same vacuum condition and for same time. Infiltration height was measured and microstructure and fracture behavior of composite were investigated. It has been found that infiltration height and fracture strength were increased with particulate reinforcement sizes. It has also been determined that molten metal temperature facilitates infiltration.

The synthetic behaviors of carbon nanotubes (CNTs) by Fe/MgO catalysts were investigated in 0~90 wt.% range of MgO mixture ratios by catalytic chemical vapor deposition (CCVD) process. The CNTs were synthesized with 40 minutes of synthetic time, and 923 K of synthetic temperature using 0.1 L/min of ethylene gas and 1.0 L/min of hydrogen gas as synthetic and carrier gas, respectively. As the increase of synthetic temperatures and times, the diameters of CNTs become thicker. The carbon yield showed in a parabolic curve as MgO content increased and the maximum carbon yield was obtained at 30 wt.% of MgO. There were no obvious changes in the diameters of CNTs respect to the change of MgO content. Fe/MgO CNTs showed good crystalinity by High Resolution Transmission Electron microscope (HR-TEM) analysis. The behaviors of Fe/MgO CNTs have a tendency of depending on synthetic time and temperature rather than MgO content.

Sputter Cu(1-4.5at.%Mg) alloy를 100mTorr이하의 산소압력에서 온도를 증가시키며 열처리하였을 때 표연과 계면에서 형성된 MgO의 확산방지막 특성을 살펴보았다 먼저, Cu(Mg)/SiO2/Si 구조의 샘플을 열처리했을 때 계면에서는 2Mg+SiO2→2MgO+Si의 화학반응에 의해 MgO가 형성되는데 이 MgO충에 의해 Cu가 SiO2로 확산되는 것이 현저하게 감소하였다. TiN/Si 기판 위에서도 Cu(Mg)과 TiN 계면에 MgO가 형성되어 Cu(4.5at.%Mg)의 경우 800˚C까지 Cu와 Si의 확산을 방지할 수 있었다. 표면에 형성된 MgO위에 Si을 증착하여 Si/MgO(150 Å)/Cu(Mg)/SiO2/Si구조로 만든 후 열처리했을 때 150 Å의 MgO는 700˚C까지 Si과 Cu의 확산을 방지할 수 있었다. 표면에 형성된 MgO(150 Å)의 누설전류특성은 break down 5V, 누설전류 10-7A/cm2의 값을 나타냈다. 또한 Si3N4/MgO 이중구조에서는 매우 낮은 누설전류밀도를 나타냈으며 MgO에 의해 Si3N4 증착시 안정적인 계면이 형성됨을 확인하였다.